CN107652622A - A kind of high-strength anti-flaming cable for building and preparation method thereof - Google Patents
A kind of high-strength anti-flaming cable for building and preparation method thereof Download PDFInfo
- Publication number
- CN107652622A CN107652622A CN201711022972.0A CN201711022972A CN107652622A CN 107652622 A CN107652622 A CN 107652622A CN 201711022972 A CN201711022972 A CN 201711022972A CN 107652622 A CN107652622 A CN 107652622A
- Authority
- CN
- China
- Prior art keywords
- parts
- plasticizer
- master batch
- sodium hydroxide
- halogen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
It is prepared the invention discloses a kind of high-strength anti-flaming cable for building and preparation method thereof, including by the raw material of following parts by weight：30 40 parts of diatomite, 20 35 parts of sodium hydroxide solution, 20 35 parts of phenolic resin, 10 15 parts of high density polyethylene (HDPE), 10 20 parts of boehmite, 15 30 parts of organo montmorillonite, 15 35 parts of ABS resin, 12 parts of silicone master batch.The present invention is added in combination antioxidant, lubricant, vulcanizing agent, plasticizer, halogen-free flame retardants, stabilizer and plasticizer using the proportioning of the above-mentioned raw materials such as diatomite, sodium hydroxide solution, phenolic resin, high density polyethylene (HDPE), boehmite, organo montmorillonite, ABS resin, silicone master batch, pentaerythrite progress science and carries out reaction fusion, process of preparing is simple, prepared product has preferable fire protection flame retarding, insulating properties, is adapted to use in multiple fields.
Description
Technical field
The present invention relates to technical field of cable production, and in particular to a kind of high-strength anti-flaming cable for building and its preparation side
Method.
Background technology
At present, it is also continuous to the quality requirement of cable with the development of the social economy, electric wire dosage increases rapidly
Improve, such as the cable used in the industries such as steel, metallurgy, electric power, chemical industry, oil, service life, anti-electromagnetism to cable
Requirement in terms of interference, pull resistance, shielding properties and high temperature resistant is all especially high, only meets the requirements, and could improve these
Security when being manufactured in field.
Electric power is the energy using electric energy as power, and the invention and application of electric power have started second of industrialization climax, from
This science and technology changes the life of people.In order to ensure the Electrical Safety of people, it is necessary on the electric equipment products surface for having insulating requirements
Coat insulating materials.Insulating materials is for making device in the material electrically to insulate, that is, can prevent what electric current passed through
Material.Its resistivity is very high, has good electrical insulation capability and high-temperature physical property, also with long shelf-life, moisture resistivity
The features such as good and fire-retardant.
The content of the invention
To solve the above problems, the invention provides a kind of high-strength anti-flaming cable for building and preparation method thereof.
To achieve the above object, the technical scheme taken of the present invention is：
A kind of high-strength anti-flaming cable for building and preparation method thereof, including be prepared by the raw material of following parts by weight：Diatom
Native 30-40 parts, sodium hydroxide solution 20-35 parts, phenolic resin 20-35 parts, high density polyethylene (HDPE) 10-15 parts, boehmite 10-20
Part, organo montmorillonite 15-30 parts, ABS resin 15-35 parts, silicone master batch 1-2 parts, pentaerythrite 5-10 parts, fume colloidal silica
1-10 parts, Tissuemat E 1-5 parts, ethylene-tetrafluoroethylene copolymer 2-5 parts, glass fibre 5-10 parts, antioxidant 10-30 parts, profit
Lubrication prescription 10-20 parts, vulcanizing agent 10-30 parts, plasticizer 10-20 parts, halogen-free flame retardants 15-35 parts, stabilizer 1-10 parts and plasticising
Agent 2-7 parts.
Further, the antioxidant is the double octadecyl esters of thio-2 acid, and the lubricant is silicone master batch, silicone master batch
One or more in ester, polyvinyl chloride wax, the vulcanizing agent are benzoyl peroxide, and the plasticizer is phthalic acid ester
Class compound, the halogen-free flame retardants are phosphorus series non-halogen fire retardant, and the stabilizer is barium cadmium zinc.
