CN109202235A - 焊枪导电咀气咀防飞溅层 - Google Patents

焊枪导电咀气咀防飞溅层 Download PDF

Info

Publication number
CN109202235A
CN109202235A CN201811293612.9A CN201811293612A CN109202235A CN 109202235 A CN109202235 A CN 109202235A CN 201811293612 A CN201811293612 A CN 201811293612A CN 109202235 A CN109202235 A CN 109202235A
Authority
CN
China
Prior art keywords
nozzle
coating
air nozzle
conductive
conductive nozzle
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811293612.9A
Other languages
English (en)
Inventor
刘强
石唯
石唯一
赵孔标
陈福兰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing Dongxin Welding Technology Co Ltd
Nantong Shipping College
Original Assignee
Nanjing Dongxin Welding Technology Co Ltd
Nantong Shipping College
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanjing Dongxin Welding Technology Co Ltd, Nantong Shipping College filed Critical Nanjing Dongxin Welding Technology Co Ltd
Priority to CN201811293612.9A priority Critical patent/CN109202235A/zh
Publication of CN109202235A publication Critical patent/CN109202235A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种焊枪导电咀气咀防飞溅层，导电咀的外部设有气咀，导电咀的前端略伸出气咀，焊丝由导电咀的中心位置伸出，导电咀的外壁面覆盖有第一涂层，第一涂层包裹导电咀的前端部位；气咀的内壁上覆盖有第二涂层，第一涂层与第二涂层采用塘瓷、玻璃釉或高温涂料制成。本发明无需各种清枪器，减少了工作程序，加快了焊接生产速度，提高了生产效率。

