CN109206914A - A kind of low temperature resistant silica gel and chlorinated butyl rubber intermingling material and preparation method - Google Patents
A kind of low temperature resistant silica gel and chlorinated butyl rubber intermingling material and preparation method Download PDFInfo
- Publication number
- CN109206914A CN109206914A CN201811249073.9A CN201811249073A CN109206914A CN 109206914 A CN109206914 A CN 109206914A CN 201811249073 A CN201811249073 A CN 201811249073A CN 109206914 A CN109206914 A CN 109206914A
- Authority
- CN
- China
- Prior art keywords
- parts
- type
- butyl rubber
- silica gel
- chlorinated butyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of low temperature resistant silica gel and chlorinated butyl rubber intermingling material and preparation method, including following component and parts by weight: 100 parts of silica gel;50 parts of chlorinated butyl rubber;30 parts of 220 type of carbon black;25 parts of 330 type of carbon black;35 parts of calcium carbonate;6.5 parts of zinc oxide;3.5 parts of magnesia;1 part of stearic acid;1 part of microwax;2 parts of fully refined paraffin wax;2.2 parts of softening agent;3 parts of plasticizer DOS type;2.75 parts of diphenylguanidine CP type;1 part of promotor P-1528 type;1 part of 445 type of anti-aging agent;1.5 parts of vulcanizing agent.Low temperature resistant silica gel obtained by the present invention and chlorinated butyl rubber intermingling material have the excellent properties such as preferable high temperature resistant, corrosion-resistant, ageing-resistant, wear-resistant, have greatly reinforced the service life of rubber pad, simple production process.
Description
Technical field
The present invention relates to field of rubber preparation more particularly to a kind of low temperature resistant silica gel and chlorinated butyl rubber intermingling material and systems
Preparation Method.
Background technique
Rubber industry is one of important foundation industry of national economy, and it is indispensable that it not only provides daily life for people
The light industrys rubber product such as daily, medical, and mentioned to the heavy industry such as digging, traffic, building, machinery, electronics and new industry
For various rubber system production equipments or rubber components.And current automobile industry is higher and higher for the performance requirement of rubber.
Summary of the invention
The present invention is to provide a kind of low temperature resistant silica gel and chlorinated butyl rubber intermingling material and system to solve above-mentioned deficiency
Preparation Method is had excellent performance, and greatly improves service life.
Above-mentioned purpose of the invention is realized by technical solution below: a kind of low temperature resistant silica gel and chlorinated butyl rubber are total
Mixed material, it is characterised in that: including following component and parts by weight: 100 parts of silica gel;50 parts of chlorinated butyl rubber;220 type 30 of carbon black
Part;25 parts of 330 type of carbon black;35 parts of calcium carbonate;6.5 parts of zinc oxide;3.5 parts of magnesia;1 part of stearic acid;1 part of microwax;Refining
2 parts of paraffin;2.2 parts of softening agent;3 parts of plasticizer DOS type;2.75 parts of diphenylguanidine CP type;1 part of promotor P-1528 type;Anti-aging agent
445 1 part of types;1.5 parts of vulcanizing agent.
The preparation method of above-mentioned intermingling material is that first raw material silica gel and chlorinated butyl rubber will be taken according to parts by weight to be cut into carefully
Mixing in mixer is added after little particle, 80-90 DEG C of heating temperature, is stirred 20 minutes and is obtained with the mixing speed of 50-60r/min
Colloid substances;220 type of carbon black, 330 type of carbon black, calcium carbonate, zinc oxide, oxidation is added into above-mentioned colloid substances according to parts by weight
Magnesium, microwax, fully refined paraffin wax, softening agent, plasticizer DOS type, diphenylguanidine CP type, promotor P-1528 type, is prevented always stearic acid
445 type of agent and vulcanizing agent stir evenly;It is subsequently placed into vulcanizer to be vulcanized, curing temperature is 175 DEG C, in elevated temperature cure process
In, it is pressurizeed 4 minutes at 50 DEG C at pressurization 3 minutes, 80 DEG C, vulcanization time is 30 minutes.
