CN108947323A - Artificial stone straight grain decorative pattern board fabrication method - Google Patents
Artificial stone straight grain decorative pattern board fabrication method Download PDFInfo
- Publication number
- CN108947323A CN108947323A CN201810733115.XA CN201810733115A CN108947323A CN 108947323 A CN108947323 A CN 108947323A CN 201810733115 A CN201810733115 A CN 201810733115A CN 108947323 A CN108947323 A CN 108947323A
- Authority
- CN
- China
- Prior art keywords
- slurry
- auxiliary
- tone
- mass
- color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses artificial stone straight grain decorative pattern board fabrication methods, comprising the following steps: artificial stone straight grain decorative pattern board fabrication method, comprising the following steps: a. first prepares mass-tone slurry；B. after carry out major-minor mill base material preparation after the completion of step a again；C. time auxiliary mill base material preparation is being carried out after the completion of step b；D. in the preparation for carrying out equipment after the completion of step c；E. after the completion of step d, the processing of artificial stone straight grain diamond plate is carried out again, by imitating the color effects that natural straight grain entity plane materiel had both reached natural stone, timber, fire-proof plate in setting, it can accomplish again seamless spliced, and play antibacterial effect, the plate of different batches can be spliced, solve the disadvantage that it is seamless spliced it is difficult, antibacterial effect is poor, color poor continuity, convenient for popularization and use.
Description
Technical field
The present invention relates to artificial slabstone processing method technical fields, specially artificial stone straight grain decorative pattern board fabrication method.
Background technique
Entity plane materiel, scientific name be mineral-filled polymer composite, it be with methyl methacrylate (MMA, also known as
Acryl or unsaturated polyester resin (upr) are matrix, are that pigment and other adjuvants are added in filler by natural ore powder, through pouring
Type casting moulding or vacuum mo(u)lding or the composite material of compression molding.The non-porous homogeneous of the composite material, the composition through whole thickness have
There is homogeneity；The continuous surface for being difficult to discover seam can be made in they, and product surface can be made to reply by maintenance and renovation
As before, manufacturing process is a kind of chemical material reaction process, be generated with the progress of human society science and technology and
It is that a kind of novel environment friendly is multiple that the Practical science material artificial stone also continuously improved, which is mainly used in architectural decoration it,
Condensation material.Compared to traditional construction materials such as stainless steel, ceramics, artificial stone is not only vdiverse in function, various colors, and application range is also more wide
It is general.
Currently, existing artificial solid material plate can cooperate artificial stone to be processed, but in actual use, mesh
Preceding linear decorative pattern mainly embodies in natural stone, timber, fire-proof plate, according to the growth requirement in market, in various decorations
Increasingly it is intended to linear decorative pattern using upper, the problem of natural stone, timber, fire-proof plate, cannot accomplishes seamless spelling
It connects, no antibacterial effect, the continuity of color is not reproducible, these are all physical presence and urgent problem.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the defects of the prior art, provide artificial stone straight grain diamond plate manufacturer
Method had not only reached the color effects of natural stone, timber, fire-proof plate by imitating natural straight grain entity plane materiel in setting, but also can accomplish
Seamless spliced, and play antibacterial effect, the plate of different batches can be spliced, solve it is seamless spliced it is difficult, antibacterial effect is poor,
The shortcomings that poor continuity of color, convenient for promoting the use of.
To solve the above problems, artificial stone straight grain decorative pattern board fabrication method, comprising the following steps:
A. mass-tone slurry is prepared first；
B. after carry out major-minor mill base material preparation after the completion of step a again；
C. time auxiliary mill base material preparation is being carried out after the completion of step b；
D. in the preparation for carrying out equipment after the completion of step c；
E. after the completion of step d, then the processing of artificial stone straight grain diamond plate is carried out.
As a kind of preferred embodiment of the invention, in the step a；Mass-tone slurry be pure acryl resin 35%,
Titanium dioxide slurry 0.4%, carbon black slurry 0.065%, iron oxide red slurry 0.045%, pigment yellow slurry 0.13%, NDM0.13%, EGDMA1.5%,
BYK5150.18%, curing agent 0.1%, aluminium hydroxide 62.45%.
As a kind of preferred embodiment of the invention, in the step b: major-minor mill base material is pure acryl resin
38%, titanium dioxide slurry 0.4%, carbon black slurry 0.12%, paratonere slurry 0.1%, color Huang slurry 0.15%, NDM0.12%,
EGDMA1.1%, BYK5150.13%, curing agent 0.1%, aluminium hydroxide 59.78%.
