CN109183431A - A kind of fast-drying aqueous spinning coating of environmental protection and preparation method thereof - Google Patents
A kind of fast-drying aqueous spinning coating of environmental protection and preparation method thereof Download PDFInfo
- Publication number
- CN109183431A CN109183431A CN201810926925.7A CN201810926925A CN109183431A CN 109183431 A CN109183431 A CN 109183431A CN 201810926925 A CN201810926925 A CN 201810926925A CN 109183431 A CN109183431 A CN 109183431A
- Authority
- CN
- China
- Prior art keywords
- fast
- environmental protection
- spinning coating
- agent
- drying aqueous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fast-drying aqueous spinning coatings of environmental protection and preparation method thereof；Its component includes 80~100 parts of water-base resin, 1~5 part of nanometer heat setting vresin, 2~5 parts of water, assists 0.15~1.5 part of film forming matter, and 0.5~1 part of thickener, 0.5~1 part of levelling agent and 0.5~1 part of wetting agent.Environmentally friendly quick-drying spinning coating of the invention and preparation method thereof expands the processing service performance of spinning coating so that baking time shortens, and improves drying condition limitation.
Description
Technical field
The present invention relates to a kind of water-based spinning coatings and preparation method thereof, and in particular to a kind of fast-drying aqueous weaving painting of environmental protection
Layer and preparation method thereof.
Background technique
Emulsification lotion is the paint that film forming matter is prepared after water-thinned paints refers to, keeps solvent type resin molten in organic solvent,
Then so that resin dispersion is formed lotion in water by strong mechanical stirring with the help of emulsifier, referred to as after emulsify lotion,
Manufactured paint can be diluted in construction with water；Water-based spinning coating is not available compared with high glass transition temperature resin at present, is caused
Drying time is slow, increases baking temperature and time, generates environmental issue；In addition drying problem also annoyings water-based spinning coating
User, if using more drying equipment, and energy loss is caused, generate secondary environmental issue.
Summary of the invention
(1) technical problems to be solved
To solve the above problems, the invention proposes a kind of fast-drying aqueous spinning coatings of environmental protection and preparation method thereof, so that
Drying temperature reduces, and drying time shortens, and improves drying condition limitation, and the low temperature drying for expanding water-based spinning coating uses
Performance.
(2) technical solution
The fast-drying aqueous spinning coating of environmental protection of the invention；Including 80~100 parts of water-base resin, nanometer heat setting vresin 1~5
Part, 2~5 parts of water, assist 0.15~1.5 part of film forming matter, 0.5~1 part of thickener, 0.5~1 part of levelling agent and wetting agent 0.5~
1 part.
It further include 0.5~1 part of dispersing agent as a better embodiment of the present embodiment.
As a better embodiment of the present embodiment, the dispersing agent is Siloxane-Oxyalkylene Copolymers class dispersing agent.
It further include 0.5~1 part of defoaming agent as a better embodiment of the present embodiment.
As a better embodiment of the present embodiment, the defoaming agent is the aqueous solid and polysiloxanes of polyethylene glycol
Mixture class defoaming agent.
As a better embodiment of the present embodiment, the heat setting vresin is the aqueous heat setting vresin of nano inorganic.
As a better embodiment of the present embodiment, the thickener is the swollen class thickener of alkali soluble.
The preparation method of the fast-drying aqueous spinning coating of environmental protection of the invention, it is characterised in that: the method is specific as follows: point
It does not prepare in accordance with the following steps:
The first step sequentially adds water-base resin, nanometer heat setting vresin, dispersing agent, wetting agent by formula, stirs at low speed 5 points
Clock, and revolving speed is stepped up to 600~700 turns, obtain product I；
Second step is added after levelling agent high speed dispersion 15 minutes into product I, and defoaming agent reduction of speed is added and stirs 5 minutes, obtains
To product II；
Third step is added thickener into product II and adjusts viscosity, obtains product III；
4th step by product III by obtaining product after 200 mesh net filtrations, and is packed.
As preferred embodiment, wherein water-base resin and the water of thickener equal proportion are diluted.
Further include filler as preferred embodiment, the filler is titanium dioxide, calcium carbonate, it is a kind of in talcum powder or
It is several.
As preferred embodiment, the heat setting vresin is nano inorganic material.
As preferred embodiment, the defoaming agent is the aqueous solid of polyethylene glycol and the mixture class of polysiloxanes
Defoaming agent.
As preferred embodiment, the thickener is the swollen class thickener of alkali soluble.
(3) beneficial effect
Compared with prior art, the fast-drying aqueous spinning coating of environmental protection and preparation method thereof of the invention, the feature of environmental protection improves, and does
It is dry simple, reduce energy loss；Due to using reduced TG tenderness resin, so that substrate adhesion increases；Operate environmental requirement
Relax, reduces probability of unsuccessfully doing over again；Reduce cost；Improve hardness.
Specific embodiment
Embodiment one: the fast-drying aqueous spinning coating of environmental protection of the invention, the component mass ratio composition: water-base resin 90
Part, nanometer heat setting vresin 3, and the water 3 of this nanometer of heat setting vresin is dissolved, auxiliary film forming matter 1, thickener 0.75, levelling agent 0.65,
And the water 0.75 of dilution thickener, wetting agent 0.85.
The first step sequentially adds water-base resin, nanometer heat setting vresin, dispersing agent, wetting agent by formula, stirs at low speed 5 points
Clock, and revolving speed is stepped up to 600 turns, obtain product I；
Second step is added after levelling agent high speed dispersion 15 minutes into product I, and defoaming agent reduction of speed is added and stirs 5 minutes, obtains
To product II；
Third step is added thickener into product II and adjusts viscosity, obtains product III；
4th step by product III by obtaining product after 200 mesh net filtrations, and is packed.
