CN109161314A - A kind of insulated paint and preparation method thereof prepared using recycled PET as raw material - Google Patents
A kind of insulated paint and preparation method thereof prepared using recycled PET as raw material Download PDFInfo
- Publication number
- CN109161314A CN109161314A CN201810891354.8A CN201810891354A CN109161314A CN 109161314 A CN109161314 A CN 109161314A CN 201810891354 A CN201810891354 A CN 201810891354A CN 109161314 A CN109161314 A CN 109161314A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- recycled pet
- prepared
- insulated paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of insulated paint prepared using recycled PET as raw material, and prepared by the raw material of following quality proportioning: recycled PET is sliced 300-350 parts, 200-230 parts of glycerol, 0.5-1 parts of zinc acetate, 80-100 parts of propylene glycol, 400-500 parts of maleic anhydride, 1-1.5 parts of hydroquinone, 1000-1100 parts of styrene, 15-20 parts of cumyl peroxide.The raw material that the present invention uses cheaply preferably obtains;Solidfied material high mechanical strength, coil are firmly bonded, excellent insulating property;Extension paint amount is plentiful, and paint film is rich in toughness.
Description
Technical field
The present invention relates to insulated paint fields, and in particular to a kind of insulated paint prepared using recycled PET as raw material and its preparation
Method.
Background technique
China is polyethylene terephthalate (PET) bottle consumption big country, can all generate a large amount of waste PET every year
Bottle, but since domestic recycling approach basic source is in roadside stands, and the reclaimer of most of domestic recycling producers is especially clear
It washes equipment to fall behind, causes the PET quality of recycling lower;Along with reducing product through degrading when extruder secondary operation
Viscosity;In addition, a series of problems, such as that there is also flow stabilities is poor, crystallization rate is slow, product impact is poor, so that recycled PET
Reprocessing using being restricted.
Recycled PET is not applied in insulated paint also at present.
Based on the above situation, the invention proposes a kind of insulated paint and preparation method thereof prepared using recycled PET as raw material
Problem above can effectively be solved.
Summary of the invention
The purpose of the present invention is to provide a kind of insulated paint and preparation method thereof prepared using recycled PET as raw material.This hair
The raw material of bright use cheaply preferably obtains;Solidfied material high mechanical strength, coil are firmly bonded, excellent insulating property;It is plentiful to hang paint amount, paint
Film is rich in toughness.
The present invention is achieved through the following technical solutions:
A kind of insulated paint prepared using recycled PET as raw material, prepared by the raw material of following quality proportioning: recycled PET is sliced
300-350 parts, it is 200-230 parts of glycerol, 0.5-1 parts of zinc acetate, 80-100 parts of propylene glycol, 400-500 parts of maleic anhydride, right
1-1.5 parts of benzenediol, 1000-1100 parts of styrene, 15-20 parts of cumyl peroxide.
As a preferred embodiment, prepared by the raw material of following quality proportioning: recycled PET is sliced 310-340 parts, glycerol
210-220 parts, 0.8-1 parts of zinc acetate, 85-95 parts of propylene glycol, 425-470 parts of maleic anhydride, hydroquinone 1.1-1.5
Part, 1050-1100 parts of styrene, 18-19 parts of cumyl peroxide.
A kind of insulated paint prepared using recycled PET as raw material the preparation method is as follows:
A, 300-350 parts of recycled PET slice, 200-230 parts of glycerol, 0.5-1 parts of zinc acetate are put into reaction kettle together,
200-205 DEG C of heat temperature raising heat preservation opens stirring in 4 hours, continues heat preservation 5 hours;
B, propylene glycol 80-100 parts, 400-500 parts of maleic anhydride, 1-1.5 parts of hydroquinone are then put into, then is heated up
To 200 DEG C, heat preservation to acid value is less than 10mgkoH/g;
C, 50 DEG C slowly are cooled to by 1000-1100 parts of addition reaction kettles of styrene;
D, cumyl peroxide 15-20 parts is added to stir evenly.
