CN109023683A - Transparent elastic force fish silk shoes cloth preparation method and its product and application - Google Patents
Transparent elastic force fish silk shoes cloth preparation method and its product and application Download PDFInfo
- Publication number
- CN109023683A CN109023683A CN201811002906.1A CN201811002906A CN109023683A CN 109023683 A CN109023683 A CN 109023683A CN 201811002906 A CN201811002906 A CN 201811002906A CN 109023683 A CN109023683 A CN 109023683A
- Authority
- CN
- China
- Prior art keywords
- elastic force
- force fish
- silk
- cloth
- sheet stock
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of transparent elastic force fish silk shoes cloth preparation method and its product and application, preparation method includes the following steps: (1) preparing material；(2) it is sliced；(3) it reels off raw silk from cocoons；(4) clot；(5) woven fabric；(6) it is formed；Transparent elastic force fish screen cloth provided by the invention using reasonable set terylene, spandex and TPU quality proportioning and manufactured elastic force fish silk weave, relative to traditional elastic force fish silk with more preferable elasticity, pull resistance and resistance to tortuosity, flexibility is good, and air permeability effect is good, and has transparent effect.Transparent elastic force fish screen cloth provided by the invention can be applied to shoes cloth, it is more elastic relative to traditional textile vamp, tensile property is strong, and flexibility and resistance to tortuosity are good, long service life, good permeability simultaneously, the comfort of shoes can be effectively promoted, and there is transparent effect, novel appearance, contemporary people have been able to satisfy for beauty and personalized demand, have been conducive to wide popularization and application.
Description
Technical field
The invention belongs to shoes Strand Feeding Technique fields, and in particular to a kind of transparent elastic force fish silk shoes cloth preparation method and its system
Product and application.
Background technique
With the development of society, living standard is constantly progressive, requirement of the people for dress is also higher and higher, and shoes are
Necessity in people's daily life, being through on foot prevents foot from coming to harm, and requirement of the people for shoes is more and more, shoes
Comfort level, style and color are the problem of paying much attention to when consumer buys shoes.
Currently, vamp is mostly to be made of textile material.Or TPU film or other thermoplastic materials are placed into
It in woven vamp, then earnestly forms through high frequency or hot-forming, shape is mainly the TPU or other thermoplastic films by surface
Class material is made by post-processing, fits on vamp made from textile material.This structure will not be it is permanent firm, not
In curved wearing process of breaking and delamination is easy to happen under different amblent air temperatures or is fallen off, and air permeability effect is not to manage very much
Think, while also not having elasticity, influence snugness of fit, in addition, also not having transparent effect, appearance is common, it is difficult to meet
Contemporary people are for beauty and personalized demands.
Summary of the invention
In view of the above-mentioned deficiencies, one of the object of the invention is, it is simple to provide a kind of technique, it is easy to accomplish, it can quickly make
It is good to make air permeability effect, comfort is high, and the transparent elastic force fish silk shoes of the silk shoes cloth products of the transparent elastic force fish with transparent effect
Cloth preparation method.
The second purpose of the present invention is provide a kind of transparent elastic force fish screen cloth, the ventilative effect of the transparent elastic force fish screen cloth
Fruit is good, has elasticity, and have transparent effect.
The three of the object of the invention are, provide a kind of transparent elastic force fish screen cloth and are applied to shoes cloth.Effectively promote shoes
The comfort of son, and there is transparent effect, novel appearance, to meet contemporary people for beauty and personalized demand.
To achieve the above object, the technical solution provided by the present invention is: a kind of transparent elastic force fish silk shoes cloth preparation method,
Itself the following steps are included:
(1) preparing material: preparation terylene block, spandex block and TPU block；
(2) it is sliced: terylene block, spandex block and TPU block is sliced, terylene sheet stock, spandex sheet stock and TPU piece is made
Material；
(3) it reels off raw silk from cocoons: extruder is added in terylene sheet stock, spandex sheet stock and TPU sheet stock, melt squeezing out by extruder and take out
Elastic force fish silk is made in silk；
(4) clot: by elastic force fish silk on drum, elastic force fish silk reel is obtained；
(5) it woven fabric: by elastic force fish silk reel on knitting machine, is woven by knitting machine, embryo cloth is made；
(6) it is formed: heat-shaping is carried out to embryo cloth, transparent elastic force fish silk shoes cloth products are made.
