CN108948850A - A kind of aqueous copper gold pigment and preparation method thereof - Google Patents
A kind of aqueous copper gold pigment and preparation method thereof Download PDFInfo
- Publication number
- CN108948850A CN108948850A CN201810779204.8A CN201810779204A CN108948850A CN 108948850 A CN108948850 A CN 108948850A CN 201810779204 A CN201810779204 A CN 201810779204A CN 108948850 A CN108948850 A CN 108948850A
- Authority
- CN
- China
- Prior art keywords
- copper gold
- aqueous
- acid
- pigment
- aqueous copper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of aqueous copper gold pigment and preparation method thereof, a kind of aqueous copper gold pigment is formulated: copper gold paste 55-80% by the raw material of following weight percents content;Corrosion inhibiter 0.2-1%;Organic coating material 15-30%;Dispersing agent 1-5%;Disintegrating agent 1-10%;Wherein, the copper gold paste is prepared by the solvent that 20-30% is added in Cu-Zn alloy powder.Present invention efficiently solves the surface treatment of existing Cu-Zn alloy powder there are the problem of, aqueous copper gold pigment provided by the invention has the advantages that cladding is securely complete, form and aspect are stable and process economy is environmentally friendly in water-based system.
Description
Technical field
The present invention relates to metal powder surface processing techniques more particularly to a kind of aqueous copper gold pigment and preparation method thereof.
Background technique
Cu-Zn alloy powder is a kind of using copper, zinc as sheet alloy powder superfine made of primary raw material, because its Zn content is not
Together, the colors such as yellow, golden yellow, crimson can be presented.Cu-Zn alloy powder can be widely applied to printing, weaving, stamp, building decoration, technique decorations
The industries such as product, metal carving.At this stage, the imitative metallic paint and ink prepared by Cu-Zn alloy powder, is still to be released based on solvent type
The a large amount of solvents put cause great pressure to ecological environment, while can also damage people's health.As people's environmental protection is anticipated
The enhancing of knowledge, the appearance of national environmental protection policies and regulations, it is imperative to imitate metallic paint Water-borne modification.
Cu-Zn alloy powder, can not in water paint and ink due to there is the addition of the lipophilicity substances such as stearic acid in grinding technics
Dispersion, and the erosion due to substances such as water, acid, alkali, oxygen to copper, zinc are easy to cause Cu-Zn alloy powder appearance change colour, reunite, emitting
The problems such as bubble.It is used to stablize Cu-Zn alloy powder in water-based system, needs for Cu-Zn alloy powder to be surface-treated.Existing Cu-Zn alloy powder
Surface treatment have and handled using chromium compounds, or form silicon dioxide film with collosol and gel, or double using organic-inorganic
Layer cladding.But environment can be caused greatly to pollute by being handled using chromium, application is restricted;The speed of collosol and gel
Be difficult to uniform, and Cu-Zn alloy powder surface is irregular, the silicon dioxide film of formation there are it is imperfect easy to fall off the problems such as;Using organic nothing
Machine double-coating, manufacturing process is cumbersome, need to expend a large amount of manpower and material resources, and in manufacturing process with many ethyl alcohol come
It cleans and works as solvent, pole is not environmentally.
Therefore, how to overcome existing Cu-Zn alloy powder surface treatment cladding it is insecure it is imperfect, form and aspect are unstable and uneconomical
The defect of environmental protection is industry urgent problem to be solved.
Summary of the invention
The present invention in order to solve existing Cu-Zn alloy powder surface treatment cladding it is insecure it is imperfect, form and aspect are unstable and uneconomical
The problem of environmental protection proposes a kind of aqueous copper gold that securely complete, form and aspect stabilization and process economy environmental protection are coated in water-based system
Pigment and preparation method thereof.
A kind of aqueous copper gold pigment proposed by the present invention, is formulated by the raw material of following weight percents content:
Copper gold paste 55-80%;Corrosion inhibiter 0.2-1%;Organic coating material 15-30%;Dispersing agent 1-5%;Disintegrating agent 1-10%;
Wherein, the copper gold paste by Cu-Zn alloy powder be added 20-30% solvent be prepared, solvent be medicinal white oils, soybean oil methyl ester,
At least one of tung oil butyl ester.
Preferably, the corrosion inhibiter is benzotriazole or 2- benzothiazolyl mercaptan.
Preferably, the organic coating material is alcohol ethoxylates or the non-ionic water macromolecule with emulsification function
Compound.
