CN109010889A - A kind of bentonite deodorizer - Google Patents

A kind of bentonite deodorizer Download PDF

Info

Publication number
CN109010889A
CN109010889A CN201811072033.1A CN201811072033A CN109010889A CN 109010889 A CN109010889 A CN 109010889A CN 201811072033 A CN201811072033 A CN 201811072033A CN 109010889 A CN109010889 A CN 109010889A
Authority
CN
China
Prior art keywords
parts
bentonite
powder
deodorant
deodorizer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201811072033.1A
Other languages
Chinese (zh)
Inventor
不公告发明人
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianjin Zhongtian Jingke Technology Co Ltd
Original Assignee
Tianjin Zhongtian Jingke Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianjin Zhongtian Jingke Technology Co Ltd filed Critical Tianjin Zhongtian Jingke Technology Co Ltd
Priority to CN201811072033.1A priority Critical patent/CN109010889A/en
Publication of CN109010889A publication Critical patent/CN109010889A/en
Withdrawn legal-status Critical Current

Abstract

The invention belongs to deodorant processing technique field, specifically a kind of bentonite deodorizer.The bentonite deodorizer component and its weight fraction ratio are as follows: 70~80 parts of bentonite in powder, 35~45 parts of tourmaline powder, nano-TiO235~45 parts of powder, 30~45 parts of hydroxylapatite powder, 20~25 parts of bamboo charcoal powder, 10~15 parts of yellow cinnamon leaf, illiteracy are close to spend 10~15 parts, 15~20 parts of osmund, 10~15 parts of Chinese lantern, 15~18 parts of 8~12 Fen, pivot of Celastrus angulatus storage.Preparation method be first will be bentonite modified, then with tourmaline, nano-TiO2It is compound to prepare composite material, then plant material is crushed, finally composite material, smashed plant materials used and hydroxylapatite powder, bamboo charcoal powder are mixed up to deodorant of the invention.Deodorant good deodorization effect of the invention, harmless, no pollution to the environment, can fundamentally remove stink substances, safe and convenient to use.

Description

A kind of bentonite deodorizer
The application is the divisional application of following application: the applying date is on November 22nd, 2017, application No. is 201711171777.4 entitled a kind of bentonite deodorizer and preparation method thereof.
Technical field
The invention belongs to deodorant processing technique field, specifically a kind of bentonite deodorizer.
Background technique
In the ambient enviroment that we live, often there are many undesirable smell, these peculiar smell can bring uncomfortable sense to people Feel or even some peculiar smell are poisonous and harmful substances, these substances can endanger health after being absorbed by humans and animals.In order to improve life Environment cleans living environment more comfortably, and people are using the bad smell in various methods removal environment.Deodorizing methods at present Predominantly following three types: physical deodorization, chemical deodorizing, biological deodorizing.Physical deodorization is excellent by using absorption property Adsorbent malodor molecule is adsorbed onto porous media achievees the purpose that deodorization or shelter evil using natural aromatic substance Stink is to mitigate stench.Chemical deodorizing be using using oxidation, reduction decomposition, neutralization reaction, addition reaction, condensation reaction, from The odorant of generation is become odorless substance to eliminate foul smell by sub- exchange reaction etc..Biological deodorizing mainly utilizes microorganism Odorant, which is degraded, can play inhibiting effect to stench evolution in solid, liquid phase, but be difficult to send out to the stench given out The effect of the waving and strain that can utilize is limited.
The deodorising product occurred currently on the market has: solid-state deodorant, spray, air freshener etc., although these Foul smell can be removed to a certain extent, but most of is mainly to contain chemical component, it is difficult to be biodegradable or to people Body is harmful.Bentonite is the nonmetallic minerals using montmorillonite as main mineral constituent, has strong hygroscopicity and dilatancy, can inhale The water of attached 8~15 times of own vols, volume expansion is up to several times to 30 times；Have to gas, water and organic compound very strong Adsorptivity.Bentonite is odorless, tasteless, nontoxic environmental-friendly, and as a kind of deodorant, good deodorization effect is quick, keeps Time is long, low in cost.
