CN105297398A - After-finishing process of textile fabric - Google Patents

Abstract

The invention discloses an after-finishing process of a textile fabric. The after-finishing process comprises the following steps: (1) adding the following components into 30 parts of de-ionized water in parts by mass: 1-2 parts of antimony trioxide, 2.8 parts of high-chlorine diethanol laurate, 0.9 part of silver carbonate, 2.6 parts of 1,3-dimethyl-4,5-dyhydroxyl imidazolone methyl ether, and mixing and uniformly stirring; (2) slowly adding the following components in parts by mass: 1.7 parts of n-butyl sodium naphthalene sulfonate, 5.1 parts of 1,3-butanediol, 1-9 parts of clove essential oil and 2.3 parts of rosinyl waterborne polyurethane, and further stirring until the components are sufficiently and uniformly mixed to prepare a finishing agent; and (3) padding a fabric into an impregnation solution containing the finishing agent to be subjected to padding treatment, and drying at a constant temperature. According to the after-finishing process of the textile fabric, provided by the invention, the finished fabric has excellent inflaming retarding, antibacterial, anti-wrinkle and anti-static performances, and strong washing fastness.

Description

The postfinishing process of weaving face fabric

Technical field

The present invention relates to the postfinishing process of weaving face fabric.

Background technology

Fire-retardant, antibacterial, crease-resistant, antistatic performance and the washing fastness of existing fabric all have much room for improvement.

Summary of the invention

The object of the present invention is to provide a kind of postfinishing process of weaving face fabric, the fabric after its arrangement has excellent fire-retardant, antibacterial, crease-resistant, antistatic performance, and washability is strong.

For achieving the above object, technical scheme of the present invention designs a kind of postfinishing process of weaving face fabric, comprises the steps:

1) in 30 parts by mass deionized waters, drop into 1 ~ 2 parts by mass antimonous oxide, 2.8 parts by mass height chlorine diethanol bay salt, 0.9 parts by mass silver carbonate, 2.6 parts by mass 1,3-dimethyl-4,5-dihydroxy imidazolone methyl ether mixing, stir;

2) slowly add 1.7 parts by mass normal-butyl sodium naphthalene sulfonates, 5.1 parts by mass 1,3-BDOs, 1.9 parts by mass clove oils, 2.3 parts by mass rosin based aqueous polyurethanes more simultaneously, continue to stir, to fully mixing, obtained finishing agent;

3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.

Preferably, the postfinishing process of weaving face fabric, comprises the steps:

1) in 30 parts by mass deionized waters, drop into 1 parts by mass antimonous oxide, 2.8 parts by mass height chlorine diethanol bay salt, 0.9 parts by mass silver carbonate, 2.6 parts by mass 1,3-dimethyl-4,5-dihydroxy imidazolone methyl ether mixing, stir;

2) slowly add 1.7 parts by mass normal-butyl sodium naphthalene sulfonates, 5.1 parts by mass 1,3-BDOs, 1.9 parts by mass clove oils, 2.3 parts by mass rosin based aqueous polyurethanes more simultaneously, continue to stir, to fully mixing, obtained finishing agent;

3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.

Preferably, the postfinishing process of weaving face fabric, comprises the steps:

1) in 30 parts by mass deionized waters, drop into 2 parts by mass antimonous oxides, 2.8 parts by mass height chlorine diethanol bay salt, 0.9 parts by mass silver carbonate, 2.6 parts by mass 1,3-dimethyl-4,5-dihydroxy imidazolone methyl ether mixing, stir;

2) slowly add 1.7 parts by mass normal-butyl sodium naphthalene sulfonates, 5.1 parts by mass 1,3-BDOs, 1.9 parts by mass clove oils, 2.3 parts by mass rosin based aqueous polyurethanes more simultaneously, continue to stir, to fully mixing, obtained finishing agent;

3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.

Advantage of the present invention and beneficial effect are: the postfinishing process providing a kind of weaving face fabric, and the fabric after its arrangement has excellent fire-retardant, antibacterial, crease-resistant, antistatic performance, and washability is strong.

Detailed description of the invention

Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.