Wherein, the alcohol ethoxylate is positive structure alkyl alcohol ethoxylates and isomery alkyl alcohol ethoxylates;Institute
Stating the non-ionic water high-molecular compound with emulsification function is polyox-yethylene-polyoxypropylene block copolymer, poly- methyl-prop
Olefin(e) acid ester, polyoxyethylene ether, at least one of polyoxyethylene rouge and polyacrylate.
Preferably, the dispersing agent is phosphate, phosphoric acid, phosphate, contains sulfonic aqueous high molecular or contain carboxyl
Aqueous high molecular one kind.
Wherein, described to contain sulfonic aqueous high molecular for styrene sulfonic acid, methacrylic sulfonic acid, 2- acrylamide -2-
The formation of at least one of methyl propane sulfonic acid, methacrylic acid -2-ethanesulfonic acid ester, -2 hydroxyl -1- propyl sulfonic acid of 3- allyloxy
Polymer or copolymer;The carboxylic aqueous high molecular is methacrylic acid, butyl acrylate, maleic acid, maleic acid
At least one of acid anhydride, 2,2- dihydromethyl propionic acid and 2,2- dimethylolpropionic acid are the polymer or copolymer that monomer is formed.
Preferably, the disintegrating agent is carboxymethyl cellulose, starch ethanol hydrochlorate, cross-linked carboxymethyl salt, polyvinyl pyrrole
At least one of alkanone, crosslinked polyvinylpyrrolidone and alginate.
The invention also provides a kind of preparation methods of aqueous copper gold pigment, and its step are as follows:
Step 1: weighing copper gold paste, corrosion inhibiter, organic coating material, dispersing agent and the disintegrating agent in proportion;
Step 2: the corrosion inhibiter being added in the copper gold paste, stir half an hour, be uniformly mixed;
Step 3: the organic coating material and dispersing agent being added in mixture made from step 2 again, stir two hours, cladding is equal
It is even;
Step 4: the disintegrating agent being added in mixture made from step 3, is stirred one hour, is uniformly mixed;
Step 5: by mixed slurry extruding pelletization made from step 4, then being dried in vacuo baking, remove solvent.
The present invention forms protective layer on copper surface using benzotriazole, 2- benzothiazolyl mercaptan, being capable of effective ground resistance
The erosion of water blocking, oxygen, acid, alkali to Cu-Zn alloy powder enables copper gold pigment that form and aspect to be kept to stablize in water-based system.The phosphoric acid of use
There is extremely strong adsorptivity to Cu-Zn alloy powder with phosphate group, can make to coat stronger complete;It can be with alcohol ethoxylate collocation
Play better water dispersible and alcohol ether dispersibility.Using carboxylic aqueous high molecular and contain sulfonic aqueous high molecular
At least one of collocation with the non-ionic water high-molecular compound with emulsification function, this combination cladding is securely complete,
There are good dispersibility, excellent yellowing resistance energy.The collocation of corrosion inhibiter, organic coating material and dispersing agent uses, and makes aqueous copper
Golden pigment cladding is securely complete, and form and aspect are stablized.The preparation method of aqueous copper gold pigment of the invention is simple, has largely saved people
Power and material resources, whole preparation process only joined a small amount of solvent, and can recycle when vacuum drying, Bu Huizhi
Run in air, it is very environmentally friendly.
Specific embodiment
The present invention is described further combined with specific embodiments below.
A kind of aqueous copper gold pigment proposed by the present invention, can be formulated by the raw material of following weight percents content:
Copper gold paste 55-80%;Corrosion inhibiter 0.2-1%;Organic coating material 15-30%;Dispersing agent 1-5%;Disintegrating agent 1-10%;
Wherein, the copper gold paste by Cu-Zn alloy powder be added 20-30% solvent be prepared, solvent be medicinal white oils, soybean oil methyl ester,
At least one of tung oil butyl ester.
The corrosion inhibiter is benzotriazole and 2- benzothiazolyl mercaptan.
The organic coating material is alcohol ethoxylates or the non-ionic water high-molecular compound with emulsification function.
Wherein, the alcohol ethoxylate is positive structure alkyl alcohol ethoxylates and isomery alkyl alcohol ethoxylates;It is described that there is cream
The non-ionic water high-molecular compound for changing function is polyox-yethylene-polyoxypropylene block copolymer, polymethacrylates, gathers
Ethylene oxide ether, at least one of polyoxyethylene rouge and polyacrylate.
