CN109098464A - A kind of renovation technology of old tile floor - Google Patents
A kind of renovation technology of old tile floor Download PDFInfo
- Publication number
- CN109098464A CN109098464A CN201810984974.6A CN201810984974A CN109098464A CN 109098464 A CN109098464 A CN 109098464A CN 201810984974 A CN201810984974 A CN 201810984974A CN 109098464 A CN109098464 A CN 109098464A
- Authority
- CN
- China
- Prior art keywords
- tile
- glue
- interface processing
- rubber cement
- old
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of renovation technologies of old tile floor, comprising: is diluted with water L-BOND interface treating agent, and the L-BOND interface treating agent after dilution is stirred evenly with glue for tile and is mixed to form interface processing material；It is criticized on old tile floor and scrapes the interface processing material progress interface processing, form interface processing layer, and solid；Glue for tile and water are stirred evenly and are mixed to form glue for tile rubber cement；Glue for tile rubber cement is uniformly coated on respectively on interface processing layer using flute profile scraper and the back side of new ceramic tile and is combed into uniform stripe shape respectively；New tile laying on old ceramic tile and is sufficiently rubbed to pressure, air is discharged.Method of the renovation technology of old tile floor of the invention to need to remove when fundamentally solving traditional refurbishing old ceramic tiles, improve efficiency, reduce unnecessary human and material resources, financial resources, a large amount of noise, dust and the building waste generated without demolishing process.
Description
Technical field
The present invention relates to terrace reconditioning technology fields, more specifically to a kind of renovation technology of old tile floor.
Background technique
The mode of traditional old ceramic tile of transformation is to remove old ceramic tile, then remakes levelling and horizontal processing, then is pasted new
Ceramic tile.Here the problem is that: old ceramic tile demolishing process can generate a large amount of noise, dust and building waste, and remove
Cheng Zhonghui generates the splashing of particle, also the hidden danger of injury can be generated to construction worker, and do not meet the objective of sustainable development.
Summary of the invention
The purpose of the present invention is to provide a kind of renovation technologies of old tile floor, solve old ceramic tile in the prior art
It needs to remove time-consuming and laboriously to renovate and leads to lead to the problem of a large amount of noise, dust, rubbish and insecurity etc..
The technical proposal for solving the technical problem of the invention is: a kind of renovation technology of old tile floor, comprising:
S1, L-BOND interface treating agent is diluted with water, the L-BOND interface treating agent after dilution is stirred with glue for tile
It is uniformly mixed to form interface processing material；
S2, it is criticized on old tile floor and scrapes the interface processing material progress interface processing, form interface processing layer, and do
Gu；
S3, it glue for tile and water is stirred evenly is mixed to form glue for tile rubber cement；
S4, using flute profile scraper by glue for tile rubber cement be uniformly coated on interface processing layer respectively and the back side of new ceramic tile and
It is combed into uniform stripe shape respectively；
S5, pressure by new tile laying on old ceramic tile and is sufficiently rubbed, air is discharged.
In renovation technology of the invention, in step sl, the amount of water and L- that L-BOND interface treating agent is diluted with water
The mass ratio of BOND interface treating agent is 1:0.8~1.2.
In renovation technology of the invention, in step sl, the matter of L-BOND interface treating agent and glue for tile after dilution
Amount is than being 1:3~5.
In renovation technology of the invention, in step s 2, the interface processing layer with a thickness of 1-1.5mm.
In renovation technology of the invention, in step s 2, drying time of interface processing layer >=for 24 hours.
In renovation technology of the invention, in step s 2, interface processing material completes interface after preparation within 20min
Processing；In step s 5, glue for tile rubber cement completes coating after preparation within 60min.
In renovation technology of the invention, in step s 4, the mass ratio of the glue for tile and water is 1:0.15~0.3.
In renovation technology of the invention, in step s 5, it is respectively coated on interface processing layer with the back side of new ceramic tile
Glue for tile rubber cement with a thickness of 5-8.5mm.