As an improvement of the present invention, the quality of the terylene sheet stock in the step (3), spandex sheet stock and TPU sheet stock
Percentage are as follows: terylene sheet stock 5~15%, spandex sheet stock 5~15%, TPU sheet stock 70~90%.
As an improvement of the present invention, the heating of the extruder is divided into six areas for being sequentially connected and connecing, wherein first
The temperature in area is set as 195~205 degree, and the temperature in the secondth area is set as 205~215 degree, and the temperature in third area is set as 210~
220 degree, the temperature in the 4th area is set as 220~230 degree, and the temperature in the 5th area is set as 225~235 degree, the temperature in die head area
It is set as 205~215 degree.
As an improvement of the present invention, the speed that the extrusion of the extruder in the step (3) is reeled off raw silk from cocoons is 5~15 ms/min.
As an improvement of the present invention, the fiber number of the elastic force fish silk is 75~150D.
As an improvement of the present invention, the knitting machine is tricot machine or weft machine, the volume cloth speed of tricot machine therein
Degree is set as 200~400 yards/day, and the volume cloth speed of weft machine is set as 400~500 yards/day.
As an improvement of the present invention, the step (6) specifically includes the following steps:
(6.1) it preheats: embryo cloth being preheated, the temperature of preheating is set as 38~42 degree；
(6.2) it is sent into: the embryo cloth after preheating is sent into rotary infrared baking machine, and in the shape of a spiral successively wound on rotary infrared
In feeding screw shaft in roasting machine, the speed feeding forward which is 100~120 revs/min with revolving speed, heating
Temperature is set as 38~42 degree；
(6.3) it heats: keeping the revolving speed of rotary infrared baking machine constant, the heating temperature of rotary infrared baking machine is slowly turned up extremely
100 degree；
(6.4) it keeps the temperature: when temperature rises to 100 degree, heat-insulation pressure keeping 15~25 minutes, the pressure adjustment in rotary infrared baking machine
Revolving speed for 110~130 pas, rotary infrared baking machine is adjusted to 50~70 revs/min.
As an improvement of the present invention, the heating temperature adjustment process time in the step (6.2) is 20~40 points
Clock.
A kind of transparent elastic force fish screen cloth is woven by elastic force fish silk by weft machine or tricot machine, the elastic force
The material quality percentage of fish silk are as follows: terylene 5~15%, spandex 5~15%, TPU70~90%.
As an improvement of the present invention, the fiber number of the elastic force fish silk is 75~150D.
A kind of above-mentioned transparent elastic force fish screen cloth is applied to shoes cloth.
The invention has the benefit that the technique that the present invention provides transparent elastic force fish silk shoes cloth preparation method is simple, it is easy to
Realize, can quick Fabrication to go out air permeability effect good, comfort is high, and the silk shoes cloth products of the transparent elastic force fish with transparent effect.This
Invention provide transparent elastic force fish screen cloth using reasonable set terylene, spandex and TPU quality proportioning and manufactured elastic force fish
Silk weaves, and relative to traditional elastic force fish silk with more preferable elasticity, pull resistance and resistance to tortuosity, flexibility is good, thoroughly
Gas effect is good, and has transparent effect.Transparent elastic force fish screen cloth provided by the invention can be applied to shoes cloth, relative to
Traditional textile vamp is more elastic, and tensile property is strong, and flexibility and resistance to tortuosity are good, long service life, while good permeability, energy
The comfort of shoes is effectively promoted, and there is transparent effect, is not needed to be dyed not only, traditional dyeing process is gone in saving, shortens life
The period is produced, cost, improving production efficiency, and novel appearance are reduced, has been able to satisfy contemporary people for beauty and personalized need
It asks, is conducive to wide popularization and application.
With reference to the accompanying drawing with embodiment, the invention will be further described.
Detailed description of the invention
Fig. 1 is fabrication processing figure of the invention.