Chinese patent 200810175768.7 discloses bentonite deodorizer and preparation method thereof, and the invention is first to bentonite It is modified and aluminum sulfate modified alta-mud is prepared, be further added by zeolite/active carbon and/or essence.The preparation method comprises the following steps: bentonite Raw material is broken, then bentonite is added in aluminum sulfate solution, adjusts Ph, and whip modified filters, dry, roast aluminum sulfate changes Property bentonite, add other additives such as zeolite, activated carbon and/or essence, be uniformly mixed up to the bentonite deodorization Agent.
Chinese patent 201511006390.4 discloses a kind of deodorant for refrigerator, the deodorant by following parts by weight original Material composition: 10-15 parts of active carbon, 10-15 parts of diatomite, 3-5 parts of bentonite, 2-5 parts of calcium oxide, 15-20 parts of lemon peel, peppermint 3-5 parts, 6-10 parts of dried orange peel, 5-8 parts of orange peel, 8-10 parts of tealeaves ground-slag, 8-15 parts of honeysuckle, 3-6 parts of rose.
Chinese patent 201010118073.2 discloses a kind of deodorant, and the deodorant of the invention is by following weight proportion Bulk pharmaceutical chemicals are made: rhizoma atractylodis 5%, kaempferia galamga 7%, wrinkled giant hyssop 4%, peppermint 3%, Paris polyphylla 5%, Changshan 5%, folium isatidis 3%, Radix Isatidis 5%, eupatorium 7%, safflower 14%, honeysuckle 14%, the tuber of stemona 8%, rhizome of cyrtomium 9%, kuh-seng 8%, frutus cnidii 3% are made.Preparation Method are as follows: above-mentioned raw materials medicine is fitted into big tank, is added water to cook, filter and remove residue obtains filtrate, concentration, cooling sub-bottle it is filling to get Deodorant.
It is most of to remain as physical absorption although deodorant develops in terms of toward natural green, or cover stench The sending of taste can not fundamentally solve the problems, such as foul smell.
Summary of the invention
The present invention provides a kind of bentonite deodorizer, the deodorant good deodorization effect, it is harmless, to environment without dirt Dye, can fundamentally remove stink substances, safe and convenient to use.
The present invention is implemented as follows: a kind of bentonite deodorizer, the bentonite deodorizer component and its weight fraction ratio Are as follows: 70~80 parts of bentonite in powder, 35~45 parts of tourmaline powder, nano-TiO235~45 parts of powder, 30~45 parts of hydroxylapatite powder, 20~25 parts of bamboo charcoal powder, 10~15 parts of yellow cinnamon leaf, illiteracy are close to spend 10~15 parts, 15~20 parts of osmund, 10~15 parts of Chinese lantern, bitter skin 8~12 Fen, pivot of rattan stores 15~18 parts.
As a further improvement of the present invention, the bentonite in powder, tourmaline powder, nano-TiO2, hydroxylapatite powder, The particle size of bamboo charcoal powder is 240 mesh.
