CN109054974A - A kind of magnesium alloy water-soluble metalworking liquid and preparation method thereof - Google Patents
A kind of magnesium alloy water-soluble metalworking liquid and preparation method thereof Download PDFInfo
- Publication number
- CN109054974A CN109054974A CN201811193600.9A CN201811193600A CN109054974A CN 109054974 A CN109054974 A CN 109054974A CN 201811193600 A CN201811193600 A CN 201811193600A CN 109054974 A CN109054974 A CN 109054974A
- Authority
- CN
- China
- Prior art keywords
- parts
- magnesium alloy
- agent
- water
- soluble metalworking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of magnesium alloy water-soluble metalworking liquids and preparation method thereof; magnesium alloy water-soluble metalworking liquid is made of pH adjusting agent, surfactant, antirust agent, corrosion inhibiter, hard water resistance stabilizer, magnesium alloy protective agent, defoaming agent and fungicide, and surplus adds to 100 parts by base oil and deionized water.The pH adjusting agent of required weight, corrosion inhibiter, antirust agent and base oil and deionized water are mixed evenly first, 40 DEG C~60 DEG C are heated to after solution is transparent, is cooled to room temperature after keeping the temperature 45~65min;Magnesium alloy protective agent, hard water resistance stabilizer, surfactant, defoaming agent and the fungicide that configured required weight is added in solvent are stated then up and is stirred evenly, and product is magnesium alloy water-soluble metalworking liquid.Cutting fluid in the present invention has lower viscosity, and can prevent sky gas and water and it is all it is multi-environment magnesium alloy parts are caused to corrode, can effectively maintain stability, there is good inoxidizability.
Description
Technical field
The invention belongs to industrial lubrication cutting fluid technical fields, particularly relate to a kind of magnesium alloy water-soluble metalworking liquid
And preparation method thereof.
Background technique
The features such as AM60 magnesium alloy has good plasticity, weldability and corrosion resistance, can bear Smaller load, is commonly used for flying
Machine industry bracket and small components.But in the machining such as turning drill jig, in order to guarantee the complete of machining accuracy and workpiece surface
Property, need a kind of cutting fluid that it is made to have good greasy property, cooling performance, rustless property, oil removing cleaning performance, anti-corrosive properties
It can be with easily dilutable performance.And existing most of cutting fluids are mainly the alloy materials such as ferro-aluminum steel in the market in currently available technology
, in most of process, using these cutting fluids in the prior art, rapidoprint can be made to aoxidize especially fast, nothing
Method reaches the requirement of processing.
There are some specific magnesium alloy cutting fluids in the prior art, these magnesium alloy cutting fluids are frequently used in magnesium alloy thin
In the Precision Machining of wall part, but Mg alloy thin wall part is contacted with cutting fluid in process can bring a series of ask
Topic: (1) magnesium alloy can form MgO or Mg (OH) on surface in air, aqueous solution or other hybird environments2, these substances exist
Magnesium alloy outer layer forms layer of surface film, and this skin covering of the surface easily dissolves, and cannot play and internal material is prevented to continue to send out with extraneous
The effect of raw reaction;(2) in Precision Machining, in order to improve the production efficiency and workpiece quality, general more demanding cutting are fast
Degree, at this moment cutting temperature is very high, and dedicated magnesium alloy cutting fluid is unable to reach good cooling effect in the market in the prior art;
(3) in the case where low cutting speed and the small amount of feeding, part long processing time, at this moment finished work surface can change colour even
Oxidation, the strong influence machining accuracy and surface quality of part.Therefore, how a kind of processing request that can satisfy is provided
Cutting fluid is the technical issues of current those skilled in the art need to be solved.
Summary of the invention
The present invention in order to overcome the shortcomings of the prior art, provide a kind of anti-oxidant magnesium alloy water-soluble metalworking liquid and its
Preparation method.
The present invention is achieved by the following technical solutions: a kind of magnesium alloy water-soluble metalworking liquid, and the magnesium alloy is water-soluble
Cutting fluid is made of the raw material of following weight parts: 2~5 parts of pH adjusting agent, 3~8 parts of surfactant, 4~10 parts of antirust agent,
1~2 part of corrosion inhibiter, 1~4 part of hard water resistance stabilizer, 2~5 parts of magnesium alloy protective agent, 2~4 parts of defoaming agent and fungicide 2~4
Part, surplus adds to 100 parts by base oil and deionized water.
