CN109183430A - A kind of environmental protection is anti-to cohere water-based spinning coating and preparation method thereof - Google Patents
A kind of environmental protection is anti-to cohere water-based spinning coating and preparation method thereof Download PDFInfo
- Publication number
- CN109183430A CN109183430A CN201810926921.9A CN201810926921A CN109183430A CN 109183430 A CN109183430 A CN 109183430A CN 201810926921 A CN201810926921 A CN 201810926921A CN 109183430 A CN109183430 A CN 109183430A
- Authority
- CN
- China
- Prior art keywords
- water
- cohere
- environmental protection
- spinning coating
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Resist the invention discloses a kind of environmental protection and coheres water-based spinning coating and preparation method thereof；Its component includes 80~100 parts of water-base resin, and nanometer is anti-to cohere 1~5 part of resin, 2~5 parts of water, assists 0.15~1.5 part of film forming matter, and 0.5~1 part of thickener, 0.5~1 part of levelling agent and 0.5~1 part of wetting agent.Environmental protection of the invention is anti-to cohere spinning coating and preparation method thereof, so that weaving finished product packaging process is not cohering, expands the processing service performance of spinning coating.
Description
Technical field
The present invention relates to a kind of water-based spinning coatings and preparation method thereof, and in particular to a kind of environmental protection is anti-to cohere water-based spinning
Coating and preparation method thereof.
Background technique
Emulsification lotion is the paint that film forming matter is prepared after water-thinned paints refers to, keeps solvent type resin molten in organic solvent,
Then so that resin dispersion is formed lotion in water by strong mechanical stirring with the help of emulsifier, referred to as after emulsify lotion,
Manufactured paint can be diluted in construction with water；Water-based spinning coating is not available compared with high glass transition temperature resin at present, is caused
Weaving finished product coheres the user for being stranded water-based spinning coating, if using more drying equipment, and energy loss is caused, it produces
Raw secondary environmental issue.
Summary of the invention
(1) technical problems to be solved
Water-based spinning coating and preparation method thereof is cohered to solve the above problems, resisting the invention proposes a kind of environmental protection, is made
Obtaining drying temperature reduces, and drying time shortens, and improves drying condition limitation, and making finished product, there is no cohere phenomenon.
(2) technical solution
Environmental protection of the invention is anti-to cohere water-based spinning coating；The component mass ratio composition includes water-base resin 80~100
Part, nanometer is anti-to cohere 1~5 part of resin, 2~5 parts of water, assist 0.15~1.5 part of film forming matter, 0.5~1 part of thickener, and levelling agent
0.5~1 part and 0.5~1 part of wetting agent.
It further include 0.5~1 part of dispersing agent as a better embodiment of the present embodiment.
As a better embodiment of the present embodiment, the dispersing agent is Siloxane-Oxyalkylene Copolymers class dispersing agent.
It further include 0.5~1 part of defoaming agent as a better embodiment of the present embodiment.
As a better embodiment of the present embodiment, the defoaming agent is the aqueous solid and polysiloxanes of polyethylene glycol
Mixture class defoaming agent.
As a better embodiment of the present embodiment, the heat setting vresin is the aqueous heat setting vresin of nano inorganic.
As a better embodiment of the present embodiment, the thickener is the swollen class thickener of alkali soluble.
The anti-preparation method for cohering water-based spinning coating of environmental protection of the invention, comprising:
The first step, is sequentially added that water-base resin, nanometer are anti-to cohere resin, dispersing agent, wetting agent by formula, stirs at low speed 5
Minute, and revolving speed is stepped up to 600~700 turns, obtain product I；
Second step is added after levelling agent high speed dispersion 15 minutes into product I, and defoaming agent reduction of speed is added and stirs 5 minutes, obtains
To product II；
Third step is added thickener into product II and adjusts viscosity, obtains product III；
4th step by product III by obtaining product after 200 mesh net filtrations, and is packed.