As a preferred embodiment, a kind of insulated paint prepared using recycled PET as raw material the preparation method is as follows:
A, 310-340 parts of recycled PET slice, 210-220 parts of glycerol, 0.8-1 parts of zinc acetate are put into reaction kettle together,
200-205 DEG C of heat temperature raising heat preservation opens stirring in 4 hours, continues heat preservation 5 hours;
B, propylene glycol 85-95 parts, 425-470 parts of maleic anhydride, 1.1-1.5 parts of hydroquinone are then put into, then is risen
For temperature to 200 DEG C, heat preservation to acid value is less than 10mgkoH/g;
C, 50 DEG C slowly are cooled to by 1050-1100 parts of addition reaction kettles of styrene;
D, cumyl peroxide 18-19 parts is added to stir evenly.
Compared with prior art, the present invention have the following advantages that and the utility model has the advantages that
The raw material that the present invention uses cheaply preferably obtains;Solidfied material high mechanical strength, coil are firmly bonded, excellent insulating property;
Extension paint amount is plentiful, and paint film is rich in toughness.
Specific embodiment
The present invention is described in further detail below with reference to embodiment, embodiments of the present invention are not limited thereto.
Test method described in following embodiments or test method are unless otherwise specified conventional method;The reagent
And material is obtained from routine business approach, or prepare in conventional manner unless otherwise specified.
Embodiment 1:
A kind of insulated paint prepared using recycled PET as raw material, prepared by the raw material of following quality proportioning: recycled PET is sliced
300-350 parts, it is 200-230 parts of glycerol, 0.5-1 parts of zinc acetate, 80-100 parts of propylene glycol, 400-500 parts of maleic anhydride, right
1-1.5 parts of benzenediol, 1000-1100 parts of styrene, 15-20 parts of cumyl peroxide.
Embodiment 2:
As a preferred embodiment, prepared by the raw material of following quality proportioning: recycled PET is sliced 310-340 parts, glycerol
210-220 parts, 0.8-1 parts of zinc acetate, 85-95 parts of propylene glycol, 425-470 parts of maleic anhydride, hydroquinone 1.1-1.5
Part, 1050-1100 parts of styrene, 18-19 parts of cumyl peroxide.
Embodiment 3:
A kind of insulated paint prepared using recycled PET as raw material the preparation method is as follows:
A, 300-350 parts of recycled PET slice, 200-230 parts of glycerol, 0.5-1 parts of zinc acetate are put into reaction kettle together,
200-205 DEG C of heat temperature raising heat preservation opens stirring in 4 hours, continues heat preservation 5 hours;
B, propylene glycol 80-100 parts, 400-500 parts of maleic anhydride, 1-1.5 parts of hydroquinone are then put into, then is heated up
To 200 DEG C, heat preservation to acid value is less than 10mgkoH/g;
C, 50 DEG C slowly are cooled to by 1000-1100 parts of addition reaction kettles of styrene;
D, cumyl peroxide 15-20 parts is added to stir evenly.
Embodiment 4:
A kind of insulated paint prepared using recycled PET as raw material the preparation method is as follows:
A, 310-340 parts of recycled PET slice, 210-220 parts of glycerol, 0.8-1 parts of zinc acetate are put into reaction kettle together,
200-205 DEG C of heat temperature raising heat preservation opens stirring in 4 hours, continues heat preservation 5 hours;
B, propylene glycol 85-95 parts, 425-470 parts of maleic anhydride, 1.1-1.5 parts of hydroquinone are then put into, then is risen
For temperature to 200 DEG C, heat preservation to acid value is less than 10mgkoH/g;
C, 50 DEG C slowly are cooled to by 1050-1100 parts of addition reaction kettles of styrene;
D, cumyl peroxide 18-19 parts is added to stir evenly.
Embodiment 5:
A kind of insulated paint prepared using recycled PET as raw material the preparation method is as follows:
A, 310 parts of recycled PET slice, 210 parts of glycerol, 0.8 part of zinc acetate are put into reaction kettle together, heat temperature raising
200 DEG C of heat preservations open stirring in 4 hours, continue heat preservation 5 hours;
B, 85 parts of propylene glycol, 425 parts of maleic anhydride, 1.1 parts of hydroquinone are then put into, then is warming up to 200 DEG C, is protected
Temperature is less than 10mgkoH/g to acid value;
C, 50 DEG C slowly are cooled to by 1050 parts of addition reaction kettles of styrene;
D, 18 parts of cumyl peroxide are added to stir evenly.