Low temperature resistant silica gel obtained by the present invention and chlorinated butyl rubber intermingling material have preferable high temperature resistant, it is corrosion-resistant,
The excellent properties such as ageing-resistant, wear-resistant, have greatly reinforced the service life of rubber pad, simple production process.
Specific embodiment
The present invention is described in further detail below with reference to embodiment.
Embodiment 1
A kind of low temperature resistant silica gel and chlorinated butyl rubber intermingling material and preparation method, including following component and parts by weight:
100 parts of silica gel;50 parts of chlorinated butyl rubber;30 parts of 220 type of carbon black;25 parts of 330 type of carbon black;35 parts of calcium carbonate;6.5 parts of zinc oxide;
3.5 parts of magnesia;1 part of stearic acid;1 part of microwax;2 parts of fully refined paraffin wax;2.2 parts of softening agent;3 parts of plasticizer DOS type;Promotor
2.75 parts of DCP type;1 part of promotor P-1528 type;1 part of 445 type of anti-aging agent;1.5 parts of vulcanizing agent.
Preparation method be first raw material silica gel and chlorinated butyl rubber will be taken to be cut into fine particle according to parts by weight after be added it is close
Mixing in mill, is stirred 20 minutes with the mixing speed of 50r/min and obtains colloid substances by 80 DEG C of heating temperature;According to parts by weight
220 type of carbon black, 330 type of carbon black, calcium carbonate, zinc oxide, magnesia, stearic acid, microwax, refining are added into above-mentioned colloid substances
Paraffin, softening agent, plasticizer DOS type, diphenylguanidine CP type, promotor P-1528 type, 445 type of anti-aging agent and vulcanizing agent stirring are equal
It is even;Vulcanizer is subsequently placed into be vulcanized, curing temperature is 175 DEG C, during elevated temperature cure, pressurizes 3 minutes at 50 DEG C, 80
DEG C when pressurize 4 minutes, vulcanization time be 30 minutes.
The above description is only an embodiment of the present invention, is not intended to limit the scope of the invention, all to utilize this hair
Equivalent structure or equivalent flow shift made by bright specification and embodiment content, it is relevant to be applied directly or indirectly in other
Technical field is included within the scope of the present invention.
Claims (2)
1. a kind of low temperature resistant silica gel and chlorinated butyl rubber intermingling material, which is characterized in that including following component and parts by weight: silicon
100 parts of glue;50 parts of chlorinated butyl rubber;30 parts of 220 type of carbon black;25 parts of 330 type of carbon black;35 parts of calcium carbonate;6.5 parts of zinc oxide;Oxygen
Change 3.5 parts of magnesium;1 part of stearic acid;1 part of microwax;2 parts of fully refined paraffin wax;2.2 parts of softening agent;3 parts of plasticizer DOS type;Promotor
2.75 parts of DCP type;1 part of promotor P-1528 type;1 part of 445 type of anti-aging agent;1.5 parts of vulcanizing agent.
2. the preparation method of a kind of low temperature resistant silica gel and chlorinated butyl rubber intermingling material according to claim 1, feature
It is, mixing in mixer will be added after first raw material silica gel and chlorinated butyl rubber being taken according to parts by weight to be cut into fine particle, adds
80-90 DEG C of hot temperature is stirred 20 minutes with the mixing speed of 50-60r/min and obtains colloid substances;According to parts by weight to above-mentioned glue
220 type of carbon black, 330 type of carbon black, calcium carbonate, zinc oxide, magnesia, stearic acid, microwax, fully refined paraffin wax, soft is added in body object
Agent, plasticizer DOS type, diphenylguanidine CP type, promotor P-1528 type, 445 type of anti-aging agent and vulcanizing agent stir evenly;Then
It is put into vulcanizer to be vulcanized, curing temperature is 175 DEG C, during elevated temperature cure, is added at pressurization 3 minutes, 80 DEG C at 50 DEG C
Pressure 4 minutes, vulcanization time are 30 minutes.