CN107652596A - A kind of fire-resistant cable material of high temperature resistant cracking resistance and preparation method thereof - Google Patents
A kind of fire-resistant cable material of high temperature resistant cracking resistance and preparation method thereof Download PDFInfo
- Publication number
- CN107652596A CN107652596A CN201711026930.4A CN201711026930A CN107652596A CN 107652596 A CN107652596 A CN 107652596A CN 201711026930 A CN201711026930 A CN 201711026930A CN 107652596 A CN107652596 A CN 107652596A
- Authority
- CN
- China
- Prior art keywords
- parts
- fire
- plasticizer
- cable material
- resistant cable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
It is prepared the invention discloses a kind of fire-resistant cable material of high temperature resistant cracking resistance and preparation method thereof, including by the raw material of following parts by weight:4 third 30 40 parts of fluorubber, 20 35 parts of trioctyl trimellitate (TOTM), 20 35 parts of polyphenylene oxide resin, 10 15 parts of zinc molybdate, 10 20 parts of saponite, 15 30 parts of talcum powder, 15 35 parts of melamine cyanurate, 12 parts of stearic acid.The present invention is added in combination antioxidant, lubricant, compatilizer, plasticizer, fire retardant, stabilizer and plasticizer using the proportioning of the above-mentioned raw materials such as 4 third fluorubber, trioctyl trimellitate (TOTM), polyphenylene oxide resin, zinc molybdate, saponite, talcum powder, melamine cyanurate, stearic acid, polybutylene terephthalate (PBT) progress science and carries out reaction fusion, process of preparing is simple, prepared product has preferable fire protection flame retarding, insulating properties, is adapted to use in multiple fields.
Description
Technical field
The present invention relates to technical field of cable production, and in particular to a kind of fire-resistant cable material of high temperature resistant cracking resistance and its preparation
Method.
Background technology
At present, it is also continuous to the quality requirement of cable with the development of the social economy, electric wire dosage increases rapidly
Improve, such as the cable used in the industries such as steel, metallurgy, electric power, chemical industry, oil, service life, anti-electromagnetism to cable
Requirement in terms of interference, pull resistance, shielding properties and high temperature resistant is all especially high, only meets the requirements, and could improve these
Security when being manufactured in field.
Electric power is the energy using electric energy as power, and the invention and application of electric power have started second of industrialization climax, from
This science and technology changes the life of people.In order to ensure the Electrical Safety of people, it is necessary on the electric equipment products surface for having insulating requirements
Coat insulating materials.Insulating materials is for making device in the material electrically to insulate, that is, can prevent what electric current passed through
Material.Its resistivity is very high, has good electrical insulation capability and high-temperature physical property, also with long shelf-life, moisture resistivity
The features such as good and fire-retardant.
The content of the invention
To solve the above problems, the invention provides a kind of fire-resistant cable material of high temperature resistant cracking resistance and preparation method thereof.
To achieve the above object, the technical scheme taken of the present invention is:
A kind of fire-resistant cable material of high temperature resistant cracking resistance and preparation method thereof, including be prepared by the raw material of following parts by weight:Four
Third fluorubber 30-40 parts, trioctyl trimellitate (TOTM) 20-35 parts, polyphenylene oxide resin 20-35 parts, zinc molybdate 10-15 parts, saponite 10-
20 parts, talcum powder 15-30 parts, melamine cyanurate 15-35 parts, stearic acid 1-2 parts, polybutylene terephthalate (PBT) 5-
10 parts, fume colloidal silica 1-10 parts, modified carbide slag powder 1-5 parts, maleic anhydride grafted ethene-vinyl acetate copolymerization 2-5
Part, nanocrystal cellulose 5-10 parts, antioxidant 10-30 parts, lubricant 10-20 parts, compatilizer 10-30 parts, plasticizer 10-20
Part, fire retardant 15-35 parts, stabilizer 1-10 parts and plasticizer 2-7 parts.
Further, the antioxidant is the double octadecyl esters of thio-2 acid, the lubricant be stearic acid, stearate,
One or more in polyvinyl chloride wax, the compatilizer are the H of POE-g-M I, and the plasticizer is phthalate chemical combination
Thing, the flame-retardants melamine, the stabilizer are barium cadmium zinc.
