CN109233072A - A kind of PE plastic barrel - Google Patents

A kind of PE plastic barrel Download PDF

Info

Publication number
CN109233072A
CN109233072A CN201811191031.4A CN201811191031A CN109233072A CN 109233072 A CN109233072 A CN 109233072A CN 201811191031 A CN201811191031 A CN 201811191031A CN 109233072 A CN109233072 A CN 109233072A
Authority
CN
China
Prior art keywords
parts
plastic barrel
plastic
polyethylene
antioxidant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811191031.4A
Other languages
Chinese (zh)
Inventor
汤荣耀
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangmen Henglong Plastic Products Co Ltd
Original Assignee
Jiangmen Henglong Plastic Products Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangmen Henglong Plastic Products Co Ltd filed Critical Jiangmen Henglong Plastic Products Co Ltd
Priority to CN201811191031.4A priority Critical patent/CN109233072A/en
Publication of CN109233072A publication Critical patent/CN109233072A/en
Pending legal-status Critical Current

Abstract

The invention belongs to a kind of methods of plastic material processing, more particularly to a kind of PE plastic barrel, including following parts by weight raw material: 75-90 parts of polyethylene, 40-45 parts of polyvinyl chloride, 17-25 parts of vinyltrimethoxysilane, 15-20 parts of polyethylene octene elastomer, 20-25 parts of polyether-ketone, 20-25 parts of silicon carbide, 20-25 parts of butyronitrile, 15-20 parts of hesperetin, 25-30 parts of plasticized modifier, 7-15 parts of reinforced modifier, 0.1-0.4 parts of lubricant, 0.7-1.0 parts of antioxidant, kaolin 10-15 parts of burning, 3.0-3.5 parts of adipic acid propanediol polyester, peroxidating is hesitated 5-8 parts of propyl benzene alcohol, 10-20 parts of vinyl acetate, 0.3-1.5 parts of fire retardant and ultraviolet absorbing agent 0.7-1 .0 part；Raw material is put into high-speed mixer and is stirred 45min, mixture is made；Extrusion plastic particle again；Plastic grain is put into blow moulding machine, squeezes out blank；By blow molding machine mold, PE plastic barrel is made.The present invention provides a kind of PE plastic barrel, and plastic barrel either intensity or toughness is enabled to all to be greatly improved.

Description

A kind of PE plastic barrel
Technical field
The invention belongs to a kind of methods of plastic material processing, and in particular to a kind of PE plastic barrel.
Background technique
The material for being used to prepare plastic barrel mostly uses the thermoplastics such as polyethylene (PE), polypropylene (PE), usually adopts It is made with blow molding, injection molding, is chiefly used in containing the industries liquid, solids such as chemical industry, pesticide, medicine, food, hardware electronics, electromechanics Product；PE base plastic barrel hardness, modulus and in terms of have outstanding performance, be more suitable for doing structural material use.Existing skill For art since PE black brittleness is poor, notch impact strength is low, haveed the defects that by plastic barrel prepared by PE substrate it is certain, therefore how Can be improved its toughness is a problem to be solved.
The present invention provides a kind of PE plastic barrels, so that the service performance of plastic barrel in all respects is greatly improved.
Summary of the invention
It is another object of the invention to provide a kind of PE plastic barrels, enable to plastic barrel either intensity or toughness All it is greatly improved.