Specific embodiment
Embodiment 1: referring to Fig. 1, a kind of transparent elastic force fish silk shoes cloth preparation method provided in this embodiment comprising following
Step:
(1) preparing material: preparation terylene block, spandex block and TPU block；
(2) it is sliced: terylene block, spandex block and TPU block is sliced, terylene sheet stock, spandex sheet stock and TPU piece is made
Material；
(3) it reels off raw silk from cocoons: extruder is added in terylene sheet stock, spandex sheet stock and TPU sheet stock, when in the hopper for putting into extruder, institute
The mass percent of the terylene sheet stock, spandex sheet stock and TPU sheet stock stated are as follows: terylene sheet stock 5%, spandex sheet stock 5, TPU sheet stock 90%.
Melt squeezing out by extruder and reel off raw silk from cocoons, the speed that the extrusion of the extruder is reeled off raw silk from cocoons is preferably 5~15 ms/min, specifically
It can accordingly be selected according to the fiber number reeled off raw silk from cocoons.The excellent fiber number of the elastic force fish silk is 75~150D, and fiber number is smaller, then squeezes out pumping
The speed of silk is accordingly slack-off, and such as when the fiber number of elastic force fish silk is 75D, then squeezing out the speed reeled off raw silk from cocoons is 5 ms/min.By reeling off raw silk from cocoons
Afterwards, elastic force fish silk is made；The heating of the extruder is divided into six areas for being sequentially connected and connecing, wherein the temperature in the firstth area is set as
195~205 degree, preferably 200 degree；The temperature in the secondth area is set as 205~215 degree, preferably 210 degree；The temperature in third area
It is set as 210~220 degree, preferably 215 degree；The temperature in the 4th area is set as 220~230 degree, preferably 225 degree；5th area
Temperature be set as 225~235 degree, preferably 230 degree；The temperature in die head area is set as 210 degree, preferably 200 degree；
(4) clot: by elastic force fish silk average rate on drum, elastic force fish silk reel is obtained；
(5) woven fabric: by elastic force fish silk reel on the wire charging mechanism of knitting machine, line sending is carried out by wire charging mechanism, passes through knitting
The woven fabric mechanism of machine is woven, and embryo cloth is made；
(6) it is formed: heat-shaping is carried out to embryo cloth, transparent elastic force fish silk shoes cloth products are made.
In the present embodiment, the knitting machine be tricot machine, the volume cloth speed of tricot machine be preferably set to 200~400 yards/
It.Daily with 24 hours continuous productions.Specifically it can accordingly be selected according to the fiber number of elastic force fish silk.The fiber number of elastic force fish silk
Smaller, the speed for compiling cloth speed is accordingly slack-off, and the fiber number of elastic force fish silk is bigger, and the speed for compiling cloth speed then accordingly becomes faster.It is other
In embodiment, weft machine can be selected according to the demand of client, the volume cloth speed of weft machine be preferably set to 400~500 yards/
It.Equally, the volume cloth speed of weft machine is also accordingly to be selected according to the fiber number of elastic force fish silk.The fiber number of elastic force fish silk is smaller,
The speed for compiling cloth speed is accordingly slack-off, and the fiber number of elastic force fish silk is bigger, and the speed for compiling cloth speed then accordingly becomes faster.
The step (6) is specifically includes the following steps: (6.1) preheat: preheating to embryo cloth, the temperature of preheating is set as
38 degree；(6.2) it is sent into: the embryo cloth after preheating is sent into rotary infrared baking machine, the rotary infrared baking machine includes cabinet, should
Horizontal in cabinet to be equipped with feeding screw shaft, the inner wall of cabinet is equipped with the infrared heating pipe towards the feeding screw shaft；
The feeding screw shaft is by being arranged driving device driving rotation outside the enclosure；Embryo cloth after preheating is successively wound in the shape of a spiral
In the feeding screw shaft in rotary infrared baking machine, the feeding screw shaft is with revolving speed for 100~120 revs/min of speed
The revolving speed of feeding forward, feeding screw shaft is controlled by driving device.(6.3) it heats: keeping the revolving speed of rotary infrared baking machine
It is constant, the heating temperature of rotary infrared baking machine is slowly turned up to 100 degree, entire heating temperature adjustment process time is 40 points
Clock；(6.3) keep the temperature: when temperature rises to 100 degree, heat-insulation pressure keeping 15 minutes, the pressure in rotary infrared baking machine was adjusted to 110
The revolving speed of~130 pas, rotary infrared baking machine is adjusted to 50~70 revs/min.
