CN109082034A - A kind of environment-friendly electric wire cable insulation material - Google Patents
A kind of environment-friendly electric wire cable insulation material Download PDFInfo
- Publication number
- CN109082034A CN109082034A CN201810892336.1A CN201810892336A CN109082034A CN 109082034 A CN109082034 A CN 109082034A CN 201810892336 A CN201810892336 A CN 201810892336A CN 109082034 A CN109082034 A CN 109082034A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- wire cable
- electric wire
- cable insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environment-friendly electric wire cable insulation materials, including, resin-oatmeal, plasticizer, coarse whiting, clay, auxiliary agent, fire retardant, stabilizer and lubricant, the environment-friendly electric wire cable insulation material include following parts by weight: 95-108 parts of resin-oatmeal, 40-50 parts of plasticizer, 40-50 parts of coarse whiting, 1-7 parts of clay, 1-6 parts of auxiliary agent, 1-4 parts of fire retardant, 2-8 parts of stabilizer and 0-1 parts of lubricant；A kind of environment-friendly electric wire cable insulation material of the invention has the advantages that the good feature of environmental protection, good flame resistance, intensity are high and ageing resistance is good, and the feature of environmental protection is mainly reflected in halogen-free environmental；It is added to lubricant in raw material of the invention, has the advantages that lubricity is good, fire resistance is good, corrosion resistance is good and chemical property is stable；Heretofore described fire retardant is flame retardant of magnesium hydroxide, helps to improve the flame retardant property of environmentally friendly insulated wire cable material；Heretofore described stabilizer is calcium zinc stabilizer.
Description
Technical field
The present invention relates to a kind of insulating materials to belong to macromolecule more particularly to a kind of environment-friendly electric wire cable insulation material
Field of material technology.
Background technique
In today that high-tech is grown rapidly, it is better that more and more electrical equipment wire and cables require insulation effect
Good environment-friendlyinsulation insulation material carries out the insulation of electrical equipment or wire and cable.In work on hand and life, existing electric wire
The a large amount of smog and toxic, corrosive gas that are released when cable fire first is that pollution environment, second is that in fire it is dangerous because
Element hampers safe escape and the fire-fighting work of people in a fire, makes lives and properties by heavy losses, while with communication
The development of cause, auto industry and computer industry, especially aviation wire, line for cars, high temperature instrument cable, oil drilling
Many occasions such as platform cable, have increasing need for that the feature of environmental protection is good, electric wire and cable material of good flame resistance, good insulating.
Current many cable insulation materials cannot bear high temperature, and pollute environment because can release dioxin in burning,
And threaten human health.Therefore environment amenable wire cable insulating material will be a kind of development trend.
In addition, the problem that existing CABLE MATERIALS is low and easy to aging there is also intensity.
Summary of the invention
The purpose of the present invention is in view of the deficienciess of the prior art, providing a kind of has the good feature of environmental protection, good flame resistance, strong
Degree height and the good environment-friendly electric wire cable insulation material of ageing resistance.
To achieve the above object, the present invention provides a kind of environment-friendly electric wire cable insulation materials, including, resin-oatmeal, plasticising
Agent, coarse whiting, clay, auxiliary agent, fire retardant, stabilizer and lubricant, the environment-friendly electric wire cable insulation material include following heavy
Measure part: 95-108 parts of resin-oatmeal, 40-50 parts of plasticizer, 40-50 parts of coarse whiting, 1-7 parts of clay, 1-6 parts of auxiliary agent, fire retardant 1-4
Part, 2-8 parts of stabilizer and 0-1 parts of lubricant.
As a further improvement of the foregoing solution, the environment-friendly electric wire cable insulation material in parts by weight, including
Following parts by weight: 100 parts of resin-oatmeal, 46 parts of plasticizer, 46 parts of coarse whiting, 4 parts of clay, 3 parts of auxiliary agent, 2 parts of fire retardant, stabilizer 5
Part and 0.6 part of lubricant.
As a further improvement of the foregoing solution, the resin-oatmeal is Corvic WS-1300.
As a further improvement of the foregoing solution, the plasticizer is that dioctyl terephthalate or trimellitic acid three are pungent
One of which in ester.
As a further improvement of the foregoing solution, the stabilizer is calcium zinc stabilizer.
As a further improvement of the foregoing solution, the lubricant is stearic acid.
As a further improvement of the foregoing solution, the fire retardant is flame retardant of magnesium hydroxide.
The invention has the benefit that a kind of environment-friendly electric wire cable insulation material of the invention has the feature of environmental protection good, fire-retardant
The advantage that property is good, intensity is high and ageing resistance is good, the feature of environmental protection are mainly reflected in halogen-free environmental；Profit is added in raw material of the invention
Lubrication prescription has the advantages that lubricity is good, fire resistance is good, corrosion resistance is good and chemical property is stable；Heretofore described fire retardant
For flame retardant of magnesium hydroxide, the flame retardant property of environmentally friendly insulated wire cable material is helped to improve；Heretofore described stabilizer
For calcium zinc stabilizer, which can make high molecular polymer under the radiation of light, can prevent or slow down photochemical reaction, prolong
The process of slow light aging, to achieve the purpose that extend the environmentally friendly insulated wire cable materials'use service life.
Specific embodiment
In order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below in conjunction with implementation of the invention
Example, is clearly and completely described the technical solution of the embodiment of the present invention.Obviously, described embodiment is of the invention
A part of the embodiment, instead of all the embodiments.Based on described the embodiment of the present invention, those of ordinary skill in the art
Every other embodiment obtained, shall fall within the protection scope of the present invention.
