CN109228780A - A kind of inner wall has silver layer or the glassware of layer gold and preparation method thereof - Google Patents
A kind of inner wall has silver layer or the glassware of layer gold and preparation method thereof Download PDFInfo
- Publication number
- CN109228780A CN109228780A CN201811103813.8A CN201811103813A CN109228780A CN 109228780 A CN109228780 A CN 109228780A CN 201811103813 A CN201811103813 A CN 201811103813A CN 109228780 A CN109228780 A CN 109228780A
- Authority
- CN
- China
- Prior art keywords
- glassware
- layer
- silver
- gold
- paste
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of inner walls to have silver layer or the glassware of layer gold and preparation method thereof, makes production method of the glassware internal chamber wall with silver layer or layer gold the object of the present invention is to provide a kind of.The binding force of production method environmental protection, silver or gold and glass carrier is strong, simple production process.And raw material can be saved, brightness is high, and stereoscopic effect is good.By production production step by step, such a inner wall has just completed (glassware) with the glassware of silver layer or layer gold.
Description
Technical field
The production method that technical field is related to glassware class and noble silver or golden combined process.
Background technique:
Glass is that have sparkling and crystal-clear magnificent fine and glossy colorful substance, is lived using all kinds of nature of glass made of various fashion skills
Vessel are had uniqueness, plastic arts and are widely used in people's lives and social activities using function, not only
Technique is exquisite, and has very much Cultural Implication.
Silver and gold are rare metals, there is saying for the symbol of wealth from ancient times.And with disinfection and sterilization, the function promoted longevity
Effect.Increase silver layer or layer gold in glassware class internal chamber wall, and with exquisite auspicious pattern, making glassware more seems exquisite
It is exquisitely carved, show wealth and rank.Make people while using glassware, the pursuit for health of having got back collects practical, ornamental, collection
It is integrated.
Summary of the invention:
The purpose of the present invention is provide a kind of system for making glassware internal chamber wall with silver layer or layer gold regarding to the issue above
Make method.The binding force of production method environmental protection, silver or gold and glass carrier is strong, simple production process.And raw material can be saved,
Brightness is high, and stereoscopic effect is good.
Technique production process:
1, finished glass vessel spare (such as glass teapot, handleless teacup, teacup, the wine for meeting national food hygienic standard are selected
Pot, wine cup etc.).
2, super fine silver powder (fineness is in 1900-2100 mesh) or ultrafine gold powder (fineness is in 1900-2100 mesh), acetic acid second are selected
Ester solution, resin binder, super-fine zinc dust (fineness is in 1900-2100 mesh).By super fine silver powder or bronze, super-fine zinc dust, acetic acid
Ethyl ester, resin binder reconcile together in proportion.It is mixed at a temperature of placing it in 15-25 DEG C, stirs 3-5 minutes, silver is made
Slurry or gold paste.The viscosity of reconciliation is suitble to be sprayed subject to mist with R2 type gas spray gun, and silver paste or gold paste is made with above-mentioned raw materials blending
It is spare.
Silver paste formula and ratio:
7.5 grams of silver powder of (1900-2100 mesh), 2.5 grams of zinc powder, ethyl acetate 20ml of (1900-2100 mesh), resin binder
10ml is placed at a temperature of 15-25 DEG C after mixing its four kinds of raw materials, stirs 3-5 minutes, silver paste is made.
Gold paste formula and ratio:
7.5 grams of bronze of (1900-2100 mesh), 2.5 grams of zinc powder, ethyl acetate 20ml of (1900-2100 mesh), resin binder
10ml is placed at a temperature of 15-25 DEG C after mixing its four kinds of raw materials, stirs 3-5 minutes, gold paste is made.
3, it selects 0.1mm thin plastic piece or 0.1mm thin metal piece to be fabricated to, is suitble to paste glassware internal chamber wall table
The picture of the hollow out auspicious pattern in face, made hollow out picture will be accorded with according to the shape of glassware luminal wall surface, area
Conjunction requires spare.
4, clean up the dust dirt of glassware luminal wall surface with pure water, and with 2KW hand electric dryer or
It is placed in 50-100 DEG C of heating in 101 type 4KW air dry ovens, to constant temperature 1-2 hours, drying or drying glassware internal chamber wall table
The residual moisture content in face.
5, it by the hollow out picture of manufactured certain specification, is uniformly smeared with hairbrush in reverse side and obtains viscose binder more one layer,
The one side for being coated with adhesive is uniformly tightly attached to the place of required stickup on the surface of glassware internal chamber wall.
6, the silver paste prepared or gold paste are uniformly sprayed on to the glassware for posting pierced pattern picture with R2 type gas spray gun
(can also be sprayed on the surface of glassware internal chamber wall of not textures piece) on the surface of internal chamber wall, or with flat hairbrush smear silver paste or
Gold paste can also.