As the preferred embodiment of the present invention, magnesium alloy water-soluble metalworking liquid of the present invention by following weight parts raw material group
At: 3~4 parts of pH adjusting agent, 5~7 parts of surfactant, 6~8 parts of antirust agent, 1.2~1.8 parts of corrosion inhibiter, hard water resistance stabilization
2~3 parts of agent, 3~4 parts of magnesium alloy protective agent, 2.5~3.5 parts of defoaming agent and 2.4~3.6 parts of fungicide, surplus by base oil and
Deionized water adds to 100 parts.
As preferred forms of the invention, magnesium alloy water-soluble metalworking liquid of the present invention by following weight parts raw material group
At: 3.5 parts of pH adjusting agent, 5.5 parts of surfactant, 7 parts of antirust agent, 1.5 parts of corrosion inhibiter, 2.5 parts of hard water resistance stabilizer, magnesium
3.5 parts of alloy protecting agent, 3 parts of defoaming agent and 3 parts of fungicide, surplus adds to 100 parts by base oil and deionized water.
PH adjusting agent includes polyhydroxy polyamines class organic base or inorganic base and the fatty ten alcohol polyoxyethylene ether of isomery, and polyhydroxy is more
Amine organic base includes triethanolamine, and inorganic base includes potassium hydroxide.It is able to maintain that the certain pH environment of system and long-term steady
Fixed, isomery ten alcohol polyoxyethylene ether of fat are efficient dispersing agent and wetting agent, play the role of mechanical isolation, are easier with acid
It washes away.
Surfactant includes anionic surfactant and nonionic surfactant, and anionic surfactant includes
Polyoxyethylene alkoxy ether sulfonic acid sodium and natural sodium sulfonate, nonionic surfactant include ethoxylated dodecyl alcohol and dipropyl
Glycol monobutyl ether.Surfactant can effectively connect hydrophilic and oleophilic ingredient therein, so that whole system is not easy to be broken,
Improve the stability of cutting fluid.
Enuatrol the preparation method is as follows: industrial oleic acid is first warming up to 70 DEG C, then slowly in anionic surfactant
The mass ratio of the slow sodium hydrate aqueous solution that mass percent is added and is 50%, industrial oleic acid and sodium hydroxide is 5:2, maintains temperature
Then degree keeps the temperature 1.5h between 70 DEG C~75 DEG C, enuatrol is made.
Antirust agent is YL-1082 water soluble anti-rust agent or RT-9411 without oil type rust preventive, and wherein YL-1082 water solubility is anti-
Agent of becoming rusty is a kind of environment-friendly water-soluble antirust agent without sodium nitrite, is combined by polycarboxylate, complexing agent etc., antirust
Agent has no effect to postorder processing, getting rusty and corrode prevented also from workpiece and lathe.
Corrosion inhibiter includes benzotriazole (T706), Benzotriazole Derivative (L39), alkyl phosphate and alkyl phosphoric acid
Ester derivant (ASI-80/OPS-75E/MDIT/CPNF-3/9218LA), corrosion inhibiter have certain corrosion inhibition, can protect
Magnesium alloy be not corroded with it is non-discolouring.
Hard water resistance stabilizer includes the hard water resistance emulsifier of ether hydroxy acid class, and the hard water resistance emulsifier of ether hydroxy acid class includes ethylene glycol list
Butyl ether, diethylene glycol monobutyl ether and glycerine, hard water resistance stabilizer possess certain hard water resistance effect, can significantly improve this
The stability of magnesium alloy cutting fluid.
Magnesium alloy protective agent includes ether carboxylic acid, the emulsifier containing EO, alkyl Pluronic F-127 ether phosphate and dipropylene glycol
Monobutyl ether, ether carboxylic acid, the emulsifier containing EO, alkyl Pluronic F-127 ether phosphate and Dipropylene glycol mono-n-butyl Ether according to (1.5~
2.5): (3~4): (2~3): the mass ratio of (1.5~2) configures, and magnesium alloy protective agent can play magnesium alloy well
Protecting effect, the also stability of maintenance system to a certain extent.
Defoaming agent includes type siloxane, and the present invention uses polysiloxane defoaming agent, and defoaming agent can be further improved magnesium conjunction
The antifoam performance of golden cutting fluid.
Fungicide be wide spectrum hypotoxicity fungicide, including 2- benzisothiazole-3-ketone, Hexahydrotriazine, BBIT complexing agent,
Di-2-ethylhexylphosphine oxide morpholine and 4- benzisothiazole -4- ketone are sterilized, fungicide can effectively inhibit the growth of bacterium and maintain body
The biological stability of system, prolongs the service life.
