CN109082156A - A kind of imitative metal red ink and preparation method thereof - Google Patents
A kind of imitative metal red ink and preparation method thereof Download PDFInfo
- Publication number
- CN109082156A CN109082156A CN201810985205.8A CN201810985205A CN109082156A CN 109082156 A CN109082156 A CN 109082156A CN 201810985205 A CN201810985205 A CN 201810985205A CN 109082156 A CN109082156 A CN 109082156A
- Authority
- CN
- China
- Prior art keywords
- parts
- ink
- weight
- red
- imitative metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to field of ink manufacture, more particularly to a kind of imitative metal red ink and preparation method thereof.A kind of imitative metal red ink, including each component and parts by weight are as follows: 4504 4.5-5.7 parts of pearl powders, it is 211 3.3-3.6 parts of pearl powders, color ink 19.7-21.5 parts bright red, 58.6-62.4 parts of rhodo color ink, 13.4-15.5 parts of gloss oil ink, 10-12 parts of diluent, 0.6-0.8 parts of defoaming agent, 2-4 parts of curing agent.A kind of imitative metal red ink provided by the invention and preparation method thereof, used component and weight proportion can make the imitative metal red ink being in bright colors, the ink color is true to nature simultaneously, and adhesive force is strong, fast drying, glossiness and good leveling property, is not cracked, is not easy to spread and do not occur pin-hole phenomena.
Description
Technical field
The present invention relates to field of ink manufacture, more particularly to a kind of imitative metal red ink and preparation method thereof.
Background technique
Imitative metal red ink uses more, existing skill in the decoration or label of glass, PMMA plastics and Related product
Art prints beauty's color ink a value between 40-45, and metallic red redness can be lower, accordingly, it is difficult to reach highlighted printing effect.
Summary of the invention
In view of the above-mentioned problems, the purpose of the present invention is to provide a kind of imitative metal red ink and preparation method thereof, the oil
Ink is in bright colors.
The technical solution adopted by the present invention to solve the technical problems is:
A kind of imitative metal red ink, including each component and parts by weight are as follows: 4504 4.5-5.7 parts of pearl powders, 211 pearls
It is 3.3-3.6 parts of light powder, color ink 19.7-21.5 parts bright red, 58.6-62.4 parts of rhodo color ink, gloss oil ink 13.4-15.5
Part, 10-12 parts of diluent, 0.6-0.8 parts of defoaming agent, 2-4 parts of curing agent.
Further, each component and parts by weight of the diluent are as follows: 22-30 parts of isobutyl acetate, isopropyl acid 7-11
Part, 4-6 parts of ethyl acetate, 3- methyl -3- methoxyl group -11-15 parts of n-butyl alcohol.
Preferably, the bright red color ink includes following components and parts by weight: 35-38 parts of epoxy acrylic resin, second
5-9 parts of acid butyl ester, 41-45 parts of large red colorant；The gloss oil ink includes following components and parts by weight: epoxy acrylic
30-35 parts of resin, 10-14 parts of dipropylene glycol diacrylate；The rhodo color ink includes following components and parts by weight: ring
24-30 parts of oxypropylene acid resin, 4-8 parts of o-benzoyl yl benzoic acid macrogol ester, 25-35 parts of rose colorant.
The ingredient of the curing agent is amido amine.
The preparation method of the imitative metal red ink, comprising the following steps:
(1) ingredient is measured by following components and parts by weight, be placed in mixer: bright red color ink 19.7-21.5 parts,
58.6-62.4 parts of rhodo color ink, 13.4-15.5 parts of gloss oil ink, 10-12 parts of diluent, 0.6-0.8 parts of defoaming agent, solidification
2-4 parts of agent；
(2) in mixer, above-mentioned ingredient is stirred evenly；
(3) above-mentioned mixer is placed in 72-75 DEG C degree Celsius of temperature and is toasted 25-30 minutes.
A kind of imitative metal red ink provided by the invention and preparation method thereof, used component and weight proportion can
The imitative metal red ink being in bright colors is made, while the ink color is true to nature, adhesive force is strong, fast drying, glossiness and stream
Levelling is good, is not cracked, is not easy to spread and do not occur pin-hole phenomena.
Specific embodiment
Technical solution of the present invention is described in detail With reference to embodiment so that advantages of the present invention and
Feature can be easier to be readily appreciated by one skilled in the art, to make apparent specific boundary to protection scope of the present invention
It is fixed.
Embodiment 1
(1) configuration ink composition:
Bright red color ink, following components according to parts by weight: 35 parts of epoxy acrylic resin, 8 parts of butyl acetate, large red
It 45 parts of colorant, stirs evenly；
Gloss oil ink, following components according to parts by weight: 31 parts of epoxy acrylic resin, dipropylene glycol diacrylate 11
Part, it stirs evenly；
Rhodo color ink, following components according to parts by weight: 30 parts of epoxy acrylic resin, o-benzoyl yl benzoic acid is poly-
It 6 parts of glycol ester, 28 parts of rose colorant, stirs evenly.
(2) prepared and diluted agent
The diluent, following components according to parts by weight: 30 parts of isobutyl acetate, 10 parts of isopropyl acid, ethyl acetate 5
Part, 3- methyl -3- methoxyl group -15 parts of n-butyl alcohol stirs evenly.
(3) ingredient is measured by following components and parts by weight, be placed in mixer: 19.7 parts of bright red color ink, rhodo
58.9 parts of color ink, 13.4 parts of gloss oil ink, 12 parts of diluent, 0.6 part of defoaming agent, 2 parts of curing agent；Ingredient stirs evenly；Institute
The ingredient for stating curing agent is amido amine.Defoaming agent is silicone emulsion.
