CN109137496A - A kind of preparation method of soft antibacterial non-woven fabrics - Google Patents
A kind of preparation method of soft antibacterial non-woven fabrics Download PDFInfo
- Publication number
- CN109137496A CN109137496A CN201810960296.XA CN201810960296A CN109137496A CN 109137496 A CN109137496 A CN 109137496A CN 201810960296 A CN201810960296 A CN 201810960296A CN 109137496 A CN109137496 A CN 109137496A
- Authority
- CN
- China
- Prior art keywords
- woven fabrics
- parts
- antibacterial
- preparation
- soft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of preparation method of soft antibacterial non-woven fabrics, including following operating procedure: (1) by N, N- dimethylamino ethyl acrylate, t-butylaminoethyl methacrylate mixing after, continue thereto be added dehydrated alcohol be used as solvent, stir with, initiator is added, heating is condensed back reaction, is rinsed using deionized water, drying, obtains the antibacterial agent of white powder；(2) alpha-arbutin, stearoyl lactate, octyl benzene oxygen polyethyleneoxy are added into acetone, softening agent is made；(3) after mixing by antibacterial agent, softening agent, dispersing agent, acetone, non-woven fabrics finishing fluid is made；(4) it by non-woven fabrics normal temperature dipping in non-woven fabrics finishing fluid after immersion treatment, takes out non-woven fabrics, after pre-dried, then is rinsed using deionized water, be dried, soft antibacterial non-woven fabrics is made.Soft antibacterial non-woven fabrics produced by the present invention, anti-microbial property is excellent, and pliability is higher, excellent quality.
Description
Technical field
The invention belongs to antibacterial nonwoven cloth preparation technical fields, and in particular to a kind of preparation side of soft antibacterial non-woven fabrics
Method.
Background technique
Non-woven fabrics is also known as nonwoven fabric, is made of fiber orient or random, because of appearance and certain property with cloth
Can and be called cloth.Non-woven fabrics has moisture-proof, ventilative, flexible, light, not combustion-supporting, easy decomposition, nontoxic nonirritant, color
The features such as abundant, cheap, recyclable, mostly using polypropylene (pp material) pellet is raw material, through high-temperature fusion, spray
Silk, paving guiding principle, hot pressing are batched continuous one-step and are produced.Antibacterial nonwoven cloth is the environment-friendly materials of a new generation, such product has
The advantages that strength is high, protective performance is excellent, breathes freely comfortable, environmentally friendly, non-toxic and tasteless, is currently widely used for medicine and hygiene fields,
Such as operation dress, operating cap, surgical packs, operation cover, sterilization bandage, protective garment.But in the prior art, antibacterial obtained
Non-woven fabrics, although antibacterial effect is excellent, antibacterial material can seriously affect the pliability of non-woven fabrics, cause non-woven fabrics there is
The poor technological deficiency of pliability.
Summary of the invention
In order to solve the above technical problem, the present invention provides a kind of preparation methods of soft antibacterial non-woven fabrics.
The present invention is achieved by the following technical solutions.
A kind of preparation method of soft antibacterial non-woven fabrics, including following operating procedure:
(1) by weight, by 33-45 parts of N, N- dimethylamino ethyl acrylate, 20-25 parts of t-butyl aminoethyls
Ethyl ester after mixing, continues to be added 33-40 parts of dehydrated alcohols thereto as solvent, stirs with after, continue to add thereto
Enter 0.1-0.4 parts of initiators, under nitrogen protection, 78-82 DEG C is warming up to, after being condensed back reaction 2-3 hours, using deionization
The polymerizate that water rinses after drying, obtains the antibacterial agent of white powder；
(2) by weight, by 11-16 parts of alpha-arbutins, 5-9 parts of stearoyl lactates, 1-4 parts of octyl benzene oxygen polyethyleneoxies
It is added into 20-25 parts of acetone, softening agent is made；
(3) by weight, 3-9 parts of antibacterial agents, 11-15 parts of softening agents, 1-2 parts of dispersing agents, 75-80 parts of acetone are uniformly mixed
Afterwards, non-woven fabrics finishing fluid is made；
(4) by non-woven fabrics normal temperature dipping in non-woven fabrics finishing fluid after immersion treatment 20-25min, non-woven fabrics is taken out, at predrying
After reason, then using deionized water rinse after, be dried, be made soft antibacterial non-woven fabrics.
Specifically, in above-mentioned steps (1), initiator is di-isopropyl peroxydicarbonate, two hexamethylene of dicetyl peroxydicarbonate
Any one in ester.
Specifically, in above-mentioned steps (3), dispersing agent is triethyl group hexyl phosphoric acid, any one in lauryl sodium sulfate
Kind.
Specifically, in above-mentioned steps (4), the mass ratio of non-woven fabrics and non-woven fabrics finishing fluid is 1:3-5.
Specifically, in above-mentioned steps (4), the temperature of pre-dried is 45 DEG C, and the time of pre-dried is 30min,
The temperature of drying process is 75-80 DEG C, and the time of drying process is 60-80min.