Base oil includes the 20# machine oil that mass percent is 70% kerosene and mass percent is 30%.Base oil can make
Free acid content in cutting fluid is lower than 0.2%, so as to effectively prevent cutting fluid to cause to corrode to magnesium alloy parts, and
Mixed base oil has lower viscosity, can reach better cooling effect.
The invention also discloses a kind of preparation method of magnesium alloy water-soluble metalworking liquid, which specifically includes as follows
Step:
(1) pH adjusting agent of required weight, corrosion inhibiter, antirust agent and base oil and deionized water are mixed first
Uniformly, it is heated to 40 DEG C~60 DEG C after solution is transparent, is cooled to room temperature after keeping the temperature 45~65min, solvent is made;
(2) magnesium alloy protective agent, the hard water resistance stabilizer, table that configured required weight is added in solvent are stated then up
Face activating agent, defoaming agent and fungicide simultaneously stir evenly, and product is amber transparent liquid, which is magnesium alloy
Water-soluble metalworking liquid.
The beneficial effects of the present invention are: the cutting fluid in the present invention has lower viscosity, and sky gas and water can be prevented
And it is all it is multi-environment magnesium alloy parts are caused to corrode, can effectively maintain stability, have good inoxidizability.It can be
In actual processing, lubrication, cooling and non-discolouring effect are played, and biology can be maintained for a long time under very high pH value condition
Stability, without having to worry about have a large amount of magnesium soaps precipitation the phenomenon that.Cutting fluid in present invention no hydrogen when for magnesium alloy cutting
Release, it is ensured that the safety of production process carries out and environmental protection.The effective solution of the present invention magnesium alloy material in actual processing
Expect inflammable, temperature is excessively high to lead to problems such as deformation and workpiece surface corrosion black, greatly extend cutting-tool's used life and
Surface roughness is improved well, ensure that the machining accuracy of workpiece.
Specific embodiment
Below in conjunction with specific embodiment, the present invention is described in detail.
Embodiment 1: a kind of magnesium alloy water-soluble metalworking liquid, the magnesium alloy water-soluble metalworking liquid by following weight parts raw material
Composition: 2 parts of pH adjusting agent, 3 parts of surfactant, 4 parts of antirust agent, 1 part of corrosion inhibiter, 1 part of hard water resistance stabilizer, magnesium alloy are protected
2 parts of agent of shield, 2 parts of defoaming agent and 2 parts of fungicide, surplus adds to 100 parts by base oil and deionized water.
PH adjusting agent is one or more of fatty ten alcohol polyoxyethylene ether of triethanolamine, potassium hydroxide or isomery;
Surfactant is polyoxyethylene alkoxy ether sulfonic acid sodium, natural sodium sulfonate, ethoxylated dodecyl alcohol or dipropylene glycol mono butyl
One or more of ether.Antirust agent is YL-1082 water soluble anti-rust agent or RT-9411 without oil type rust preventive;Corrosion inhibiter is benzene
And one or more of triazole, Benzotriazole Derivative, alkyl phosphate or alkyl phosphate derivative.
Hard water resistance stabilizer is one or more of ethylene glycol monobutyl ether, diethylene glycol monobutyl ether or glycerine.Magnesium closes
Golden protective agent is by ether carboxylic acid, the emulsifier containing EO, alkyl Pluronic F-127 ether phosphate and Dipropylene glycol mono-n-butyl Ether according to (1.5
~2.5): (3~4): (2~3): the mass ratio of (1.5~2) configures.Defoaming agent is polysiloxane defoaming agent, and fungicide is
2- benzisothiazole-3-ketone, Hexahydrotriazine, BBIT complexing agent, sterilization di-2-ethylhexylphosphine oxide morpholine or 4- benzisothiazole -4- ketone
One or more of.The 20# machine oil that the kerosene and mass percent that base oil is 70% by mass percent are 30% forms
Mixed base oil.
The invention also discloses a kind of preparation method of magnesium alloy water-soluble metalworking liquid, which specifically includes as follows
Step:
(1) pH adjusting agent of required weight, corrosion inhibiter, antirust agent and base oil and deionized water are mixed first
Uniformly, it is heated to 40 DEG C~60 DEG C after solution is transparent, is cooled to room temperature after keeping the temperature 45~65min, solvent is made;
(2) magnesium alloy protective agent, the hard water resistance stabilizer, table that configured required weight is added in solvent are stated then up
Face activating agent, defoaming agent and fungicide simultaneously stir evenly, and product is amber transparent liquid, which is magnesium alloy
Water-soluble metalworking liquid.