(4) above-mentioned mixer is placed in 75 DEG C degrees Celsius of temperature and is toasted 25 minutes, obtain imitative metal red ink.
Embodiment 2
(1) configuration ink composition:
Bright red color ink, following components according to parts by weight: 38 parts of epoxy acrylic resin, 9 parts of butyl acetate, large red
It 42 parts of colorant, stirs evenly；
Gloss oil ink, following components according to parts by weight: 35 parts of epoxy acrylic resin, dipropylene glycol diacrylate 12
Part, it stirs evenly；
Rhodo color ink, following components according to parts by weight: 30 parts of epoxy acrylic resin, o-benzoyl yl benzoic acid is poly-
It 8 parts of glycol ester, 35 parts of rose colorant, stirs evenly.
(2) prepared and diluted agent
The diluent, following components according to parts by weight: 28 parts of isobutyl acetate, 9 parts of isopropyl acid, 5 parts of ethyl acetate,
3- methyl -3- methoxyl group -12 parts of n-butyl alcohol, stirs evenly.
(3) ingredient is measured by following components and parts by weight, be placed in mixer: 20.5 parts of bright red color ink, rhodo
60.5 parts of color ink, 15.5 parts of gloss oil ink, 12 parts of diluent, 0.8 part of defoaming agent, 4 parts of curing agent；Ingredient stirs evenly；Institute
The ingredient for stating curing agent is amido amine.Defoaming agent is silicone emulsion.
(4) above-mentioned mixer is placed in 72 DEG C degrees Celsius of temperature and is toasted 30 minutes, obtain imitative metal red ink.
Embodiment 3
(1) configuration ink composition:
Bright red color ink, following components according to parts by weight: 37 parts of epoxy acrylic resin, 7 parts of butyl acetate, large red
It 43 parts of colorant, stirs evenly；
Gloss oil ink, following components according to parts by weight: 30 parts of epoxy acrylic resin, dipropylene glycol diacrylate 13
Part, it stirs evenly；
Rhodo color ink, following components according to parts by weight: 28 parts of epoxy acrylic resin, o-benzoyl yl benzoic acid is poly-
It 7 parts of glycol ester, 27 parts of rose colorant, stirs evenly.
(2) prepared and diluted agent
The diluent, following components according to parts by weight: 30 parts of isobutyl acetate, 11 parts of isopropyl acid, ethyl acetate 4
Part, 3- methyl -3- methoxyl group -12 parts of n-butyl alcohol stirs evenly.
(3) ingredient is measured by following components and parts by weight, be placed in mixer: 19.7 parts of bright red color ink, rhodo
58.6 parts of color ink, 15.5 parts of gloss oil ink, 12 parts of diluent, 0.8 part of defoaming agent, 4 parts of curing agent；Ingredient stirs evenly；Institute
The ingredient for stating curing agent is amido amine.Defoaming agent is silicone emulsion.
(4) above-mentioned mixer is placed in 75 DEG C degrees Celsius of temperature and is toasted 30 minutes, obtain imitative metal red ink.
After ink printing, the red main presentation metal of metal is red；
L:43~44, a:54~54.5, b:7.5~7.9.
L value refers to brightness value, indicates that magnitude i.e. black and white of the color in shading value, a value are equal to a color red
Position (- a represents green, and+a represents red) on green axis, b value is equal to position of the color on champac axis, and (- b represents indigo plant
Color ,+b represent Huang).
The above description is only a preferred embodiment of the present invention, is not intended to limit the scope of the invention, all utilizations
Equivalent structure or equivalent flow shift made by present specification is applied directly or indirectly in other relevant technologies
Field is included within the scope of the present invention.
Claims (5)
1. a kind of imitative metal red ink, which is characterized in that including each component and parts by weight are as follows: 4504 pearl powder 4.5-
It is 5.7 parts, 211 3.3-3.6 parts of pearl powders, color ink 19.7-21.5 parts bright red, 58.6-62.4 parts of rhodo color ink, gloss oil ink
13.4-15.5 parts, 10-12 parts of diluent, 0.6-0.8 parts of defoaming agent, 2-4 parts of curing agent.
2. imitative metal red ink according to claim 1, which is characterized in that each component and parts by weight of the diluent
Number are as follows: 22-30 parts of isobutyl acetate, 7-11 parts of isopropyl acid, 4-6 parts of ethyl acetate, 3- methyl -3- methoxyl group-n-butyl alcohol 11-15
Part.
3. imitative metal red ink according to claim 2, it is characterised in that: the bright red color ink includes following components
And parts by weight: 35-38 parts of epoxy acrylic resin, 5-9 parts of butyl acetate, 41-45 parts of large red colorant；The gloss oil oil
Ink includes following components and parts by weight: 30-35 parts of epoxy acrylic resin, 10-14 parts of dipropylene glycol diacrylate；It is described
Rhodo color ink includes following components and parts by weight: 24-30 parts of epoxy acrylic resin, the poly- second two of o-benzoyl yl benzoic acid
4-8 parts of alcohol ester, 25-35 parts of rose colorant.
4. imitative metal red ink according to claim 3, it is characterised in that: the ingredient of the curing agent is amide groups
Amine.
5. imitating the preparation method of metal red ink described in a kind of claim 1, it is characterised in that: the following steps are included:
(1) ingredient is measured by following components and parts by weight, be placed in mixer: bright red color ink 19.7-21.5 parts, rhodo
58.6-62.4 parts of color ink, 13.4-15.5 parts of gloss oil ink, 10-12 parts of diluent, 0.6-0.8 parts of defoaming agent, curing agent 2-4
Part；
(2) in mixer, above-mentioned ingredient is stirred evenly；
(3) above-mentioned mixer is placed in 72-75 DEG C degree Celsius of temperature and is toasted 25-30 minutes.