An embodiment provides one kind to have the good feature of environmental protection, good flame resistance, intensity height and ageing resistance good
Environment-friendly electric wire cable insulation material, including resin-oatmeal, plasticizer, coarse whiting, clay, auxiliary agent, fire retardant, stabilizer and lubrication
Agent, the environment-friendly electric wire cable insulation material in parts by weight, including following parts by weight: 95-108 parts of resin-oatmeal, plasticising
40-50 parts of agent, 40-50 parts of coarse whiting, 1-7 parts of clay, 1-6 parts of auxiliary agent, 1-4 parts of fire retardant, 2-8 parts of stabilizer and lubricant 0-1
Part.
Further, the resin-oatmeal is Corvic WS-1300.
Further, the plasticizer is the one of which in three monooctyl ester of dioctyl terephthalate or trimellitic acid.
Further, the stabilizer is calcium zinc stabilizer.
Further, the lubricant is stearic acid.
Further, the fire retardant is flame retardant of magnesium hydroxide.
Embodiment 1
A kind of environment-friendly electric wire cable insulation material of the present embodiment, comprises the following components in parts by weight: 100 parts of resin-oatmeal,
46 parts of plasticizer, 46 parts of coarse whiting, 4 parts of clay, 3 parts of auxiliary agent, 2 parts of fire retardant, 5 parts of stabilizer and 0.6 part of lubricant.
Embodiment 2
A kind of environment-friendly electric wire cable insulation material of the present embodiment, comprises the following components in parts by weight: 80 parts of resin-oatmeal increases
44 parts of agent of modeling, 44 parts of coarse whiting, 3 parts of clay, 2 parts of auxiliary agent, 1 part of fire retardant, 4 parts of stabilizer and 0.4 part of lubricant.
Embodiment 3
A kind of environment-friendly electric wire cable insulation material of the present embodiment, comprises the following components in parts by weight: 90 parts of resin-oatmeal increases
45 parts of agent of modeling, 45 parts of coarse whiting, 3 parts of clay, 2 parts of auxiliary agent, 2 parts of fire retardant, 4 parts of stabilizer and 0.5 part of lubricant.
Embodiment 4
A kind of environment-friendly electric wire cable insulation material of the present embodiment, comprises the following components in parts by weight: 120 parts of resin-oatmeal,
48 parts of plasticizer, 48 parts of coarse whiting, 6 parts of clay, 5 parts of auxiliary agent, 4 parts of fire retardant, 7 parts of stabilizer and 0.8 part of lubricant.
Embodiment 5
A kind of environment-friendly electric wire cable insulation material of the present embodiment, comprises the following components in parts by weight: 110 parts of resin-oatmeal,
47 parts of plasticizer, 47 parts of coarse whiting, 5 parts of clay, 4 parts of auxiliary agent, 3 parts of fire retardant, 6 parts of stabilizer and 0.7 part of lubricant.
A kind of environment-friendly electric wire cable insulation material according to above-described embodiment has the good feature of environmental protection, good flame resistance, strong
Degree is high and the good advantage of ageing resistance, the feature of environmental protection are mainly reflected in halogen-free environmental；It is added to lubricant in raw material of the invention, has
Have the advantages that lubricity is good, fire resistance is good, corrosion resistance is good and chemical property is stable；Heretofore described fire retardant is hydroxide
Magnesium fire retardant helps to improve the flame retardant property of environmentally friendly insulated wire cable material；Heretofore described stabilizer is that calcium zinc is steady
Determine agent, which can make high molecular polymer under the radiation of light, can prevent or slow down photochemical reaction, postpone light aging
Process, to achieve the purpose that extend the environmentally friendly insulated wire cable materials'use service life.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (7)
1. a kind of environment-friendly electric wire cable insulation material, including resin-oatmeal, plasticizer, coarse whiting, clay, auxiliary agent, fire retardant, stabilizer
And lubricant, it is characterised in that: the environment-friendly electric wire cable insulation material includes following parts by weight: 95-108 parts of resin-oatmeal,
40-50 parts of plasticizer, 40-50 parts of coarse whiting, 1-7 parts of clay, 1-6 parts of auxiliary agent, 1-4 parts of fire retardant, 2-8 parts of stabilizer and lubricant
0-1 parts.
2. a kind of environment-friendly electric wire cable insulation material according to claim 1, it is characterised in that: the environment-friendly electric wire cable
Insulating materials in parts by weight, including following parts by weight: 100 parts of resin-oatmeal, 46 parts of plasticizer, 46 parts of coarse whiting, clay 4
Part, 3 parts of auxiliary agent, 2 parts of fire retardant, 5 parts of stabilizer and 0.6 part of lubricant.
3. a kind of environment-friendly electric wire cable insulation material according to claim 1, it is characterised in that: the resin-oatmeal is polychlorostyrene
Vinyl WS-1300.
4. a kind of environment-friendly electric wire cable insulation material according to claim 1, it is characterised in that: the plasticizer is to benzene
One of which in three monooctyl ester of diformazan dioctyl phthalate or trimellitic acid.
5. a kind of environment-friendly electric wire cable insulation material according to claim 1, it is characterised in that: the stabilizer is calcium zinc
Stabilizer.
6. a kind of environment-friendly electric wire cable insulation material according to claim 1, it is characterised in that: the lubricant is tristearin
Acid.
7. a kind of environment-friendly electric wire cable insulation material according to claim 1, it is characterised in that: the fire retardant is hydrogen-oxygen
Change magnesium fire retardant.