Embodiment 2: magnesium alloy water-soluble metalworking liquid of the present invention is determined that, using matched proportion density, processing is used by machining load
The configuration of Shi Yushui is compared for 1:20, and general control concentration range is 5%~10% to differ.One kind is present embodiments provided about magnesium
The preparation method of alloy cutting fluid auxiliary agent and cutting fluid.The each component of inoxidizability cutting fluid auxiliary agent of the present invention is as shown in table 1:
Table 1: anti-oxidant cutting fluid auxiliary agent
Raw material | It matches (mass parts) |
Ethylene glycol | 4 |
Tall oil acid sodium salt | 4 |
Enuatrol | 3 |
Dinonylnaphthalene sulfonic acid zinc | 2 |
Polyoxyethylene alkoxy ether sulfonic acid sodium | 2 |
Distearyl amine | 2 |
Double ten four carbon alcohols rouge | 4 |
Water | 45 |
In the present invention inoxidizability auxiliary agent the preparation method comprises the following steps: (1) by tall oil acid sodium salt, enuatrol and double ten four carbon alcohols
Rouge mixing, is heated to 30~50 DEG C, obtains mixture A after being stirred to react 20~40min;(2) it is rapidly cooled to after boiling boiling
It 70~80 DEG C, adds distearyl amine and polyoxyethylene alkoxy ether sulfonic acid sodium stirs evenly, obtain mixture B.It (3) will mixing
Object B is added while stirring in mixture A, remaining residual components is added at 40~50 DEG C, after stirring for temperature range control,
20~30min of high-speed stirred under 1400~1600r/min.
Magnesium alloy water-soluble metalworking liquid auxiliary agent in the present invention is made of the raw material of following weight parts: 3~5 parts of ethylene glycol,
4~5 parts of tall oil acid sodium salt, 3~4 parts of enuatrol, 2~3 parts of dinonylnaphthalene sulfonic acid zinc, polyoxyethylene alkoxy ether sulfonic acid sodium 1
~2 parts, 2~3 parts of distearyl amine, 3~4 parts and 40~50 parts of water of double ten four carbon alcohols rouge.
Magnesium alloy water-soluble metalworking liquid of the present invention is made of the raw material of following weight parts: pH adjusting agent 2~3, antirust agent 3
~4 parts, 1~2 part of corrosion inhibiter, 1~2 part of hard water resistance stabilizer, 2~3 parts of defoaming agent and 2~3 parts of fungicide, 3~5 parts of auxiliary agent,
Surplus adds to 100 parts by base oil and deionized water.Each parts by weight of raw materials in embodiment 2 is as shown in table 2:
Table 2: magnesium alloy water-soluble metalworking liquid
Raw material | It matches (mass parts) |
Triethanolamine | 2 |
Polyglycerol fatty acid | 1 |
YL-1082 water soluble anti-rust agent | 4 |
Benzotriazole Derivative (L39) | 1 |
Diethylene glycol monobutyl ether | 1 |
Polysiloxanes | 2 |
2- benzisothiazole-3-ketone | 2 |
Auxiliary agent | 4 |
Base oil and deionized water | Add to 100 |
Magnesium alloy water-soluble metalworking liquid of the present invention the preparation method comprises the following steps: by deionized water, triethanolamine, polyglycerol fatty acid
It is mixed with YL-1082 water soluble anti-rust agent, is heated to 40~50 DEG C, is stirred at 1000~1500r/min, benzo is then added
Triazole derivatives (L39), diethylene glycol monobutyl ether, polysiloxanes and 2- benzisothiazole-3-ketone, are stirring evenly and then adding into
Auxiliary agent, and it is stirred to react 40~60min at 800~900r/min, other residual components are added, continue 15~25min of stirring
?.
Embodiment 3: a kind of magnesium alloy water-soluble metalworking liquid, the magnesium alloy water-soluble metalworking liquid by following weight parts raw material
Composition: 5 parts of pH adjusting agent, 8 parts of surfactant, 10 parts of antirust agent, 2 parts of corrosion inhibiter, 4 parts of hard water resistance stabilizer, magnesium alloy
5 parts of protective agent, 4 parts of defoaming agent and 4 parts of fungicide, surplus adds to 100 parts by base oil and deionized water.
For each embodiment in the clearer description present invention, table 1 is each in magnesium alloy water-soluble metalworking liquid of the present invention
The raw material proportioning of embodiment.
Table 3: the raw material proportioning of each embodiment in magnesium alloy water-soluble metalworking liquid
Finally it should be noted that the above content is merely illustrative of the technical solution of the present invention, rather than the present invention is protected
The limitation of range, the simple modification or equivalent replacement that those skilled in the art carry out technical solution of the present invention,
All without departing from the spirit and scope of technical solution of the present invention.