It is 7, inner wall surface being pasted with hollow out picture (or there be not paste picture) and sprayed the glassware of silver paste or gold paste,
It is placed in 101 type 4KW air dry ovens, is heated to 30-50 DEG C, constant temperature 30-60 minutes, to silver slurry layer or gold paste layer solidization
After take out.If you need to increase thickness, above-mentioned spraying can be repeated several times or smear operation.
8, it is clamped with metal tweezers, the hollow out picture on glassware luminal wall surface is thrown off, in glassware inner wall
Solidization silver powder layer required for surface is formed or bronze layer luckiness pierced pattern, it is desirable that patterned sides are along neat and clear, exposing
Glassware part the bright noresidue in inner wall part.
9, the surface of inner wall is placed on the glassware of dry silver powder layer or bronze layer pattern (or there be not pattern) box
In 15KW Elema resistance furnace high-temperature heating equipment, it is heated to 500-700 DEG C, is taken out after constant temperature 1-2 hours, makes glassware
The surface of internal chamber wall forms the silver layer or layer gold (or after not patterned silver layer or layer gold) of pierced pattern, and room temperature is down in placement.
10,150 mesh flap wheels and fiber polishing wheel on grinding machine flexible axle are hung with 220V, cleans out silver layer or layer gold surface
To clean and tidy, patterned sides along neatly, product is made to meet the requirements.
11, remove what the extra other places of silver powder or bronze and glassware generated in operation generated in operation
Dirt is packed and stored after qualified by inspection.
Such a inner wall has just completed (glassware) with the glassware of silver layer or layer gold.
Specific embodiment
It is next combined with specific embodiments below that the present invention will be further described.
Embodiment
1, finished glass vessel spare (such as glass teapot, handleless teacup, teacup, the wine for meeting national food hygienic standard are selected
Pot, wine cup etc.)；
2, super fine silver powder (fineness is in 1900-2100 mesh) or ultrafine gold powder (fineness is in 1900-2100 mesh), acetic acid second are selected
Ester solution, resin binder, super-fine zinc dust (fineness is in 1900-2100 mesh).By super fine silver powder or bronze, super-fine zinc dust, acetic acid
Ethyl ester, resin binder reconcile together in proportion.It places it at a temperature of 15-25 DEG C, stirs 3-5 minutes.The viscosity of reconciliation
It is suitble to be sprayed subject to mist with R2 type gas spray gun, silver paste is made with above-mentioned raw materials blending or gold paste is spare；
Silver paste or gold paste configuration proportion are as follows:
(- 2100 mesh of 1900 mesh) silver powder or 7.5 grams of bronze, 2.5 grams of zinc powder, ethyl acetate 20ml of (1900-2100 mesh), tree
Rouge adhesive 10ml, after mixing, is set at 15-25 DEG C, stirs 3-5 minutes, silver paste or gold paste is made.
3, it selects 0.1mm thin plastic piece or 0.1mm thin metal piece to be fabricated to, is suitble to paste glassware internal chamber wall table
The picture of the hollow out auspicious pattern in face, made hollow out picture will be accorded with according to the shape of glassware luminal wall surface, area
Conjunction requires spare；
4, clean out the dust dirt of glassware luminal wall surface with pure water, and with 2KW hand electric dryer or
It is placed in 101 type 4KW electric drying oven with forced convections and is heated to 50 DEG C -100 DEG C, constant temperature 1-2 hours, dry up or dry glassware inner cavity
Residual moisture content on wall surface；
5, it by the hollow out picture of manufactured certain specification, is uniformly smeared with hairbrush in reverse side and obtains viscose binder more one layer,
The one side for being coated with adhesive is uniformly tightly attached to the place of stickup required for the surface of glass internal chamber wall；
6, the silver paste prepared or gold paste are uniformly sprayed on to the glassware inner cavity for posting pierced pattern with R2 type gas spray gun
It (can also be sprayed on the surface of glassware internal chamber wall of not textures piece) on the surface of wall, or smear silver paste or gold paste with flat hairbrush
It can also.
7, glassware that is hollow out picture (or there be not textures piece) and having sprayed silver paste or gold paste is posted on the surface of internal chamber wall
It is placed in 101 type 4KW air dry ovens, is heated to 30-50 DEG C, constant temperature 30-60 minutes, to silver slurry layer or gold paste layer solidization
After take out.If you need to increase thickness, above-mentioned spraying can be repeated several times or smear operation.
8, it is clamped with metal tweezers, the hollow out picture of glassware luminal wall surface is thrown off, in the table of glassware inner wall
It is formed on face and does cured silver powder layer or bronze layer luckiness pierced pattern (or the dry silver powder layer or bronze layer for not having textures), it is desirable that figure
Case edge is neat and clear, the bright noresidue in luminal wall surface part of the glassware part of exposing.
9, the surface of internal chamber wall is placed on the glassware of dry silver powder layer or dry bronze layer pattern (or there be not pattern)
In box 15KW Elema resistance furnace high-temperature heating equipment, it is heated to 500-700 DEG C, is taken out after constant temperature 1-2 hours, makes glass
The surface of vessel internal chamber wall forms the silver layer or layer gold (or not patterned silver layer or layer gold) for having pierced pattern, and placement is down to
Room temperature.
