CN108328980A - Combined assembled wallboard of polystyrene and preparation method thereof - Google Patents

Combined assembled wallboard of polystyrene and preparation method thereof Download PDF

Info

Publication number
CN108328980A
CN108328980A CN201810264802.1A CN201810264802A CN108328980A CN 108328980 A CN108328980 A CN 108328980A CN 201810264802 A CN201810264802 A CN 201810264802A CN 108328980 A CN108328980 A CN 108328980A
Authority
CN
China
Prior art keywords
polystyrene
assembled wallboard
combined assembled
mold
combined
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810264802.1A
Other languages
Chinese (zh)
Inventor
高昭宗
蔡菲
吴刚
伍绍溢
涂当悟
田江海
刘远和
王祥
邓华
王玉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shougang Shuicheng Iron And Steel (group) Saide Construction Co Ltd
Original Assignee
Shougang Shuicheng Iron And Steel (group) Saide Construction Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shougang Shuicheng Iron And Steel (group) Saide Construction Co Ltd filed Critical Shougang Shuicheng Iron And Steel (group) Saide Construction Co Ltd
Priority to CN201810264802.1A priority Critical patent/CN108328980A/en
Publication of CN108328980A publication Critical patent/CN108328980A/en
Pending legal-status Critical Current

Abstract

A kind of combined assembled wallboard of polystyrene and preparation method thereof, is related to building material technical field.Per 1m in the combined assembled wallboard of the polystyrene3Including:236 295kg of cement, 44 55kg of flyash, 90 112.5kg of sand, 24 30kg of rubble, polyethylene build 4 5kg of grain, 2.408 3kg of rubber powder, 0.48 0.6kg of cellulose, 200 300kg of 0.96 1.4kg of water-reducing agent, 0.962 1.2kg of short basalt fiber and water.The combined assembled wallboard of polystyrene provided by the invention has many advantages, such as light-weight, insulation, fire-proof sound insulation, convenient transportation, cheap.The present invention also provides the preparation methods of the combined assembled wallboard of above-mentioned polystyrene.