Further, a kind of fire-resistant cable material of high temperature resistant cracking resistance, including be prepared by the raw material of following parts by weight:Four
Third fluorubber 32-38 parts, trioctyl trimellitate (TOTM) 22-30 parts, polyphenylene oxide resin 23-30 parts, zinc molybdate 12-14 parts, saponite 11-
18 parts, talcum powder 16-20 parts, melamine cyanurate 23-28 parts, stearic acid 1-2 parts, polybutylene terephthalate (PBT) 6-
9 parts, fume colloidal silica 3-7 parts, modified carbide slag powder 2-4 parts, maleic anhydride grafted ethene-vinyl acetate copolymerization 3-5 parts,
Nanocrystal cellulose 6-9 parts, antioxidant 15-26 parts, lubricant 14-18 parts, compatilizer 13-24 parts, plasticizer 14-19 parts,
Fire retardant 22-29 parts, stabilizer 3-9 parts and plasticizer 3-6 parts.
Further, a kind of preparation method of the fire-resistant cable material of high temperature resistant cracking resistance, comprises the following steps:
S1,4 third fluorubber 32-38 parts, trioctyl trimellitate (TOTM) 22-30 parts, polyphenylene oxide resin 23-30 are weighed according to parts by weight
Part, zinc molybdate 12-14 parts, saponite 11-18 parts, talcum powder 16-20 parts, melamine cyanurate 23-28 parts, stearic acid 1-2
Part, polybutylene terephthalate (PBT) 6-9 parts, fume colloidal silica 3-7 parts, modified carbide slag powder 2-4 parts, maleic anhydride grafting
Ethylene-vinyl acetate c 3-5 parts, nanocrystal cellulose 6-9 parts are added in ultrasonic agitation dispersion machine, are carried out ultrasound and are stirred
Mix scattered, obtain mixed material;
S2, the mixed material obtained by step S1 poured into double-screw extruding pelletizing machine, extruded at 160-250 DEG C of temperature
It is granulated;Obtain fire-resistant cable material;
S3, antioxidant 15-26 parts, lubricant 14-18 parts, compatilizer 13-24 will be added in the fire-resistant cable material obtained by step S2
Part, plasticizer 14-19 parts, fire retardant 22-29 parts, stabilizer 3-9 parts and plasticizer 3-6 parts, reacted at being 55-88 DEG C in temperature
15-35min;Then 10-30min is quickly stirred with 400-900r/min speed, produces this product.
Further, a kind of fire-resistant cable material of high temperature resistant cracking resistance, including be prepared by the raw material of following parts by weight:Four
Third 35 parts of fluorubber, 25 parts of trioctyl trimellitate (TOTM), 27 parts of polyphenylene oxide resin, 13 parts of zinc molybdate, 16 parts of saponite, talcum powder 18
Part, 25 parts of melamine cyanurate, 1 part of stearic acid, 7 parts of polybutylene terephthalate (PBT), 5 parts of fume colloidal silica, change
3 parts of property calcium carbide ground-slag, 4 parts of maleic anhydride grafted ethene-vinyl acetate copolymerization, 7 parts of nanocrystal cellulose, antioxidant 19
Part, 17 parts of lubricant, 16 parts of compatilizer, 17 parts of plasticizer, 26 parts of fire retardant, 5 parts of stabilizer and 4 parts of plasticizer.
The present invention is using 4 third fluorubber, trioctyl trimellitate (TOTM), polyphenylene oxide resin, zinc molybdate, saponite, talcum powder, three
Poly cyanamid cyanurate, stearic acid, polybutylene terephthalate (PBT), fume colloidal silica, modified carbide slag powder, maleic anhydride
The above-mentioned raw materials such as grafted ethene-vinyl acetate copolymerization, nanocrystal cellulose carry out science proportioning be added in combination antioxidant,
Lubricant, compatilizer, plasticizer, fire retardant, stabilizer and plasticizer carry out reaction fusion, and process of preparing is simple, made
Standby product has preferable fire protection flame retarding, insulating properties, is adapted to use in multiple fields.
Embodiment
In order that objects and advantages of the present invention are more clearly understood, the present invention is carried out with reference to embodiments further detailed
Explanation.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not intended to limit the present invention.