Technical principle of the invention is: the present invention is compounded with other substances for basic material with bentonite to prepare and remove Smelly dose.Due to being mostly calcium-base bentonite, calcium-base bentonite water imbibition, dilatancy, plasticity, thermal stability in raw material bentonite It is strong etc. no sodium bentonite, it needs to be modified raw material bentonite, improves bentonitic utility value.It is swollen to raw material first Profit soil carries out sodium modification, and the calcium-base bentonite contained in raw material is modified as sodium bentonite, is improved between bentonite crystal layer Layer away from improving bentonite water absorption rate and expansion multiple, ion exchange capacity improved, so as to improve bentonitic adsorption effect.Make It is lower, from a wealth of sources and easily remove in modifying process, the good Na of sodium effect with price2CO3As sodium agent, using magnetic force Blender makes bentonite be uniformly dispersed in ultrapure water, is conducive to Na2CO3Sodium agent comes into full contact with bentonite.It is configured to 20% Slurries, suitably free Na is provided+Concentration is conducive to Na+With Ca2+Exchange reaction promotes natridization reaction mobile to positive direction, Be conducive to the progress of natridization reaction, while being conducive to the drying in later period.If the concentration of slurries improves again, Na+Na when excessive concentration+ Ionization rate is big, and electro kinetic potential is high, and activity is strong, makes the Na for having reached balance originally+With Ca2+Swap status is destroyed, excessively Na+Make modified sodium bentonite quality decline instead, influences sodium effect.Water-bath heating can make reaction mass heated equal It is even, and temperature can be controlled preferably, and the phenomenon that not will lead to bumping.Sodium effect can be improved in 75~80 DEG C of temperature Fruit, bentonitic expansion capacity and colloid index are gradually increased after sodium, and excessively high temperature can aggravate ion motion, destroy sodium ion With the exchange equilibrium of calcium ions and magnesium ions, sodium effect is made to be deteriorated.Bentonite after sodium modification carries out high-temperature roasting, can make Bentonite successively loses the combination water in surface water, water of hydration and structural framework, reduces moisture film to the absorption resistance of polluter； Part is located at the impurity in bentonite channel and gap, is pulled away together with the moisture lost, and channel and gap are opened, thus Bentonite adsorption performance is set to change, maturing temperature will not be such that bentonite undergoes phase transition at 250~300 DEG C, will not destroy swollen Moisten soil skeleton structure, its specific surface area is made to reach maximum.It is crushed again after roasting, increases bentonite surface area, increased and inhale Attached action site.
Tourmaline has permanent band Electricity Functional, while having the function of good antibacterial, sterilizing, deodorization etc.；Tourmaline produces Raw hydroxyl ion can also dispel the various peculiar smell such as pet, oil smoke, air-conditioning, keep the fresh of air；Nano-TiO2With excellent Photocatalytic activity, and have the characteristics that nontoxic, resistance to photochemical corrosion, without secondary pollution, it is lasting, long-acting that it can assign product Antibiotic and sterilizing ability；Bentonite has large specific surface area, and hole is more, the stable advantage of property.By bentonite, tourmaline, receive Rice TiO2It carries out compound, nano-TiO can be made2Crystal is evenly distributed, and solves nano-TiO2The disadvantages of hardly possible recycles, is easy to reunite, simultaneously The dispersion performance for improving tourmaline, enhances the comprehensive performance of tourmaline.In the composite the natural electric polarity of tourmaline particles, Environmental functional properties and the nano-TiO such as infra-red radiation and release anion2Photocatalytic activity organically combines, and improves TiO2Catalysis Efficiency, bentonite can adsorb the stink substances in environment, tourmaline and nano-TiO2It can be by the stink in swelling soil pores Substance and pollutant are decomposed, and the stink generated in environment can be inherently eliminated.
Hydroxylapatite biology compatibility is good, while there is excellent ion-exchange performance and adsorption capacity to keep its right Most of heavy metal ion, anion and organic pollutant have good absorption fixed function.Bamboo charcoal powder has loose more The structure in hole, molecule is fine and closely woven porous, and quality is hard；There is very strong adsorption capacity, can purify that air, to eliminate peculiar smell, moisture absorption anti- Mould, antibacterial expelling parasite.By bentonite, tourmaline, nano-TiO2, hydroxyapatite, bamboo charcoal powder compounded, hydroxyl phosphorus can be improved The particle dispersion of lime stone reduces agglomeration traits, improves interface compatibility, hydroxyapatite is made to possess better adsorption capacity.Bamboo Charcoal contains adsorption hole, but hole count is insufficient, and aperture is not big enough, and the ability for adsorbing stink substances is not strong enough, can be with by compounding Increase the adsorption hole of deodorant significantly, have expansion to entire deodorant, the adsorption capacity of deodorant can not only increased By force, the dosage of deodorant can also be reduced when reaching identical adsorption effect.