As a kind of preferred embodiment of the invention, in the step c: secondary auxiliary mill base material is pure acryl resin
37%, titanium dioxide slurry 0.12%, carbon black slurry 0.18%, iron oxide red slurry 0.11%, color Huang slurry 0.18%, NDM0.12%,
EGDMA1.1%, BYK5150.15%, curing agent 0.1%, aluminium hydroxide 60.94%.
As a kind of preferred embodiment of the invention, in the step d: equipment are as follows: mass-tone mashing pump, catalyst pump,
Major ingredient vacuum pump, mass-tone automatic casting machine, auxiliary mill base material pump 2, catalyst pump 2, auxiliary material vacuum pump 1, static mixer 1
Set, 2 cun of wired hoses, 1.5 cun of hoses, mechanical hand 1.
It further include its method for producing in the step e, step includes as a kind of preferred embodiment of the invention
It is as follows；
S1, first by major-minor color be mounted in mixing tube, the left direction normally moved towards towards steel band assembly line, secondary auxiliary color mounted in mixing
Pipe, the right direction normally moved towards towards steel band assembly line, mass-tone, auxiliary mill base material pass through static mixing tube simultaneously, through robot arm,
It is cast on assembly line by required decorative pattern program, prepares mass-tone slurry: prepared mass-tone slurry according to formula, surveyed before production
Examination, viscosity control is at 9-12Pa.S/35 DEG C, and reaction time control is in 14-17min, and 105-115 DEG C of reaction temperature, major-minor mill base
Material: at 5-6.5Pa.S/34-38 DEG C, reaction time control is 105-115 DEG C of reaction temperature, secondary auxiliary in 14-18min for viscosity control
Mill base material: viscosity control is at 5-6.5Pa.S/34-38 DEG C, and reaction time control is in 14-18min, and 105-115 DEG C of reaction temperature；
After S2, step S1, the slurry of two auxiliary colors and mass-tone is prepared by process recipe list requirement, the slurry of auxiliary color is close
Degree is smaller than mass-tone, and auxiliary chromoresin ratio is 2-4% higher than mass-tone resin ratio, tests the parameter of good various major-minor colors, and test is closed
After lattice, pipe laying, auxiliary colour tube is attached slurry pipeline and mixing duct according to the direction of major-minor color and secondary auxiliary color, by formula
It is required that setting the Cast parameters of each auxiliary color；
After S3, step S2, pipeline puts on inner membrance to major ingredient pipeline as requested, respectively connects 5 length of tubing, auxiliary color
Pipeline is put on inner membrance as requested by pipeline, respectively connects mashing pump with 4 stainless steel tubes, steel wire is used behind mashing pump
Hose connection, installs static mixer, static mixer is fixed position on assembly line, static mixing tube two sides connect respectively
Enter two kinds of auxiliary colors, major ingredient pipe is connected with static mixing tube, the mass-tone slurry pipe connected is connected with auxiliary mill base expects pipe
The distance steel band 5cm on robotic arm；
It after S4, step S3, then is poured, casting material temperature control system recalls mechanical hand program at 35-38 DEG C, opens
Mechanical hand, whether inspection machine hand program and speed are normal, and required speed is adjusted according to the thickness and density of decorative pattern, speed
It is more thinner closeer to spend faster decorative pattern, is then turned on mass-tone casting, mass-tone and two auxiliary colors, three colors after opening auxiliary mill base material casting 30s
It comes out, material is taped against in production line by specified program by mechanical hand, line speed is in 1.4- via static mixer
1.6m/min starts the mashing pump, catalyst pump and mixer of auxiliary color, and major-minor color flow is 3kg/min, and secondary auxiliary color flow is
2kg/min starts to start mass-tone when auxiliary mill base material enters mixing tube, and mass-tone flow is 24kg/min, and vacuum degree exists
0.65MPa, opens robotic arm by the program set, and steel band speed 1.48m/min is arranged according to casting amount, checks anti-on line
It is 14min between seasonable；
After S5, step S4, then cutting plate work is carried out, automatic length cutting plate size 3668mm is set as requested, examined
Look into plate it is offline having a size of length 3668mm, width 817mm, with a thickness of 14.7mm；
After S6, step S5, then sanding is carried out, carries out repairing broadside, width 762mm, positive back side sanding, sand as required
With a thickness of 12.35mm after light, inspection appearance finally is being carried out, after color and lines meet the requirements, is carrying out surface coating work.