To solve the above-mentioned problems, the present invention provides a kind of PE plastic barrels, including following parts by weight raw material:
75-90 parts of polyethylene, 40-45 parts of polyvinyl chloride, 17-25 parts of vinyltrimethoxysilane, polyethylene octene are total 15-20 parts of elastomer, 20-25 parts of polyether-ketone, 20-25 parts of silicon carbide, 20-25 parts of butyronitrile, 15-20 parts of hesperetin, toughening modifying 25-30 parts of agent, 7-15 parts of reinforced modifier, 0.1-0.4 parts of lubricant, 0.7-1.0 parts of antioxidant, 10-15 parts of calcium carbonate, oneself 3.0-3.5 parts of diacid propanediol polyester, peroxidating half-heartedness 5-8 parts of propyl benzene alcohol, 10-20 parts of vinyl acetate, fire retardant 0.3-1.5 Part, 1-2 parts of calcium zinc stabilizer and 0.7-1.0 parts of ultraviolet absorbing agent；
Above-mentioned raw materials are put into high-speed mixer and are stirred, 45min is stirred at a temperature of 100-120 DEG C, mixing is equal It is even at mixture；
Above-mentioned mixture is placed in twin screw extruder hopper, extrusion plastic particle；
Plastic grain is put into blow moulding machine, blow moulding machine barrel temperature is set as 100 DEG C, squeezes out blank；
Blank is put into blow molding machine mold, PE plastic barrel is made.
Wherein, the first groove is arranged in the one side wall of the PE plastic barrel, stores a bung in first groove.
Preferably, the second groove is arranged in another side wall of the PE plastic barrel, and phosphor strip is arranged in second groove.
Preferably, the PE plastic barrel is horizontally arranged with multiple reinforcing ribs.
Preferably, the plasticized modifier includes that inorganic nano-particle toughening epoxy resin or Inorganic Superfine Particles increase Tough polymer.
Preferably, the reinforced modifier includes maleic anhydride inoculated polypropylene and glass fibre.
Preferably, the lubricant is paraffin and stearic mixture, the paraffin and the stearic substance Amount ratio be 1:1.
Preferably, the antioxidant antioxidant 1010
Preferably, the fire retardant is tributyl phosphate.
Preferably, including following parts by weight raw material:
80-85 parts of polyethylene, 42-43 parts of polyvinyl chloride, 19-23 parts of vinyltrimethoxysilane, polyethylene octene are total 15-20 parts of elastomer, 21-24 parts of polyether-ketone, 20-25 parts of silicon carbide, 20-25 parts of butyronitrile, 15-20 parts of hesperetin, toughening modifying 27-28 parts of agent, 10-15 parts of reinforced modifier, 0.2-0.4 parts of lubricant, 0.8-1.0 parts of antioxidant, 10-12 parts of calcium carbonate, 3.0-3.5 parts of adipic acid propanediol polyester, peroxidating half-heartedness 5-8 parts of propyl benzene alcohol, 15-20 parts of vinyl acetate, fire retardant 1.0-1.5 Part, 1.5-2 parts of calcium zinc stabilizer and 0.8-1.0 parts of ultraviolet absorbing agent.
Preferably, including following parts by weight raw material:
83 parts of polyethylene, 42 parts of polyvinyl chloride, 20 parts of vinyltrimethoxysilane, polyethylene octene elastomer 18 Part, 23 parts of polyether-ketone, 21 parts of silicon carbide, 25 parts of butyronitrile, 17 parts of hesperetin, 28 parts of plasticized modifier, 13 parts of reinforced modifier, profit 0.3 part of lubrication prescription, 0.8 part of antioxidant, 10 parts of calcium carbonate, 3.0 parts of adipic acid propanediol polyester, 7 parts of propyl benzene alcohol of peroxidating half-heartedness, 18 parts of vinyl acetate, 1.3 parts of fire retardant, 1 part of calcium zinc stabilizer and 0.9 part of ultraviolet absorbing agent.
Beneficial effects of the present invention
1, the plasticized modifier of a kind of PE plastic barrel provided by the invention, addition can be improved the toughness of plastic barrel, add The reinforced modifier added can be improved the intensity of plastic barrel, to realize, to improve its while not reducing PE original intensity tough The effect of property.
2, reinforcing rib is used in a kind of PE plastic barrel provided by the invention, plastic barrel can be prevented to be squeezed in use process Compressive strain.
3, a kind of PE plastic barrel provided by the invention, uses lubricant, can be improved the lustrous surface of plastic barrel product Degree.