10,150 mesh flap wheels and fiber polishing wheel on grinding machine flexible axle are hung with 220V, cleans out glassware internal chamber wall
Silver layer or layer gold surface to clean and tidy, it is desirable that figuratum edge is neat, and product be made to meet the requirements；
11, remove what the extra other places of silver powder or bronze and glassware generated in operation generated in operation
Dirt is packed and stored after qualified by inspection,
Such a inner wall has just completed (glassware) with the glassware of silver layer or layer gold.
Glassware class of the present invention, super fine silver powder, ultrafine gold powder, super-fine zinc dust, resin binder, ethyl acetate
And the markets such as forced air drying heating, heating equipment and loop wheel machine are commercially available.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Made any modifications, equivalent replacements, and improvements etc., should all be included in the protection scope of the present invention within mind and principle.
Claims (1)
1. a kind of inner wall has silver layer or the glassware of layer gold and preparation method thereof, comprising the following steps:
1, finished glass vessel spare (such as glass teapot, handleless teacup, teacup, wine pot, the wine for meeting national food hygienic standard are selected
Cup etc.).
2, selection super fine silver powder (fineness is in 1900-2100 mesh) or bronze (fineness is in 1900-2100 mesh), ethyl acetate solution,
Resin binder, super-fine zinc dust (fineness is in 1900-2100 mesh).By super fine silver powder or bronze, super-fine zinc dust, ethyl acetate, tree
Rouge adhesive is concocted together in proportion, is placed it at a temperature of 15-25 DEG C, stirs 3-5 minutes, silver paste or gold paste is made, and is adjusted
The viscosity of sum is suitble to be sprayed subject to mist with R2 type gas spray gun, and silver paste is made with above-mentioned raw materials blending or gold paste is spare.
Silver paste or gold paste formula and ratio:
(1900-2100 mesh) silver powder or 7.5 grams of bronze, 2.5 grams of zinc powder, ethyl acetate 20ml of (1900-2100 mesh), resin-bonding
Agent 10ml is placed at a temperature of 15-25 DEG C after mixing its above raw material, stirs 3-5 minutes, silver paste or gold paste is made.
3, it selects 0.1mm thin plastic piece or 0.1mm thin metal piece to be fabricated to, is suitble to paste glassware luminal wall surface
The picture of hollow out auspicious pattern, made hollow out picture will be wanted according to the shape of glassware luminal wall surface, area coinciding
It asks for perfection use.
4, the dust dirt of glassware luminal wall surface is cleaned out with pure water, and with hand-held 2KW hair drier or is placed in
It is heated to 50-100 DEG C in 101 type 4KW air dry ovens, constant temperature 1-2 hours, dries up or dry glassware luminal wall surface
Remain moisture content.
5, it by the hollow out picture of manufactured certain specification, is uniformly smeared with hairbrush in reverse side and obtains viscose binder more one layer, will applied
It is wiped with the one sides for obtaining viscose binder more and is uniformly tightly attached to the place pasted required for the surface of glassware internal chamber wall.
6, the silver paste prepared or gold paste are uniformly sprayed on to the glassware internal chamber wall for posting pierced pattern with R2 type gas spray gun
It (can also be sprayed on the surface of glassware internal chamber wall of not textures piece) on surface, or smear silver paste or gold paste with flat hairbrush
It can.
7, glassware that is hollow out picture (or there be not textures piece) and having sprayed silver paste or gold paste is posted on the surface of internal chamber wall, places
In 101 type 4KW air dry ovens, 30-50 DEG C is heated, constant temperature 30-60 minutes, is taken after silver slurry layer or gold paste layer solidization
Out.If you need to increase thickness, the operation of above-mentioned spraying or smearing can be repeated several times.
8, it is clamped with metal tweezers, the hollow out picture of glassware luminal wall surface is thrown off, on the surface of glassware inner wall
Solidization silver powder layer required for being formed or bronze layer luckiness pierced pattern, it is desirable that patterned sides are along neat and clear, the glass of exposing
Glass vessel local interior wall part is clean and tidy bright (do not have textures piece does not reveal glass bottom).
9, the glassware of the silver powder layer by inner wall with solidization or bronze layer pattern (or not having pattern) is placed on box 15KW
In Elema resistance furnace high-temperature heating equipment, it is heated to 500-700 DEG C, is taken out after constant temperature 1-2 hours, makes glassware inner cavity
Wall forms the silver layer or layer gold (or not patterned silver layer or layer gold) of pierced pattern, and room temperature is down in placement.
10,150 mesh flap wheels and fiber polishing wheel on grinding machine flexible axle are hung with 220V, cleans out silver layer or layer gold surface to whole
Clean, patterned sides make product meet the requirements along neatly.
11, the dirt that the extra other places of silver powder or bronze and glassware generated in operation generate in operation is removed
Dirt is packed and stored after qualified by inspection.Such a inner wall has just completed (one with the glassware of silver layer or layer gold
Glassware).