Description

Combined assembled wallboard of polystyrene and preparation method thereof
Technical field
The present invention relates to a kind of building material technical fields, and the combined assembled wallboard of more particularly to a kind of polystyrene and Preparation method.
Background technology
Assembled architecture is built made of assemble in site by prefabricated component component, production fast with construction speed Advantage at low cost has obtained the extensive concern and popularization of people, and domestic assembled architecture technology is also immature at present, still In developing stage, and cost and the not absolute advantage of traditional architecture, the development of assembled architecture industry is seriously hindered, because This, researches and develops and is suitble to the building material of assembled architecture imperative.
The plank of existing assembled architecture wallboard is in the majority with PC concrete panels, uses precast concrete wall panel, passes through Splicing is completed in live big machinery lifting, but existing PC precast concrete wall panels itself are heavy at present, transport difficult, scene Big machinery is needed to allocate and transport, cost is high, cannot meet existing use demand.
Therefore, it is necessary to the assembled wallboards that a kind of light-weight and thermal and insulating performance and fire protecting performance are excellent
Invention content
The purpose of the present invention is to provide a kind of combined assembled wallboard of polystyrene, with light-weight, insulation, Fire-proof sound insulation, convenient transportation, it is cheap the advantages that.
Another object of the present invention is to provide a kind of preparation methods of the combined assembled wallboard of polystyrene, with work The advantages of skill is simple and convenient to operate.
The present invention solves its technical problem using following technical scheme to realize.
A kind of combined assembled wallboard of polystyrene, per 1m3The combined assembled wallboard of polystyrene include:
Further, in a preferred embodiment of the present invention, above-mentioned per 1m3The combined assembled wallboard of polystyrene further include The binder of 2.1-3.7kg.
Further, in a preferred embodiment of the present invention, above-mentioned binder is selected from sodium metasilicate, the poly- ammonia of montmorillonite intercalation At least two in ester, lauryl sodium sulfate.
Further, in a preferred embodiment of the present invention, the granularity of above-mentioned sand is 0.1-0.3mm;Preferably, the grain of rubble Degree is 1-5mm.
Further, in a preferred embodiment of the present invention, the length of above-mentioned short basalt fiber is 3-8cm, a diameter of 25- 65μm。
Further, in a preferred embodiment of the present invention, the granularity of above-mentioned rubber powder is 100-200 mesh.
The present invention also provides the preparation methods of the combined assembled wallboard of above-mentioned polystyrene comprising following steps:
It assembles to obtain mold according to the size shape of required component;
The mesh flake that short basalt fiber interweaves is put into mold;
Cement, flyash, sand, rubble, polyethylene are built grain, rubber powder, cellulose, water-reducing agent and water to be mixed in proportion Composite material is uniformly obtained to be poured into mold, polishing, maintenance, demould.
Further, in a preferred embodiment of the present invention, above-mentioned that short basalt fiber is interweaved to obtain at least three pieces of grids The parallel arranged superposed of piece is in mold.
Further, in a preferred embodiment of the present invention, above-mentioned composite material is poured into mold is added by gluing before Knot agent and water are uniformly mixed obtained viscose glue, stir evenly.
Further, in a preferred embodiment of the present invention, it is above-mentioned poured using plastic film wrapped in maintenance processes after Mold.
The advantageous effect of the combined assembled wallboard of polystyrene of the embodiment of the present invention and preparation method thereof is:The present invention is real It applies in the combined assembled wallboard of polystyrene of example offer per 1m3Including:Cement 236-295kg, flyash 44-55kg, sand 90- 112.5kg, rubble 24-30kg, polyethylene build a 4-5kg, rubber powder 2.408-3kg, cellulose 0.48-0.6kg, water-reducing agent 0.96-1.4kg, short basalt fiber 0.962-1.2kg and water 200-300kg.The compound dress of polystyrene provided by the invention Has many advantages, such as light-weight, insulation, fire-proof sound insulation, convenient transportation, cheap with formula wallboard.The present invention also provides upper The preparation method for stating the combined assembled wallboard of polystyrene assembles to obtain mold, in mold according to the size shape of required component It is inside put into the mesh flake that short basalt fiber interweaves, cement, flyash, sand, rubble, polyethylene are built into grain, rubber powder, fiber Element, water-reducing agent and water be mixed evenly to obtain in proportion composite material be poured into mold, polishing, maintenance, demoulding.The polyphenyl The preparation method of the combined assembled wallboard of ethylene has the advantages that simple for process, easy to operate.
Description of the drawings
In order to illustrate the technical solution of the embodiments of the present invention more clearly, below will be to needed in the embodiment attached Figure is briefly described, it should be understood that the following drawings illustrates only certain embodiments of the present invention, therefore is not construed as pair The restriction of range for those of ordinary skill in the art without creative efforts, can also be according to this A little attached drawings obtain other relevant attached drawings.
Fig. 1 is the schematic diagram of the combined assembled wallboard of polystyrene prepared by the embodiment of the present invention 1;
Fig. 2 is the schematic diagram of the combined assembled wallboard of polystyrene prepared by the embodiment of the present invention 2.
Specific implementation mode
It in order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below will be in the embodiment of the present invention Technical solution be clearly and completely described.The person that is not specified actual conditions in embodiment, builds according to normal condition or manufacturer The condition of view carries out.Reagents or instruments used without specified manufacturer is the conventional production that can be obtained by commercially available purchase Product.
Combined assembled wallboard of the polystyrene of the embodiment of the present invention and preparation method thereof is specifically described below.
An embodiment of the present invention provides a kind of combined assembled wallboards of polystyrene, per 1m3The compound assembly of polystyrene Formula wallboard includes:
Cement 236-295kg, flyash 44-55kg, sand 90-112.5kg, rubble 24-30kg, polyethylene build a 4-5kg, Rubber powder 2.408-3kg, cellulose 0.48-0.6kg, water-reducing agent 0.96-1.4kg, short basalt fiber 0.962-1.2kg and water 200-300kg;Preferably, per 1m3The combined assembled wallboard of polystyrene further include 2.1-3.7kg binder;More preferably , binder in sodium metasilicate, montmorillonite intercalation polyurethane, lauryl sodium sulfate at least two;Preferably, sand Granularity is 0.1-0.3mm;Preferably, the granularity of rubble is 1-5mm;It is further preferred that the length of short basalt fiber is 3- 8cm, a diameter of 25-65 μm;Still more preferably, the granularity of rubber powder is 100-200 mesh.
The combined assembled wallboard of polystyrene provided by the invention has light-weight, insulation, fire-proof sound insulation, transporter Just the advantages that, cheap.The combined assembled wallboard of the polystyrene is made using cement, flyash as base-material, sand and rubble For aggregate, polyethylene builds grain, rubber powder and cellulose makes connection between base-material and aggregate form stable connection bone as modifying agent Frame system, improves the structural strength and flexibility, anti-crack ability of product, and makes it have higher heat insulation and preservation effect, the Black Warrior Rock staple fiber and the binder of selection can further improve the overall construction intensity and toughness of product, ensure that product has There is higher structural strength and toughness under the premise of compared with low weight.
The present invention also provides the preparation methods of the combined assembled wallboard of above-mentioned polystyrene comprising following steps:
It assembles to obtain mold according to the size shape of required component;
The mesh flake that short basalt fiber interweaves is put into mold;Preferably, short basalt fiber is interweaved The arranged superposed parallel at least three pieces of mesh flakes is in mold.
Cement, flyash, sand, rubble, polyethylene are built grain, rubber powder, cellulose, water-reducing agent and water to be mixed in proportion Composite material is uniformly obtained to be poured into mold, polishing, maintenance, demould.Preferably, before composite material being poured into mold It is added and obtained viscose glue is uniformly mixed by binder and water, stir evenly.It is furthermore preferred that using plastic foil packet in maintenance processes Wrap up in the mold after pouring.
The present invention provides the preparation methods of the combined assembled wallboard of polystyrene, prepare wallboard structure needed for first The specific size shape of part is made and assembling obtains mold, and the net to be interweaved by short basalt fiber is then put into mold Cement, flyash, sand, rubble, polyethylene are finally built grain, rubber powder, cellulose, water-reducing agent and water and mixed in proportion and stirred by lattice piece It mixes and uniformly obtains that composite material is poured into mold, polishing, maintenance, demoulding obtain product.The combined assembled wall of the polystyrene The preparation method of plate has the advantages that simple for process, easy to operate, and high, the thermal insulation separation thermal effect with structural strength can be prepared The combined assembled wallboard of the good polystyrene of fruit.
The feature and performance of the present invention are described in further detail with reference to embodiments.
Embodiment 1
A kind of combined assembled wallboard of polystyrene is present embodiments provided, specific preparation method is as follows:
It assembles to obtain mold according to the size shape of required component;
By every 1m3The standard of mold volumes 1.1kg short basalt fibers weighs short basalt fiber, by short basalt fiber Four mesh flakes are woven into, four mesh flakes are put into mold.
By every 1m3There is mold volumes 245kg cement, 45kg flyash, 90kg sand, 26kg rubbles, 4.2kg polyethylene to build The standard of grain, 2.41kg rubber powders, 0.5kg celluloses, 1kg water-reducing agents and 240kg water is mixed evenly to obtain after weighing raw material Composite material is poured into mold, polished, conserved, demoulded, poured using plastic film wrapped in maintenance processes by composite material Mold afterwards, the combined assembled wallboard of polystyrene being prepared are as shown in Figure 1.
Embodiment 2
A kind of combined assembled wallboard of polystyrene is present embodiments provided, specific preparation method is as follows:
It assembles to obtain mold according to the size shape of required component;
By every 1m3The standard of mold volumes 1.2kg short basalt fibers weighs short basalt fiber, by short basalt fiber It is woven into three pieces mesh flake, is put into three pieces mesh flake is parallel in mold.
By every 1m3Mold volumes have 290kg cement, 52kg flyash, 110kg sand, 27kg rubbles, 4.7kg polyethylene Build grain, 2.9kg rubber powders, 0.55kg celluloses, 1.3kg water-reducing agents and 290kg water standard weigh raw material after be mixed evenly Composite material is obtained, composite material is poured into mold, polish, conserve, is demoulded, the compound assembly of the polystyrene being prepared Formula wallboard is as shown in Figure 2.
Embodiment 3
A kind of combined assembled wallboard of polystyrene is present embodiments provided, specific preparation method is as follows:
It assembles to obtain mold according to the size shape of required component;
By every 1m3The standard of mold volumes 0.98kg short basalt fibers weighs short basalt fiber, by the short fibre of basalt Dimension is woven into a piece of mesh flake, and mesh flake is put into mold.
By every 1m3There is mold volumes 280kg cement, 48kg flyash, 95kg sand, 30kg rubbles, 4kg polyethylene to build The standard of grain, 2.5kg rubber powders, 0.6kg celluloses, 1.2kg water-reducing agents and 260kg water is mixed evenly to obtain after weighing raw material 1.1kg sodium metasilicate and 1.1kg lauryl sodium sulfate are incorporated in 20kg water and obtain binder by composite material, and binder is molten Liquid is added in composite material and is uniformly mixed, and is then poured into mold, polishing, maintenance, demoulds.
In conclusion the combined assembled wallboard of polystyrene provided in an embodiment of the present invention have light-weight, insulation, Fire-proof sound insulation, convenient transportation, it is cheap the advantages that.The present invention also provides the systems of the combined assembled wallboard of above-mentioned polystyrene Preparation Method has the advantages that simple for process, easy to operate.
Embodiments described above is a part of the embodiment of the present invention, instead of all the embodiments.The reality of the present invention The detailed description for applying example is not intended to limit the range of claimed invention, but is merely representative of the selected implementation of the present invention Example.Based on the embodiments of the present invention, those of ordinary skill in the art are obtained without creative efforts Every other embodiment, shall fall within the protection scope of the present invention.