Wherein, heat setting vresin is nano inorganic material, and granular size is 14 nanometers.
Embodiment two: the fast-drying aqueous spinning coating of environmental protection of the invention, the component mass ratio composition: water-base resin 80
Part, 1 part of nanometer heat setting vresin, and dissolve 1 part of water of this nanometer of heat setting vresin, assist 0.15 part of film forming matter, 0.5 part of thickener,
0.5 part of levelling agent, and dilution 0.5 part of water, 0.5 part of wetting agent of thickener.
The first step sequentially adds water-base resin, nanometer heat setting vresin, dispersing agent, wetting agent by formula, stirs at low speed 5 points
Clock, and revolving speed is stepped up to 600 turns, obtain product I；
Second step is added after levelling agent high speed dispersion 10 minutes into product I, and defoaming agent reduction of speed is added and stirs 5 minutes, obtains
To product II；
Third step is added thickener into product II and adjusts viscosity, obtains product III；
4th step by product III by obtaining product after 200 mesh net filtrations, and is packed.
Wherein, heat setting vresin is nano inorganic material, and granular size is 14 nanometers.
Embodiment three: the fast-drying aqueous spinning coating of environmental protection of the invention, the component mass ratio composition: water-base resin 100
Part, 5 parts of nanometer heat setting vresin, and dissolve 5 parts of water of this nanometer of heat setting vresin, assist 1.5 parts of film forming matter, 1 part of thickener, levelling
1 part of agent, and dilution 1 part of water, 1 part of wetting agent of thickener.
The first step sequentially adds water-base resin, nanometer heat setting vresin, dispersing agent, wetting agent by formula, stirs at low speed 5 points
Clock, and revolving speed is stepped up to 700 turns, obtain product I；
Second step is added after levelling agent high speed dispersion 15 minutes into product I, and defoaming agent reduction of speed is added and stirs 5 minutes, obtains
To product II；
Third step is added thickener into product II and adjusts viscosity, obtains product III；
4th step by product III by obtaining product after 200 mesh net filtrations, and is packed.
Wherein, heat setting vresin is nano inorganic material, and granular size is 14 nanometers.
Further, in above three embodiments:
Heat setting vresin is nano inorganic material.
Dispersing agent is Siloxane-Oxyalkylene Copolymers class dispersing agent.
Defoaming agent is the aqueous solid of polyethylene glycol and the mixture class defoaming agent of polysiloxanes.
Thickener is the swollen class thickener of alkali soluble.,
Effect example:
Coated substrate is dried in drying oven, and drying temperature is oven temperature.
| Embodiment 1 | Embodiment 2 | Embodiment 3 | The prior art | |
| Drying temperature | 80 | 77 | 85 | 90 DEG C or more |
| Drying time | 70s | 80s | 77s | 10 minutes or more |
The standard that drying time selects is the drying in forced air convection baking oven, corresponding with drying temperature.
Fast-drying aqueous spinning coating of environmental protection of the invention and preparation method thereof, using low Tg resin, cooperation is received
The use of rice heat setting vresin, the hydroxyl condensation for playing self-crosslinking react, the stringent limitation of solution drying condition, coating fast drying,
Since main plexiglas temperature is low, attaching is puted forth effort.
The above-described embodiments are merely illustrative of preferred embodiments of the present invention, not to structure of the invention
Think and range is defined.Without departing from the design concept of the invention, ordinary people in the field is to technology of the invention
The all variations and modifications that scheme is made, should all drop into protection scope of the present invention, the claimed technology contents of the present invention,
It is all described in the claims.
Claims (8)
1. a kind of fast-drying aqueous spinning coating of environmental protection, which is characterized in that including 80~100 parts of water-base resin, nanometer heat setting vresin 1
~5 parts, 2~5 parts of water, assist 0.15~1.5 part of film forming matter, 0.5~1 part of thickener, 0.5~1 part of levelling agent and wetting agent
0.5~1 part.
2. the fast-drying aqueous spinning coating of environmental protection according to claim 1, it is characterised in that: further include dispersing agent 0.5~1
Part.
3. the fast-drying aqueous spinning coating of environmental protection according to claim 2, it is characterised in that: the dispersing agent is polyether-modified
Polysiloxane-based dispersing agent.
4. the fast-drying aqueous spinning coating of environmental protection according to claim 2, it is characterised in that: further include defoaming agent 0.5~1
Part.
5. the fast-drying aqueous spinning coating of environmental protection according to claim 4, it is characterised in that: the defoaming agent is polyethylene glycol
Aqueous solid and polysiloxanes mixture class defoaming agent.
6. the fast-drying aqueous spinning coating of environmental protection according to claim 1, it is characterised in that: the heat setting vresin is nanometer nothing
The aqueous heat setting vresin of machine.
7. the fast-drying aqueous spinning coating of environmental protection according to claim 1, it is characterised in that: the thickener is the swollen class of alkali soluble
Thickener.
8. a kind of preparation method of the fast-drying aqueous spinning coating of environmental protection characterized by comprising
The first step sequentially adds water-base resin, nanometer heat setting vresin, dispersing agent, wetting agent by formula, stirs at low speed 5 minutes, and
Revolving speed is stepped up to 600~700 turns, obtains product I；
Second step is added after levelling agent high speed dispersion 15 minutes into product I, and defoaming agent reduction of speed is added and stirs 5 minutes, is produced
Object II；
Third step is added thickener into product II and adjusts viscosity, obtains product III；
4th step by product III by obtaining product after 200 mesh net filtrations, and is packed.