In renovation technology of the invention, in step s 5, the flute profile scraper has multiple comb teeth, each comb teeth
Width be 10mm, the spacing between two adjacent comb teeth is 10mm；The glue for tile glue combed by the flute profile scraper
The width of the striped of slurry is 10mm；The spacing of adjacent stripes is 10mm；The flute profile scraper has straight flange, and glue for tile rubber cement is applied
Cloth makes the glue for tile rubber cement on four sides of new ceramic tile form chamfering at the back side of new ceramic tile, using the straight flange of the flute profile scraper.
In renovation technology of the invention, in step s 5, glue for tile rubber cement is distinguished into even spread using flute profile scraper
On interface processing layer and when the back side of new ceramic tile, the comb teeth back with basal plane and new ceramic tile where interface processing layer respectively
Basal plane where face is in 45 ° -60 °.
The renovation technology for implementing old tile floor of the invention has the advantages that old tile floor of the invention
Renovation technology on the bright and clean old tile floor of surface compact using with fabulous two-way affinity interface processing material come it is auxiliary
It helps the stickup of new ceramic tile and then completes the renovation processing of old tile floor, thus when fundamentally solving traditional refurbishing old ceramic tiles
The method for needing to remove, improves efficiency, reduces unnecessary human and material resources, financial resources, generates without demolishing process a large amount of
Noise, dust and building waste.
Specific embodiment
Below with reference to embodiment, the renovation technology of old tile floor of the invention is described further:
The present invention relates to a kind of renovation technologies of old tile floor, comprising:
S0, base treatment: basal plane is answered smooth, solid, clean, and old ceramic tile must not have hollowing, should clean out ceramic tile surface
Dust, grease stain, dirt the defects of, local hollowing region, it is necessary to stirred evenly again with the high mending mortar of moral after first being rooted out,
Hollowing region is filled and led up, is finally cleaned out dust and rubbish with broom.
S1, L-BOND interface treating agent is diluted with water, the L-BOND interface treating agent after dilution is stirred with glue for tile
It is uniformly mixed to form interface processing material, the equipment such as electric blender can be used and stir to subject to being rolled into a ball entirely without fecula；Wherein,
Glue for tile can be PD-301, PD-506 etc.；The amount of water and the interface L-BOND that L-BOND interface treating agent is diluted with water
The mass ratio for managing agent is 1:0.8~1.2, i.e. in the range of 1:0.8 to 1:1.2, preferably 1；The interface L-BOND after dilution
The mass ratio for managing agent and glue for tile is 1:3~5, i.e. in the range of 1:5 to 1:3, preferably 1:4；It should be noted that interface
Reason material preferably completes interface processing after preparation within 20min.
S2, it is criticized on old tile floor and scrapes the interface processing material progress interface processing, form interface processing layer, and do
Gu；Wherein, interface processing layer with a thickness of 1-1.5mm, preferably 1.5mm；The drying time of interface processing layer >=for 24 hours.
S3, it glue for tile and water is stirred evenly is mixed to form glue for tile rubber cement, the equipment such as electric blender can be used and stir
It mixes to subject to being rolled into a ball entirely without fecula；Wherein, the mass ratio of glue for tile and water is 1:0.15~0.3, the i.e. model of 1:0.15 to 1:0.3
In enclosing, preferably 1:0.22；It should be noted that brick glue rubber cement completes coating after preparation preferably within 60min.
S4, using flute profile scraper by glue for tile rubber cement be uniformly coated on interface processing layer respectively and the back side of new ceramic tile and
It is combed into uniform stripe shape respectively.
When ceramic tile rubber cement is coated on interface processing layer, it can be first segmented cellular snap line, to improve adhesive layer thickness and put down
Whole degree.
In this step, flute profile scraper is that the common scraper of patch block, specific structure are no longer gone to live in the household of one's in-laws on getting married in detail in the prior art
It states, the preferred 10mm × 10mm of the specification of flute profile scraper, or other specifications, depending on as needed；In the preferred embodiment,
Flute profile scraper has multiple comb teeth, and the width of each comb teeth is 10mm, and the spacing between two adjacent comb teeth is 10mm；Quilt
The width of the striped of the glue for tile rubber cement of flute profile scraper combing is 10mm；The spacing of adjacent stripes is 10mm.