In the plant material of addition, yellow cinnamon leaf has the function of that analgesic, antibacterial, drive are compacted；Close flower is covered with antibacterial, anti-inflammatory Effect, moreover it is possible to play the role of dispelling wind and heat, nourish the liver to improve visual acuity, move back screen；Osmund can remove stench；Chinese lantern have heat-clearing and fire-reducing, The benefits of anti-inflammatory detoxification, moreover it is possible to treat hemorrhoid；Pivot storage has the function of desinsection removing dampness to relieve itching；Celastrus angulatus is a kind of chlordane, The insects in environment can be killed.The function of deodorant is enhanced by the addition of plant material, while adsorbing foul smell The effects of antibacterial, anti-inflammatory, desinsection can also be played, additionally it is possible to which dispelling wind and heat nourishes the liver to improve visual acuity.These plant materials are from a wealth of sources, Adaptability is strong, readily available, and the cost of deodorant can be greatly lowered.
The present invention has following good result:
1. the raw material that the present invention uses do not have any harm for environment and human body.
2. deodorant raw material sources of the invention are abundant, green safe, it can be widely used, long service life, with later Deodorant can work as Fertilizer application, can cross retain and conserve soil moisture in the soil, improve soil texture, increase the gas permeability of soil.
3. deodorant made from does not add chemical agent, safety, health, and deodorizing effect is significant.
4. bentonite is developed, technical support is provided for my area's bentonite ore deep processing, has been widened bentonitic Application value.
Specific embodiment
A kind of bentonite deodorizer of the description present invention with reference to embodiments, these descriptions are not to make to the content of present invention It is further to limit.
Embodiment 1
It is bentonite modified: to take 78 parts of bentonite in powder and 120 parts of ultrapure waters to be configured to medicinal bentonite suspension, in magnetic stirrer On stir evenly, then weigh natrium carbonicum calcinatum be added to be configured in medicinal bentonite suspension 20% slurries, slurries are put into Heating stirring reaction is carried out in water-bath, heating temperature is 76 DEG C, mixing speed 20r/min, mixing time 85min, from Heart washing carries out high-temperature roasting after dry, maturing temperature is 250 DEG C, and ball mill is put into after roasting and is ground to get changing Property bentonite powder.
It prepares composite material: modified alta-mud powder being taken to be placed in reaction kettle, 45 parts of tourmaline powder, nano-TiO is added2Powder 42 parts, 35 parts of hydroxylapatite powder, 25 parts of bamboo charcoal powder are added 53 parts of glycerine, are uniformly mixed, temperature is raised to 270 DEG C 1.8h is reacted in lower progress oil bath, primary every 0.5h stirring, stands after oil bath, pours out supernatant, then with ultrapure water cleaning, drying After be put into ball mill carry out grinding be prepared into nanocomposite.
The pretreatment of plant material: it takes by 15 parts dry of yellow cinnamon leaf, cover and close spend 11 parts, 13 parts of osmund, Chinese lantern 14 Part, 11 parts of Celastrus angulatus, pivot store 17 parts of mixed-powders for being ground into 230 mesh.
The mixing of material: mixed-powder, nanocomposite is taken to be stirred after mixing up to bentonite deodorizer.
The deodorant that the present invention is prepared is put into ventilative beanbag, it, will be small equipped with deodorant per packed 10g Cloth bag is placed in lavatory, is calculated by lavatory size, wherein every square metre is placed 1 bag, continuous placement 3 days can obviously be felt To lavatory stink disappear, detected with detector, with do not place the deodorant that the embodiment is prepared lavatory between it is right According to deodorizing rate has reached 90%.
Embodiment 2
It is bentonite modified: to take 70 parts of bentonite in powder and 150 parts of ultrapure waters to be configured to medicinal bentonite suspension, in magnetic stirrer On stir evenly, then weigh natrium carbonicum calcinatum be added to be configured in medicinal bentonite suspension 20% slurries, slurries are put into Heating stirring reaction is carried out in water-bath, heating temperature is 78 DEG C, mixing speed 25r/min, mixing time 60min, from Heart washing carries out high-temperature roasting after dry, maturing temperature is 200 DEG C, and ball mill is put into after roasting and is ground to get changing Property bentonite powder.