Claims (10)

1. a kind of combined assembled wallboard of polystyrene, which is characterized in that per 1m3The combined assembled wallboard of polystyrene include:
2. the combined assembled wallboard of polystyrene according to claim 1, which is characterized in that per 1m3Polystyrene it is compound Assembled wallboard further includes the binder of 2.1-3.7kg.
3. the combined assembled wallboard of polystyrene according to claim 2, which is characterized in that the binder is selected from silicon At least two in sour sodium, montmorillonite intercalation polyurethane, lauryl sodium sulfate.
4. the combined assembled wallboard of polystyrene according to claim 1, which is characterized in that the granularity of the sand is 0.1- 0.3mm;Preferably, the granularity of the rubble is 1-5mm.
5. the combined assembled wallboard of polystyrene according to claim 1, which is characterized in that the short basalt fiber Length is 3-8cm, a diameter of 25-65 μm.
6. the combined assembled wallboard of polystyrene according to claim 1, which is characterized in that the granularity of the rubber powder is 100-200 mesh.
7. the preparation method of the combined assembled wallboard of polystyrene as described in any one of claim 1-6, which is characterized in that It includes the following steps:
It assembles to obtain mold according to the size shape of required component;
It is put into the mesh flake that short basalt fiber interweaves in the mould;
Cement, flyash, sand, rubble, polyethylene are built grain, rubber powder, cellulose, water-reducing agent and water to be mixed evenly in proportion Composite material is obtained to be poured into mold, polishing, maintenance, demould.
8. the preparation method of the combined assembled wallboard of polystyrene according to claim 7, which is characterized in that will be described profound Military rock staple fiber interweaves to obtain arranged superposed that at least three pieces of mesh flakes are parallel in the mold.
9. the preparation method of the combined assembled wallboard of polystyrene according to claim 7, which is characterized in that will be described multiple Condensation material is added before being poured into the mold and is uniformly mixed obtained viscose glue by binder and water, stirs evenly.
10. the preparation method of the combined assembled wallboard of polystyrene according to claim 7, which is characterized in that described Mold after being poured using plastic film wrapped in maintenance processes.
CN201810264802.1A 2018-03-28 2018-03-28 Combined assembled wallboard of polystyrene and preparation method thereof Pending CN108328980A (en)