Further, a kind of high-strength anti-flaming cable for building, including be prepared by the raw material of following parts by weight：Diatom
Native 32-38 parts, sodium hydroxide solution 22-30 parts, phenolic resin 23-30 parts, high density polyethylene (HDPE) 12-14 parts, boehmite 11-18
Part, organo montmorillonite 16-20 parts, ABS resin 23-28 parts, silicone master batch 1-2 parts, pentaerythrite 6-9 parts, fume colloidal silica
3-7 parts, Tissuemat E 2-4 parts, ethylene-tetrafluoroethylene copolymer 3-5 parts, glass fibre 6-9 parts, antioxidant 15-26 parts, lubrication
Agent 14-18 parts, vulcanizing agent 13-24 parts, plasticizer 14-19 parts, halogen-free flame retardants 22-29 parts, stabilizer 3-9 parts and plasticizer 3-
6 parts.
Further, a kind of preparation method of high-strength anti-flaming cable for building, comprises the following steps：
S1, by phenolic resin 23-30 parts, high density polyethylene (HDPE) 12-14 parts, Tissuemat E 2-4 parts, ethylene-tetrafluoroethylene be copolymerized
Thing 3-5 parts are uniform by the progress banburying of banburying stove；Then antioxidant 15-26 parts, lubricant 14-18 parts, vulcanizing agent 13-24 are added
Part, plasticizer 14-19 parts, halogen-free flame retardants 22-29 parts, stabilizer 3-9 parts and plasticizer 3-6 part banburyings are uniformly mixed
Material；
S2, by diatomite 32-38 parts, boehmite 11-18 parts, organo montmorillonite 16-20 parts, silicone master batch 1-2 parts in 400-600
2-4 hours are calcined at DEG C, 3-4% sodium hydroxide solution 22-30 parts is added, is ground 1-2 hours, adds 12-15% salt
Acid solution, regulation pH value are 4-5, are aged 10-15 hours, and repeated hydrogenation sodium hydroxide solution regulation lapping liquid pH is neutrality, filters, dries
It is dry to obtain filler powder；Pentaerythrite 6-9 parts, fume colloidal silica 3-7 parts, glass fibre 6-9 parts are added to ultrasonic agitation again
In dispersion machine, carry out ultrasonic agitation and be uniformly dispersed, obtain mixed material；
S3, the compound obtained by step S1 and step S2 are obtained to material first carry out extruding pelletization at 110-140 DEG C of temperature, then
With, by being molded on cable extruding machine, obtaining fire-resistant cable material together with metal core wire.
Further, a kind of high-strength anti-flaming cable for building, including be prepared by the raw material of following parts by weight：Diatom
35 parts of soil, 25 parts of sodium hydroxide solution, 27 parts of phenolic resin, 13 parts of high density polyethylene (HDPE), 16 parts of boehmite, organo montmorillonite 18
Part, 25 parts of ABS resin, 1 part of silicone master batch, 7 parts of pentaerythrite, 5 parts of fume colloidal silica, 3 parts of Tissuemat E, ethene-tetrafluoro
4 parts of ethylene copolymer, 7 parts of glass fibre, 19 parts of antioxidant, 17 parts of lubricant, 16 parts of vulcanizing agent, 17 parts of plasticizer, Halogen resistance
Fire 4 parts of 26 parts of agent, 5 parts of stabilizer and plasticizer.
The present invention is taken off using diatomite, sodium hydroxide solution, phenolic resin, high density polyethylene (HDPE), boehmite, organic illiteracy
Soil, ABS resin, silicone master batch, pentaerythrite, fume colloidal silica, Tissuemat E, ethylene-tetrafluoroethylene copolymer, glass fibers
The proportioning that the above-mentioned raw materials such as dimension carry out science is added in combination antioxidant, lubricant, vulcanizing agent, plasticizer, halogen-free flame retardants, stably
Agent and plasticizer carry out reaction fusion, and process of preparing is simple, and prepared product has preferable fire protection flame retarding, insulating properties
Can, it is adapted to use in multiple fields.
Embodiment
In order that objects and advantages of the present invention are more clearly understood, the present invention is carried out with reference to embodiments further detailed
Explanation.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not intended to limit the present invention.
The present invention includes being prepared by the raw material of following parts by weight：Diatomite 30-40 parts, sodium hydroxide solution
20-35 parts, phenolic resin 20-35 parts, high density polyethylene (HDPE) 10-15 parts, boehmite 10-20 parts, organo montmorillonite 15-30 parts,
ABS resin 15-35 parts, silicone master batch 1-2 parts, pentaerythrite 5-10 parts, fume colloidal silica 1-10 parts, Tissuemat E 1-5 parts,
Ethylene-tetrafluoroethylene copolymer 2-5 parts, glass fibre 5-10 parts, antioxidant 10-30 parts, lubricant 10-20 parts, vulcanizing agent 10-
30 parts, plasticizer 10-20 parts, halogen-free flame retardants 15-35 parts, stabilizer 1-10 parts and plasticizer 2-7 parts.