The present invention includes being prepared by the raw material of following parts by weight:4 third fluorubber 30-40 parts, tri trimellitate
Monooctyl ester 20-35 parts, polyphenylene oxide resin 20-35 parts, zinc molybdate 10-15 parts, saponite 10-20 parts, talcum powder 15-30 parts, melamine
Amine cyanurate 15-35 parts, stearic acid 1-2 parts, polybutylene terephthalate (PBT) 5-10 parts, fume colloidal silica 1-10 parts,
Modified carbide slag powder 1-5 parts, maleic anhydride grafted ethene-vinyl acetate copolymerization 2-5 parts, nanocrystal cellulose 5-10 parts,
Antioxidant 10-30 parts, lubricant 10-20 parts, compatilizer 10-30 parts, plasticizer 10-20 parts, fire retardant 15-35 parts, stabilizer
1-10 parts and plasticizer 2-7 parts.
The antioxidant is the double octadecyl esters of thio-2 acid, and the lubricant is stearic acid, stearate, polyvinyl chloride wax
In one or more, the compatilizer is the H of POE-g-M I, and the plasticizer is phthalate compound, the resistance
Agent melamine is fired, the stabilizer is barium cadmium zinc.
A kind of fire-resistant cable material of high temperature resistant cracking resistance, including be prepared by the raw material of following parts by weight:4 third fluorubber
32-38 parts, trioctyl trimellitate (TOTM) 22-30 parts, polyphenylene oxide resin 23-30 parts, zinc molybdate 12-14 parts, saponite 11-18 parts, cunning
Stone flour 16-20 parts, melamine cyanurate 23-28 parts, stearic acid 1-2 parts, polybutylene terephthalate (PBT) 6-9 parts, gas
Phase method white carbon 3-7 parts, modified carbide slag powder 2-4 parts, maleic anhydride grafted ethene-vinyl acetate copolymerization 3-5 parts, nano junction
Crystalline cellulose 6-9 parts, antioxidant 15-26 parts, lubricant 14-18 parts, compatilizer 13-24 parts, plasticizer 14-19 parts, fire retardant
22-29 parts, stabilizer 3-9 parts and plasticizer 3-6 parts.
A kind of preparation method of the fire-resistant cable material of high temperature resistant cracking resistance, comprises the following steps:
S1,4 third fluorubber 32-38 parts, trioctyl trimellitate (TOTM) 22-30 parts, polyphenylene oxide resin 23-30 are weighed according to parts by weight
Part, zinc molybdate 12-14 parts, saponite 11-18 parts, talcum powder 16-20 parts, melamine cyanurate 23-28 parts, stearic acid 1-2
Part, polybutylene terephthalate (PBT) 6-9 parts, fume colloidal silica 3-7 parts, modified carbide slag powder 2-4 parts, maleic anhydride grafting
Ethylene-vinyl acetate c 3-5 parts, nanocrystal cellulose 6-9 parts are added in ultrasonic agitation dispersion machine, are carried out ultrasound and are stirred
Mix scattered, obtain mixed material;
S2, the mixed material obtained by step S1 poured into double-screw extruding pelletizing machine, extruded at 160-250 DEG C of temperature
It is granulated;Obtain fire-resistant cable material;
S3, antioxidant 15-26 parts, lubricant 14-18 parts, compatilizer 13-24 will be added in the fire-resistant cable material obtained by step S2
Part, plasticizer 14-19 parts, fire retardant 22-29 parts, stabilizer 3-9 parts and plasticizer 3-6 parts, reacted at being 55-88 DEG C in temperature
15-35min;Then 10-30min is quickly stirred with 400-900r/min speed, produces this product.
Embodiment 1:
A kind of preparation method of the fire-resistant cable material of high temperature resistant cracking resistance, comprises the following steps:
S1,38 parts of 4 third fluorubber, 30 parts of trioctyl trimellitate (TOTM), 30 parts of polyphenylene oxide resin, zinc molybdate are weighed according to parts by weight
14 parts, 18 parts of saponite, 20 parts of talcum powder, 28 parts of melamine cyanurate, 2 parts of stearic acid, polybutylene terephthalate (PBT) 9
Part, 7 parts of fume colloidal silica, 4 parts of modified carbide slag powder, 5 parts of maleic anhydride grafted ethene-vinyl acetate copolymerization, nano junction
9 parts of crystalline cellulose is added in ultrasonic agitation dispersion machine, is carried out ultrasonic agitation and is disperseed, obtains mixed material;
S2, the mixed material obtained by step S1 poured into double-screw extruding pelletizing machine, carrying out extrusion at 160 DEG C of temperature makes
Grain;Obtain fire-resistant cable material;
S3,26 parts of antioxidant, 18 parts of lubricant, 24 parts of compatilizer, plasticizer will be added in the fire-resistant cable material obtained by step S2
6 parts of 19 parts, 29 parts of fire retardant, 9 parts of stabilizer and plasticizer, react 30min at being 90 DEG C in temperature;Then with 800r/min's
Speed quickly stirs 25min, produces this product.
