CN109020202A - Spill golden glaze and preparation method thereof - Google Patents
Spill golden glaze and preparation method thereof Download PDFInfo
- Publication number
- CN109020202A CN109020202A CN201811067988.8A CN201811067988A CN109020202A CN 109020202 A CN109020202 A CN 109020202A CN 201811067988 A CN201811067988 A CN 201811067988A CN 109020202 A CN109020202 A CN 109020202A
- Authority
- CN
- China
- Prior art keywords
- glaze
- parts
- component
- golden
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses one kind to spill golden glaze and preparation method thereof, and the component and each component mass parts that glaze used in it contains are as follows: 10-15 parts of potassium feldspar；It is 10-15 parts quartzy；8-10 parts of barium carbonate；60 parts -80 parts of glass powder；20-30 parts of iron oxide；Rotten sodium powder 0.5-2 parts.Glaze paint golden light four of the invention is penetrated, and is illuminated to a kind of flammule of people, just like the feeling in fairyland.
Description
Technical field
The present invention relates to one kind to spill golden glaze and preparation method thereof.
Background technique
Currently, the moulding of porcelain billet is the basis of quality product in porcelain industry, the allotment of glaze keeps porcelain more gorgeous
It is colorful.The porcelain billet of same moulding often because of the difference of glaze paint, and generates different influences to the vision of consumer, that golden light
Four penetrate, the glaze paint that flammule illuminates porcelain can be made a kind of to people just like fairyland feeling, this be also current porcelain industry it is a kind of when
Still.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies of existing technologies, one kind is provided and spills golden glaze, its glaze paint
Golden light four is penetrated, and is illuminated to a kind of flammule of people, just like the feeling in fairyland.
In order to solve the above technical problems, glaze used in it contains the technical scheme is that one kind spills golden glaze
Component and each component mass parts it is as follows:
10-15 parts of potassium feldspar；
It is 10-15 parts quartzy；
8-10 parts of barium carbonate；
60 parts -80 parts of glass powder；
20-30 parts of iron oxide；
Rotten sodium powder 0.5-2 parts.
The present invention also provides a kind of preparation method for spilling golden glaze, the step of method in contain:
S1: it stocks up according to each component and each component mass parts；
S2: according to material: ball: mass ratio=1:1:1.8 of water, wet ball grinding 14~18 hours, the glaze after ball milling crossed 325
After mesh, it is stand-by to be modulated into the glaze slip that specific gravity is 1.4~1.6；
S3: taking clean green body, soaked directly on green body using glaze slip glaze or bubble glaze or leaching glaze, then 1180 DEG C-
It is fired under 1250 DEG C of temperature environment.
After above-mentioned technical proposal, of the invention spills golden glaze, and glaze paint golden light four is penetrated, and illuminates to a kind of flammule of people,
Just like the feeling in fairyland.
Specific embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, to the present invention make into
One step detailed description.
Embodiment one
One kind spilling golden glaze, and the component and each component mass parts that glaze used in it contains are as follows:
10 parts of potassium feldspar；
10 parts of quartz；
8 parts of barium carbonate；
60 parts of glass powder；
20 parts of iron oxide；
0.5 part of rotten sodium powder.
Contain in the step of this spills the preparation method of golden glaze, method:
S1: it stocks up according to each component and each component mass parts；
S2: according to material: ball: mass ratio=1:1:1.8 of water, wet ball grinding 14 hours, the glaze after ball milling crossed 325 meshes
Afterwards, it is stand-by to be modulated into the glaze slip that specific gravity is 1.4~1.6；
S3: taking clean green body, soaked directly on green body using glaze slip glaze or bubble glaze or leaching glaze, then 1180 DEG C-
It is fired under 1250 DEG C of temperature environment.
Embodiment two
One kind spilling golden glaze, and the component and each component mass parts that glaze used in it contains are as follows:
15 parts of potassium feldspar；
15 parts of quartz；
10 parts of barium carbonate；
80 parts of glass powder；
30 parts of iron oxide；
2 parts of rotten sodium powder.
Contain in the step of this spills the preparation method of golden glaze, method:
S1: it stocks up according to each component and each component mass parts；
S2: according to material: ball: mass ratio=1:1:1.8 of water, wet ball grinding 18 hours, the glaze after ball milling crossed 325 meshes
Afterwards, it is stand-by to be modulated into the glaze slip that specific gravity is 1.4~1.6；
S3: taking clean green body, soaked directly on green body using glaze slip glaze or bubble glaze or leaching glaze, then 1180 DEG C-
It is fired under 1250 DEG C of temperature environment.
Embodiment three
One kind spilling golden glaze, and the component and each component mass parts that glaze used in it contains are as follows:
12 parts of potassium feldspar；
12 parts of quartz；
9 parts of barium carbonate；
70 parts of glass powder；
25 parts of iron oxide；
1 part of rotten sodium powder.
Contain in the step of this spills the preparation method of golden glaze, method:
S1: it stocks up according to each component and each component mass parts；
S2: according to material: ball: mass ratio=1:1:1.8 of water, wet ball grinding 16 hours, the glaze after ball milling crossed 325 meshes
Afterwards, it is stand-by to be modulated into the glaze slip that specific gravity is 1.4~1.6；
S3: taking clean green body, soaked directly on green body using glaze slip glaze or bubble glaze or leaching glaze, then 1180 DEG C-
It is fired under 1250 DEG C of temperature environment.
What three above embodiment was prepared spills golden glaze, by that can give people one it has been observed that its glaze paint golden light four is penetrated
Kind flammule illuminates, just like the feeling in fairyland, meets design requirement.
Particular embodiments described above has carried out further in detail the purpose of the present invention, technical scheme and beneficial effects
It describes in detail bright, it should be understood that the above is only a specific embodiment of the present invention, is not intended to restrict the invention, it is all
Within the spirit and principles in the present invention, any modification, equivalent substitution, improvement and etc. done should be included in guarantor of the invention
Within the scope of shield.
Claims (2)
1. one kind spills golden glaze, it is characterised in that the component and each component mass parts that glaze used in it contains are as follows:
10-15 parts of potassium feldspar；
It is 10-15 parts quartzy；
8-10 parts of barium carbonate；
60 parts -80 parts of glass powder；
20-30 parts of iron oxide；
Rotten sodium powder 0.5-2 parts.
2. one kind spills the preparation method of golden glaze as described in claim 1, it is characterised in that contain in the step of method:
S1: it stocks up according to each component and each component mass parts；
S2: according to material: ball: mass ratio=1:1:1.8 of water, wet ball grinding 14~18 hours, the glaze after ball milling crossed 325 meshes
Afterwards, it is stand-by to be modulated into the glaze slip that specific gravity is 1.4~1.6；
S3: taking clean green body, glaze or bubble glaze or leaching glaze is soaked directly on green body using glaze slip, then at 1180 DEG C -1250 DEG C
Temperature environment under fire.