It prepares composite material: modified alta-mud powder being taken to be placed in reaction kettle, 35 parts of tourmaline powder, nano-TiO is added2Powder 45 parts, 38 parts of hydroxylapatite powder, 24 parts of bamboo charcoal powder are added 51 parts of glycerine, are uniformly mixed, temperature is raised to 300 DEG C 2.0h is reacted in lower progress oil bath, primary every 0.5h stirring, stands after oil bath, pours out supernatant, then with ultrapure water cleaning, drying After be put into ball mill carry out grinding be prepared into nanocomposite.
The pretreatment of plant material: it takes by 10 parts dry of yellow cinnamon leaf, cover and close spend 15 parts, 12 parts of osmund, Chinese lantern 13 Part, 12 parts of Celastrus angulatus, pivot store 15 parts of mixed-powders for being ground into 240 mesh.
The mixing of material: mixed-powder, nanocomposite is taken to be stirred after mixing up to bentonite deodorizer.
The deodorant that the present embodiment is prepared uniformly is scattered in pig house, the stink of pig house disappears substantially after 3 days, can It is obviously improved the environment of pig house, and the red dot after 15 days with pig disappears substantially, upgrowth situation is good.
Embodiment 3
It is bentonite modified: to take 80 parts of bentonite in powder and 125 parts of ultrapure waters to be configured to medicinal bentonite suspension, in magnetic stirrer On stir evenly, then weigh natrium carbonicum calcinatum be added to be configured in medicinal bentonite suspension 20% slurries, slurries are put into Heating stirring reaction is carried out in water-bath, heating temperature is 79 DEG C, mixing speed 35r/min, mixing time 90min, from Heart washing carries out high-temperature roasting after dry, maturing temperature is 280 DEG C, and ball mill is put into after roasting and is ground to get changing Property bentonite powder.
It prepares composite material: modified alta-mud powder being taken to be placed in reaction kettle, 38 parts of tourmaline powder, nano-TiO is added2Powder 35 parts, 42 parts of hydroxylapatite powder, 22 parts of bamboo charcoal powder are added 50 parts of glycerine, are uniformly mixed, temperature is raised to 250 DEG C 1.9h is reacted in lower progress oil bath, primary every 0.5h stirring, stands after oil bath, pours out supernatant, then with ultrapure water cleaning, drying After be put into ball mill carry out grinding be prepared into nanocomposite.
The pretreatment of plant material: it takes by 12 parts dry of yellow cinnamon leaf, cover and close spend 10 parts, 15 parts of osmund, Chinese lantern 11 Part, 8 parts of Celastrus angulatus, pivot store 15 parts of mixed-powders for being ground into 200 mesh.
The mixing of material: mixed-powder, nanocomposite is taken to be stirred after mixing up to bentonite deodorizer.
The deodorant that the present embodiment is prepared is added in sludge, and addition weight is the 4~8% of sludge, deodorant Uniformly in investment sludge, stirred evenly in investment, room temperature stands 10min stink and slightly subtracts after mixing, and 20h is completely eliminated Stink.
Embodiment 4
It is bentonite modified: to take 75 parts of bentonite in powder and 130 parts of ultrapure waters to be configured to medicinal bentonite suspension, in magnetic stirrer On stir evenly, then weigh natrium carbonicum calcinatum be added to be configured in medicinal bentonite suspension 20% slurries, slurries are put into Heating stirring reaction is carried out in water-bath, heating temperature is 75 DEG C, mixing speed 30r/min, mixing time 80min, from Heart washing carries out high-temperature roasting after dry, maturing temperature is 300 DEG C, and ball mill is put into after roasting and is ground to get changing Property bentonite powder.
It prepares composite material: modified alta-mud powder being taken to be placed in reaction kettle, 40 parts of tourmaline powder, nano-TiO is added2Powder 38 parts, 45 parts of hydroxylapatite powder, 20 parts of bamboo charcoal powder are added 55 parts of glycerine, are uniformly mixed, temperature is raised to 260 DEG C 1.8h is reacted in lower progress oil bath, primary every 0.5h stirring, stands after oil bath, pours out supernatant, then with ultrapure water cleaning, drying After be put into ball mill carry out grinding be prepared into nanocomposite.
