CN105297417A - Needle-punched non-woven fabric - Google Patents
Needle-punched non-woven fabric Download PDFInfo
- Publication number
- CN105297417A CN105297417A CN201510886547.0A CN201510886547A CN105297417A CN 105297417 A CN105297417 A CN 105297417A CN 201510886547 A CN201510886547 A CN 201510886547A CN 105297417 A CN105297417 A CN 105297417A
- Authority
- CN
- China
- Prior art keywords
- parts
- mass
- finishing
- stir
- finishing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a needle-punched non-woven fabric treated by a finishing process. The finishing process comprises the following steps: (1) adding the following components into 12 parts of de-ionized water in parts by mass: 1-2 parts of zinc stearate, 2.3 parts of octadecyl methacrylate, 1.7 parts of polyoxyethylene trimethyl ammonium chloride and 2.2 parts of sodium chloride, and mixing and uniformly stirring; (2) slowly adding the following components in parts by mass: 1.6 parts of dodecyl trimethyl ammonium bromide, 2.1 parts of triethanolamine oleate, 0.9 part of litsea cubeba essential oil and 1.3 parts of polyacrylic acid, and further stirring until the components are sufficiently and uniformly mixed to prepare a finishing agent; and (3) padding a fabric into an impregnation solution containing the finishing agent to be subjected to padding treatment and drying at a constant temperature. The needle-punched non-woven fabric treated by the finishing process has excellent antibacterial, inflaming retarding and anti-static performances.
Description
Technical field
The present invention relates to needle punched non-woven fabrics.
Background technology
Antibacterial, fire-retardant, the antistatic performance of existing cloth all have much room for improvement.
Summary of the invention
The object of the present invention is to provide a kind of needle punched non-woven fabrics, it is through finishing technique process, has excellent antibacterial, fire-retardant, antistatic performance.
For achieving the above object, technical scheme of the present invention is a kind of needle punched non-woven fabrics of design, and it is through finishing technique process, and this finishing technique comprises the steps:
1) in 12 parts by mass deionized waters, drop into 1 ~ 2 parts by mass zinc stearate, 2.3 parts by mass octadecyl acrylate, 1.7 parts by mass polyethylene glycol oxide trimethyl ammonium chlorides, 2.2 parts by mass sodium chloride mixing, stir;
2) slowly add 1.6 parts by mass DTABs, 2.1 parts by mass trihydroxy ethylamine oleate soaps, 0.9 parts by mass litsea cubeba oil, 1.3 parts by mass polyacrylic acid more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) cloth is padded process in containing the maceration extract of finishing agent, constant temperature drying.
Preferably, needle punched non-woven fabrics, it is through finishing technique process, and this finishing technique comprises the steps:
1) in 12 parts by mass deionized waters, drop into 1 parts by mass zinc stearate, 2.3 parts by mass octadecyl acrylate, 1.7 parts by mass polyethylene glycol oxide trimethyl ammonium chlorides, 2.2 parts by mass sodium chloride mixing, stir;
2) slowly add 1.6 parts by mass DTABs, 2.1 parts by mass trihydroxy ethylamine oleate soaps, 0.9 parts by mass litsea cubeba oil, 1.3 parts by mass polyacrylic acid more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) cloth is padded process in containing the maceration extract of finishing agent, constant temperature drying.
Preferably, needle punched non-woven fabrics, it is through finishing technique process, and this finishing technique comprises the steps:
1) in 12 parts by mass deionized waters, drop into 2 parts by mass zinc stearates, 2.3 parts by mass octadecyl acrylate, 1.7 parts by mass polyethylene glycol oxide trimethyl ammonium chlorides, 2.2 parts by mass sodium chloride mixing, stir;
2) slowly add 1.6 parts by mass DTABs, 2.1 parts by mass trihydroxy ethylamine oleate soaps, 0.9 parts by mass litsea cubeba oil, 1.3 parts by mass polyacrylic acid more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) cloth is padded process in containing the maceration extract of finishing agent, constant temperature drying.