Specific embodiment
The present invention is described in further detail below, to enable those skilled in the art's refer to the instruction text being capable of evidence To implement.
To solve the above-mentioned problems, the present invention provides a kind of PE plastic barrels, including following parts by weight raw material:
75-90 parts of polyethylene, 40-45 parts of polyvinyl chloride, 17-25 parts of vinyltrimethoxysilane, polyethylene octene are total 15-20 parts of elastomer, 20-25 parts of polyether-ketone, 20-25 parts of silicon carbide, 20-25 parts of butyronitrile, 15-20 parts of hesperetin, toughening modifying 25-30 parts of agent, 7-15 parts of reinforced modifier, 0.1-0.4 parts of lubricant, 0.7-1.0 parts of antioxidant, 10-15 parts of calcium carbonate, oneself 3.0-3.5 parts of diacid propanediol polyester, peroxidating half-heartedness 5-8 parts of propyl benzene alcohol, 10-20 parts of vinyl acetate, fire retardant 0.3-1.5 Part, 1-2 parts of calcium zinc stabilizer and 0.7-1.0 parts of ultraviolet absorbing agent；
Above-mentioned raw materials are put into high-speed mixer and are stirred, 45min is stirred at a temperature of 100-120 DEG C, mixing is equal It is even at mixture；
Above-mentioned mixture is placed in twin screw extruder hopper, extrusion plastic particle；
Plastic grain is put into blow moulding machine, blow moulding machine barrel temperature is set as 100 DEG C, squeezes out blank；
Blank is put into blow molding machine mold, PE plastic barrel is made.
Wherein, the first groove is arranged in the one side wall of the PE plastic barrel, stores a bung in first groove.
Above-mentioned chemical raw material includes that plasticized modifier, reinforced modifier, lubricant, antioxidant and ultraviolet light are inhaled certainly Receiving agent has good toughness and intensity by plastic barrel made from premix, mixture, extrusion and injection molding, respectively The defects such as kind auxiliary agent cooperates, synergistic effect, and the weatherability of improvement PE itself is poor, toughness is low.The spare bung of side wall setting, After anti-lost bung, carrys out lid plastic barrel without the bung of suitable model, cause inconvenient for use.
On the basis of above situation, another embodiment, the PE plastic barrel is horizontally arranged with multiple reinforcing ribs.
So that molding plastic products are not deformed in use process.
On the basis of the above embodiments, the second groove is arranged in another side wall of another embodiment, the PE plastic barrel, Phosphor strip is set in second groove.
When being convenient for electricity failure at night in this way, plastic barrel is used.
On the basis of the above embodiments, another embodiment, the plasticized modifier include inorganic nano-particle toughening Epoxy resin or Inorganic Superfine Particles toughening polymer.
Inorganic nano-particle toughening epoxy resin, i.e. nanoparticle have the performances such as epoxy resin toughness, intensity, rigidity It increases substantially.Nano-meter CaCO33Epoxy resin toughened key is evenly dispersed, mechanical stirring nm CaCO3Dispersion particle diameter about Tens microns；The nm CaCO dispersed through ultrasonic activation3The about several microns of dispersion particle diameter；With 5% silane coupling agent.(KH- 550/ ethyl alcohol) processing nmCaCO3(110-120 DEG C of dry 1h) dispersion particle diameter about 100nm.
Inorganic Superfine Particles toughening polymer, i.e. Inorganic Superfine Particles toughening adhesive are an effective methods, A possibility that Inorganic Superfine Particles surface non-matching atom is more, is physically or chemically combined with polymer generation are big, enhance particle And the combination of basal body interface, thus certain load can be born, have the function of enhancing, toughening.
On the basis of the above embodiments, another embodiment, the reinforced modifier include maleic anhydride grafting poly- third Alkene and glass fibre.