A kind of transparent elastic force fish screen cloth is woven by elastic force fish silk by weft machine or tricot machine, the elastic force
The material quality percentage of fish silk are as follows: terylene 5%, spandex 5%, TPU 90%.
A kind of above-mentioned transparent elastic force fish screen cloth is applied to shoes cloth.
Embodiment 2: a kind of transparent elastic force fish silk shoes cloth preparation method provided in this embodiment comprising following steps:
(1) preparing material: preparation terylene block, spandex block and TPU block；(2) be sliced: to terylene block, spandex block and
TPU block is sliced, and terylene sheet stock, spandex sheet stock and TPU sheet stock is made；(3) reel off raw silk from cocoons: by terylene sheet stock, spandex sheet stock and
Extruder is added in TPU sheet stock, when in the hopper for putting into extruder, the matter of the terylene sheet stock, spandex sheet stock and TPU sheet stock
Measure percentage are as follows: terylene sheet stock 10%, spandex sheet stock 10, TPU sheet stock 80%.After reeling off raw silk from cocoons, elastic force fish silk is made；(4) clot:
By elastic force fish silk average rate on drum, elastic force fish silk reel is obtained；(5) elastic force fish silk reel woven fabric: is mounted in knitting machine
Wire charging mechanism on, line sending is carried out by wire charging mechanism, is woven by the woven fabric mechanism of knitting machine, be made embryo cloth；(6) fixed
Type: (6.1) preheating: embryo cloth is preheated, the temperature of preheating is set as 40 degree；(6.2) it is sent into: the embryo cloth after preheating is sent into
Rotary infrared baking machine, and in the shape of a spiral successively in the feeding screw shaft in rotary infrared baking machine, the feeding spiral shell
The speed feeding forward that rotary shaft is 100~120 revs/min with revolving speed, heating temperature are set as 40 degree；(6.3) it heats: keeping rotation
The revolving speed of rotatable infrared baking machine is constant, the heating temperature of rotary infrared baking machine is slowly turned up to 100 degree, entire heating temperature tune
Whole process time is 20 minutes；(6.3) it keeps the temperature: when temperature rises to 100 degree, heat-insulation pressure keeping 20 minutes, rotary infrared baking machine
Interior pressure is adjusted to 110~130 pas, and the revolving speed of rotary infrared baking machine is adjusted to 65 revs/min.After heat-shaping, it is made
Transparent elastic force fish silk shoes cloth products.
A kind of transparent elastic force fish screen cloth is woven by elastic force fish silk by weft machine or tricot machine, the elastic force
The material quality percentage of fish silk are as follows: terylene 10%, spandex 10%, TPU 80%.
A kind of above-mentioned transparent elastic force fish screen cloth is applied to shoes cloth.
Embodiment 3: a kind of transparent elastic force fish silk shoes cloth preparation method provided in this embodiment comprising following steps:
(1) preparing material: preparation terylene block, spandex block and TPU block；(2) be sliced: to terylene block, spandex block and
TPU block is sliced, and terylene sheet stock, spandex sheet stock and TPU sheet stock is made；(3) reel off raw silk from cocoons: by terylene sheet stock, spandex sheet stock and
Extruder is added in TPU sheet stock, when in the hopper for putting into extruder, the matter of the terylene sheet stock, spandex sheet stock and TPU sheet stock
Measure percentage are as follows: terylene sheet stock 15%, spandex sheet stock 15, TPU sheet stock 70%.After reeling off raw silk from cocoons, elastic force fish silk is made；(4) clot:
By elastic force fish silk average rate on drum, elastic force fish silk reel is obtained；(5) elastic force fish silk reel woven fabric: is mounted in knitting machine
Wire charging mechanism on, line sending is carried out by wire charging mechanism, is woven by the woven fabric mechanism of knitting machine, be made embryo cloth；(6) fixed
Type: (6.1) preheating: embryo cloth is preheated, the temperature of preheating is set as 42 degree；(6.2) it is sent into: the embryo cloth after preheating is sent into
Rotary infrared baking machine, and in the shape of a spiral successively in the feeding screw shaft in rotary infrared baking machine, the feeding spiral shell
The speed feeding forward that rotary shaft is 110 revs/min with revolving speed, heating temperature are set as 42 degree；(6.3) it heats: keeping rotary
The revolving speed of infrared baking machine is constant, the heating temperature of rotary infrared baking machine is slowly turned up to 100 degree, entire heating temperature adjusted
The journey time is 25 minutes；(6.3) it keeps the temperature: when temperature rises to 100 degree, heat-insulation pressure keeping 25 minutes, in rotary infrared baking machine
Pressure is adjusted to 120 pas, and the revolving speed of rotary infrared baking machine is adjusted to 70 revs/min.After carrying out heat-shaping to embryo cloth, it is made
Transparent elastic force fish silk shoes cloth products.