From the above technical scheme, it can be seen that the beneficial effects of the present invention are:
A kind of preparation method of soft antibacterial non-woven fabrics provided by the invention, process flow is short, easy to operate, obtained soft anti-
Bacterium non-woven fabrics, anti-microbial property is excellent, and pliability is higher, excellent quality.Wherein, white powder made from step (1)
Antibacterial agent can effectively inhibit the growth and breeding of pathogenic microorganisms, while the bond strength of antibacterial agent and non-woven fabrics is high, amino
In the presence of, moreover it is possible to the effective surface energy for promoting non-woven fabrics enhances the pliability of non-woven fabrics；The softening agent that step (2) provides, α-bear
Fruit glycosides can effectively promote the color of non-woven fabrics and further promote the flexibility of non-woven fabrics, stearoyl lactate, pungent
Base benzene oxygen polyethyleneoxy can further promote the surface energy of non-woven fabrics, enhance the elasticity and pliability of non-woven fabrics.
Specific embodiment
The following examples are intended to illustrate the invention but are not intended to limit the scope of the invention.Reality used in the examples
The condition of applying can be for further adjustments according to the condition of producer, and unaccounted implementation condition is usually conventional laboratory conditions.
Embodiment 1
A kind of preparation method of soft antibacterial non-woven fabrics, including following operating procedure:
(1) by weight, by 33 parts of N, N- dimethylamino ethyl acrylate, 20 parts of t-butylaminoethyl methacrylates are mixed
After conjunction uniformly, continues to be added 33 parts of dehydrated alcohols thereto as solvent, stir with after, continuation is added 0.1 part thereto and draws
Agent is sent out, under nitrogen protection, is warming up to 78 DEG C, after being condensed back reaction 2 hours, is produced using the polymerization that deionized water is rinsed
Object after drying, obtains the antibacterial agent of white powder；
(2) by weight, by 11 parts of alpha-arbutins, 5 parts of stearoyl lactates, 1 part of octyl benzene oxygen polyethyleneoxy be added to
In 20 parts of acetone, softening agent is made；
(3) by weight, nothing after mixing by 3 parts of antibacterial agents, 11 parts of softening agents, 1 part of dispersing agent, 75 parts of acetone, is made
Woven fabric finishing fluid；
(4) non-woven fabrics normal temperature dipping after immersion treatment 20min, is taken out into non-woven fabrics, pre-dried in non-woven fabrics finishing fluid
Afterwards, it after then being rinsed using deionized water, is dried, soft antibacterial non-woven fabrics is made.
Specifically, in above-mentioned steps (1), initiator is di-isopropyl peroxydicarbonate.
Specifically, in above-mentioned steps (3), dispersing agent is triethyl group hexyl phosphoric acid.
Specifically, in above-mentioned steps (4), the mass ratio of non-woven fabrics and non-woven fabrics finishing fluid is 1:3.
Specifically, in above-mentioned steps (4), the temperature of pre-dried is 45 DEG C, and the time of pre-dried is 30min,
The temperature of drying process is 75 DEG C, and the time of drying process is 60min.
Embodiment 2
A kind of preparation method of soft antibacterial non-woven fabrics, including following operating procedure:
(1) by weight, by 38 parts of N, N- dimethylamino ethyl acrylate, 23 parts of t-butylaminoethyl methacrylates are mixed
After conjunction uniformly, continues to be added 36 parts of dehydrated alcohols thereto as solvent, stir with after, continuation is added 0.3 part thereto and draws
Agent is sent out, under nitrogen protection, 80 DEG C is warming up to, is condensed back after reacting 2.5 hours, the polymerization rinsed using deionized water
Product after drying, obtains the antibacterial agent of white powder；
(2) by weight, by 13 parts of alpha-arbutins, 7 parts of stearoyl lactates, 3 parts of octyl benzene oxygen polyethyleneoxies be added to
In 23 parts of acetone, softening agent is made；
(3) by weight, nothing after mixing by 6 parts of antibacterial agents, 13 parts of softening agents, 2 parts of dispersing agents, 78 parts of acetone, is made
Woven fabric finishing fluid；
(4) non-woven fabrics normal temperature dipping after immersion treatment 23min, is taken out into non-woven fabrics, pre-dried in non-woven fabrics finishing fluid
Afterwards, it after then being rinsed using deionized water, is dried, soft antibacterial non-woven fabrics is made.
Specifically, in above-mentioned steps (1), initiator is di-isopropyl peroxydicarbonate.
Specifically, in above-mentioned steps (3), dispersing agent is lauryl sodium sulfate.
Specifically, in above-mentioned steps (4), the mass ratio of non-woven fabrics and non-woven fabrics finishing fluid is 1:4.
Specifically, in above-mentioned steps (4), the temperature of pre-dried is 45 DEG C, and the time of pre-dried is 30min,
The temperature of drying process is 78 DEG C, and the time of drying process is 70min.
