CN109208148A - There is the method for weaving of light triangle profile polyester fiber Yu tencel fiber color textile fabric - Google Patents

There is the method for weaving of light triangle profile polyester fiber Yu tencel fiber color textile fabric Download PDF

Info

Publication number
CN109208148A
CN109208148A CN201710541363.XA CN201710541363A CN109208148A CN 109208148 A CN109208148 A CN 109208148A CN 201710541363 A CN201710541363 A CN 201710541363A CN 109208148 A CN109208148 A CN 109208148A
Authority
CN
China
Prior art keywords
polyester fiber
triangle profile
color
light triangle
profile polyester
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710541363.XA
Other languages
Chinese (zh)
Inventor
梅山标
陈秀苗
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Shuixing Home Textile Co Ltd
Original Assignee
Shanghai Shuixing Home Textile Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Shuixing Home Textile Co Ltd filed Critical Shanghai Shuixing Home Textile Co Ltd
Priority to CN201710541363.XA priority Critical patent/CN109208148A/en
Publication of CN109208148A publication Critical patent/CN109208148A/en
Pending legal-status Critical Current

Abstract

The present invention is a kind of method for weaving for having light triangle profile polyester fiber Yu tencel fiber color textile fabric.What it included the following steps: 1) to have light triangle profile polyester fiber has color spinning: 1.1) preparing the Masterbatch containing polyester and compound Masterbatch;1.2) progress spinning obtains strand after bright PET chips being carried out pre-crystallized processing;1.3) strand is stretched, relaxation heat setting processing, then carries out cutting packing, obtains the color silk of light triangle profile polyester fiber;2) it spins: to there is light triangle profile polyester fiber color silk to spin, having obtained light triangle profile polyester fiber dyed yarn;3) it weaves: selecting existing primary colors tencel yarn as warp thread, will have light triangle profile polyester fiber dyed yarn as the warp thread after weft yarn, with starching and be interleaved, obtain colored woven fabric;4) final finishing: colored woven fabric is singed processing by a positive and a negative, carries out colored woven fabric after singing to boil cloth desizing.