The pretreatment of plant material: it takes by 14 parts dry of yellow cinnamon leaf, cover and close spend 13 parts, 10 parts of osmund, Chinese lantern 15 Part, 10 parts of Celastrus angulatus, pivot store 18 parts of mixed-powders for being ground into 210 mesh.
The mixing of material: mixed-powder, nanocomposite is taken to be stirred after mixing up to bentonite deodorizer.
The deodorant that the present embodiment volume is prepared equably is dispersed in the living room of pet dog, is padding one above thoroughly The cloth of gas, for 24 hours after pet dog living room odorless, pet dog hair health is smooth after 2 weeks, trichomadesis reduce.
Embodiment 5
It is bentonite modified: to take 73 parts of bentonite in powder and 140 parts of ultrapure waters to be configured to medicinal bentonite suspension, in magnetic stirrer On stir evenly, then weigh natrium carbonicum calcinatum be added to be configured in medicinal bentonite suspension 20% slurries, slurries are put into Heating stirring reaction is carried out in water-bath, heating temperature is 80 DEG C, mixing speed 40r/min, mixing time 75min, from Heart washing carries out high-temperature roasting after dry, maturing temperature is 220 DEG C, and ball mill is put into after roasting and is ground to get changing Property bentonite powder.
It prepares composite material: modified alta-mud powder being taken to be placed in reaction kettle, 42 parts of tourmaline powder, nano-TiO is added2Powder 40 parts, 30 parts of hydroxylapatite powder, 23 parts of bamboo charcoal powder are added 54 parts of glycerine, are uniformly mixed, temperature is raised to 280 DEG C 2.0h is reacted in lower progress oil bath, primary every 0.5h stirring, stands after oil bath, pours out supernatant, then with ultrapure water cleaning, drying After be put into ball mill carry out grinding be prepared into nanocomposite.
The pretreatment of plant material: it takes by 13 parts dry of yellow cinnamon leaf, cover and close spend 12 parts, 14 parts of osmund, Chinese lantern 10 Part, 9 parts of Celastrus angulatus, pivot store 16 parts of mixed-powders for being ground into 220 mesh.
The mixing of material: mixed-powder, nanocomposite is taken to be stirred after mixing up to bentonite deodorizer.
The deodorant that the present embodiment is prepared is put into ventilative beanbag, and every bag of weight 15g takes 1 bag to be put into refrigerator, It is observed after 15h, the stink in refrigerator completely disappears, inviolateness in refrigerator after placing 1 week.
The above embodiment of the present invention scheme is only the description of the invention and cannot limit the present invention, is pointed out in claim Product of the present invention constituent, component ratio, the range of preparation method parameter, and above-mentioned explanation does not point out ginseng of the present invention Therefore several ranges any change within the meaning and scope equivalent to the claims of the present invention, is all considered to be It is included within the scope of the claims.
The present invention is created by multidigit deodorant processing staff's long-term work experience accumulation, and by creative work Out, deodorant of the invention is green safe healthy, pollution-free, and deodorizing effect is significant, can be widely applied, for bentonitic depth Processing has far-reaching influence.

Claims (3)

1. a kind of bentonite deodorizer, which is characterized in that constituent is as follows: 78 parts of bentonite in powder, 120 parts of ultrapure water, electrically 45 parts of mountain flour, nano-TiO242 parts of powder, 35 parts of hydroxylapatite powder, 25 parts of bamboo charcoal powder, 53 parts of glycerine, dry yellow cinnamon leaf 15 Part, cover it is close spend 11 parts, 13 parts of osmund, 14 parts of Chinese lantern, 11 Fen, pivot of Celastrus angulatus store 17 parts.
2. a kind of bentonite deodorizer according to claim 1, characterized in that the bentonite in powder, is received tourmaline powder Rice TiO2, hydroxylapatite powder, bamboo charcoal powder particle size be 240 mesh.
3. a kind of bentonite deodorizer according to claim 1 or 2, characterized in that the bentonite deodorizer is used for The deodorizing process of residential location.
CN201811072033.1A 2017-11-22 2017-11-22 A kind of bentonite deodorizer Withdrawn CN109010889A (en)