The dispersing agent is phosphate, phosphoric acid, phosphate, contains sulfonic aqueous high molecular or carboxylic aqueous height
One kind of molecule.Wherein, described to contain sulfonic aqueous high molecular for styrene sulfonic acid, methacrylic sulfonic acid, 2- acrylamide-
At least one of 2- methyl propane sulfonic acid, methacrylic acid -2-ethanesulfonic acid ester, -2 hydroxyl -1- propyl sulfonic acid of 3- allyloxy shape
At polymer or copolymer;The carboxylic aqueous high molecular is methacrylic acid, butyl acrylate, maleic acid, Malaysia
At least one of acid anhydrides, 2,2- dihydromethyl propionic acid and 2,2- dimethylolpropionic acid are the polymer or copolymerization that monomer is formed
Object.
The disintegrating agent is carboxymethyl cellulose, starch ethanol hydrochlorate, cross-linked carboxymethyl salt, polyvinylpyrrolidone, friendship
Join at least one of polyvinylpyrrolidone and alginate.
The present invention is described further combined with specific embodiments below.
Embodiment 1
Aqueous copper gold pigment has consisting of ingredient:
Aqueous copper gold method for preparing pigment is as follows:
Step 1: 1800 grams of medicinal white oils are added in 6200 grams of Cu-Zn alloy powders, half an hour is stirred in kneader, becomes copper gold
Slurry.
Step 2: 20 grams of benzotriazole corrosion inhibiter are added, half an hour is stirred, is uniformly mixed.
Step 3: 1500 grams of polyethoxy isomerous tridecanols and 100 grams of propyl phosphoric acid are added, stir two hours, mixing is equal
It is even.
Step 4: 380 grams of alginic acid ammonia are added, stir one hour, is uniformly mixed.
Step 5: paste mixture is taken out, it is granulated using Screw Extrusion, the diameter of particle is 3mm.
Step 6: the pellet produced is dried in vacuo in baking pan remove solvent, baking temperature be 70 DEG C, vacuum degree be-
100kPa。
Embodiment 2
Aqueous copper gold pigment has consisting of ingredient:
Steps are as follows for aqueous copper gold method for preparing pigment:
Step 1: 1350 grams of medicinal white oils are added in 5400 grams of Cu-Zn alloy powders, half an hour is stirred in kneader, becomes copper gold
Slurry.
Step 2: 60 grams of benzotriazole corrosion inhibiter are added, half an hour is stirred, is uniformly mixed.
Step 3: 2250 grams of polyox-yethylene-polyoxypropylene block copolymers and 300 grams of sulfonic group waterborne polyesters are added, stir
It mixes two hours, is uniformly mixed.
Step 4: 640 grams of polyvinylpyrrolidones are added, stir one hour, is uniformly mixed.
Step 5: paste mixture is taken out, it is granulated using Screw Extrusion, the diameter of particle is 5mm.
Step 6: the pellet produced is dried in vacuo in baking pan remove solvent, baking temperature be 50 DEG C, vacuum degree be-
90kPa。
Embodiment 3
Aqueous copper gold pigment has consisting of ingredient:
Steps are as follows for aqueous copper gold method for preparing pigment:
Step 1: 1200 grams of medicinal white oils are added in 4300 grams of Cu-Zn alloy powders, half an hour is stirred in kneader, becomes copper gold
Slurry.
Step 2: 100 grams of 2- benzothiazolyl mercaptan corrosion inhibiter are added, half an hour is stirred, is uniformly mixed.
Step 3: 3000 grams of polyox-yethylene-polyoxypropylene block copolymers and 400 grams of Sodium Polyacrylates are added, stirring two
Hour, it is uniformly mixed.
Step 4: 1000 grams of crosslinked polyvinylpyrrolidone are added, stir one hour, is uniformly mixed.
Step 5: paste mixture is taken out, it is granulated using Screw Extrusion, the diameter of particle is 4mm.
Step 6: the pellet produced is dried in vacuo in baking pan remove solvent, baking temperature be 90 DEG C, vacuum degree be-
80kPa。
Embodiment 4
Aqueous copper gold pigment is made of following raw material:
Steps are as follows for aqueous copper gold method for preparing pigment:
Step 1: 2000 grams of medicinal white oils are added in 5000 grams of Cu-Zn alloy powders, half an hour is stirred in kneader, becomes copper gold
Slurry.
Step 2: 60 grams of 2- benzothiazolyl mercaptan corrosion inhibiter are added, half an hour is stirred, is uniformly mixed.
Step 3: 2340 grams of polyethoxy isomerous tridecanols and 500 grams of lauryl alcohol phosphate monoesters are added, stir two hours,
It is uniformly mixed.
