CN109181485A - A kind of anti-corrosion terrace priming paint - Google Patents
A kind of anti-corrosion terrace priming paint Download PDFInfo
- Publication number
- CN109181485A CN109181485A CN201811043916.XA CN201811043916A CN109181485A CN 109181485 A CN109181485 A CN 109181485A CN 201811043916 A CN201811043916 A CN 201811043916A CN 109181485 A CN109181485 A CN 109181485A
- Authority
- CN
- China
- Prior art keywords
- bisphenol
- curing agent
- catalyst
- epoxide resin
- priming paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention includes modified epoxy, curing agent and catalyst, and the mass parts ratio of the modified epoxy, curing agent and catalyst is 30-40,20-30,25-30；The modified epoxy is bisphenol A epoxide resin；The bisphenol A epoxide resin is prepared by the raw material of following parts by weight: phenol 20-40, acetone 50-60 and hydrogen chloride 5-15；The curing agent is the Polyamide Epoxy of 50-60 parts by weight；The preparation method of the bisphenol A epoxide resin, include the following steps: to be sufficiently mixed a certain amount of acetone with phenol in closed container, make catalyst with dry hydrogen chloride to be reacted under normal pressure, regulating and controlling temperature reacts at 50-60 DEG C, 8-9h is reacted, so that gas phase chlorination hydrogen concentration is maintained at 96% or more during reflection.Primary raw material of the bisphenol A epoxide resin as terrace is used in the present invention, there is excellent mechanical property, and easy processing, setting rate are fast, it is corrosion-resistant.
Description
Technical field
The present invention relates to technical fields, more particularly to a kind of anti-corrosion terrace priming paint.
Background technique
Epoxide terrace is alternatively referred to as epoxy ground, is to use epoxide terrace paint, in conjunction with specific terrace construction technique, field ground
One kind terrace made of decoration construction.Epoxide terrace is used for functional terrace from the outset: such as anti-corrosion, wear-resisting, anti-skidding, developing to
General general industry terrace；In addition to functional requirement, also there is good decorative effect.It is obtained in industry ground slab
On the basis of must being widely applied, with the continuous improvement of people's living standards, being promoted and applied in house decoration.Ground
Level ground paint has become China's one of industry with the fastest developing speed, is suitable for various places, such as: workshop, computer room, warehouse, laboratory,
Ward, operating room, workshop etc..
Increase in demand of the workshop for the anti-static function of terrace in existing construction technology, will appear ground in use
The phenomenon that level ground anti-static effect is poor, terrace blistering or delamination, affects anti-static effect, the service life of terrace shortens.
Summary of the invention
In order to overcome the above-mentioned deficiencies of the prior art, the present invention provides a kind of anti-corrosion terrace priming paint.
The technical scheme adopted by the invention is that: a kind of anti-corrosion terrace priming paint, including modified epoxy, curing agent and
The mass parts ratio of catalyst, the modified epoxy, curing agent and catalyst is 30-40,20-30,25-30.
Further, the modified epoxy is bisphenol A epoxide resin.
Further, the bisphenol A epoxide resin is prepared by the raw material of following parts by weight: phenol 20-40, acetone
50-60 and hydrogen chloride 5-15.
Further, the curing agent is the Polyamide Epoxy of 50-60 parts by weight.
Further, the preparation method of the bisphenol A epoxide resin, including the following steps: will be certain in closed container
The acetone of amount is sufficiently mixed with phenol, is made catalyst with dry hydrogen chloride and is reacted under normal pressure, regulating and controlling temperature reacts on
At 50-60 DEG C, 8-9h is reacted, so that gas phase chlorination hydrogen concentration is maintained at 96% or more during reflection.
Compared with prior art, the beneficial effects of the present invention are: using bisphenol A epoxide resin as terrace in the present invention
Primary raw material has excellent mechanical property, and easy processing, setting rate are fast, corrosion-resistant.
Specific embodiment
In order to deepen the understanding of the present invention, below with reference to embodiment, the present invention is further described, which only uses
In explaining the present invention, protection scope of the present invention is not constituted and limited.
Embodiment 1:
A kind of anti-corrosion terrace priming paint, including modified epoxy, curing agent and catalyst, the modified epoxy, solidification
The mass parts of agent and catalyst ratio is 30,20,25.
In the above-described embodiments, modified epoxy is bisphenol A epoxide resin, and the bisphenol A epoxide resin is by following heavy
The raw material of amount part is prepared: phenol 25, acetone 53 and hydrogen chloride 7, and the curing agent is the daiamid epoxy tree of 50 parts by weight
Rouge.
In the above-described embodiments, the preparation method of bisphenol A epoxide resin includes the following steps: one in closed container
Quantitative acetone is sufficiently mixed with phenol, is made catalyst with dry hydrogen chloride and is reacted under normal pressure, regulating and controlling temperature reaction
At 50 DEG C, 8h is reacted, so that gas phase chlorination hydrogen concentration is maintained at 96% or more during reflection.
Embodiment 2:
A kind of anti-corrosion terrace priming paint, including modified epoxy, curing agent and catalyst, the modified epoxy, solidification
The mass parts of agent and catalyst ratio is 30,30,30.
In the above-described embodiments, modified epoxy is bisphenol A epoxide resin, and the bisphenol A epoxide resin is by following heavy
The raw material of amount part is prepared: phenol 35, acetone 58 and hydrogen chloride 12, and the curing agent is the daiamid epoxy tree of 60 parts by weight
Rouge.
In the above-described embodiments, the preparation method of bisphenol A epoxide resin includes the following steps: one in closed container
Quantitative acetone is sufficiently mixed with phenol, is made catalyst with dry hydrogen chloride and is reacted under normal pressure, regulating and controlling temperature reaction
At 60 DEG C, 9h is reacted, so that gas phase chlorination hydrogen concentration is maintained at 96% or more during reflection.
What the embodiment of the present invention was announced is preferred embodiment, and however, it is not limited to this, the ordinary skill people of this field
Member, easily according to above-described embodiment, understands spirit of the invention, and make different amplification and variation, but as long as not departing from this
The spirit of invention, all within the scope of the present invention.
Claims (5)
1. a kind of anti-corrosion terrace priming paint, it is characterised in that: including modified epoxy, curing agent and catalyst, the modification
The mass parts ratio of epoxy resin, curing agent and catalyst is 30-40,20-30,25-30.
2. anti-corrosion terrace priming paint according to claim 1, it is characterised in that: the modified epoxy is bisphenol-A ring
Oxygen resin.
3. anti-corrosion terrace priming paint according to claim 2, it is characterised in that: the bisphenol A epoxide resin is by following heavy
The raw material of amount part is prepared: phenol 20-40, acetone 50-60 and hydrogen chloride 5-15.
4. anti-corrosion terrace priming paint according to claim 1, it is characterised in that: the curing agent is 50-60 parts by weight
Polyamide Epoxy.
5. the preparation method of the bisphenol A epoxide resin according to Claims 2 or 3, characterized by the following steps:
A certain amount of acetone is sufficiently mixed with phenol in closed container, makees catalyst with dry hydrogen chloride and carries out under normal pressure instead
It answers, regulating and controlling temperature reacts at 50-60 DEG C, reacts 8-9h, so that gas phase chlorination hydrogen concentration is maintained at 96% or more during reflection.