The antioxidant is the double octadecyl esters of thio-2 acid, and the lubricant is silicone master batch, silicone master batch ester, polychlorostyrene second
One or more in alkene wax, the vulcanizing agent are benzoyl peroxide, and the plasticizer is phthalate compound,
The halogen-free flame retardants is phosphorus series non-halogen fire retardant, and the stabilizer is barium cadmium zinc.
A kind of high-strength anti-flaming cable for building, including be prepared by the raw material of following parts by weight：Diatomite 32-38
It is part, sodium hydroxide solution 22-30 parts, phenolic resin 23-30 parts, high density polyethylene (HDPE) 12-14 parts, boehmite 11-18 parts, organic
It is montmorillonite 16-20 parts, ABS resin 23-28 parts, silicone master batch 1-2 parts, pentaerythrite 6-9 parts, fume colloidal silica 3-7 parts, poly-
Ethylene waxes 2-4 parts, ethylene-tetrafluoroethylene copolymer 3-5 parts, glass fibre 6-9 parts, antioxidant 15-26 parts, lubricant 14-18
Part, vulcanizing agent 13-24 parts, plasticizer 14-19 parts, halogen-free flame retardants 22-29 parts, stabilizer 3-9 parts and plasticizer 3-6 parts.
A kind of preparation method of high-strength anti-flaming cable for building, comprises the following steps：
S1, by phenolic resin 23-30 parts, high density polyethylene (HDPE) 12-14 parts, Tissuemat E 2-4 parts, ethylene-tetrafluoroethylene be copolymerized
Thing 3-5 parts are uniform by the progress banburying of banburying stove；Then antioxidant 15-26 parts, lubricant 14-18 parts, vulcanizing agent 13-24 are added
Part, plasticizer 14-19 parts, halogen-free flame retardants 22-29 parts, stabilizer 3-9 parts and plasticizer 3-6 part banburyings are uniformly mixed
Material；
S2, by diatomite 32-38 parts, boehmite 11-18 parts, organo montmorillonite 16-20 parts, silicone master batch 1-2 parts in 400-600
2-4 hours are calcined at DEG C, 3-4% sodium hydroxide solution 22-30 parts is added, is ground 1-2 hours, adds 12-15% salt
Acid solution, regulation pH value are 4-5, are aged 10-15 hours, and repeated hydrogenation sodium hydroxide solution regulation lapping liquid pH is neutrality, filters, dries
It is dry to obtain filler powder；Pentaerythrite 6-9 parts, fume colloidal silica 3-7 parts, glass fibre 6-9 parts are added to ultrasonic agitation again
In dispersion machine, carry out ultrasonic agitation and be uniformly dispersed, obtain mixed material；
S3, the compound obtained by step S1 and step S2 are obtained to material first carry out extruding pelletization at 110-140 DEG C of temperature, then
With, by being molded on cable extruding machine, obtaining fire-resistant cable material together with metal core wire.
Embodiment 1：
A kind of preparation method of high-strength anti-flaming cable for building, comprises the following steps：
S1,26 parts of phenolic resin, 13 parts of high density polyethylene (HDPE), 3 parts of Tissuemat E, 4 parts of ethylene-tetrafluoroethylene copolymer passed through
It is uniform that banburying stove carries out banburying；Then 15 parts of antioxidant, 15 parts of lubricant, 15 parts of vulcanizing agent, 18 parts of plasticizer, Halogen resistance are added
5 parts of 26 parts of agent of combustion, 6 parts of stabilizer and plasticizer banburyings uniformly obtain compound；
S2,33 parts of diatomite, 13 parts of boehmite, 15 parts of organo montmorillonite, 2 parts of silicone master batch calcined 3 hours at 430 DEG C,
3% 25 parts of sodium hydroxide solution is added, is ground 2 hours, adds 14% hydrochloric acid solution, regulation pH value is 4, and ageing 15 is small
When, repeated hydrogenation sodium hydroxide solution regulation lapping liquid pH is neutrality, filtering, dries and obtains filler powder；8 parts of pentaerythrite, gas again
4 parts of phase method white carbon, 7 parts of glass fibre are added in ultrasonic agitation dispersion machine, are carried out ultrasonic agitation and are uniformly dispersed, are mixed
Material；
S3, the compound obtained by step S1 and step S2 obtained to material first carry out extruding pelletization at 130 DEG C of temperature, then with gold
Belong to cored wire together by being molded on cable extruding machine, obtain fire-resistant cable material.