Description

There is the method for weaving of light triangle profile polyester fiber Yu tencel fiber color textile fabric
Technical field
The present invention relates to a kind of method for weaving of home textile product, especially disclose one kind have light triangle profile polyester fiber with The method for weaving of tencel fiber color textile fabric.
Background technique
Since the fiber used in nature for the mankind is limited, the appearance of synthetic fibers becomes certainty.Terylene is generation Boundary yield is maximum, and most widely used synthetic fibers kind accounts for 60% or more of world's synthetic fibers yield, be largely used to dress material, The textiles such as bedding, various trimming cloth, defence and military particular fabric and other industrial fibre products.Synthetic fibers It is synthesized by polymer chemistry substance, there is the features such as strongly good, resistance to acid and alkali is strong, be concerned by people.Since people are to each The consumption idea of kind textile product also changes constantly, and the requirement to textile product is also more and more, and the innovation of product is gradually As a kind of development trend.Light triangle profile polyester fiber (light triangle profile dacron thread) is that a kind of excellent Silk is former Material, on the basis of holding polyester original superperformance, fabric sheen is softer, and translucency is good, and bulkiness is good, hand for it Sense, stain resistance, anti-fluffing and anti-pilling ability etc. are excellent compared with conventional polyester fabric.And tencel fiber is that one kind is with wood pulp The natural regeneration cellulose fibre that raw material is produced through solvent spinning process, it has " comfort, " intensity " of terylene, woolens of cotton " the luxurious aesthetic feeling " of object and " the unique sense of touch " of silk and " softness, which is hung down, to be fallen ", no matter in the state of dry or wet, great toughness. In a wet state, it is the cellulose fibre that the first wet strength outclass cotton;A hundred percent natural material, in addition environmental protection Manufacturing process, allow life style, for this, to cater to the demand of modern consumer completely with conservation of nature environment, and green ring It protects, can be rated as the green fiber of 21 century.
There is light triangle profile dacron thread on the basis of holding terylene original superperformance, since fibre section is triangle Shape, it is a kind of excellent Silk raw material, fabric sheen is softer, light transmission that good luster is soft but have pendency to feel Property is good, and bulkiness is good;Feel, stain resistance, anti-fluffing and anti-pilling ability etc. are excellent compared with conventional polyester fabric.Tencel fiber It is formed by 100% pure natural wood pulp spinning, moisture absorption is ventilative, intensity is high, washing shrinkage is low, and production process green non-pollution is one The kind stronger synthetic fibers of comfort.
Many is had existed currently on the market using synthetic fibers as the home textile product of raw material, although synthetic fiber fabric has Many advantages, but still there are many problems, and homogeneity is serious.
Domestic and international relevant enterprise, research institution are to university in succession in the related performance study for having light triangle profile polyester fiber Many researchs have been made in exploitation and New Processing with its blending product etc., and all achieve certain effect.But Be there are the problem of it is also very significant.
Such as: application No. is: 201110331165.3 application for a patent for invention discloses a kind of fine denier bright triangular profiled The production method of fiber uses fused mass directly spinning One-step production route production to prepare a kind of fine denier bright triangular profiled fiber, The spinneret for the isosceles triangle micropore that this method is 60~100 ° using apex angle angle, micropore bottom edge side length be 0.25~ 0.35mm;It uses melt flow to quantify polyester fondant for the melt metering pump of 0.5~1.0ccm/rev and is sent to each filament spinning component; Gained filament number < 1.3dtex, multifilament hole count are 15F~48F.There is light triangle profile terylene by what this method was prepared FDY, not only possess that wearability is good, soft performance fine and smooth, ventilative, drapability is good, there are also a kind of special flash of light effects Fruit.But requirement of this method to equipment is high, and the cost of production is also relatively high.
Application No. is: the utility model patent of 201420865093.X discloses a kind of coloured flash of light special-shaped polyester filament yarn, The long filament section is to imitate hollow shape structure, and inside is equilateral pentagon, and outside is equilateral pentagon, wherein internal equilateral pentagon It is same center with external equilateral pentagon, the extended line of internal equilateral pentagon side length passes through external equilateral pentagonal each Vertex.The patent makes fiber have multiple planes of refraction by increase fibrous inside and external corner angle, improves light in fiber Internal refractive intensity and light transmitting, improve the flash of light bright spot of fiber, enhance the refraction index of fiber, inside and outside for inversion Concentric equilateral pentagon, light have extraordinary reflecting effect when being incident on fiber surface, while in being incident on through fiber When the equilateral pentagon in portion, since the refractive index difference and occurring of air repeatedly reflects and reflection, light intensity after refraction is improved, And increase fiber shining point, therefore have the function of reinforcing fiber flash effect.But requirement of the patent to raw material is relatively high, And equipment is poor to the shape stability of the odd-shaped cross section of fiber.
Application No. is: 200910048559.0 patent of invention discloses a kind of colored non-conventional dimensionally stable polyester multifilament Fiber and preparation method thereof adjusts polyester in melt by centainly proportion, then the content of pigment Masterbatch and additive is led to Drying and dehydrating is crossed, is melted, is squeezed, spinning, cooling forming oils, batches, and heating stretches, thermal finalization, and inspection is classified as finished product Silk.Invention preparation can be completed on conventional spinning equipment, and tow strip is dry uniformly, and color is evenly distributed, and can be widely applied to take With field, furnishing fields and industrial field, fabric is smooth, has the characteristics that soft glossy, and breaking strength is high, and extension at break is low, It can guarantee that fabric geometric dimension is stablized, be unlikely to deform, fabric resilience is good, and creep and relaxation are small, and boiling water shrinkage is low, It is unlikely to deform under the high temperature conditions, stability can be improved.But it is relatively more to need to use chemicals during the invention, contained Element uncertain whether can be hazardous to the human body.
Application No. is 201510057780.8 patent of invention, a kind of functional fiber dyed yarn, fabric and its system are disclosed Preparation Method, the invention are related to a kind of fiber dyed yarn with antibacterial functions, fabric and preparation method thereof.Its functional fiber dyed yarn Staple in bulk used is by being modified processing, the branch of yarn with forming modifying agent by nano silver, chitosan and nano-titanium dioxide The single thread or strand-single twist that number is 10S~60S are 300~1300 twists/m, the twist of strand be 150~1300 twist/ Rice;Thus the color textile fabric that functional fiber dyed yarn is woven into has splendid uvioresistant and anti-microbial property.Although the patent A kind of color textile fabric is invented, but the invention is not directed to light triangle profile terylene and the color of tencel is spun.