Description

焊枪导电咀气咀防飞溅层
技术领域
本发明涉及电焊机技术领域，具体涉及防止飞溅粘在焊枪导电咀或气咀上的方法。
背景技术
常用的CO2焊机, MIG焊机或MAG焊机的送丝机上都有一导电咀，焊丝从导电咀中送出，进行焊接。在导电咀外有一气咀，保护气体从气咀中流出，对电弧进行保护。在焊接时会产生飞溅，飞溅是熔化的金属小球，熔化的金属小球，碰到同为金属铜或铁的导电咀或气咀，使导电咀或气咀局部也熔化，冷却后与飞来的金属小球熔为一本，形成飞溅，飞溅经常粘在导电咀的端部和侧面以及气咀的内壁，如图1所示，粘连的飞溅使送丝不畅，影响焊接质量。因此，尽管焊接机器人和各种自动焊机的机械，电气设计都很先进，本应能较长时间连续地进行自动焊接，但经常因飞溅堵住了导电咀，使自动焊不得不仃下来，为此，焊接机器人均配备有完善的”清枪器”，可以清除导电咀上粘连的飞溅。此外还有市售的防堵膏。这些措施对防止飞溅对焊接的影响均有一定效果，但仍有不足之处。使用”清枪器” ，增加了机器人的工作程序，降低了生产速度。防堵膏是一种半流动的油脂类物品，在电弧的高温下，很快挥发，失效，因此要经常去涂，同样影响生产速度。因此，清除飞溅是焊接机器人和各种自动焊机的机械能否顺利应用，加快焊接生产速度必须解决的一个关键问题。
发明内容
为了解决上述的技术问题，本发明提供了一种焊枪导电咀气咀防飞溅层。
本发明的技术方案为：一种焊枪导电咀气咀防飞溅层，导电咀的外部设有气咀，导电咀的前端略伸出气咀，焊丝由导电咀的中心位置伸出，导电咀的外壁面覆盖有第一涂层，第一涂层包裹导电咀的前端部位；气咀的内壁上覆盖有第二涂层。
进一步地，所述导电咀为铜质材料制成，第一涂层为非金属物质，工艺方法为铜上塘瓷。
进一步地，所述气咀为铁质材料制成，第二涂层为非金属物质，工艺方法为铁上塘瓷。
进一步地，所述导电咀为铜质材料制成，气咀为铁质材料制成，第一涂层与第二涂层为玻璃釉。
进一步地，所述导电咀为铜质材料制成，气咀为铁质材料制成，第一涂层与第二涂层为高温涂料制成。
进一步地，所述第一涂层与第二涂层的厚度在0.5~5mm之间。
本发明的有益效果为：本发明通过第一涂层覆盖在导电咀的外壁以及第二涂层覆盖在气咀的内壁，使得飞溅不易粘接在导电咀的外壁与气咀的内壁上，不需要在焊接时清除粘连的飞溅，无需各种清枪器，减少了工作程序，加快了焊接生产速度，提高了生产效率，使焊接机器人和各种自动焊接没有清飞溅的垢病，而能正常不间断地焊接。
附图说明
下面结合附图和实施例对本发明作进一步说明。
图1是现有技术的结构示意图。
图2是本发明的结构示意图。
具体实施方式
下面结合附图对本发明的具体实施方式作进一步说明，本实施例不构成对本发明的限制。
如图1所示，一种焊枪导电咀气咀防飞溅层，包括导电咀1、焊丝2、气咀3、第一涂层4、第二涂层5。
导电咀1的外部套设有气咀3，导电咀1的前端略伸出气咀3，焊丝2由导电咀1的中心位置伸出。
导电咀1的外壁面覆盖有第一涂层4，第一涂层4包裹导电咀1的前端部位。气咀3的内壁上覆盖有第二涂层5。
实施例1
导电咀1为铜质材料制成，在铜质导电咀上覆盖一层高熔点不易挥发的非金属物质，第一涂层4为非金属物质，实际是在铜上塘瓷，是景泰兰工艺的一种具体应用。
实施例2
气咀3为铁质材料制成，在铁质气咀上覆盖一层高熔点不易挥发的非金属物质，第二涂层5为非金属物质，实际是在铁上塘瓷，是塘瓷工艺的一种具体应用。
实施例3
导电咀1为铜质材料制成，气咀3为铁质材料制成，在铜质导电咀或铁质气咀上覆盖一层高熔点不易挥发的非金属物质，第一涂层4与第二涂层5为玻璃釉，实际是在铜上或铁上烧结一层玻璃釉。
实施例4
导电咀1为铜质材料制成，气咀3为铁质材料制成，在铜质导电咀或铁质气咀上覆盖一层高熔点不易挥发的非金属物质，第一涂层4与第二涂层5为高温涂料制成，实际是在铜上或铁上涂一层高温涂料如XZ-T1001或XZ-T1003，这类涂料耐温15000C，短时可达18000C。第一涂层4与第二涂层5的涂层厚度可在1~5mm之间。
导电咀1覆盖第一涂层以及气咀3覆盖第二涂层的作用为：
第一种情况：由于存在第一涂层与第二涂层，熔化状态的金属小球的热量传不到导电咀的外壁或气咀的内壁。
第二种情况：熔化状态的金属小球的热量不足以熔化复盖在导电咀的第一涂层和气咀的第二涂层，飞溅粘不到导电咀和气咀的上。
第三种情况：飞溅即使熔化了导电咀的第一涂层和气咀的第二涂层，由于飞溅具有金属属性，不会与非金属属性的第一涂层或者第二涂层结合。
以上所述，仅是本发明的较佳实施例而已，不用于限制本发明，本领域技术人员可以在本发明的实质和保护范围内，对本发明做出各种修改或等同替换，这种修改或等同替换也应视为落在本发明技术方案的保护范围内。

Claims (6)

1.一种焊枪导电咀气咀防飞溅层，其特征在于：导电咀的外部设有气咀，导电咀的前端略伸出气咀，焊丝由导电咀的中心位置伸出，导电咀的外壁面覆盖有第一涂层，第一涂层包裹导电咀的前端部位；气咀的内壁上覆盖有第二涂层。
2.根据权利要求1所述的焊枪导电咀气咀防飞溅层，其特征在于：所述导电咀为铜质材料制成，第一涂层为非金属物质，工艺方法为铜上塘瓷。
3.根据权利要求1所述的焊枪导电咀气咀防飞溅层，其特征在于：所述气咀为铁质材料制成，第二涂层为非金属物质，工艺方法为铁上塘瓷。
4.根据权利要求1所述的焊枪导电咀气咀防飞溅层，其特征在于：所述导电咀为铜质材料制成，气咀为铁质材料制成，第一涂层与第二涂层为玻璃釉。
5.根据权利要求1所述的焊枪导电咀气咀防飞溅层，其特征在于：所述导电咀为铜质材料制成，气咀为铁质材料制成，第一涂层与第二涂层为高温涂料制成。
6.根据权利要求5所述的焊枪导电咀气咀防飞溅层，其特征在于：所述第一涂层与第二涂层的厚度在0.5~5mm之间。
CN201811293612.9A 2018-11-01 2018-11-01 焊枪导电咀气咀防飞溅层 Pending CN109202235A (zh)