Embodiment 6:
A kind of insulated paint prepared using recycled PET as raw material the preparation method is as follows:
A, 340 parts of recycled PET slice, 220 parts of glycerol, 1 part of zinc acetate are put into reaction kettle together, heat temperature raising 205
DEG C heat preservation opens stirring in 4 hours, continues to keep the temperature 5 hours;
B, 95 parts of propylene glycol, 470 parts of maleic anhydride, 1.5 parts of hydroquinone are then put into, then is warming up to 200 DEG C, is protected
Temperature is less than 10mgkoH/g to acid value;
C, 50 DEG C slowly are cooled to by 1100 parts of addition reaction kettles of styrene;
D, 19 parts of cumyl peroxide are added to stir evenly.
Embodiment 7:
A kind of insulated paint prepared using recycled PET as raw material the preparation method is as follows:
A, 320 parts of recycled PET slice, 215 parts of glycerol, 0.9 part of zinc acetate are put into reaction kettle together, heat temperature raising
200 DEG C of heat preservations open stirring in 4 hours, continue heat preservation 5 hours;
B, 90 parts of propylene glycol, 450 parts of maleic anhydride, 1.3 parts of hydroquinone are then put into, then is warming up to 200 DEG C, is protected
Temperature is less than 10mgkoH/g to acid value;
C, 50 DEG C slowly are cooled to by 1080 parts of addition reaction kettles of styrene;
D, 18.5 parts of cumyl peroxide are added to stir evenly.
The above is only presently preferred embodiments of the present invention, not does limitation in any form to the present invention, it is all according to
According to technical spirit any simple modification to the above embodiments of the invention, equivalent variations, protection of the invention is each fallen within
Within the scope of.
Claims (4)
1. a kind of insulated paint prepared using recycled PET as raw material, it is characterised in that: prepared: being returned by the raw material of following quality proportioning
It receives PET and is sliced 300-350 parts, 200-230 parts of glycerol, 0.5-1 parts of zinc acetate, 80-100 parts of propylene glycol, maleic anhydride
400-500 parts, 1-1.5 parts of hydroquinone, 1000-1100 parts of styrene, 15-20 parts of cumyl peroxide.
2. the insulated paint according to claim 1 prepared using recycled PET as raw material, it is characterised in that: matched by following quality
It is prepared by the raw material of ratio: recycled PET be sliced 310-340 parts, 210-220 parts of glycerol, 0.8-1 parts of zinc acetate, 85-95 parts of propylene glycol,
425-470 parts of maleic anhydride, 1.1-1.5 parts of hydroquinone, 1050-1100 parts of styrene, cumyl peroxide 18-19
Part.
3. the insulated paint according to claim 1 prepared using recycled PET as raw material, it is characterised in that: described with recycled PET
For raw material preparation insulated paint the preparation method is as follows:
A, 300-350 parts of recycled PET slice, 200-230 parts of glycerol, 0.5-1 parts of zinc acetate are put into reaction kettle together, is heated
200-205 DEG C of heat preservation of heating opens stirring in 4 hours, continues heat preservation 5 hours;
B, propylene glycol 80-100 parts, 400-500 parts of maleic anhydride, 1-1.5 parts of hydroquinone are then put into, then is warming up to
200 DEG C, heat preservation to acid value is less than 10mgkoH/g;
C, 50 DEG C slowly are cooled to by 1000-1100 parts of addition reaction kettles of styrene;
D, cumyl peroxide 15-20 parts is added to stir evenly.
4. the insulated paint according to claim 2 prepared using recycled PET as raw material, it is characterised in that: described with recycled PET
For raw material preparation insulated paint the preparation method is as follows:
A, 310-340 parts of recycled PET slice, 210-220 parts of glycerol, 0.8-1 parts of zinc acetate are put into reaction kettle together, is heated
200-205 DEG C of heat preservation of heating opens stirring in 4 hours, continues heat preservation 5 hours;
B, propylene glycol 85-95 parts, 425-470 parts of maleic anhydride, 1.1-1.5 parts of hydroquinone are then put into, then is warming up to
200 DEG C, heat preservation to acid value is less than 10mgkoH/g;
C, 50 DEG C slowly are cooled to by 1050-1100 parts of addition reaction kettles of styrene;
D, cumyl peroxide 18-19 parts is added to stir evenly.