Embodiment 2:
A kind of preparation method of the fire-resistant cable material of high temperature resistant cracking resistance, comprises the following steps:
S1,35 parts of 4 third fluorubber, 25 parts of trioctyl trimellitate (TOTM), 27 parts of polyphenylene oxide resin, zinc molybdate are weighed according to parts by weight
13 parts, 16 parts of saponite, 18 parts of talcum powder, 25 parts of melamine cyanurate, 1 part of stearic acid, polybutylene terephthalate (PBT) 7
Part, 5 parts of fume colloidal silica, 3 parts of modified carbide slag powder, 4 parts of maleic anhydride grafted ethene-vinyl acetate copolymerization, nano junction
7 parts of crystalline cellulose is added in ultrasonic agitation dispersion machine, is carried out ultrasonic agitation and is disperseed, obtains mixed material;
S2, the mixed material obtained by step S1 poured into double-screw extruding pelletizing machine, carrying out extrusion at 250 DEG C of temperature makes
Grain;Obtain fire-resistant cable material;
S3,19 parts of antioxidant, 17 parts of lubricant, 16 parts of compatilizer, plasticizer will be added in the fire-resistant cable material obtained by step S2
4 parts of 17 parts, 26 parts of fire retardant, 5 parts of stabilizer and plasticizer, react 27min at being 88 DEG C in temperature;Then with 700r/min's
Speed quickly stirs 18min, produces this product.
Embodiment 3:
A kind of preparation method of the fire-resistant cable material of high temperature resistant cracking resistance, comprises the following steps:
S1,32 parts of 4 third fluorubber, 22 parts of trioctyl trimellitate (TOTM), 23 parts of polyphenylene oxide resin, zinc molybdate are weighed according to parts by weight
12 parts, 11 parts of saponite, 16 parts of talcum powder, 23 parts of melamine cyanurate, 1 part of stearic acid, polybutylene terephthalate (PBT) 6
Part, 3 parts of fume colloidal silica, 2 parts of modified carbide slag powder, 3 parts of maleic anhydride grafted ethene-vinyl acetate copolymerization, nano junction
6 parts of crystalline cellulose is added in ultrasonic agitation dispersion machine, is carried out ultrasonic agitation and is disperseed, obtains mixed material;
S2, the mixed material obtained by step S1 poured into double-screw extruding pelletizing machine, carrying out extrusion at 190 DEG C of temperature makes
Grain;Obtain fire-resistant cable material;
S3,15 parts of antioxidant, 14 parts of lubricant, 13 parts of compatilizer, plasticizer will be added in the fire-resistant cable material obtained by step S2
3 parts of 14 parts, 22 parts of fire retardant, 3 parts of stabilizer and plasticizer, react 20min at being 65 DEG C in temperature;Then with 500r/min's
Speed quickly stirs 15min, produces this product.
The present invention is using 4 third fluorubber, trioctyl trimellitate (TOTM), polyphenylene oxide resin, zinc molybdate, saponite, talcum powder, three
Poly cyanamid cyanurate, stearic acid, polybutylene terephthalate (PBT), fume colloidal silica, modified carbide slag powder, maleic anhydride
The above-mentioned raw materials such as grafted ethene-vinyl acetate copolymerization, nanocrystal cellulose carry out science proportioning be added in combination antioxidant,
Lubricant, compatilizer, plasticizer, fire retardant, stabilizer and plasticizer carry out reaction fusion, and process of preparing is simple, made
Standby product has preferable fire protection flame retarding, insulating properties, is adapted to use in multiple fields.
Described above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, under the premise without departing from the principles of the invention, some improvements and modifications can also be made, these improvements and modifications also should
It is considered as protection scope of the present invention.
