CN105040431A - Finishing process for garment material - Google Patents
Finishing process for garment material Download PDFInfo
- Publication number
- CN105040431A CN105040431A CN201510352091.XA CN201510352091A CN105040431A CN 105040431 A CN105040431 A CN 105040431A CN 201510352091 A CN201510352091 A CN 201510352091A CN 105040431 A CN105040431 A CN 105040431A
- Authority
- CN
- China
- Prior art keywords
- mass
- parts
- fabric
- garment material
- finishing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a finishing process for a garment material. The finishing process comprises the following steps: 1, fabric weaving; 2, pretreatment; 3, padding treatment. The garment material subjected to the finishing process has the advantages of being resistant to bacteria and washing, and high in hydrophilic performance.
Description
Technical field
The present invention relates to a kind of finishing technique of garment material.
Background technology
Existing a lot of fabric has water proofing property due to technological problems major part, can not possess certain hydrophilicity, sweat can absorb and discharge by the fabric with hydrophilicity rapidly, guarantee drying property when wearing, if sweat can not be discharged timely on skin or on fabric, be easy to cause growing and breeding of bacterium, bring certain disease harm; Existing material treatment technique need to strengthen in this respect, and existing fabric also exists easily wrinkle, not washable problem after finishing technique.
Summary of the invention
The technical problem to be solved in the present invention is to provide one and has anti-microbial property, water-fastness, and has the finishing technique of the garment material of hydrophilicity.
For solving the problem, the present invention adopts following technical scheme: a kind of finishing technique of garment material, is divided into following step:
The first step: weaving of fabric
Second step: pre-treatment
3rd step: pad process.
Further, the concrete of fabric knitting of the described first step is: fabric is woven polyester thing, comprises 100% dacron or polyester cotton, 30-70D, and density is 300-400t.
As preferably, what described pre-treatment was concrete is: first the smoked plum extractive of the trihydroxy methyl ethylene urea of 3.4 parts by mass, 2.6 parts by mass, the olefin(e) acid resin of 1.7 parts by mass are put in the deionized water of 13 parts by mass, stir; Adding the castor oil acid butyl ester sodium sulphate of 1.8 parts by mass, the poly amic acid of 2.7 parts by mass afterwards successively, continue to stir, to fully mixing, forming finishing agent.
Further, describedly pad that process is concrete is: be first mixed in maceration extract by the finishing agent of second step gained, being immersed in by the fabric of first step gained is mixed with in the maceration extract of finishing agent again, each position of fabric can be covered by impregnated liquid, constant temperature drying afterwards.
Further, the described technological parameter related in process that pads is: pH value 4-5; Bake out temperature 80-90 DEG C; Baking temperature 120-130 DEG C/min.
The beneficial effect of the finishing technique of garment material of the present invention is: the overall step of finishing technique of this garment material is relatively simple, and has anti-microbial property through the fabric of this kind of PROCESS FOR TREATMENT, simultaneously more water-fastness, and has certain hydrophilicity.
Detailed description of the invention
A finishing technique for garment material, is divided into following step:
The first step: weaving of fabric
Second step: pre-treatment
3rd step: pad process
The concrete of the fabric knitting of the described first step is: fabric is woven polyester thing, comprises 100% dacron or polyester cotton, 30-70D, and density is 300-400t.What described pre-treatment was concrete is: first the smoked plum extractive of the trihydroxy methyl ethylene urea of 3.4 parts by mass, 2.6 parts by mass, the olefin(e) acid resin of 1.7 parts by mass are put in the deionized water of 13 parts by mass, stir; Adding the castor oil acid butyl ester sodium sulphate of 1.8 parts by mass, the poly amic acid of 2.7 parts by mass afterwards successively, continue to stir, to fully mixing, forming finishing agent.Describedly pad that process is concrete is: be first mixed in maceration extract by the finishing agent of second step gained, then the fabric of first step gained is immersed in is mixed with in the maceration extract of finishing agent, each position of fabric can be covered by impregnated liquid, constant temperature drying afterwards.The described technological parameter related in process that pads is: pH value 4-5; Bake out temperature 80-90 DEG C; Baking temperature 120-130 DEG C/1min.
The beneficial effect of the finishing technique of garment material of the present invention is: the overall step of finishing technique of this garment material is relatively simple, and has anti-microbial property through the fabric of this kind of PROCESS FOR TREATMENT, simultaneously more water-fastness, and has certain hydrophilicity.
The above, be only the specific embodiment of the present invention, but protection scope of the present invention is not limited thereto, and any change of expecting without creative work or replacement, all should be encompassed within protection scope of the present invention.Therefore, the protection domain that protection scope of the present invention should limit with claims is as the criterion.
Claims (5)
1. a finishing technique for garment material, is characterized in that: be divided into following step:
The first step: weaving of fabric
Second step: pre-treatment
3rd step: pad process.
2. the finishing technique of garment material according to claim 1, is characterized in that: the concrete of the fabric knitting of the described first step is: fabric is woven polyester thing, comprises 100% dacron or polyester cotton, 30-70D, and density is 300-400t.
3. the finishing technique of garment material according to claim 1, it is characterized in that: what described pre-treatment was concrete is: first the smoked plum extractive of the trihydroxy methyl ethylene urea of 3.4 parts by mass, 2.6 parts by mass, the olefin(e) acid resin of 1.7 parts by mass are put in the deionized water of 13 parts by mass, stir; Adding the castor oil acid butyl ester sodium sulphate of 1.8 parts by mass, the poly amic acid of 2.7 parts by mass afterwards successively, continue to stir, to fully mixing, forming finishing agent.
4. the finishing technique of garment material according to claim 1, it is characterized in that: described in pad that process is concrete is: first the finishing agent of second step gained is mixed in maceration extract, being immersed in by the fabric of first step gained is mixed with in the maceration extract of finishing agent again, the each position of fabric can be covered by impregnated liquid, constant temperature drying afterwards.
5. the finishing technique of garment material according to claim 1, is characterized in that: the described technological parameter related in process that pads is: pH value 4-5; Bake out temperature 80-90 DEG C; Baking temperature 120-130 DEG C/min.