Compared with prior art, beneficial effects of the present invention are as follows:
Artificial stone straight grain decorative pattern board fabrication method of the present invention had both reached natural by imitating natural straight grain entity plane materiel in setting
Stone, timber, fire-proof plate color effects, and can accomplish seamless spliced, and play antibacterial effect, the plate of different batches can be into
Row splicing, solve the disadvantage that it is seamless spliced it is difficult, antibacterial effect is poor, color poor continuity, convenient for popularization and use.
Specific embodiment
The present invention provides a kind of technical solution: artificial stone straight grain decorative pattern board fabrication method, comprising the following steps:
A. mass-tone slurry is prepared first；
B. after carry out major-minor mill base material preparation after the completion of step a again；
C. time auxiliary mill base material preparation is being carried out after the completion of step b；
D. in the preparation for carrying out equipment after the completion of step c；
E. after the completion of step d, then the processing of artificial stone straight grain diamond plate is carried out.
In the step a；Mass-tone slurry is pure acryl resin 35%, titanium dioxide slurry 0.4%, carbon black slurry 0.065%, iron oxide red
Slurry 0.045%, pigment yellow starch 0.13%, NDM0.13%, EGDMA1.5%, BYK5150.18%, curing agent 0.1%, hydroxide
Aluminium 62.45%.
In the step b: major-minor mill base material is pure acryl resin 38%, titanium dioxide slurry 0.4%, carbon black slurry 0.12%, face
Expect that red slurry 0.1%, color Huang starch 0.15%, NDM0.12%, EGDMA1.1%, BYK5150.13%, curing agent 0.1%, hydrogen-oxygen
Change aluminium 59.78%.
In the step c: secondary auxiliary mill base material is pure acryl resin 37%, titanium dioxide slurry 0.12%, carbon black slurry 0.18%, iron
Red slurry 0.11%, color Huang starch 0.18%, NDM0.12%, EGDMA1.1%, BYK5150.15%, curing agent 0.1%, hydrogen-oxygen
Change aluminium 60.94%.
In the step d: equipment are as follows: mass-tone mashing pump, catalyst pump, major ingredient vacuum pump, mass-tone automatic casting machine, auxiliary color
Mashing pump 2, catalyst pump 2, auxiliary material vacuum pump 1,1 set, 2 cun wired hoses of static mixer, 1.5 cun of hoses, machines
1, hand.
It further include its method for producing in the step e, step includes as follows；
S1, first by major-minor color be mounted in mixing tube, the left direction normally moved towards towards steel band assembly line, secondary auxiliary color mounted in mixing
Pipe, the right direction normally moved towards towards steel band assembly line, mass-tone, auxiliary mill base material pass through static mixing tube simultaneously, through robot arm,
It is cast on assembly line by required decorative pattern program, prepares mass-tone slurry: prepared mass-tone slurry according to formula, surveyed before production
Examination, viscosity control is at 9-12Pa.S/35 DEG C, and reaction time control is in 14-17min, and 105-115 DEG C of reaction temperature, major-minor mill base
Material: at 5-6.5Pa.S/34-38 DEG C, reaction time control is 105-115 DEG C of reaction temperature, secondary auxiliary in 14-18min for viscosity control
Mill base material: viscosity control is at 5-6.5Pa.S/34-38 DEG C, and reaction time control is in 14-18min, and 105-115 DEG C of reaction temperature；
After S2, step S1, the slurry of two auxiliary colors and mass-tone is prepared by process recipe list requirement, the slurry of auxiliary color is close
Degree is smaller than mass-tone, and auxiliary chromoresin ratio is 2-4% higher than mass-tone resin ratio, tests the parameter of good various major-minor colors, and test is closed
After lattice, pipe laying, auxiliary colour tube is attached slurry pipeline and mixing duct according to the direction of major-minor color and secondary auxiliary color, by formula
It is required that setting the Cast parameters of each auxiliary color；
After S3, step S2, pipeline puts on inner membrance to major ingredient pipeline as requested, respectively connects 5 length of tubing, auxiliary color
Pipeline is put on inner membrance as requested by pipeline, respectively connects mashing pump with 4 stainless steel tubes, steel wire is used behind mashing pump
Hose connection, installs static mixer, static mixer is fixed position on assembly line, static mixing tube two sides connect respectively
Enter two kinds of auxiliary colors, major ingredient pipe is connected with static mixing tube, the mass-tone slurry pipe connected is connected with auxiliary mill base expects pipe
The distance steel band 5cm on robotic arm；
It after S4, step S3, then is poured, casting material temperature control system recalls mechanical hand program at 35-38 DEG C, opens
Mechanical hand, whether inspection machine hand program and speed are normal, and required speed is adjusted according to the thickness and density of decorative pattern, speed
It is more thinner closeer to spend faster decorative pattern, is then turned on mass-tone casting, mass-tone and two auxiliary colors, three colors after opening auxiliary mill base material casting 30s
It comes out, material is taped against in production line by specified program by mechanical hand, line speed is in 1.4- via static mixer
1.6m/min starts the mashing pump, catalyst pump and mixer of auxiliary color, and major-minor color flow is 3kg/min, and secondary auxiliary color flow is
2kg/min starts to start mass-tone when auxiliary mill base material enters mixing tube, and mass-tone flow is 24kg/min, and vacuum degree exists
0.65MPa, opens robotic arm by the program set, and steel band speed 1.48m/min is arranged according to casting amount, checks anti-on line
It is 14min between seasonable；
After S5, step S4, then cutting plate work is carried out, automatic length cutting plate size 3668mm is set as requested, examined
Look into plate it is offline having a size of length 3668mm, width 817mm, with a thickness of 14.7mm；
After S6, step S5, then sanding is carried out, carries out repairing broadside, width 762mm, positive back side sanding, sand as required
With a thickness of 12.35mm after light, inspection appearance finally is being carried out, after color and lines meet the requirements, is carrying out surface coating work.