Summary of the invention
It is an object of the invention to overcome problems of the prior art, one kind is provided it is effectively improved product and fluff Ball, product obtained are good, soft comfortable with glossiness light triangle profile polyester fiber and tencel fiber color textile fabric Method for weaving.
The present invention is implemented as follows: a kind of weaving side for having light triangle profile polyester fiber Yu tencel fiber color textile fabric Method, characterized by the following steps:
1) have light triangle profile polyester fiber has color spinning:
1.1) dye molecule and white polyester are sliced after passing through Computer color testing according to the deployed colorant Masterbatch of pre-set color, And the colorant Masterbatch prepared is dried into 1-2h at 100 DEG C of baking oven;Then by the mass ratio of 1:50 by the coloring after drying Agent Masterbatch is mixed with the polyester slice after pre-crystallized drying, with common plastics extruder melt extruded at item, after water-bath cooling Pelleter pelletizing is made the Masterbatch containing polyester and compounds Masterbatch;
1.2) after bright PET chips being carried out pre-crystallized processing, with it is described mix color tablets by screw extruder sufficiently melt mix It closes uniformly and squeezes out, spinning is successively carried out by nozzle block after spinning manifold, is wound into bucket after strand is cooling;Wherein Pre-crystallized treated bright PET chips are 2:1-5:1 with the specific gravity for mixing color tablets;The spinneret of the nozzle block Hole is triangle spinneret orifice, aperture 0.25mm, L/R 2.5;Spinning temperature is 280-295 DEG C;Wind-warm syndrome when strand is cooling is 18-22 DEG C, wind speed 0.45m/s-0.5m/s;
1.3) strand for being wound into bucket that step 1.2 obtains is stretched, relaxation heat setting processing, then carries out cutting and beats Packet, obtains the color silk of light triangle profile polyester fiber;
2) it spins: light triangle profile polyester fiber color silk having been obtained to step 1.3 and has been spinned, drafting uses 6 one threads simultaneously It closes and carries out two simultaneously, process of roving gives 3.8 twirls of yarn/10cm twist;Light triangle profile polyester fiber dyed yarn is obtained;
3) it weaves: selecting existing primary colors tencel yarn as warp thread, warping is carried out to warp thread first, then become using potato Property starch CPL slurry sizing, slurry groove temperature be 90 ± 5 DEG C, finally have light triangle profile polyester fiber dyed yarn for what step 2 was spun It is interleaved as the warp thread after weft yarn, with starching, obtains colored woven fabric;
4) final finishing: colored woven fabric that step 3 obtains is singed processing by a positive and a negative, temperature of singing is 900 DEG C -1000 DEG C, colored woven fabric is carried out after singing to boil cloth desizing.
In the step 1.1 of step 1, during by the Masterbatch prepared dry 1-2h at 100 DEG C of baking oven, every 5- 10min is stirred.
In the step 2: the temperature in workshop is controlled at 25-30 DEG C in spinning process, and relative humidity is in 75%-80%.For Guarantee spinning go on smoothly and yarn quality, talcum powder can be used to carry out antistatic treatment to spinning functional component.
The beneficial effects of the present invention are: by that will there is light triangle profile polyester fiber dyed yarn to be interleaved with tencel yarn, Produce the home textile product with bright eye pool, soft comfortable.Spinning is carried out again by compounding Masterbatch, is solved to a certain extent In spinning process of having determined the problem of uneven dyeing.In addition, having the spinning of light triangle profile polyester fiber using spun tool is coloured Yarn is formed with light triangle profile polyester fiber dyed yarn, and resulting color-woven fabric does not have to carry out again after being interleaved with tencel yarn Dyeing solves the problems, such as that dyeing polyester fibers difficulty, the color of fabric are uniformly vivid.Since polyester fiber is odd-shaped cross section, change Fabric pilling problem has been apt to it, product produced by the present invention has the glossiness of high quality, can widen the more of home textile product type Memberization.
Specific embodiment
The present invention includes the following steps:
1) have light triangle profile polyester fiber has color spinning:
1.1) dye molecule difficult mixed once compared with white polyester slice is uniform, and therefore, dye molecule and white polyester are cut Piece passes through after Computer color testing according to the deployed colorant Masterbatch of pre-set color, and by the colorant Masterbatch prepared in baking oven Dry 1-2h, every 5-10min are stirred at 100 DEG C;Then by 1:50 mass ratio by after drying colorant Masterbatch with Polyester slice mixing after pre-crystallized drying, with common plastics extruder melt extruded at item, pelleter pelletizing after water-bath cooling, The Masterbatch containing polyester is made and compounds Masterbatch;
1.2) after bright PET chips being carried out pre-crystallized processing, with it is described mix color tablets by screw extruder sufficiently melt mix It closes uniformly and squeezes out, spinning is successively carried out by nozzle block after spinning manifold, is wound into bucket after strand is cooling;Wherein Pre-crystallized treated bright PET chips are 2:1-5:1 with the specific gravity for mixing color tablets;The spinneret of the nozzle block Hole is triangle spinneret orifice, aperture 0.25mm, L/R 2.5;Spinning temperature is 280-295 DEG C;Wind-warm syndrome when strand is cooling is 18-22 DEG C, wind speed 0.45m/s-0.5m/s;
1.3) strand for being wound into bucket that step 1.2 obtains is stretched, relaxation heat setting processing, then carries out cutting and beats Packet, obtains the color silk of light triangle profile polyester fiber;
2) it spins: light triangle profile polyester fiber color silk having been obtained to step 1.3 and has been spinned, the workshop in spinning process Temperature is controlled at 25-30 DEG C, and relative humidity is in 75%-80%.In order to guarantee spinning go on smoothly and yarn quality, can be used slide Mountain flour carries out antistatic treatment to spinning functional component.Drafting is using 6 one threads and closes and carries out two and improve irregularity, Process of roving gives 3.8 twirls of yarn/10cm twist, makes it have enough intensity, reduces broken end and accident in spinning process It stretches;Light triangle profile polyester fiber dyed yarn is obtained;
3) it weaves: selecting existing primary colors tencel yarn as warp thread, warping is carried out to warp thread first, then become using potato Property starch CPL slurry sizing, slurry groove temperature be 90 ± 5 DEG C, finally have light triangle profile polyester fiber dyed yarn for what step 2 was spun It is interleaved as the warp thread after weft yarn, with starching, obtains colored woven fabric;
4) final finishing: colored woven fabric that step 3 obtains is singed processing by a positive and a negative, temperature of singing is 900 DEG C -1000 DEG C, it is singed due to polyester fiber and is easy to be hardened when the temperature is excessively high or melt, the quenching between burner need to be reinforced, after singing Colored woven fabric is carried out to boil cloth desizing.

