CN109192888A - A kind of metal-coated membrane applied to lithium battery - Google Patents
A kind of metal-coated membrane applied to lithium battery Download PDFInfo
- Publication number
- CN109192888A CN109192888A CN201810809829.4A CN201810809829A CN109192888A CN 109192888 A CN109192888 A CN 109192888A CN 201810809829 A CN201810809829 A CN 201810809829A CN 109192888 A CN109192888 A CN 109192888A
- Authority
- CN
- China
- Prior art keywords
- layer
- metal
- lithium battery
- coated membrane
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of metal-coated membranes applied to lithium battery, including being located at middle layer, middle layer both sides are surface-treated layer, the outer surface of surface-treated layer is coated with metal layer, the middle layer is PET film, surface-treated layer is rough rough layer or the high adhesive layer of attachment fastness, and the metal layer is aluminium film or copper film, is covered with micro-hole in the middle layer.Equipped with micro-hole, when metal-coated membrane, is full of micro-hole, so that the two panels metal film separated by PET film can reduce resistance with intercommunication conduction, the conducting effect of enhancing tow sides metal layer electric current.
Description
Technical field
The invention belongs to lithium battery manufacturing technology fields, are related to a kind of metal-coated membrane applied to lithium battery.
Background technique
The packaging of lithium battery is gradually changed to soft aluminizer outer packing from hard steel shell, the aluminum hull of low and middle-end, using plating
After aluminium film, realize that lithium battery aluminum amount is few, the aluminizer on both sides is separated by plastic foil, causes resistance to increase, the conducting energy of electric current
Power decline.
Summary of the invention
The purpose of the present invention is there is the above problem in view of the prior art, propose a kind of applied to the gold-plated of lithium battery
Belong to film, be equipped with micro-hole, micro-hole is full of when metal-coated membrane, so that the two panels metal film separated by PET film can be with intercommunication conduction.
Object of the invention can be realized by the following technical scheme: a kind of metal-coated membrane applied to lithium battery, special
Sign is, including is located at middle layer, and middle layer both sides are surface-treated layer, and the outer surface of surface-treated layer is coated with metal layer, institute
Stating middle layer is PET film, and surface-treated layer is rough rough layer or the high adhesive layer of attachment fastness, the metal layer are
Aluminium film or copper film are covered with micro-hole in the middle layer.
Further, the rough layer is sandblasting layer.
Further, the adhesive layer is using sided corona treatment, electric spark processing, plasma treatment, plating NI processing, plating
The one or more such as ALO processing, chemical treatment coating, NAOH immersion.Adhesive layer increases between aluminizer, copper plating film and PET film
Attachment fastness.
Further, the aluminium film is with a thickness of 0.3-2.5 microns;
Further, the copper film thickness is 0.2-1.2 microns;
Further, the adhesive layer is with a thickness of 0.005-0.05 microns.
Further, the diameter of the micro-hole is 10-100 microns, 0.5-1 millimeters of spacing.
Compared with prior art, the metal-coated membrane that should be used for lithium battery has the advantage that
1. being provided with micro-hole, the conducting effect of enhancing tow sides metal layer electric current reduces resistance;
2. being provided with micro-hole, enhance the binding strength of tow sides metal layer and film;
3. aluminium film, copper film tensile strength is high, ductility is good, density is small, the weight of lithium battery is reduced;
4. middle layer is PET film, realize that lithium battery aluminum amount is few, final products safety is promoted;
5. subsequent can increase types of functionality substance on metal film base material, increase application range.
Detailed description of the invention
Fig. 1 is the cross-sectional view that should be used for the metal-coated membrane of lithium battery.
In figure, 1, middle layer;11, micro-hole;2, surface-treated layer;3, metal layer.
Specific embodiment
Following is a specific embodiment of the present invention in conjunction with the accompanying drawings, technical scheme of the present invention will be further described,
However, the present invention is not limited to these examples.
Embodiment one
As shown in Figure 1, the metal-coated membrane of lithium battery should be used for, including it is located at middle layer 1,1 both sides of middle layer are surface
Process layer 2, the outer surface of surface-treated layer 2 are coated with metal layer 3, and the middle layer 1 is PET film, surface-treated layer 2 be it is concave-convex not
Flat rough layer, the metal layer 3 are aluminium film, are covered with micro-hole 11 in the middle layer 1.
The rough layer is sandblasting layer, and the diameter of the micro-hole 11 is 10-100 microns, 0.5-1 millimeters of spacing.
The aluminium film is with a thickness of 0.3-2.5 microns;The adhesive layer is with a thickness of 0.005-0.05 microns.
Embodiment two
Surface-treated layer 2 is the high adhesive layer of attachment fastness, the adhesive layer be using sided corona treatment, electric spark processing,
The one or more such as ALO is handled, chemical treatment coating, NAOH impregnate are plated in plasma treatment, plating NI processing.Adhesive layer increases plating
Attachment fastness between aluminium film, copper plating film and PET film.
The metal layer 3 is copper film, and copper film thickness is 0.2-1.2 microns.
Specific embodiment described herein is only an example for the spirit of the invention.The neck of technology belonging to the present invention
The technical staff in domain can make various modifications or additions to the described embodiments or replace by a similar method
In generation, however, it does not deviate from the spirit of the invention or beyond the scope of the appended claims.
Claims (7)
1. a kind of metal-coated membrane applied to lithium battery, which is characterized in that including being located at middle layer, middle layer both sides are at surface
Layer is managed, the outer surface of surface-treated layer is coated with metal layer, and the middle layer is PET film, and surface-treated layer is rough thick
Rough layer or the high adhesive layer of attachment fastness, the metal layer are aluminium film or copper film, are covered with micro-hole in the middle layer.
2. a kind of metal-coated membrane applied to lithium battery according to claim 1, which is characterized in that the rough layer is
Sandblasting layer.
3. a kind of metal-coated membrane applied to lithium battery according to claim 1, which is characterized in that the adhesive layer is to adopt
With sided corona treatment, electric spark processing, plasma treatment, plating NI processing, plating ALO processing, chemical treatment coating, NAOH impregnate etc. one
Kind is several.
4. a kind of metal-coated membrane applied to lithium battery according to claim 1, which is characterized in that the aluminium film with a thickness of
0.3-2.5 microns.
5. a kind of metal-coated membrane applied to lithium battery according to claim 1, which is characterized in that the copper film thickness is
0.2-1.2 microns.
6. a kind of metal-coated membrane applied to lithium battery according to claim 1, which is characterized in that the adhesive layer thickness
It is 0.005-0.05 microns.
7. a kind of metal-coated membrane applied to lithium battery according to claim 1, which is characterized in that the micro-hole it is straight
Diameter is 10-100 microns, 0.5-1 millimeters of spacing.