Reinforced modifier includes maleic anhydride inoculated polypropylene and glass fibre, and glass fibre has good heat resistance And mechanical strength, but because it is bad with the compatibility of PE, the maleic anhydride grafting added in reinforced modifier is poly- Propylene can greatly improve glass fibre and the compatibility and glass fibre of PE as the coupling agent between glass fibre and PE Dispersibility；Reinforced modifier and plasticized modifier cooperate, and collaboration improves the intensity and toughness of PE.
On the basis of the above embodiments, another embodiment, the lubricant are paraffin and stearic mixture, institute The ratio for stating the amount of paraffin and the stearic substance is 1:1.
The effect of external lubricant mainly improves the andfrictional conditions of the hot metal surface of polymer melt and equipment, makes plastic It is easy demoulding, it is poor with the compatibility of polymer, is easy toward external migration from melt, can be in melt and mould in forming process One layer of very thin isolation film is formed between tool, and plastics is made to be not stick to die surface.In-lubricant and polymer have good compatibility, It polymeric inner play a part of reduce polymer molecule between cohesive force, so as to improve plastic melt internal frictional heat generation and The mobility of melt.In-lubricant and the intermolecular combination of polymer long-chain be it is not strong, they there may be similar to roll The effect of bearing, therefore its own can be arranged on melt flows direction, thus slide over each other, so that internal friction reduces, this The mechanism lubricated in being exactly.
The lubricant that the present invention uses lubricates manufactured product appearance more, and the lines flow smoothly.
On the basis of the above embodiments, another embodiment, the antioxidant antioxidant 1010
By using above scheme, antioxidant 1010 is phenolic antioxidant, is one of outstanding kind of current antioxidant, right Polyethylene has brilliant antioxygenic property, can effectively extend the service life of product；Volatility is very low, and not easy to migrate, It can be effectively prevented thermal oxidative degradation of polymer material during long-term ageing, while being also a kind of efficient processing and lubrication Agent can improve discoloration-resistant of polymer material under the conditions of high temperature process.
On the basis of the above embodiments, another embodiment, the fire retardant are tributyl phosphate.
For high molecular material flame resistance can be increased, prolong the service life.
On the basis of the above embodiments, another embodiment, including following parts by weight raw material:
80-85 parts of polyethylene, 42-43 parts of polyvinyl chloride, 19-23 parts of vinyltrimethoxysilane, polyethylene octene are total 15-20 parts of elastomer, 21-24 parts of polyether-ketone, 20-25 parts of silicon carbide, 20-25 parts of butyronitrile, 15-20 parts of hesperetin, toughening modifying 27-28 parts of agent, 10-15 parts of reinforced modifier, 0.2-0.4 parts of lubricant, 0.8-1.0 parts of antioxidant, 10-12 parts of calcium carbonate, 3.0-3.5 parts of adipic acid propanediol polyester, peroxidating half-heartedness 5-8 parts of propyl benzene alcohol, 15-20 parts of vinyl acetate, fire retardant 1.0-1.5 Part, 1.5-2 parts of calcium zinc stabilizer and 0.8-1.0 parts of ultraviolet absorbing agent.
On the basis of the above embodiments, another embodiment, including following parts by weight raw material:
83 parts of polyethylene, 42 parts of polyvinyl chloride, 20 parts of vinyltrimethoxysilane, polyethylene octene elastomer 18 Part, 23 parts of polyether-ketone, 21 parts of silicon carbide, 25 parts of butyronitrile, 17 parts of hesperetin, 28 parts of plasticized modifier, 13 parts of reinforced modifier, profit 0.3 part of lubrication prescription, 0.8 part of antioxidant, 10 parts of calcium carbonate, 3.0 parts of adipic acid propanediol polyester, 7 parts of propyl benzene alcohol of peroxidating half-heartedness, 18 parts of vinyl acetate, 1.3 parts of fire retardant, 1 part of calcium zinc stabilizer and 0.9 part of ultraviolet absorbing agent.
