CN108978253A - A kind of outdoor sport fabric - Google Patents

A kind of outdoor sport fabric Download PDF

Info

Publication number
CN108978253A
CN108978253A CN201811001835.3A CN201811001835A CN108978253A CN 108978253 A CN108978253 A CN 108978253A CN 201811001835 A CN201811001835 A CN 201811001835A CN 108978253 A CN108978253 A CN 108978253A
Authority
CN
China
Prior art keywords
fabric
temperature
fiber
content
ramee
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811001835.3A
Other languages
Chinese (zh)
Inventor
相里海霞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201811001835.3A priority Critical patent/CN108978253A/en
Publication of CN108978253A publication Critical patent/CN108978253A/en
Pending legal-status Critical Current

Abstract

The present invention provides a kind of outdoor sport fabric, including ultra-fine polyester fiber, cattail wool fiber, polycarbonate, polytetrafluoroethylene fibre, acrylic fiber, ramee and copper ammonia fiber, precentagewise, the thin polyester fiber content is 20~30%, the cattail wool fiber content is 25~35%, the polycarbonate content is 15~20%, the polytetrafluoroethylene fibre content is 15~20%, the acrylic fiber content is 20~30%, the ramee content is 30~40%, the copper ammonia fiber content is 5~8%, compared with prior art, the present invention is with following the utility model has the advantages that the present invention is made to have fast light heat resistance, good permeability, antibiotic property is good, ultraviolet resistance is strong, feel silk is sliding, wearing comfort is high, the good advantage of waterproof performance.