As preferred embodiment, wherein water-base resin and the water of thickener equal proportion are diluted.
Further include filler as preferred embodiment, the filler is titanium dioxide, calcium carbonate, it is a kind of in talcum powder or
It is several.
As preferred embodiment, the heat setting vresin is nano inorganic material.
As preferred embodiment, the defoaming agent is the aqueous solid of polyethylene glycol and the mixture class of polysiloxanes
Defoaming agent.
As preferred embodiment, the thickener is the swollen class thickener of alkali soluble.
(3) beneficial effect
Compared with prior art, environmental protection of the invention is anti-coheres water-based spinning coating and preparation method thereof, and the feature of environmental protection improves,
It is dry simple, reduce energy loss；Due to using reduced TG tenderness resin, so that substrate adhesion increases；Operation environmental protection is wanted
It asks and relaxes, reduce finished product and cohere failure and do over again probability；Reduce cost.
Specific embodiment
Embodiment one: the fast-drying aqueous spinning coating of environmental protection of the invention, the component mass ratio composition: water-base resin 90
Part, nanometer is anti-to cohere resin 3, and dissolves this nanometer of anti-water 3 for cohering resin, assists film forming matter 1, thickener 0.75, levelling agent
0.65, and the water 0.75 of dilution thickener, wetting agent 0.85.
The first step, is sequentially added that water-base resin, nanometer are anti-to cohere resin, dispersing agent, wetting agent by formula, stirs at low speed 5
Minute, and revolving speed is stepped up to 600 turns, obtain product I；
Second step is added after levelling agent high speed dispersion 15 minutes into product I, and defoaming agent reduction of speed is added and stirs 5 minutes, obtains
To product II；
Third step is added thickener into product II and adjusts viscosity, obtains product III；
4th step by product III by obtaining product after 200 mesh net filtrations, and is packed.
Wherein, heat setting vresin is nano inorganic material, and granular size is 14 nanometers.
Embodiment two: the fast-drying aqueous spinning coating of environmental protection of the invention, the component mass ratio composition: water-base resin 80
Part, nanometer is anti-to cohere 1 part of resin, and dissolves this nanometer of anti-1 part of water for cohering resin, assists 0.15 part of film forming matter, thickener 0.5
Part, 0.5 part of levelling agent, and dilution 0.5 part of water, 0.5 part of wetting agent of thickener.
The first step, is sequentially added that water-base resin, nanometer are anti-to cohere resin, dispersing agent, wetting agent by formula, stirs at low speed 5
Minute, and revolving speed is stepped up to 600 turns, obtain product I；
Second step is added after levelling agent high speed dispersion 10 minutes into product I, and defoaming agent reduction of speed is added and stirs 5 minutes, obtains
To product II；
Third step is added thickener into product II and adjusts viscosity, obtains product III；
4th step by product III by obtaining product after 200 mesh net filtrations, and is packed.
Wherein, heat setting vresin is nano inorganic material, and granular size is 14 nanometers.
Embodiment three: the fast-drying aqueous spinning coating of environmental protection of the invention, the component mass ratio composition: water-base resin 100
Part, nanometer is anti-to cohere 5 parts of resin, and dissolves this nanometer of anti-5 parts of water for cohering resin, 1.5 parts of film forming matter of auxiliary, and 1 part of thickener,
1 part of levelling agent, and dilution 1 part of water, 1 part of wetting agent of thickener.
The first step, is sequentially added that water-base resin, nanometer are anti-to cohere resin, dispersing agent, wetting agent by formula, stirs at low speed 5
Minute, and revolving speed is stepped up to 700 turns, obtain product I；
Second step is added after levelling agent high speed dispersion 15 minutes into product I, and defoaming agent reduction of speed is added and stirs 5 minutes, obtains
To product II；
Third step is added thickener into product II and adjusts viscosity, obtains product III；
4th step by product III by obtaining product after 200 mesh net filtrations, and is packed.
Wherein, heat setting vresin is nano inorganic material, and granular size is 14 nanometers.