On the basis of the above embodiments, another embodiment, including following parts by weight raw material:
80 parts of polyethylene, 43 parts of polyvinyl chloride, 23 parts of vinyltrimethoxysilane, polyethylene octene elastomer 20 Part, 24 parts of polyether-ketone, 25 parts of silicon carbide, 25 parts of butyronitrile, 20 parts of hesperetin, 28 parts of plasticized modifier, 15 parts of reinforced modifier, profit 0.4 part of lubrication prescription, 1.0 parts of antioxidant, 12 parts of calcium carbonate, 3.5 parts of adipic acid propanediol polyester, 8 parts of propyl benzene alcohol of peroxidating half-heartedness, 20 parts of vinyl acetate, 1.5 parts of fire retardant, 2 parts of calcium zinc stabilizer and 1.0 parts of ultraviolet absorbing agent.
On the basis of the above embodiments, another embodiment, including following parts by weight raw material:
85 parts of polyethylene, 43 parts of polyvinyl chloride, 19 parts of vinyltrimethoxysilane, polyethylene octene elastomer 15 Part, 21 parts of polyether-ketone, 20 parts of silicon carbide, 20 parts of butyronitrile, 15 parts of hesperetin, 27 parts of plasticized modifier, 10 parts of reinforced modifier, profit 0.2 part of lubrication prescription, 0.8 part of antioxidant, 10 parts of calcium carbonate, 3.0 parts of adipic acid propanediol polyester, 5 parts of propyl benzene alcohol of peroxidating half-heartedness, 15 parts of vinyl acetate, 1.0 parts of fire retardant, 1.5 parts of calcium zinc stabilizer and 0.8 part of ultraviolet absorbing agent.
On the basis of the above embodiments, another embodiment, including following parts by weight raw material:
84 parts of polyethylene, 42 parts of polyvinyl chloride, 22 parts of vinyltrimethoxysilane, polyethylene octene elastomer 19 Part, 22 parts of polyether-ketone, 23 parts of silicon carbide, 23 parts of butyronitrile, 18 parts of hesperetin, 27 parts of plasticized modifier, 11 parts of reinforced modifier, profit 0.35 part of lubrication prescription, 0.9 part of antioxidant, 11 parts of calcium carbonate, 3.0 parts of adipic acid propanediol polyester, peroxidating half-heartedness propyl benzene alcohol 6 Part, 19 parts of vinyl acetate, 1.4 parts of fire retardant, 1.6 parts of calcium zinc stabilizer and 0.8 part of ultraviolet absorbing agent.
Inventive formulation is simple, reasonable, and the manufactured anti-toughness of plastic barrel is high through the invention, impact effect is good, and intensity is high, Production cost is low, there is preferable practicability, there is preferable market prospects, convenient for promoting the use of.
The present invention is used cooperatively by each component, substantially enhances intensity, abrasivity and the toughness of plastic barrel, is solved The plasticiser toxicity problem of original plastic barrel.
Moreover, the used raw material of the present invention is common industrial chemicals, and cheap, production cost is low.
Although the embodiments of the present invention have been disclosed as above, but its is not only in the description and the implementation listed With it can be fully applied to various fields suitable for the present invention, for those skilled in the art, can be easily Realize other modification, therefore without departing from the general concept defined in the claims and the equivalent scope, the present invention is simultaneously unlimited In specific details and embodiment shown and described herein.