Step 4: 100 grams of carboxymethyl celluloses are added, stir one hour, is uniformly mixed.
Step 5: paste mixture is taken out, it is granulated using Screw Extrusion, the diameter of particle is 3mm.
Step 6: the pellet produced is dried in vacuo in baking pan remove solvent, baking temperature be 70 DEG C, vacuum degree be-
90kPa。
Present invention efficiently solves existing Cu-Zn alloy powder surface treatment there are the problem of, the aqueous copper gold pigment of proposition is in water
Property system in have the advantages that cladding is securely complete, form and aspect are stable and process economy environmental protection.
Embodiment described above is primarily to illustrate creating conception of the invention, it is noted that for this field
Those of ordinary skill for, without departing from the inventive concept of the premise, various modifications and improvements can be made, these are all
It belongs to the scope of protection of the present invention.
Claims (10)
1. a kind of aqueous copper gold pigment, is formulated by the raw material of following weight percents content:
Copper gold paste 55-80%;Corrosion inhibiter 0.2-1%;Organic coating material 15-30%;Dispersing agent 1-5%;Disintegrating agent 1-10%;
Wherein, the copper gold paste is prepared by the solvent that 20-30% is added in Cu-Zn alloy powder.
2. aqueous copper gold pigment as described in claim 1, which is characterized in that the corrosion inhibiter be benzotriazole and/or
2- benzothiazolyl mercaptan.
3. aqueous copper gold pigment as described in claim 1, which is characterized in that the organic coating material is alcohol ethoxy chemical combination
Object or non-ionic water high-molecular compound with emulsification function.
4. aqueous copper gold pigment as claimed in claim 3, which is characterized in that the alcohol ethoxylate be positive structure and/or
Isomery alkyl alcohol ethoxylates;The non-ionic water high-molecular compound with emulsification function is polyoxyethylene-polyoxy
Propylene-based block copolymer, polymethacrylates, polyoxyethylene ether, at least one of polyoxyethylene rouge and polyacrylate.
5. aqueous copper gold pigment as described in claim 1, which is characterized in that the dispersing agent is phosphate, phosphoric acid, phosphoric acid
Salt, one kind containing sulfonic aqueous high molecular or carboxylic aqueous high molecular.
6. aqueous copper gold pigment as claimed in claim 5, which is characterized in that described to contain sulfonic aqueous high molecular for benzene second
Alkene sulfonic acid, methacrylic sulfonic acid, 2- acrylamide-2-methyl propane sulfonic, methacrylic acid -2-ethanesulfonic acid ester, 3- allyloxy -
The polymer or copolymer that at least one of 2 hydroxyl -1- propyl sulfonic acids are formed;The carboxylic aqueous high molecular is methyl
In acrylic acid, butyl acrylate, maleic acid, maleic anhydride, 2,2- dihydromethyl propionic acid and 2,2- dimethylolpropionic acid at least
A kind of polymer or copolymer formed for monomer.
7. aqueous copper gold pigment as described in claim 1, which is characterized in that the disintegrating agent is carboxymethyl cellulose, starch
At least one in glycollate, cross-linked carboxymethyl salt, polyvinylpyrrolidone, crosslinked polyvinylpyrrolidone and alginate
Kind.
8. a kind of preparation method of aqueous copper gold pigment as described in claim 1 comprising following steps:
Step 1: weighing copper gold paste, corrosion inhibiter, organic coating material, dispersing agent and the disintegrating agent in proportion;
Step 2: the corrosion inhibiter being added in the copper gold paste, stir half an hour, be uniformly mixed;
Step 3: the organic coating material and dispersing agent being added in mixture made from step 2 again, stir two hours, cladding is equal
It is even;
Step 4: the disintegrating agent being added in mixture made from step 3, is stirred one hour, is uniformly mixed;
Step 5: by mixed slurry extruding pelletization made from step 4, then being dried in vacuo baking, remove solvent.
9. preparation method as claimed in claim 8, which is characterized in that the solvent is added according to proportion for the copper gold paste
Into the Cu-Zn alloy powder, half an hour is stirred in kneader, becomes the copper gold paste.
10. preparation method as claimed in claim 8, which is characterized in that the mixed slurry is squeezed by screw extruder pelletizer
It is granulated out, the chassis hole diameter of the pelletizer is 3-5mm;The baking temperature is 50-90 DEG C, the vacuum drying baking
Roasting vacuum degree is the kPa of -80kPa~-100.