Flute profile scraper has straight flange, when glue for tile rubber cement is coated on the back side of new ceramic tile, utilizes the straight flange of flute profile scraper
The glue for tile rubber cement on four sides of new ceramic tile is set to form chamfering, in order to avoid squeeze out extra glue for tile rubber cement when pasting and pollute ceramic tile
Face.
On interface processing layer and the back side of new ceramic tile be respectively coated glue for tile rubber cement with a thickness of 5-8.5mm, preferably
6-8.5mm, more preferably 6mm, 8.5mm.
When glue for tile rubber cement is uniformly coated on interface processing layer respectively with the back side of new ceramic tile using flute profile scraper, comb
Tooth is in respectively 45 ° -60 ° with the basal plane where the back side of basal plane and new ceramic tile where interface processing layer.
S5, pressure by new tile laying on old ceramic tile and is sufficiently rubbed, air is discharged, improve completely slurry rate.
S6, surface cleaning: wet cloth and the new ceramic tile face of cleaning should be used after the completion of paving, prevents glue for tile rubber cement from polluting new porcelain
Brick.
S7, stay seam, wiping seam: the slit width between new ceramic tile should be not less than 2mm, and new tile paste finishes should be by the sundries in gap
Clean out, after completely it is solid after can joint filling.
The quality requirement of the renovation technology of old tile floor of the invention is as follows.
(1) new tile paste deviation and the method for inspection are referring to table 1
Table 1:
| Item | Project | Tolerance (㎜) | The method of inspection |
| 1 | Surface smoothness | 2.0 | With 2m guiding ruler and wedge-shaped feeler gauge inspection |
| 2 | It is straight to stitch lattice | 3.0 | It draws 5m line and is checked with steel ruler |
| 3 | Skirting is suitable for reading straight | 3.0 | 5m line is drawn, logical line is drawn less than 5m, is checked with straight steel ruler |
| 4 | Seam difference of height | 0.5 | With straight steel ruler and clearance gauge inspection |
| 5 | Plate interspace width | 2.0 | It is checked with straight steel ruler |
(2) judgment basis of hollowing
Since the glue for tile dry and hard time is often longer than " cement oil ", patch block 72h (such as encounters low temperature, high humility
When environment, this time needs to be appropriately extended) after can with profession tool tap brick face, by sound to determine whether there are hollowings.
Wherein, paste must securely for new ceramic tile brick, should be without hollowing, crack, and between every nature or the hollowing brick of standard room is not answered
More than the 5% of sum.
(3) using two-sided pulp distributing technique: being overlapped again after basal plane and all starchings of the ceramic tile back side and rub pressure, in practice it has proved that compare single side
The full slurry rate of point pasting method is high by 30%, can greatly improve the full slurry rate of adhesive layer, reduce the appearance of hollowing；According to Base Smoothness
And ceramic tile dimension uses the notched scraper of different size groove, the ceramic tile of 300 × 300mm or more should use 10mm tooth form scraper plate.
(4) full slurry rate: completely slurry rate is to influence the important indicator of paving safety, and completely slurry rate is the full of stickup glue for tile rubber cement
Degree, therefore every one piece of brick of stickup will check full slurry rate, it is desirable that completely slurry rate > 95%.
(5) new ceramic tile, which should be rubbed, is pressed onto position, and glue for tile rubber cement Ying Suiyong is with mixing.
It is described in detail below by specific embodiment.
Embodiment 1
Base treatment.The L-BOND interface treating agent for taking 4kg adds the water of 5kg to dilute, by the interface L-BOND after dilution
The PD-301 glue for tile of reason agent and 27kg are stirred using electric blender to entirely without fecula group, and interface processing material is formed；?