A kind of transparent elastic force fish screen cloth is woven by elastic force fish silk by weft machine or tricot machine, the elastic force
The material quality percentage of fish silk are as follows: terylene 15%, spandex 15%, TPU70%.
A kind of above-mentioned transparent elastic force fish screen cloth is applied to shoes cloth.
Embodiment 4: a kind of transparent elastic force fish silk shoes cloth preparation method provided in this embodiment comprising following steps:
(1) preparing material: preparation terylene block, spandex block and TPU block；(2) be sliced: to terylene block, spandex block and
TPU block is sliced, and terylene sheet stock, spandex sheet stock and TPU sheet stock is made；(3) reel off raw silk from cocoons: by terylene sheet stock, spandex sheet stock and
Extruder is added in TPU sheet stock, when in the hopper for putting into extruder, the matter of the terylene sheet stock, spandex sheet stock and TPU sheet stock
Measure percentage are as follows: terylene sheet stock 8%, spandex sheet stock 9%, TPU sheet stock 83%.After reeling off raw silk from cocoons, elastic force fish silk is made；(4) clot:
By elastic force fish silk average rate on drum, elastic force fish silk reel is obtained；(5) elastic force fish silk reel woven fabric: is mounted in knitting machine
Wire charging mechanism on, line sending is carried out by wire charging mechanism, is woven by the woven fabric mechanism of knitting machine, be made embryo cloth；(6) fixed
Type: (6.1) preheating: embryo cloth is preheated, the temperature of preheating is set as 41 degree；(6.2) it is sent into: the embryo cloth after preheating is sent into
Rotary infrared baking machine, and in the shape of a spiral successively in the feeding screw shaft in rotary infrared baking machine, the feeding spiral shell
The speed feeding forward that rotary shaft is 120 revs/min with revolving speed, heating temperature are set as 41 degree；(6.3) it heats: keeping rotary
The revolving speed of infrared baking machine is constant, the heating temperature of rotary infrared baking machine is slowly turned up to 100 degree, entire heating temperature adjusted
The journey time is 22 minutes；(6.3) it keeps the temperature: when temperature rises to 100 degree, heat-insulation pressure keeping 20 minutes, in rotary infrared baking machine
Pressure is adjusted to 115 pas, and the revolving speed of rotary infrared baking machine is adjusted to 68 revs/min.After carrying out heat-shaping to embryo cloth, it is made
Transparent elastic force fish silk shoes cloth products.
A kind of transparent elastic force fish screen cloth is woven by elastic force fish silk by weft machine or tricot machine, the elastic force
The material quality percentage of fish silk are as follows: terylene 8%, spandex 9%, TPU83%.
A kind of above-mentioned transparent elastic force fish screen cloth is applied to shoes cloth.