Embodiment 3
A kind of preparation method of soft antibacterial non-woven fabrics, including following operating procedure:
(1) by weight, by 45 parts of N, N- dimethylamino ethyl acrylate, 25 parts of t-butylaminoethyl methacrylates are mixed
After conjunction uniformly, continues to be added 40 parts of dehydrated alcohols thereto as solvent, stir with after, continuation is added 0.4 part thereto and draws
Agent is sent out, under nitrogen protection, is warming up to 82 DEG C, after being condensed back reaction 3 hours, is produced using the polymerization that deionized water is rinsed
Object after drying, obtains the antibacterial agent of white powder；
(2) by weight, by 16 parts of alpha-arbutins, 9 parts of stearoyl lactates, 4 parts of octyl benzene oxygen polyethyleneoxies be added to
In 25 parts of acetone, softening agent is made；
(3) by weight, nothing after mixing by 9 parts of antibacterial agents, 15 parts of softening agents, 2 parts of dispersing agents, 80 parts of acetone, is made
Woven fabric finishing fluid；
(4) non-woven fabrics normal temperature dipping after immersion treatment 25min, is taken out into non-woven fabrics, pre-dried in non-woven fabrics finishing fluid
Afterwards, it after then being rinsed using deionized water, is dried, soft antibacterial non-woven fabrics is made.
Specifically, in above-mentioned steps (1), initiator is di-cyclohexylperoxy di-carbonate.
Specifically, in above-mentioned steps (3), dispersing agent is lauryl sodium sulfate.
Specifically, in above-mentioned steps (4), the mass ratio of non-woven fabrics and non-woven fabrics finishing fluid is 1:5.
Specifically, in above-mentioned steps (4), the temperature of pre-dried is 45 DEG C, and the time of pre-dried is 30min,
The temperature of drying process is 80 DEG C, and the time of drying process is 80min.
Comparative example 1
Step does not add alpha-arbutin in (2), remaining operating procedure is identical with embodiment 1.
Comparative example 2
Stearoyl lactate, octyl benzene oxygen polyethyleneoxy are not added in step (2), remaining operating procedure and embodiment 2 are complete
It is identical.
Soft antibacterial non-woven fabrics is made with the method for each embodiment and comparative example respectively, then tests its bactericidal property and soft
Softness, test result are as shown in table 1:
The bactericidal property and pliability of 1 soft antibacterial non-woven fabrics of table
As shown in Table 1, soft antibacterial non-woven fabrics made from the present embodiment, anti-microbial property is excellent, and pliability is good, and quality is excellent
It is different.
It should be understood that the application of the present invention is not limited to the above for those of ordinary skills can
With improvement or transformation based on the above description, all these modifications and variations all should belong to the guarantor of appended claims of the present invention
Protect range.
Claims (5)
1. a kind of preparation method of soft antibacterial non-woven fabrics, which is characterized in that including following operating procedure:
(1) by weight, by 33-45 parts of N, N- dimethylamino ethyl acrylate, 20-25 parts of t-butyl aminoethyls
Ethyl ester after mixing, continues to be added 33-40 parts of dehydrated alcohols thereto as solvent, stirs with after, continue to add thereto
Enter 0.1-0.4 parts of initiators, under nitrogen protection, 78-82 DEG C is warming up to, after being condensed back reaction 2-3 hours, using deionization
The polymerizate that water rinses after drying, obtains the antibacterial agent of white powder；
(2) by weight, by 11-16 parts of alpha-arbutins, 5-9 parts of stearoyl lactates, 1-4 parts of octyl benzene oxygen polyethyleneoxies
It is added into 20-25 parts of acetone, softening agent is made；
(3) by weight, 3-9 parts of antibacterial agents, 11-15 parts of softening agents, 1-2 parts of dispersing agents, 75-80 parts of acetone are uniformly mixed
Afterwards, non-woven fabrics finishing fluid is made；
(4) by non-woven fabrics normal temperature dipping in non-woven fabrics finishing fluid after immersion treatment 20-25min, non-woven fabrics is taken out, at predrying
After reason, then using deionized water rinse after, be dried, be made soft antibacterial non-woven fabrics.
2. a kind of preparation method of soft antibacterial non-woven fabrics according to claim 1, which is characterized in that above-mentioned steps (1)
In, initiator is di-isopropyl peroxydicarbonate, any one in di-cyclohexylperoxy di-carbonate.
3. a kind of preparation method of soft antibacterial non-woven fabrics according to claim 1, which is characterized in that above-mentioned steps (3)
In, dispersing agent is triethyl group hexyl phosphoric acid, any one in lauryl sodium sulfate.
4. a kind of preparation method of soft antibacterial non-woven fabrics according to claim 1, which is characterized in that above-mentioned steps (4)
In, the mass ratio of non-woven fabrics and non-woven fabrics finishing fluid is 1:3-5.
5. a kind of preparation method of soft antibacterial non-woven fabrics according to claim 1, which is characterized in that above-mentioned steps (4)
In, the temperature of pre-dried is 45 DEG C, and the time of pre-dried is 30min, and the temperature of drying process is 75-80 DEG C, is done
The time of dry processing is 60-80min.