Batch scrape interface processing material on old tile floor and carry out interface processing, form the interface processing layer of 1mm thickness, and it is solid for 24 hours more than
h；It is segmented cellular snap line；The water conservancy of the PD-301 glue for tile of 100kg and 15kg is stirred with electric blender to entirely without fecula
Group；Glue for tile rubber cement is uniformly coated on interface processing layer respectively and the back side of new ceramic tile and is combed respectively using flute profile scraper
At uniform stripe shape, the width of the striped of the glue for tile rubber cement combed by flute profile scraper is 10mm, and the spacing of adjacent stripes is
10mm；And when glue for tile rubber cement is coated on the back side of new ceramic tile, the porcelain on four sides of new ceramic tile is made using the straight flange of flute profile scraper
Brick glue rubber cement forms chamfering；On interface processing layer and the back side of new ceramic tile be respectively coated glue for tile rubber cement with a thickness of 5mm；It applies
When cloth glue for tile rubber cement, holding flute profile scraper makes comb teeth respectively and where the back side of basal plane and new ceramic tile where interface processing layer
Basal plane be in 45 ° -60 °；New tile laying on old ceramic tile and is sufficiently rubbed to pressure, air is discharged, improves completely slurry rate；Paving is completed
After should use wet cloth and the new ceramic tile face of cleaning, prevent glue for tile rubber cement from polluting new ceramic tile；Slit width between new ceramic tile should be not less than
2mm, new tile paste, which finishes, to clean out the sundries in gap, after completely it is solid after can joint filling.After pasting new brick renovation
Mass effect referring to table 2.
Embodiment 2
Base treatment.The L-BOND interface treating agent for taking 5kg adds the water of 5kg to dilute, by the interface L-BOND after dilution
The PD-301 glue for tile of reason agent and 40kg are stirred using electric blender to entirely without fecula group, and interface processing material is formed；?
Batch scrape interface processing material on old tile floor and carry out interface processing, form the interface processing layer of 1.5mm thickness, and it is solid for 24 hours with
Upper h；It is segmented cellular snap line；The water conservancy of the PD-301 glue for tile of 100kg and 22kg is stirred with electric blender to entirely without life
Powder ball；Glue for tile rubber cement is uniformly coated on interface processing layer respectively and the back side of new ceramic tile and is combed respectively using flute profile scraper
Uniform stripe shape is managed into, the width of the striped of the glue for tile rubber cement combed by flute profile scraper is 10mm, and the spacing of adjacent stripes is
10mm；And when glue for tile rubber cement is coated on the back side of new ceramic tile, the porcelain on four sides of new ceramic tile is made using the straight flange of flute profile scraper
Brick glue rubber cement forms chamfering；On interface processing layer and the back side of new ceramic tile be respectively coated glue for tile rubber cement with a thickness of 8.5mm；
When being coated with glue for tile rubber cement, holding flute profile scraper makes back side institute of the comb teeth respectively with basal plane and new ceramic tile where interface processing layer
Basal plane be in 45 ° -60 °；New tile laying on old ceramic tile and is sufficiently rubbed to pressure, air is discharged, improves completely slurry rate；Paving is complete
Cheng Houying prevents glue for tile rubber cement from polluting new ceramic tile using wet cloth and the new ceramic tile face of cleaning；Slit width between new ceramic tile should be not less than
2mm, new tile paste, which finishes, to clean out the sundries in gap, after completely it is solid after can joint filling.After pasting new brick renovation
Mass effect referring to table 2.
Embodiment 3
Base treatment.The L-BOND interface treating agent for taking 6kg adds the water of 5kg to dilute, by the interface L-BOND after dilution
The PD-301 glue for tile of reason agent and 55kg are stirred using electric blender to entirely without fecula group, and interface processing material is formed；?