Claims (5)
1. a kind of fire-resistant cable material of high temperature resistant cracking resistance, it is characterised in that including being prepared by the raw material of following parts by weight:Four
Third fluorubber 30-40 parts, trioctyl trimellitate (TOTM) 20-35 parts, polyphenylene oxide resin 20-35 parts, zinc molybdate 10-15 parts, saponite 10-
20 parts, talcum powder 15-30 parts, melamine cyanurate 15-35 parts, stearic acid 1-2 parts, polybutylene terephthalate (PBT) 5-
10 parts, fume colloidal silica 1-10 parts, modified carbide slag powder 1-5 parts, maleic anhydride grafted ethene-vinyl acetate copolymerization 2-5
Part, nanocrystal cellulose 5-10 parts, antioxidant 10-30 parts, lubricant 10-20 parts, compatilizer 10-30 parts, plasticizer 10-20
Part, fire retardant 15-35 parts, stabilizer 1-10 parts and plasticizer 2-7 parts.
2. the fire-resistant cable material of a kind of high temperature resistant cracking resistance according to claim 1, it is characterised in that the antioxidant is sulphur
For the double octadecyl esters of dipropionic acid, the lubricant is stearic acid, the one or more in stearate, polyvinyl chloride wax, the phase
Appearance agent is the H of POE-g-M I, and the plasticizer is phthalate compound, the flame-retardants melamine, the stabilization
Agent is barium cadmium zinc.
3. the fire-resistant cable material of a kind of high temperature resistant cracking resistance according to claim 1, it is characterised in that including by following weight
The raw material of part is prepared:4 third fluorubber 32-38 parts, trioctyl trimellitate (TOTM) 22-30 parts, polyphenylene oxide resin 23-30 parts, molybdenum
It is sour zinc 12-14 parts, saponite 11-18 parts, talcum powder 16-20 parts, melamine cyanurate 23-28 parts, stearic acid 1-2 parts, poly-
Mutual-phenenyl two acid bromide two alcohol ester 6-9 parts, fume colloidal silica 3-7 parts, modified carbide slag powder 2-4 parts, maleic anhydride grafted ethene-
Vinyl acetate copolymerization 3-5 parts, nanocrystal cellulose 6-9 parts, antioxidant 15-26 parts, lubricant 14-18 parts, compatilizer 13-
24 parts, plasticizer 14-19 parts, fire retardant 22-29 parts, stabilizer 3-9 parts and plasticizer 3-6 parts.
A kind of 4. preparation method of the fire-resistant cable material of high temperature resistant cracking resistance according to claim 1, it is characterised in that including
Following steps:
S1,4 third fluorubber 32-38 parts, trioctyl trimellitate (TOTM) 22-30 parts, polyphenylene oxide resin 23-30 are weighed according to parts by weight
Part, zinc molybdate 12-14 parts, saponite 11-18 parts, talcum powder 16-20 parts, melamine cyanurate 23-28 parts, stearic acid 1-2
Part, polybutylene terephthalate (PBT) 6-9 parts, fume colloidal silica 3-7 parts, modified carbide slag powder 2-4 parts, maleic anhydride grafting
Ethylene-vinyl acetate c 3-5 parts, nanocrystal cellulose 6-9 parts are added in ultrasonic agitation dispersion machine, are carried out ultrasound and are stirred
Mix scattered, obtain mixed material;
S2, the mixed material obtained by step S1 poured into double-screw extruding pelletizing machine, extruded at 160-250 DEG C of temperature
It is granulated;Obtain fire-resistant cable material;
S3, antioxidant 15-26 parts, lubricant 14-18 parts, compatilizer 13-24 will be added in the fire-resistant cable material obtained by step S2
Part, plasticizer 14-19 parts, fire retardant 22-29 parts, stabilizer 3-9 parts and plasticizer 3-6 parts, reacted at being 55-95 DEG C in temperature
15-35min;Then 10-30min is quickly stirred with 400-900r/min speed, produces this product.
5. the fire-resistant cable material of a kind of high temperature resistant cracking resistance according to claim 1, it is characterised in that including by following weight
The raw material of part is prepared:4 third 35 parts of fluorubber, 25 parts of trioctyl trimellitate (TOTM), 27 parts of polyphenylene oxide resin, 13 parts of zinc molybdate,
16 parts of saponite, 18 parts of talcum powder, 25 parts of melamine cyanurate, 1 part of stearic acid, 7 parts of polybutylene terephthalate (PBT), gas
5 parts of phase method white carbon, 3 parts of modified carbide slag powder, 4 parts of maleic anhydride grafted ethene-vinyl acetate copolymerization, nanocrystal fiber
7 parts of element, 19 parts of antioxidant, 17 parts of lubricant, 16 parts of compatilizer, 17 parts of plasticizer, 26 parts of fire retardant, 5 parts of stabilizer and plasticising
4 parts of agent.