Claims (10)

1. a kind of PE plastic barrel, which is characterized in that including following parts by weight raw material:
75-90 parts of polyethylene, 40-45 parts of polyvinyl chloride, 17-25 parts of vinyltrimethoxysilane, polyethylene octene are elastic altogether 15-20 parts of body, 20-25 parts of polyether-ketone, 20-25 parts of silicon carbide, 20-25 parts of butyronitrile, 15-20 parts of hesperetin, plasticized modifier 25- 30 parts, 7-15 parts of reinforced modifier, 0.1-0.4 parts of lubricant, 0.7-1.0 parts of antioxidant, 10-15 parts of calcium carbonate, adipic acid 3.0-3.5 parts of propanediol polyester, peroxidating half-heartedness 5-8 parts of propyl benzene alcohol, 10-20 parts of vinyl acetate, 0.3-1.5 parts of fire retardant, calcium 1-2 parts and ultraviolet absorbing agent 0.7-1.0 parts of zinc stabilizer；
Above-mentioned raw materials are put into high-speed mixer and are stirred, 45min is stirred at a temperature of 100-120 DEG C, is mixed into Mixture；
Above-mentioned mixture is placed in twin screw extruder hopper, extrusion plastic particle；
Plastic grain is put into blow moulding machine, blow moulding machine barrel temperature is set as 100 DEG C, squeezes out blank；
Blank is put into blow molding machine mold, PE plastic barrel is made.
Wherein, the first groove is arranged in the one side wall of the PE plastic barrel, stores a bung in first groove.
2. PE plastic barrel as described in claim 1, which is characterized in that another side wall setting second of the PE plastic barrel is recessed Slot, second groove is interior to be arranged phosphor strip.
3. PE plastic barrel as described in claim 1, which is characterized in that the PE plastic barrel is horizontally arranged with multiple reinforcements Muscle.
4. PE plastic barrel as described in claim 1, which is characterized in that the plasticized modifier includes inorganic nano-particle toughening Epoxy resin or Inorganic Superfine Particles toughening polymer.
5. PE plastic barrel as described in claim 1, which is characterized in that the reinforced modifier includes maleic anhydride grafting poly- third Alkene and glass fibre.
6. PE plastic barrel as described in claim 1, which is characterized in that the lubricant is paraffin and stearic mixture, The ratio of the amount of the paraffin and the stearic substance is 1:1.
7. PE plastic barrel as described in claim 1, which is characterized in that the antioxidant antioxidant 1010.
8. PE plastic barrel as described in claim 1, which is characterized in that the fire retardant is tributyl phosphate.
9. PE plastic barrel as described in claim 1, which is characterized in that including following parts by weight raw material:
80-85 parts of polyethylene, 42-43 parts of polyvinyl chloride, 19-23 parts of vinyltrimethoxysilane, polyethylene octene are elastic altogether 15-20 parts of body, 21-24 parts of polyether-ketone, 20-25 parts of silicon carbide, 20-25 parts of butyronitrile, 15-20 parts of hesperetin, plasticized modifier 27- 28 parts, 10-15 parts of reinforced modifier, 0.2-0.4 parts of lubricant, 0.8-1.0 parts of antioxidant, 10-12 parts of calcium carbonate, adipic acid 3.0-3.5 parts of propanediol polyester, peroxidating half-heartedness 5-8 parts of propyl benzene alcohol, 15-20 parts of vinyl acetate, 1.0-1.5 parts of fire retardant, calcium 1.5-2 parts and ultraviolet absorbing agent 0.8-1.0 parts of zinc stabilizer.
10. PE plastic barrel as described in claim 1, which is characterized in that including following parts by weight raw material:
83 parts of polyethylene, 42 parts of polyvinyl chloride, 20 parts of vinyltrimethoxysilane, gathers at 18 parts of polyethylene octene elastomer 23 parts of ether ketone, 21 parts of silicon carbide, 25 parts of butyronitrile, 17 parts of hesperetin, 28 parts of plasticized modifier, 13 parts of reinforced modifier, lubricant 0.3 part, 0.8 part of antioxidant, 10 parts of calcium carbonate, 3.0 parts of adipic acid propanediol polyester, peroxidating half-heartedness 7 parts of propyl benzene alcohol, acetic acid 18 parts of ethylene, 1.3 parts of fire retardant, 1 part of calcium zinc stabilizer and 0.9 part of ultraviolet absorbing agent.
CN201811191031.4A 2018-10-12 2018-10-12 A kind of PE plastic barrel Pending CN109233072A (en)