The technical scheme that the present invention specifically implements is:

Embodiment 1

A postfinishing process for weaving face fabric, comprises the steps:

1) in 30 parts by mass deionized waters, drop into 1 ~ 2 parts by mass antimonous oxide, 2.8 parts by mass height chlorine diethanol bay salt, 0.9 parts by mass silver carbonate, 2.6 parts by mass 1,3-dimethyl-4,5-dihydroxy imidazolone methyl ether mixing, stir;

2) slowly add 1.7 parts by mass normal-butyl sodium naphthalene sulfonates, 5.1 parts by mass 1,3-BDOs, 1.9 parts by mass clove oils, 2.3 parts by mass rosin based aqueous polyurethanes more simultaneously, continue to stir, to fully mixing, obtained finishing agent;

3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.

Embodiment 2

The postfinishing process of weaving face fabric, comprises the steps:

1) in 30 parts by mass deionized waters, drop into 1 parts by mass antimonous oxide, 2.8 parts by mass height chlorine diethanol bay salt, 0.9 parts by mass silver carbonate, 2.6 parts by mass 1,3-dimethyl-4,5-dihydroxy imidazolone methyl ether mixing, stir;

2) slowly add 1.7 parts by mass normal-butyl sodium naphthalene sulfonates, 5.1 parts by mass 1,3-BDOs, 1.9 parts by mass clove oils, 2.3 parts by mass rosin based aqueous polyurethanes more simultaneously, continue to stir, to fully mixing, obtained finishing agent;

3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.

Embodiment 3

The postfinishing process of weaving face fabric, comprises the steps:

1) in 30 parts by mass deionized waters, drop into 2 parts by mass antimonous oxides, 2.8 parts by mass height chlorine diethanol bay salt, 0.9 parts by mass silver carbonate, 2.6 parts by mass 1,3-dimethyl-4,5-dihydroxy imidazolone methyl ether mixing, stir;

2) slowly add 1.7 parts by mass normal-butyl sodium naphthalene sulfonates, 5.1 parts by mass 1,3-BDOs, 1.9 parts by mass clove oils, 2.3 parts by mass rosin based aqueous polyurethanes more simultaneously, continue to stir, to fully mixing, obtained finishing agent;

3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.

The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.

Claims (3)

1. the postfinishing process of weaving face fabric, is characterized in that, comprises the steps:

1) in 30 parts by mass deionized waters, drop into 1 ~ 2 parts by mass antimonous oxide, 2.8 parts by mass height chlorine diethanol bay salt, 0.9 parts by mass silver carbonate, 2.6 parts by mass 1,3-dimethyl-4,5-dihydroxy imidazolone methyl ether mixing, stir;

2) slowly add 1.7 parts by mass normal-butyl sodium naphthalene sulfonates, 5.1 parts by mass 1,3-BDOs, 1.9 parts by mass clove oils, 2.3 parts by mass rosin based aqueous polyurethanes more simultaneously, continue to stir, to fully mixing, obtained finishing agent;

3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.

2. the postfinishing process of weaving face fabric according to claim 1, is characterized in that, comprises the steps:

1) in 30 parts by mass deionized waters, drop into 1 parts by mass antimonous oxide, 2.8 parts by mass height chlorine diethanol bay salt, 0.9 parts by mass silver carbonate, 2.6 parts by mass 1,3-dimethyl-4,5-dihydroxy imidazolone methyl ether mixing, stir;

2) slowly add 1.7 parts by mass normal-butyl sodium naphthalene sulfonates, 5.1 parts by mass 1,3-BDOs, 1.9 parts by mass clove oils, 2.3 parts by mass rosin based aqueous polyurethanes more simultaneously, continue to stir, to fully mixing, obtained finishing agent;

3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.

3. the postfinishing process of weaving face fabric according to claim 1, is characterized in that, comprises the steps:

1) in 30 parts by mass deionized waters, drop into 2 parts by mass antimonous oxides, 2.8 parts by mass height chlorine diethanol bay salt, 0.9 parts by mass silver carbonate, 2.6 parts by mass 1,3-dimethyl-4,5-dihydroxy imidazolone methyl ether mixing, stir;

2) slowly add 1.7 parts by mass normal-butyl sodium naphthalene sulfonates, 5.1 parts by mass 1,3-BDOs, 1.9 parts by mass clove oils, 2.3 parts by mass rosin based aqueous polyurethanes more simultaneously, continue to stir, to fully mixing, obtained finishing agent;

3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.