In artificial stone straight grain decorative pattern board fabrication method, both reach day by imitating natural straight grain entity plane materiel in setting first
Right stone, timber, fire-proof plate color effects, and can accomplish seamless spliced, and play antibacterial effect, the plate of different batches can
Spliced, solve the disadvantage that it is seamless spliced it is difficult, antibacterial effect is poor, color poor continuity, convenient for popularization and use.
The artificial stone straight grain decorative pattern board fabrication method now proposed through the invention is often carried out with processing method with certain market
Experimental Comparison, test process are as follows；
1, it after the plate to finished product and on the market is chosen respectively, then carries out assembly and checks, can compare out and splice
Gap.
2, after the plate to finished product and on the market is chosen respectively, after cooperation sterilized solution sterilizes plate face, then into
Row high-temperature sterilization is finally respectively placed the plate after the completion of disinfection, after 36 hours, carries out respectively to the surface of plate
The detection of bacterium.
3, it after the plate to finished product and on the market is chosen respectively, then carries out assembly and checks, decorative pattern can be compared out
Continuity.
Test data is as follows:
Through Experimental comparison, artificial stone straight grain decorative pattern board fabrication method made by the present invention has seamless spliced, antibacterial, face
The strong feature of the continuity of color.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention, for this field skill
For art personnel, it is clear that invention is not limited to the details of the above exemplary embodiments, and without departing substantially from spirit of the invention or
In the case where essential characteristic, the present invention can be realized in other specific forms.Therefore, in all respects, should all incite somebody to action
Embodiment regards exemplary as, and is non-limiting, the scope of the present invention by appended claims rather than on state
Bright restriction, it is intended that including all changes that fall within the meaning and scope of the equivalent elements of the claims in the present invention
It is interior.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, although referring to aforementioned reality
Applying example, invention is explained in detail, for those skilled in the art, still can be to aforementioned each implementation
Technical solution documented by example is modified or equivalent replacement of some of the technical features.It is all in essence of the invention
Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (6)
1. artificial stone straight grain decorative pattern board fabrication method, it is characterised in that: the following steps are included:
A. mass-tone slurry is prepared first；
B. after carry out major-minor mill base material preparation after the completion of step a again；
C. time auxiliary mill base material preparation is being carried out after the completion of step b；
D. in the preparation for carrying out equipment after the completion of step c；
E. after the completion of step d, then the processing of artificial stone straight grain diamond plate is carried out.
2. artificial stone straight grain decorative pattern board fabrication method according to claim 1, it is characterised in that: in the step a；Mass-tone
Slurry is pure acryl resin 35%, titanium dioxide slurry 0.4%, carbon black slurry 0.065%, iron oxide red slurry 0.045%, pigment yellow slurry
0.13%, NDM0.13%, EGDMA1.5%, BYK5150.18%, curing agent 0.1%, aluminium hydroxide 62.45%.
3. artificial stone straight grain decorative pattern board fabrication method according to claim 1, it is characterised in that: in the step b: major-minor
Mill base material is pure acryl resin 38%, titanium dioxide slurry 0.4%, carbon black slurry 0.12%, paratonere slurry 0.1%, color Huang slurry
0.15%, NDM0.12%, EGDMA1.1%, BYK5150.13%, curing agent 0.1%, aluminium hydroxide 59.78%.