Embodiment 5: a kind of transparent elastic force fish silk shoes cloth preparation method provided in this embodiment comprising following steps:
(1) preparing material: preparation terylene block, spandex block and TPU block；(2) be sliced: to terylene block, spandex block and
TPU block is sliced, and terylene sheet stock, spandex sheet stock and TPU sheet stock is made；(3) reel off raw silk from cocoons: by terylene sheet stock, spandex sheet stock and
Extruder is added in TPU sheet stock, when in the hopper for putting into extruder, the matter of the terylene sheet stock, spandex sheet stock and TPU sheet stock
Measure percentage are as follows: terylene sheet stock 9%, spandex sheet stock 10%, TPU sheet stock 81%.After reeling off raw silk from cocoons, elastic force fish silk is made；(4) clot:
By elastic force fish silk average rate on drum, elastic force fish silk reel is obtained；(5) elastic force fish silk reel woven fabric: is mounted in knitting machine
Wire charging mechanism on, line sending is carried out by wire charging mechanism, is woven by the woven fabric mechanism of knitting machine, be made embryo cloth；(6) fixed
Type: (6.1) preheating: embryo cloth is preheated, the temperature of preheating is set as 39 degree；(6.2) it is sent into: the embryo cloth after preheating is sent into
Rotary infrared baking machine, and in the shape of a spiral successively in the feeding screw shaft in rotary infrared baking machine, the feeding spiral shell
The speed feeding forward that rotary shaft is 105 revs/min with revolving speed, heating temperature are set as 39 degree；(6.3) it heats: keeping rotary
The revolving speed of infrared baking machine is constant, the heating temperature of rotary infrared baking machine is slowly turned up to 100 degree, entire heating temperature adjusted
The journey time is 19 minutes；(6.3) it keeps the temperature: when temperature rises to 100 degree, heat-insulation pressure keeping 18 minutes, in rotary infrared baking machine
Pressure is adjusted to 128 pas, and the revolving speed of rotary infrared baking machine is adjusted to 55 revs/min.After carrying out heat-shaping to embryo cloth, it is made
Transparent elastic force fish silk shoes cloth products.
A kind of transparent elastic force fish screen cloth is woven by elastic force fish silk by weft machine or tricot machine, the elastic force
The material quality percentage of fish silk are as follows: terylene 9%, spandex 10%, TPU81%.
A kind of above-mentioned transparent elastic force fish screen cloth is applied to shoes cloth.
Above-described embodiment is only the preferable embodiment of the present invention, and the present invention cannot enumerate out whole embodiment party
Formula, all technical solutions using one of above-described embodiment, or the equivalent variations done according to above-described embodiment are protected in the present invention
It protects in range.
The technique that the present invention provides transparent elastic force fish silk shoes cloth preparation method is simple, it is easy to accomplish, energy quick Fabrication is saturating out
Gas effect is good, and comfort is high, and the silk shoes cloth products of the transparent elastic force fish with transparent effect.
Transparent elastic force fish screen cloth provided by the invention is woven using elastic force fish silk, and reasonable set terylene, ammonia
The quality proportioning of synthetic fibre and TPU and manufactured elastic force fish silk, the material quality percentage of elastic force fish silk are as follows: terylene 5~15%, ammonia
Synthetic fibre 5~15%, TPU70~90%.It is soft relative to traditional elastic force fish silk with more preferable elasticity, pull resistance and resistance to tortuosity
Good toughness, air permeability effect is good, and has transparent effect.
A kind of above-mentioned transparent elastic force fish screen cloth is applied to shoes cloth.Transparent elastic force fish screen cloth provided by the invention
It can be applied to shoes cloth, more elastic relative to traditional textile vamp, tensile property is strong, and flexibility and resistance to tortuosity are good,
Long service life, while good permeability can effectively promote the comfort of shoes, and have transparent effect, not need to be dyed not only,
Traditional dyeing process is gone in saving, is shortened the production cycle, is reduced cost, improving production efficiency, and novel appearance, be able to satisfy and worked as
For people for beauty and personalized demand.When if necessary to color, only Masterbatch need to be added in the step (3)；
I.e. simultaneously by terylene sheet stock, spandex sheet stock, TPU sheet stock and Masterbatch investment extruder hopper, terylene sheet stock, spandex sheet stock and
The mixture of the quality sum of TPU sheet stock and the mass percent of Masterbatch are as follows: mixture 92~98%, Masterbatch 2~8%.Behaviour
Make simply, conveniently, to be more able to satisfy different use demands.
According to the disclosure and teachings of the above specification, those skilled in the art in the invention can also be to above-mentioned embodiment party
Formula is changed and is modified.Therefore, the invention is not limited to the specific embodiments disclosed and described above, to of the invention
Some modifications and changes should also be as falling into the scope of the claims of the present invention.In addition, although being used in this specification
Some specific terms, these terms are merely for convenience of description, does not limit the present invention in any way.Such as the present invention
Described in above-described embodiment, using the silk of other elastic force fish obtained from same or similar method and component, shoes cloth and its production
Method all falls in the scope of protection of the present invention.