Claims (10)
1. a kind of magnesium alloy water-soluble metalworking liquid, it is characterised in that: the magnesium alloy water-soluble metalworking liquid is by following weight parts
Raw material composition: 2~5 parts of pH adjusting agent, 3~8 parts of surfactant, 4~10 parts of antirust agent, 1~2 part of corrosion inhibiter, hard water resistance
1~4 part of stabilizer, 2~5 parts of magnesium alloy protective agent, 2~4 parts of defoaming agent and 2~4 parts of fungicide, surplus by base oil and go from
Sub- water adds to 100 parts.
2. magnesium alloy water-soluble metalworking liquid according to claim 1, it is characterised in that: the magnesium alloy water-soluble metalworking liquid
It is made of the raw material of following weight parts: 3~4 parts of pH adjusting agent, 5~7 parts of surfactant, 6~8 parts of antirust agent, corrosion inhibiter
1.2~1.8 parts, 2~3 parts of hard water resistance stabilizer, 3~4 parts of magnesium alloy protective agent, 2.5~3.5 parts of defoaming agent and fungicide 2.4
~3.6 parts, surplus adds to 100 parts by base oil and deionized water.
3. magnesium alloy water-soluble metalworking liquid according to claim 2, it is characterised in that: the magnesium alloy water-soluble metalworking liquid
Be made of the raw material of following weight parts: 3.5 parts of pH adjusting agent, 5.5 parts of surfactant, 7 parts of antirust agent, 1.5 parts of corrosion inhibiter,
2.5 parts of hard water resistance stabilizer, 3.5 parts of magnesium alloy protective agent, 3 parts of defoaming agent and 3 parts of fungicide, surplus is by base oil and deionization
Water adds to 100 parts.
4. magnesium alloy water-soluble metalworking liquid according to claim 1,2 or 3, it is characterised in that: the pH adjusting agent is
One or more of fatty ten alcohol polyoxyethylene ether of triethanolamine, potassium hydroxide or isomery;The surfactant is polyoxy
One or more of vinyl alkoxy ether sulfonic acid sodium, natural sodium sulfonate, ethoxylated dodecyl alcohol or Dipropylene glycol mono-n-butyl Ether.
5. magnesium alloy water-soluble metalworking liquid according to claim 1,2 or 3, it is characterised in that: the antirust agent is YL-
1082 water soluble anti-rust agents or RT-9411 are without oil type rust preventive;The corrosion inhibiter is benzotriazole, benzotriazole is derivative
One or more of object, alkyl phosphate or alkyl phosphate derivative.
6. magnesium alloy water-soluble metalworking liquid according to claim 1,2 or 3, it is characterised in that: the hard water resistance stabilizer
For one or more of ethylene glycol monobutyl ether, diethylene glycol monobutyl ether or glycerine.
7. magnesium alloy water-soluble metalworking liquid according to claim 6, it is characterised in that: the magnesium alloy protective agent is by ether carboxylic
Acid, the emulsifier containing EO, alkyl Pluronic F-127 ether phosphate and Dipropylene glycol mono-n-butyl Ether are according to (1.5~2.5): (3~4):
(2~3): the mass ratio of (1.5~2) configures.
8. magnesium alloy water-soluble metalworking liquid according to claim 1,2 or 3, it is characterised in that: the defoaming agent is poly- silicon
Oxygen alkane defoaming agent, the fungicide are 2- benzisothiazole-3-ketone, Hexahydrotriazine, BBIT complexing agent, sterilization di-2-ethylhexylphosphine oxide
One or more of quinoline or 4- benzisothiazole -4- ketone.
9. magnesium alloy water-soluble metalworking liquid according to claim 1,2 or 3, it is characterised in that: the base oil is by quality
The 20# machine oil that the kerosene and mass percent that percentage is 70% are 30% forms mixed base oil.
10. a kind of preparation method of magnesium alloy water-soluble metalworking liquid according to claim 1,2 or 3, it is characterised in that: institute
Preparation method is stated to specifically comprise the following steps:
(1) pH adjusting agent of required weight, corrosion inhibiter, antirust agent and base oil and deionized water are mixed first equal
It is even, it is heated to 40 DEG C~60 DEG C after solution is transparent, is cooled to room temperature after keeping the temperature 45~65min, solvent is made;
(2) it is living that the magnesium alloy protective agent, hard water resistance stabilizer, surface that configured required weight is added in solvent are stated then up
Property agent, defoaming agent and fungicide and stir evenly, product is amber transparent liquid, which is that magnesium alloy is water-soluble
Property cutting fluid.