Batch scrape interface processing material on old tile floor and carry out interface processing, form the interface processing layer of 1.3mm thickness, and it is solid for 24 hours with
Upper h；It is segmented cellular snap line；The water conservancy of the PD-301 glue for tile of 100kg and 30kg is stirred with electric blender to entirely without life
Powder ball；Glue for tile rubber cement is uniformly coated on interface processing layer respectively and the back side of new ceramic tile and is combed respectively using flute profile scraper
Uniform stripe shape is managed into, the width of the striped of the glue for tile rubber cement combed by flute profile scraper is 10mm, and the spacing of adjacent stripes is
10mm；And when glue for tile rubber cement is coated on the back side of new ceramic tile, the porcelain on four sides of new ceramic tile is made using the straight flange of flute profile scraper
Brick glue rubber cement forms chamfering；On interface processing layer and the back side of new ceramic tile be respectively coated glue for tile rubber cement with a thickness of 6mm；It applies
When cloth glue for tile rubber cement, holding flute profile scraper makes comb teeth respectively and where the back side of basal plane and new ceramic tile where interface processing layer
Basal plane be in 45 ° -60 °；New tile laying on old ceramic tile and is sufficiently rubbed to pressure, air is discharged, improves completely slurry rate；Paving is completed
After should use wet cloth and the new ceramic tile face of cleaning, prevent glue for tile rubber cement from polluting new ceramic tile；Slit width between new ceramic tile should be not less than
2mm, new tile paste, which finishes, to clean out the sundries in gap, after completely it is solid after can joint filling.After pasting new brick renovation
Mass effect referring to table 2.
Table 2:
It should be understood that it will be understood by those skilled in the art that it can be modified or changed according to the above description, but this
Within a little improvement or transformation should all belong to the protection domain of appended claims of the present invention.
Claims (10)
1. a kind of renovation technology of old tile floor characterized by comprising
S1, L-BOND interface treating agent is diluted with water, and the L-BOND interface treating agent after dilution is stirred with glue for tile
It is even to be mixed to form interface processing material；
S2, it is criticized on old tile floor and scrapes the interface processing material progress interface processing, form interface processing layer, and solid；
S3, it glue for tile and water is stirred evenly is mixed to form glue for tile rubber cement；
S4, glue for tile rubber cement is uniformly coated on interface processing layer and the back side of new ceramic tile and difference respectively using flute profile scraper
It is combed into uniform stripe shape；
S5, pressure by new tile laying on old ceramic tile and is sufficiently rubbed, air is discharged.
2. renovation technology according to claim 1, which is characterized in that in step sl, L-BOND interface treating agent adds water
The mass ratio of diluted amount of water and L-BOND interface treating agent is 1:0.8~1.2.
3. renovation technology according to claim 2, which is characterized in that in step sl, the interface L-BOND after dilution
The mass ratio for managing agent and glue for tile is 1:3~5.
4. renovation technology according to claim 1, which is characterized in that in step s 2, the thickness of the interface processing layer
For 1-1.5mm.
5. renovation technology according to claim 1, which is characterized in that in step s 2, the drying time of interface processing layer
≥24h。
6. renovation technology according to claim 1, which is characterized in that in step s 2, interface processing material is after preparation
Interface processing is completed within 20min；In step s 5, glue for tile rubber cement completes coating after preparation within 60min.
7. renovation technology according to claim 1, which is characterized in that in step s 4, the quality of the glue for tile and water
Than for 1:0.15~0.3.
8. renovation technology according to claim 1, which is characterized in that in step s 5, on interface processing layer and new porcelain
The back side of brick be respectively coated glue for tile rubber cement with a thickness of 5-8.5mm.
9. renovation technology according to claim 1, which is characterized in that in step s 5, the flute profile scraper has multiple
Comb teeth, the width of each comb teeth are 10mm, and the spacing between two adjacent comb teeth is 10mm；It is scraped by the flute profile
The width of the striped of the glue for tile rubber cement of knife combing is 10mm；The spacing of adjacent stripes is 10mm；
The flute profile scraper has straight flange, when glue for tile rubber cement is coated on the back side of new ceramic tile, utilizes the flute profile scraper
Straight flange makes the glue for tile rubber cement on four sides of new ceramic tile form chamfering.
10. renovation technology according to claim 9, which is characterized in that in step s 5, using flute profile scraper by glue for tile
When rubber cement is uniformly coated on interface processing layer respectively with the back side of new ceramic tile, the comb teeth is respectively and where interface processing layer
Basal plane where the back side of basal plane and new ceramic tile is in 45 ° -60 °.