Embodiment 2：
A kind of preparation method of high-strength anti-flaming cable for building, comprises the following steps：
S1,30 parts of phenolic resin, 14 parts of high density polyethylene (HDPE), 4 parts of Tissuemat E, 5 parts of ethylene-tetrafluoroethylene copolymer passed through
It is uniform that banburying stove carries out banburying；Then 26 parts of antioxidant, 18 parts of lubricant, 24 parts of vulcanizing agent, 19 parts of plasticizer, Halogen resistance are added
6 parts of 29 parts of agent of combustion, 9 parts of stabilizer and plasticizer banburyings uniformly obtain compound；
S2,38 parts of diatomite, 18 parts of boehmite, 20 parts of organo montmorillonite, 2 parts of silicone master batch calcined 4 hours at 600 DEG C,
4% 30 parts of sodium hydroxide solution is added, is ground 2 hours, adds 15% hydrochloric acid solution, regulation pH value is 5, and ageing 15 is small
When, repeated hydrogenation sodium hydroxide solution regulation lapping liquid pH is neutrality, filtering, dries and obtains filler powder；9 parts of pentaerythrite, gas again
7 parts of phase method white carbon, 9 parts of glass fibre are added in ultrasonic agitation dispersion machine, are carried out ultrasonic agitation and are uniformly dispersed, are mixed
Material；
S3, the compound obtained by step S1 and step S2 obtained to material first carry out extruding pelletization at 140 DEG C of temperature, then with gold
Belong to cored wire together by being molded on cable extruding machine, obtain fire-resistant cable material.
Embodiment 3：
A kind of preparation method of high-strength anti-flaming cable for building, comprises the following steps：
S1,23 parts of phenolic resin, 12 parts of high density polyethylene (HDPE), 2 parts of Tissuemat E, 5 parts of ethylene-tetrafluoroethylene copolymer passed through
It is uniform that banburying stove carries out banburying；Then 15 parts of antioxidant, 14 parts of lubricant, 13 parts of vulcanizing agent, 14 parts of plasticizer, Halogen resistance are added
3 parts of 22 parts of agent of combustion, 3 parts of stabilizer and plasticizer banburyings uniformly obtain compound；
S2,32 parts of diatomite, 11 parts of boehmite, 16 parts of organo montmorillonite, 1 part of silicone master batch calcined 2 hours at 400 DEG C,
3% 22 parts of sodium hydroxide solution is added, is ground 1 hour, adds 12% hydrochloric acid solution, regulation pH value is 4, and ageing 10 is small
When, repeated hydrogenation sodium hydroxide solution regulation lapping liquid pH is neutrality, filtering, dries and obtains filler powder；6 parts of pentaerythrite, gas again
3 parts of phase method white carbon, 6 parts of glass fibre are added in ultrasonic agitation dispersion machine, are carried out ultrasonic agitation and are uniformly dispersed, are mixed
Material；
S3, the compound obtained by step S1 and step S2 obtained to material first carry out extruding pelletization at 110 DEG C of temperature, then with gold
Belong to cored wire together by being molded on cable extruding machine, obtain fire-resistant cable material.
The present invention is taken off using diatomite, sodium hydroxide solution, phenolic resin, high density polyethylene (HDPE), boehmite, organic illiteracy
Soil, ABS resin, silicone master batch, pentaerythrite, fume colloidal silica, Tissuemat E, ethylene-tetrafluoroethylene copolymer, glass fibers
The proportioning that the above-mentioned raw materials such as dimension carry out science is added in combination antioxidant, lubricant, vulcanizing agent, plasticizer, halogen-free flame retardants, stably
Agent and plasticizer carry out reaction fusion, and process of preparing is simple, and prepared product has preferable fire protection flame retarding, insulating properties
Can, it is adapted to use in multiple fields.
Described above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, under the premise without departing from the principles of the invention, some improvements and modifications can also be made, these improvements and modifications also should
It is considered as protection scope of the present invention.