Advantage of the present invention and beneficial effect are: provide a kind of needle punched non-woven fabrics, and it is through finishing technique process, have excellent antibacterial, fire-retardant, antistatic performance.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of needle punched non-woven fabrics, it is through finishing technique process, and this finishing technique comprises the steps:
1) in 12 parts by mass deionized waters, drop into 1 ~ 2 parts by mass zinc stearate, 2.3 parts by mass octadecyl acrylate, 1.7 parts by mass polyethylene glycol oxide trimethyl ammonium chlorides, 2.2 parts by mass sodium chloride mixing, stir;
2) slowly add 1.6 parts by mass DTABs, 2.1 parts by mass trihydroxy ethylamine oleate soaps, 0.9 parts by mass litsea cubeba oil, 1.3 parts by mass polyacrylic acid more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) cloth is padded process in containing the maceration extract of finishing agent, constant temperature drying.
Embodiment 2
Needle punched non-woven fabrics, it is through finishing technique process, and this finishing technique comprises the steps:
1) in 12 parts by mass deionized waters, drop into 1 parts by mass zinc stearate, 2.3 parts by mass octadecyl acrylate, 1.7 parts by mass polyethylene glycol oxide trimethyl ammonium chlorides, 2.2 parts by mass sodium chloride mixing, stir;
2) slowly add 1.6 parts by mass DTABs, 2.1 parts by mass trihydroxy ethylamine oleate soaps, 0.9 parts by mass litsea cubeba oil, 1.3 parts by mass polyacrylic acid more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) cloth is padded process in containing the maceration extract of finishing agent, constant temperature drying.
Embodiment 3
Needle punched non-woven fabrics, it is through finishing technique process, and this finishing technique comprises the steps:
1) in 12 parts by mass deionized waters, drop into 2 parts by mass zinc stearates, 2.3 parts by mass octadecyl acrylate, 1.7 parts by mass polyethylene glycol oxide trimethyl ammonium chlorides, 2.2 parts by mass sodium chloride mixing, stir;
2) slowly add 1.6 parts by mass DTABs, 2.1 parts by mass trihydroxy ethylamine oleate soaps, 0.9 parts by mass litsea cubeba oil, 1.3 parts by mass polyacrylic acid more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) cloth is padded process in containing the maceration extract of finishing agent, constant temperature drying.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. needle punched non-woven fabrics, is characterized in that, it is through finishing technique process, and this finishing technique comprises the steps:
1) in 12 parts by mass deionized waters, drop into 1 ~ 2 parts by mass zinc stearate, 2.3 parts by mass octadecyl acrylate, 1.7 parts by mass polyethylene glycol oxide trimethyl ammonium chlorides, 2.2 parts by mass sodium chloride mixing, stir;
2) slowly add 1.6 parts by mass DTABs, 2.1 parts by mass trihydroxy ethylamine oleate soaps, 0.9 parts by mass litsea cubeba oil, 1.3 parts by mass polyacrylic acid more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) cloth is padded process in containing the maceration extract of finishing agent, constant temperature drying.
2. needle punched non-woven fabrics according to claim 1, is characterized in that, it is through finishing technique process, and this finishing technique comprises the steps:
1) in 12 parts by mass deionized waters, drop into 1 parts by mass zinc stearate, 2.3 parts by mass octadecyl acrylate, 1.7 parts by mass polyethylene glycol oxide trimethyl ammonium chlorides, 2.2 parts by mass sodium chloride mixing, stir;
2) slowly add 1.6 parts by mass DTABs, 2.1 parts by mass trihydroxy ethylamine oleate soaps, 0.9 parts by mass litsea cubeba oil, 1.3 parts by mass polyacrylic acid more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) cloth is padded process in containing the maceration extract of finishing agent, constant temperature drying.
3. needle punched non-woven fabrics according to claim 1, is characterized in that, it is through finishing technique process, and this finishing technique comprises the steps:
1) in 12 parts by mass deionized waters, drop into 2 parts by mass zinc stearates, 2.3 parts by mass octadecyl acrylate, 1.7 parts by mass polyethylene glycol oxide trimethyl ammonium chlorides, 2.2 parts by mass sodium chloride mixing, stir;
2) slowly add 1.6 parts by mass DTABs, 2.1 parts by mass trihydroxy ethylamine oleate soaps, 0.9 parts by mass litsea cubeba oil, 1.3 parts by mass polyacrylic acid more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) cloth is padded process in containing the maceration extract of finishing agent, constant temperature drying.