Description

A kind of outdoor sport fabric
Technical field
The present invention is a kind of outdoor sport fabric, belongs to garment material technical field.
Background technique
Modern more and more focus on improve quality of the life, outdoor sports become people after work with household, friend A kind of mode of share, it can not only keep fit and healthy, and can also promote mutual relationship and friendship, be more at one stroke ?.For people during doing outdoor sports, the clothing worn is other than will have good absorption of perspiration, gas permeability and elasticity, also Must have certain wearability and soil resistance；Especially for the fan of some extreme sports, in the process of movement may be used Rainwater or high temperature or severe cold can be encountered, at this point, atrocious weather proposes very high requirement, clothing to their clothing Object plane material in addition to material is slim and graceful, quality securely other than, it is necessary to it is waterproof, windproof, warming, cold-resistant, can be provided more for sporter More safety guarantee.
Sportswear fabric functionality in the prior art is relatively simple, and the fabric of good waterproof performance, comfort is bad, antiultraviolet Performance is bad, and fabric has a single function, so being badly in need of wanting a kind of outdoor sport fabric to solve the above-mentioned problem.
Summary of the invention
In view of the deficienciess of the prior art, it is an object of the present invention to provide a kind of outdoor sport fabric, to solve above-mentioned back The problem of being proposed in scape technology.
To achieve the goals above, the present invention is to realize by the following technical solutions: a kind of outdoor sport fabric, packet Include ultra-fine polyester fiber, cattail wool fiber, polycarbonate, polytetrafluoroethylene fibre, acrylic fiber, ramee and cuprammonium Fiber, precentagewise, the thin polyester fiber content are 20~30%, and the cattail wool fiber content is 25~35%, the poly- carbon Acid esters fiber content be 15~20%, the polytetrafluoroethylene fibre content be 15~20%, the acrylic fiber content be 20~ 30%, the ramee content is 30~40%, and the copper ammonia fiber content is 5~8%；
A kind of outdoor sport fabric preparation process the following steps are included:
Choose ultra-fine polyester fiber, cattail wool fiber, polycarbonate, polytetrafluoroethylene fibre, acrylic fiber, ramee with And copper ammonia fiber, the method sizing of low twist is respectively adopted, twist control is twisted 80, and orientation is twisted using S, the raw material warp after sizing Loom is interwoven fabric；
Fabric is immersed in dye liquor, high light fastness disperse dyes, 0.8~1.5g/L of levelling agent, chelated dispersants 0.6 are added ~1.6g/L；Dye liquor is heated up to 50~56 DEG C and keeps the temperature 10~15 minutes；Then 130 DEG C are heated up to, keeps the temperature 30~40 minutes；Drop Temperature keeps the temperature 5~drain after ten minutes to 80 DEG C again；Clear water is added after drain and 2~4g/L of soda ash, sodium hydrosulfite are added simultaneously 1~3g/L is warming up to 75~85 DEG C again, keeps the temperature 15 minutes, then drains, cleans；
Fabric after dyeing passes through tentering, is shaped into coloured fabric, and setting temperature is 118 DEG C, speed 30m/min；
Fabric after sizing is delivered to high-pressure injection overflow machine, desizing refining processing is carried out using low bath raio, pH value 8 is bathed in desizing, Refining agent 4g/L, NaOH1.8g/L, bath raio 1:12,80 DEG C of temperature, time 40min；
By the fabric after the completion of desizing refining, then alkali decrement treatment is carried out, treatment conditions are NaOH10~15g/L, temperature 85 ~95 DEG C, 10~15min of time；
The fabric after alkali decrement treatment is delivered to coating machine again, PU layers are applied on fabric by coating machine, coating machine speed 10m/min, temperature are 115 DEG C, and coating number is 2 times；
Fabric is continued through with the speed of 35~45m/min to 135~145 DEG C of baking oven drying tunnel, then continuous logical at the same rate 155~165 DEG C of setting high temperature channels are crossed, finished fabric is made after cooling.
Further, it is 10~20% that content, which is added, in the high light fastness disperse dyes；
Further, the cooling drops to 80 DEG C from 130 DEG C with the rate of 1 DEG C/min；
Further, described PU layers with a thickness of 100 μm~400 μm.
Beneficial effects of the present invention: a kind of outdoor sport fabric of the invention, because the present invention be added to ultra-fine polyester fiber, Cattail wool fiber, polycarbonate, polytetrafluoroethylene fibre, acrylic fiber, ramee and copper ammonia fiber make tool of the present invention There is fast light heat resistance, good permeability, antibiotic property is good, and ultraviolet resistance is strong, and feel silk is sliding, and wearing comfort is high, waterproof performance Good advantage.
Specific embodiment
To be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, below with reference to Specific embodiment, the present invention is further explained.
The present invention provides a kind of technical solution: a kind of outdoor sport fabric, including ultra-fine polyester fiber, cattail wool fiber, poly- Carbonic acid ester fiber, polytetrafluoroethylene fibre, acrylic fiber, ramee and copper ammonia fiber, precentagewise, thin polyester fiber contain Amount is 20~30%, and cattail wool fiber content is 25~35%, and polycarbonate content is 15~20%, and polytetrafluoroethylene fibre contains Amount is 15~20%, and acrylic fiber content is 20~30%, and ramee content is 30~40%, and copper ammonia fiber content is 5~8%；
A kind of outdoor sport fabric preparation process the following steps are included:
Choose ultra-fine polyester fiber, cattail wool fiber, polycarbonate, polytetrafluoroethylene fibre, acrylic fiber, ramee with And copper ammonia fiber, the method sizing of low twist is respectively adopted, twist control is twisted 80, and orientation is twisted using S, the raw material warp after sizing Loom is interwoven fabric；
Fabric is immersed in dye liquor, high light fastness disperse dyes, 0.8~1.5g/L of levelling agent, chelated dispersants 0.6 are added ~1.6g/L；Dye liquor is heated up to 50~56 DEG C and keeps the temperature 10~15 minutes；Then 130 DEG C are heated up to, keeps the temperature 30~40 minutes；Drop Temperature keeps the temperature 5~drain after ten minutes to 80 DEG C again；Clear water is added after drain and 2~4g/L of soda ash, sodium hydrosulfite are added simultaneously 1~3g/L is warming up to 75~85 DEG C again, keeps the temperature 15 minutes, then drains, cleans；