4. artificial stone straight grain decorative pattern board fabrication method according to claim 1, it is characterised in that: in the step c: secondary auxiliary
Mill base material is pure acryl resin 37%, titanium dioxide slurry 0.12%, carbon black slurry 0.18%, iron oxide red slurry 0.11%, color Huang slurry
0.18%, NDM0.12%, EGDMA1.1%, BYK5150.15%, curing agent 0.1%, aluminium hydroxide 60.94%.
5. artificial stone straight grain decorative pattern board fabrication method according to claim 1, it is characterised in that: in the step d: equipment
Are as follows: mass-tone mashing pump, catalyst pump, major ingredient vacuum pump, mass-tone automatic casting machine, auxiliary mill base material pump 2, it is catalyst pump 2, auxiliary
Expect vacuum pump 1,1 set, 1 cun wired hose of static mixer, 1.5 cun of hoses, mechanical hand 1.
6. artificial stone straight grain decorative pattern board fabrication method according to claim 1, it is characterised in that: also wrapped in the step e
Its method for producing is included, step includes as follows；
S1, first by major-minor color be mounted in mixing tube, the left direction normally moved towards towards steel band assembly line, secondary auxiliary color be mounted in mixing tube,
The right direction normally moved towards towards steel band assembly line, mass-tone, auxiliary mill base material are passed through static mixing tube simultaneously, through robot arm, are pressed
Required decorative pattern program is cast on assembly line, prepares mass-tone slurry: mass-tone slurry is prepared according to formula, is tested before production,
Viscosity control is at 9-12Pa.S/35 DEG C, and reaction time control is in 14-17min, and 105-115 DEG C of reaction temperature, major-minor mill base material:
Viscosity control is at 5-6.5Pa.S/34-38 DEG C, and reaction time control is in 14-18min, and 105-115 DEG C of reaction temperature, secondary auxiliary mill base
Material: viscosity control is at 5-6.5Pa.S/34-38 DEG C, and reaction time control is in 14-18min, and 105-115 DEG C of reaction temperature；
After S2, step S1, the slurry of two auxiliary colors and mass-tone is prepared by process recipe list requirement, the slurry density of auxiliary color is wanted
Smaller than mass-tone, auxiliary chromoresin ratio is 2-4% higher than mass-tone resin ratio, the parameter of the good various major-minor colors of test, after test passes,
Pipe laying, auxiliary colour tube is attached slurry pipeline and mixing duct according to the direction of major-minor color and secondary auxiliary color, by recipe requirements
Set the Cast parameters of each auxiliary color；
After S3, step S2, pipeline puts on inner membrance to major ingredient pipeline as requested, respectively connects 5 length of tubing, auxiliary colour tube
Pipeline is put on inner membrance as requested by road, respectively connects mashing pump with 4 stainless steel tubes, soft with steel wire behind mashing pump
Pipe connection, installs static mixer, static mixer is fixed position on assembly line, static mixing tube two sides are respectively connected to
Major ingredient pipe is connected with static mixing tube, the mass-tone slurry pipe connected and auxiliary mill base expects pipe is connected to by two kinds of auxiliary colors
Distance steel band 5cm on robotic arm；
It after S4, step S3, then is poured, casting material temperature control system recalls mechanical hand program at 35-38 DEG C, opens machine
Hand, whether inspection machine hand program and speed are normal, and required speed is adjusted according to the thickness and density of decorative pattern, and speed is got over
The thinner fast decorative pattern the closeer, opens and is then turned on mass-tone casting, mass-tone and two auxiliary colors after auxiliary mill base material casting 30s, three colors via
Static mixer comes out, and material is taped against in production line by specified program by mechanical hand, line speed is in 1.4-1.6m/
Min starts the mashing pump, catalyst pump and mixer of auxiliary color, and major-minor color flow is 3kg/min, and secondary auxiliary color flow is 2kg/
Min, starts to start when auxiliary mill base material enters mixing tube mass-tone, and mass-tone flow is 24kg/min, vacuum degree in 0.65MPa,
Robotic arm is opened by the program set, steel band speed 1.48m/min is set according to casting amount, checks that the reaction time is on line
14min；
After S5, step S4, then cutting plate work is carried out, automatic length cutting plate size 3668mm is set as requested, checks plate
Material it is offline having a size of length 3668mm, width 817mm, with a thickness of 14.7mm；
After S6, step S5, then sanding is carried out, carries out repairing broadside, width 762mm, positive back side sanding, after sanding as required
With a thickness of 12.35mm, inspection appearance finally is being carried out, after color and lines meet the requirements, is carrying out surface coating work.