Claims (10)
1. a kind of transparent elastic force fish silk shoes cloth preparation method, which is characterized in that itself the following steps are included:
(1) preparing material: preparation terylene block, spandex block and TPU block；
(2) it is sliced: terylene block, spandex block and TPU block is sliced, terylene sheet stock, spandex sheet stock and TPU piece is made
Material；
(3) it reels off raw silk from cocoons: extruder is added in terylene sheet stock, spandex sheet stock and TPU sheet stock, melt squeezing out by extruder and take out
Elastic force fish silk is made in silk；The wherein mass percent of terylene sheet stock, spandex sheet stock and TPU sheet stock are as follows: terylene sheet stock 5~15%,
Spandex sheet stock 5~15%, TPU sheet stock 70~90%；
(4) clot: by elastic force fish silk on drum, elastic force fish silk reel is obtained；
(5) it woven fabric: by elastic force fish silk reel on knitting machine, is woven by knitting machine, embryo cloth is made；
(6) it is formed: heat-shaping is carried out to embryo cloth, transparent elastic force fish silk shoes cloth products are made.
2. transparent elastic force fish silk shoes cloth preparation method according to claim 1, which is characterized in that the heating of the extruder
It is divided into six areas for being sequentially connected and connecing, wherein the temperature in the firstth area is set as 195~205 degree, the temperature in the secondth area is set as 205
~215 degree, the temperature in third area is set as 210~220 degree, and the temperature in the 4th area is set as 220~230 degree, the temperature in the 5th area
Degree is set as 225~235 degree, and the temperature in die head area is set as 205~215 degree.
3. transparent elastic force fish silk shoes cloth preparation method according to claim 1, which is characterized in that in the step (3)
The speed that the extrusion of extruder is reeled off raw silk from cocoons is 5~15 ms/min.
4. transparent elastic force fish silk shoes cloth preparation method according to claim 1 or 3, which is characterized in that the elastic force fish silk
Fiber number be 75~150D.
5. transparent elastic force fish silk shoes cloth preparation method according to claim 1, which is characterized in that the knitting machine is warp knit
Machine or weft machine, the volume cloth speed of tricot machine therein are set as 200~400 yards/day, and the volume cloth speed of weft machine is set as
400~500 yards/day.
6. transparent elastic force fish silk shoes cloth preparation method according to claim 1, which is characterized in that the step (6) is specific
The following steps are included:
(6.1) it preheats: embryo cloth being preheated, the temperature of preheating is set as 38~42 degree；
(6.2) it is sent into: the embryo cloth after preheating is sent into rotary infrared baking machine, and in the shape of a spiral successively wound on rotary infrared
In feeding screw shaft in roasting machine, the speed feeding forward which is 100~120 revs/min with revolving speed, heating
Temperature is set as 38~42 degree；
(6.3) it heats: keeping the revolving speed of rotary infrared baking machine constant, the heating temperature of rotary infrared baking machine is slowly turned up extremely
100 degree；
(6.4) it keeps the temperature: when temperature rises to 100 degree, heat-insulation pressure keeping 15~25 minutes, the pressure adjustment in rotary infrared baking machine
Revolving speed for 110~130 pas, rotary infrared baking machine is adjusted to 50~70 revs/min.
7. transparent elastic force fish silk shoes cloth preparation method according to claim 6, which is characterized in that in the step (6.3)
Heating temperature adjustment process time be 20~40 minutes.
8. a kind of transparent elastic force fish screen cloth, which is characterized in that it is woven by elastic force fish silk by weft machine or tricot machine,
The material quality percentage of the elastic force fish silk are as follows: terylene 5~15%, spandex 5~15%, TPU 70~90%.
9. transparent elastic force fish screen cloth according to claim 8, which is characterized in that the fiber number of elastic force fish silk is 75~
150D。
10. transparent elastic force fish screen cloth described in a kind of claim 8 or 9 is applied to shoes cloth.