Fabric after dyeing passes through tentering, is shaped into coloured fabric, and setting temperature is 118 DEG C, speed 30m/min；
Fabric after sizing is delivered to high-pressure injection overflow machine, desizing refining processing is carried out using low bath raio, pH value 8 is bathed in desizing, Refining agent 4g/L, NaOH1.8g/L, bath raio 1:12,80 DEG C of temperature, time 40min；
By the fabric after the completion of desizing refining, then alkali decrement treatment is carried out, treatment conditions are NaOH10~15g/L, temperature 85 ~95 DEG C, 10~15min of time；
The fabric after alkali decrement treatment is delivered to coating machine again, PU layers are applied on fabric by coating machine, coating machine speed 10m/min, temperature are 115 DEG C, and coating number is 2 times；
Fabric is continued through with the speed of 35~45m/min to 135~145 DEG C of baking oven drying tunnel, then continuous logical at the same rate 155~165 DEG C of setting high temperature channels are crossed, finished fabric is made after cooling.
As an embodiment of the present invention: it is 10~20% that content, which is added, in high light fastness disperse dyes.
As an embodiment of the present invention: cooling drops to 80 DEG C from 130 DEG C with the rate of 1 DEG C/min.
As an embodiment of the present invention: PU layers with a thickness of 100 μm~400 μm.
As an embodiment of the present invention: thin polyester fiber content is 20%, and cattail wool fiber content is 25%, polycarbonate Fiber content is 15%, and polytetrafluoroethylene fibre content is 15%, and acrylic fiber content is 20%, and ramee content is 30%, copper Ammonia fiber content is 5%, and it is fine to choose ultra-fine polyester fiber, cattail wool fiber, polycarbonate, polytetrafluoroethylene fibre, acrylic fibers The method sizing of low twist is respectively adopted in dimension, ramee and copper ammonia fiber, and twist control is twisted 80, and orientation is twisted using S, Raw material after sizing is interwoven fabric through loom；
Fabric is immersed in dye liquor, high light fastness disperse dyes 10%, levelling agent 0.8g/L, chelated dispersants 0.6g/ is added L；Dye liquor is heated up to 50 DEG C and keeps the temperature 10 minutes；Then 130 DEG C are heated up to, keeps the temperature 30 minutes；80 DEG C are cooled to, keeps the temperature 5 again Drain after minute；Clear water is added after drain and soda ash 2g/L, sodium hydrosulfite 1g/L are added simultaneously, is warming up to 75 DEG C again, heat preservation It 15 minutes, then drains, clean；
Fabric after dyeing passes through tentering, is shaped into coloured fabric, and setting temperature is 118 DEG C, speed 30m/min；
Fabric after sizing is delivered to high-pressure injection overflow machine, desizing refining processing is carried out using low bath raio, pH value 8 is bathed in desizing, Refining agent 4g/L, NaOH1.8g/L, bath raio 1:12,80 DEG C of temperature, time 40min；
By the fabric after the completion of desizing refining, then alkali decrement treatment is carried out, treatment conditions are NaOH10~15g/L, temperature 85 ~95 DEG C, time 10min；
The fabric after alkali decrement treatment is delivered to coating machine again, PU layers are applied on fabric by coating machine, coating machine speed 10m/min, temperature are 115 DEG C, and coating number is 2 times；
Fabric is continued through with the speed of 35m/min to 135 DEG C of baking oven drying tunnel, then continue through at the same rate 155 DEG C it is fixed Finished fabric is made after cooling in shape high temperature channel.
As an embodiment of the present invention: thin polyester fiber content is 30%, and cattail wool fiber content is 35%, polycarbonate Fiber content is 20%, and polytetrafluoroethylene fibre content is 20%, and acrylic fiber content is 30%, and ramee content is 40%, copper Ammonia fiber content is 8%, and it is fine to choose ultra-fine polyester fiber, cattail wool fiber, polycarbonate, polytetrafluoroethylene fibre, acrylic fibers The method sizing of low twist is respectively adopted in dimension, ramee and copper ammonia fiber, and twist control is twisted 80, and orientation is twisted using S, Raw material after sizing is interwoven fabric through loom；
Fabric is immersed in dye liquor, high light fastness disperse dyes 20%, levelling agent 1.5g/L, chelated dispersants 1.6g/ is added L；Dye liquor is heated up to 56 DEG C and keeps the temperature 15 minutes；Then 130 DEG C are heated up to, keeps the temperature 40 minutes；80 DEG C are cooled to, keeps the temperature 10 again Drain after minute；Clear water is added after drain and soda ash 4g/L, sodium hydrosulfite 3g/L are added simultaneously, is warming up to 85 DEG C again, heat preservation It 15 minutes, then drains, clean；
Fabric after dyeing passes through tentering, is shaped into coloured fabric, and setting temperature is 118 DEG C, speed 30m/min；
Fabric after sizing is delivered to high-pressure injection overflow machine, desizing refining processing is carried out using low bath raio, pH value 8 is bathed in desizing, Refining agent 4g/L, NaOH1.8g/L, bath raio 1:12,80 DEG C of temperature, time 40min；
By the fabric after the completion of desizing refining, then alkali decrement treatment being carried out, treatment conditions are NaOH15g/L, and 95 DEG C of temperature, when Between 10~15min；
The fabric after alkali decrement treatment is delivered to coating machine again, PU layers are applied on fabric by coating machine, coating machine speed 10m/min, temperature are 115 DEG C, and coating number is 2 times；
Fabric is continued through with the speed of 45m/min to 145 DEG C of baking oven drying tunnel, then continue through at the same rate 165 DEG C it is fixed Finished fabric is made after cooling in shape high temperature channel.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention, for this field skill For art personnel, it is clear that invention is not limited to the details of the above exemplary embodiments, and without departing substantially from spirit of the invention or In the case where essential characteristic, the present invention can be realized in other specific forms.Therefore, in all respects, should all incite somebody to action Embodiment regards exemplary as, and is non-limiting, the scope of the present invention by appended claims rather than on state Bright restriction, it is intended that including all changes that fall within the meaning and scope of the equivalent elements of the claims in the present invention It is interior.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art The other embodiments being understood that.