Claims (5)
1. a kind of high-strength anti-flaming cable for building, it is characterised in that including being prepared by the raw material of following parts by weight：Diatom
Native 30-40 parts, sodium hydroxide solution 20-35 parts, phenolic resin 20-35 parts, high density polyethylene (HDPE) 10-15 parts, boehmite 10-20
Part, organo montmorillonite 15-30 parts, ABS resin 15-35 parts, silicone master batch 1-2 parts, pentaerythrite 5-10 parts, fume colloidal silica
1-10 parts, Tissuemat E 1-5 parts, ethylene-tetrafluoroethylene copolymer 2-5 parts, glass fibre 5-10 parts, antioxidant 10-30 parts, profit
Lubrication prescription 10-20 parts, vulcanizing agent 10-30 parts, plasticizer 10-20 parts, halogen-free flame retardants 15-35 parts, stabilizer 1-10 parts and plasticising
Agent 2-7 parts.
2. a kind of high-strength anti-flaming cable for building according to claim 1, it is characterised in that the antioxidant is thio
The double octadecyl esters of dipropionic acid, the lubricant is the one or more in silicone master batch, silicone master batch ester, polyvinyl chloride wax, described
Vulcanizing agent is benzoyl peroxide, and the plasticizer is phthalate compound, the halogen-free flame retardants be phosphorus system without
Halogen fire retardant, the stabilizer are barium cadmium zinc.
3. a kind of high-strength anti-flaming cable for building according to claim 1, it is characterised in that including by following parts by weight
Raw material be prepared：Diatomite 32-38 parts, sodium hydroxide solution 22-30 parts, phenolic resin 23-30 parts, high density polyethylene (HDPE)
12-14 parts, boehmite 11-18 parts, organo montmorillonite 16-20 parts, ABS resin 23-28 parts, silicone master batch 1-2 parts, pentaerythrite
6-9 parts, fume colloidal silica 3-7 parts, Tissuemat E 2-4 parts, ethylene-tetrafluoroethylene copolymer 3-5 parts, glass fibre 6-9 parts,
It is antioxidant 15-26 parts, lubricant 14-18 parts, vulcanizing agent 13-24 parts, plasticizer 14-19 parts, halogen-free flame retardants 22-29 parts, steady
Determine agent 3-9 parts and plasticizer 3-6 parts.
4. the preparation method of a kind of high-strength anti-flaming cable for building according to claim 1, it is characterised in that including such as
Lower step：
S1, by phenolic resin 23-30 parts, high density polyethylene (HDPE) 12-14 parts, Tissuemat E 2-4 parts, ethylene-tetrafluoroethylene be copolymerized
Thing 3-5 parts are uniform by the progress banburying of banburying stove；Then antioxidant 15-26 parts, lubricant 14-18 parts, vulcanizing agent 13-24 are added
Part, plasticizer 14-19 parts, halogen-free flame retardants 22-29 parts, stabilizer 3-9 parts and plasticizer 3-6 part banburyings are uniformly mixed
Material；
S2, by diatomite 32-38 parts, boehmite 11-18 parts, organo montmorillonite 16-20 parts, silicone master batch 1-2 parts in 400-600
2-4 hours are calcined at DEG C, 3-4% sodium hydroxide solution 22-30 parts is added, is ground 1-2 hours, adds 12-15% salt
Acid solution, regulation pH value are 4-5, are aged 10-15 hours, and repeated hydrogenation sodium hydroxide solution regulation lapping liquid pH is neutrality, filters, dries
It is dry to obtain filler powder；Pentaerythrite 6-9 parts, fume colloidal silica 3-7 parts, glass fibre 6-9 parts are added to ultrasonic agitation again
In dispersion machine, carry out ultrasonic agitation and be uniformly dispersed, obtain mixed material；
S3, the compound obtained by step S1 and step S2 are obtained to material first carry out extruding pelletization at 110-140 DEG C of temperature, then
With, by being molded on cable extruding machine, obtaining fire-resistant cable material together with metal core wire.
5. a kind of high-strength anti-flaming cable for building according to claim 1, it is characterised in that including by following parts by weight
Raw material be prepared：35 parts of diatomite, 25 parts of sodium hydroxide solution, 27 parts of phenolic resin, 13 parts of high density polyethylene (HDPE), Bo Mu
It is 16 parts of stone, 18 parts of organo montmorillonite, 25 parts of ABS resin, 1 part of silicone master batch, 7 parts of pentaerythrite, 5 parts of fume colloidal silica, poly-
3 parts of ethylene waxes, 4 parts of ethylene-tetrafluoroethylene copolymer, 7 parts of glass fibre, 19 parts of antioxidant, 17 parts of lubricant, vulcanizing agent 16
Part, 17 parts of plasticizer, 26 parts of halogen-free flame retardants, 5 parts of stabilizer and 4 parts of plasticizer.