Claims (3)

1. a kind of method for weaving for having light triangle profile polyester fiber Yu tencel fiber color textile fabric, it is characterised in that: including such as Lower step:
1) have light triangle profile polyester fiber has color spinning:
1.1) dye molecule and white polyester are sliced after passing through Computer color testing according to the deployed colorant Masterbatch of pre-set color, And the colorant Masterbatch prepared is dried into 1-2h at 100 DEG C of baking oven;Then by the mass ratio of 1:50 by the coloring after drying Agent Masterbatch is mixed with the polyester slice after pre-crystallized drying, with common plastics extruder melt extruded at item, after water-bath cooling Pelleter pelletizing is made the Masterbatch containing polyester and compounds Masterbatch;
1.2) after bright PET chips being carried out pre-crystallized processing, with it is described mix color tablets by screw extruder sufficiently melt mix It closes uniformly and squeezes out, spinning is successively carried out by nozzle block after spinning manifold, is wound into bucket after strand is cooling;Wherein Pre-crystallized treated bright PET chips are 2:1-5:1 with the specific gravity for mixing color tablets;The spinneret of the nozzle block Hole is triangle spinneret orifice, aperture 0.25mm, L/R 2.5;Spinning temperature is 280-295 DEG C;Wind-warm syndrome when strand is cooling is 18-22 DEG C, wind speed 0.45m/s-0.5m/s;
1.3) strand for being wound into bucket that step 1.2 obtains is stretched, relaxation heat setting processing, then carries out cutting and beats Packet, obtains the color silk of light triangle profile polyester fiber;
2) it spins: light triangle profile polyester fiber color silk having been obtained to step 1.3 and has been spinned, drafting uses 6 one threads simultaneously It closes and carries out two simultaneously, process of roving gives 3.8 twirls of yarn/10cm twist, has obtained light triangle profile polyester fiber dyed yarn;
3) it weaves: selecting existing primary colors tencel yarn as warp thread, warping is carried out to warp thread first, then become using potato Property starch CPL slurry sizing, slurry groove temperature be 90 ± 5 DEG C, finally have light triangle profile polyester fiber dyed yarn for what step 2 was spun It is interleaved as the warp thread after weft yarn, with starching, obtains colored woven fabric;
4) final finishing: colored woven fabric that step 3 obtains is singed processing by a positive and a negative, temperature of singing is 900 DEG C -1000 DEG C, colored woven fabric is carried out after singing to boil cloth desizing.
2. the method for weaving for having light triangle profile polyester fiber Yu tencel fiber color textile fabric according to claim 1, It is characterized by: in the step 1.1 of step 1, during by the Masterbatch prepared dry 1-2h at 100 DEG C of baking oven, often 5-10min is stirred.
3. the method for weaving for having light triangle profile polyester fiber Yu tencel fiber color textile fabric according to claim 1, It is characterized by: in the step 2: the temperature in workshop is controlled at 25-30 DEG C in spinning process, and relative humidity is in 75%-80%.
CN201710541363.XA 2017-07-05 2017-07-05 There is the method for weaving of light triangle profile polyester fiber Yu tencel fiber color textile fabric Pending CN109208148A (en)