Claims (4)

1. a kind of outdoor sport fabric, including ultra-fine polyester fiber, cattail wool fiber, polycarbonate, polytetrafluoroethylene fibre, Acrylic fiber, ramee and copper ammonia fiber, it is characterised in that: precentagewise, the thin polyester fiber content be 20~ 30%, the cattail wool fiber content is 25~35%, and the polycarbonate content is 15~20%, the fibrillated polytetrafluoroethylene Dimension hplc is 15~20%, and the acrylic fiber content is 20~30%, and the ramee content is 30~40%, the cuprammonium Fiber content is 5~8%；
A kind of outdoor sport fabric preparation process the following steps are included:
Choose ultra-fine polyester fiber, cattail wool fiber, polycarbonate, polytetrafluoroethylene fibre, acrylic fiber, ramee with And copper ammonia fiber, the method sizing of low twist is respectively adopted, twist control is twisted 80, and orientation is twisted using S, the raw material warp after sizing Loom is interwoven fabric；
Fabric is immersed in dye liquor, high light fastness disperse dyes, 0.8~1.5g/L of levelling agent, chelated dispersants 0.6 are added ~1.6g/L；Dye liquor is heated up to 50~56 DEG C and keeps the temperature 10~15 minutes；Then 130 DEG C are heated up to, keeps the temperature 30~40 minutes；Drop Temperature keeps the temperature 5~drain after ten minutes to 80 DEG C again；Clear water is added after drain and 2~4g/L of soda ash, sodium hydrosulfite are added simultaneously 1~3g/L is warming up to 75~85 DEG C again, keeps the temperature 15 minutes, then drains, cleans；
Fabric after dyeing passes through tentering, is shaped into coloured fabric, and setting temperature is 118 DEG C, speed 30m/min；
Fabric after sizing is delivered to high-pressure injection overflow machine, desizing refining processing is carried out using low bath raio, pH value 8 is bathed in desizing, Refining agent 4g/L, NaOH1.8g/L, bath raio 1:12,80 DEG C of temperature, time 40min；
By the fabric after the completion of desizing refining, then alkali decrement treatment is carried out, treatment conditions are NaOH10~15g/L, temperature 85 ~95 DEG C, 10~15min of time；
The fabric after alkali decrement treatment is delivered to coating machine again, PU layers are applied on fabric by coating machine, coating machine speed 10m/min, temperature are 115 DEG C, and coating number is 2 times；
Fabric is continued through with the speed of 35~45m/min to 135~145 DEG C of baking oven drying tunnel, then continuous logical at the same rate 155~165 DEG C of setting high temperature channels are crossed, finished fabric is made after cooling.
2. a kind of outdoor sport fabric according to claim 1, it is characterised in that: the high light fastness disperse dyes add Entering content is 10~20%.
3. a kind of outdoor sport fabric according to claim 1, it is characterised in that: the cooling is with the rate of 1 DEG C/min 80 DEG C are dropped to from 130 DEG C.
4. a kind of outdoor sport fabric according to claim 1, it is characterised in that: described PU layers with a thickness of 100 μm~ 400μm。
CN201811001835.3A 2018-08-30 2018-08-30 A kind of outdoor sport fabric Pending CN108978253A (en)