Further, in above three embodiments:
Heat setting vresin is nano inorganic material.
Dispersing agent is Siloxane-Oxyalkylene Copolymers class dispersing agent.
Defoaming agent is the aqueous solid of polyethylene glycol and the mixture class defoaming agent of polysiloxanes.
Thickener is the swollen class thickener of alkali soluble.,
Effect example:
Coated substrate is dried in drying oven, and drying temperature is oven temperature.
| Embodiment 1 | Embodiment 2 | Embodiment 3 | The prior art | |
| Drying temperature | 80 | 77 | 85 | 90 DEG C or more |
| Drying time | 70s | 80s | 77s | 10 minutes or more |
| Cohere degree | Nothing | Nothing | Nothing | Have |
The standard that drying time selects is the drying in forced air convection baking oven, corresponding with drying temperature.
Environmental protection of the invention is anti-to cohere water-based spinning coating and preparation method thereof, using low Tg resin, cooperation
The anti-use for cohering resin of nanometer plays the hydroxyl condensation reaction of self-crosslinking, solves the stringent limitation of drying condition, and coating is dry
Anti- fastly to cohere, since main plexiglas temperature is low, attaching is puted forth effort.
The above-described embodiments are merely illustrative of preferred embodiments of the present invention, not to structure of the invention
Think and range is defined.Without departing from the design concept of the invention, ordinary people in the field is to technology of the invention
The all variations and modifications that scheme is made, should all drop into protection scope of the present invention, the claimed technology contents of the present invention,
It is all described in the claims.
Claims (10)
1. a kind of environmental protection is anti-to cohere water-based spinning coating, which is characterized in that 80~100 parts of water-base resin, nanometer is anti-to cohere resin 1
~5 parts, 2~5 parts of water, assist 0.15~1.5 part of film forming matter, 0.5~1 part of thickener, 0.5~1 part of levelling agent and wetting agent
0.5~1 part.
2. environmental protection according to claim 2 is anti-to cohere water-based spinning coating, which is characterized in that further include dispersing agent 0.5~1
Part.
3. environmental protection according to claim 2 is anti-to cohere water-based spinning coating characterized by comprising the dispersing agent is
Siloxane-Oxyalkylene Copolymers class dispersing agent.
4. environmental protection according to claim 2 is anti-to cohere water-based spinning coating, which is characterized in that further include defoaming agent 0.5~1
Part.
5. environmental protection according to claim 4 is anti-to cohere water-based spinning coating characterized by comprising the defoaming agent is
The aqueous solid of polyethylene glycol and the mixture class defoaming agent of polysiloxanes.
6. environmental protection according to claim 1 is anti-to cohere water-based spinning coating characterized by comprising described anti-to cohere tree
Rouge is nano inorganic material.
7. environmental protection according to claim 1 is anti-to cohere water-based spinning coating characterized by comprising the thickener is
Alkali soluble is swollen class thickener.
8. a kind of anti-preparation method for cohering water-based spinning coating of environmental protection characterized by comprising
The first step, is sequentially added that water-base resin, nanometer are anti-to cohere resin, dispersing agent, wetting agent by formula, is stirred at low speed 5 minutes,
And revolving speed is stepped up to 600~700 turns, obtain product I；
Second step is added after levelling agent high speed dispersion 15 minutes into product I, and defoaming agent reduction of speed is added and stirs 5 minutes, is produced
Object II；
Third step is added thickener into product II and adjusts viscosity, obtains product III；
4th step by product III by obtaining product after 200 mesh net filtrations, and is packed.
9. the preparation method of the fast-drying aqueous spinning coating of environmental protection according to claim 8, which is characterized in that described anti-to cohere
Resin passes through 1~5 part of water dissolved dilution.
10. the preparation method of the fast-drying aqueous spinning coating of environmental protection according to claim 8, which is characterized in that the thickening
Agent passes through 0.5~1 part of water dissolved dilution.