CN108929046A - A kind of glass fungus-proof insulating powder - Google Patents
A kind of glass fungus-proof insulating powder Download PDFInfo
- Publication number
- CN108929046A CN108929046A CN201810446115.1A CN201810446115A CN108929046A CN 108929046 A CN108929046 A CN 108929046A CN 201810446115 A CN201810446115 A CN 201810446115A CN 108929046 A CN108929046 A CN 108929046A
- Authority
- CN
- China
- Prior art keywords
- powder
- glass
- proof insulating
- fungus
- insulating powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of glass fungus-proof insulating powder, the component containing following parts by weight：Wood powder 40~50, acrylic resin 5~10, adipic acid powder 40~50, superfine silica gel powder 0.05~0.5.Cohesiveness is low in powder of the invention, favorable dispersibility, has good mobile performance, and easy sprinkling is dispersed on plate glass, in cleaning, is cleaned using soft hairbrush or makes to be rinsed with water, can cleaned out；Chemical composition and particle in mould proof glass powder can play the role of good buffer action and fungus-resistant to plate glass, and the formula materials environmental protection used is easy to get, and degradable or recoverable is environmentally friendly, have the characteristics that high efficiency.
Description
Technical field
The invention belongs to technical field of fine, and in particular to a kind of glass fungus-proof insulating powder.
Background technique
Weathering of Flat glass is the problem that many glass manufacture enterprises are frequently run onto, and in storage and is one general in transit
All over existing problem.Weathering of glass refer to glass in air environment, surface contacted with substances such as moisture in atmosphere and by
It corrodes and the phenomenon that rainbow trace, hickie or spray occurs.Weathering of glass will affect the service performance of glass, such as reduce glass
Transparency, influence optical property, reduce mechanical strength, influencing the problems such as appearance and can also make to stack when mouldy degree is more serious
Glass there is the phenomenon that bonding die, the glass as optical mirror slip or plated film then becomes waste product, cannot carry out deep processing again.
It is generallyd use at present in the surface of plate glass sprinkling fungus-proof insulating powder or mould proof insulating liquid to protect plate glass,
Compared with traditional barrier paper method, fungus-proof insulating powder has the advantages that at low cost, effective and environmentally friendly.And existing mould proof isolation
Powder generally use acid with particle be isolated be mixed, this powder fluidity is poor, is unevenly distributed, and be difficult to clean after
Thoroughly, it needs to require efforts to be handled, it is difficult to reach the requirement of glass cleaning.
Summary of the invention
In order to solve the above technical problems, the present invention provides a kind of glass fungus-proof insulating powder, there is antimildew and antibacterial, flowing dispersion
The good and easy to clean feature of property.
The technical scheme adopted by the invention to achieve the purpose is as follows：
A kind of glass fungus-proof insulating powder, the component containing following parts by weight：
It further illustrates, the acrylic resin is polymethyl methacrylate bead particles, has some strength
And transparency, rounded, uniform particle sizes, particle diameter distribution are 100~150 microns, polymethyl methacrylate bead particles surface
Static electrification, being capable of adsorbed water molecule.
It further illustrates, the superfine silica gel powder is silicon-dioxide powdery, and particle diameter distribution is 13~18 microns.
It further illustrates, the particle diameter distribution of the wood powder is 74~250 microns, the partial size point of the adipic acid powder
Cloth is 74~100 microns.
In the present invention, basic recipe of the wood powder that selection particle diameter distribution is 74~250 microns as glass fungus-proof insulating powder,
Wherein playing the role of isolation mainly as isolation particle, while wood powder has easily drop as natural macromolecular material particles
Solution, easily obtain, harmless, no pollution to the environment the characteristics of, be a kind of material of environmental protection.Since wood powder sheet is as natural height
Molecular material selects the adipic acid powder that particle diameter distribution is 74~100 microns as mould proof in formula vulnerable to microorganism decomposition
Organic acid portion in insulating powder, the carboxylic group of adipic acid are hydrophilic radical, adsorption moisture and can be formed with water acid molten
Liquid, to inhibit microbial growth, can effective protection wood powder, while the carbon chain moiety of adipic acid is hydrophobic group, makes hydrone
It not easily passs through powder inwardly to spread, using the adipic acid powder for the parts by weight for being similar to wood powder, plays antibacterial and mouldproof.
In the present invention, the polymethyl methacrylate microballon for being 100~150 microns added with a small amount of particle diameter distribution
Grain, which has micro electrostatic, and partial size is larger, can be effectively reduced in fungus-proof insulating powder between minuteness particle
Adhesive force, electrostatic effect, keep the dispersibility of fungus-proof insulating powder more preferable and be less prone to dust raising phenomenon；The bead particles can inhale
Attached water molecule has some strength to keep the drying of fungus-proof insulating powder in itself, also plays buffer action as isolation particle.
In the present invention, the superfine silica gel powder for being 13~18 microns added with micro particle diameter distribution is used as flow improver additive,
The particle flow performance that fungus-proof insulating powder can effectively be improved enables fungus-proof insulating powder to be distributed glibly in plate glass.
Compared with prior art, the beneficial effects of the present invention are：
1, the powder granule partial size of fungus-proof insulating powder is approximate, and interior cohesiveness is low, favorable dispersibility, has good mobility
Can, easy sprinkling is dispersed on plate glass, in cleaning, is cleaned using soft hairbrush or is made to be rinsed with water, can cleared up
Completely.
2, the chemical composition and particle in mould proof glass powder can play good buffer action and be prevented to plate glass
Mould bacteriostasis.
3, the formula materials environmental protection used is easy to get, and degradable or recoverable is environmentally friendly, with high efficiency
Feature.
Specific embodiment
In order to further understand the content, features and effects of the present invention, hereby enumerating following embodiment explanation.
In the present embodiment, component is with proportional quantity (parts by weight)：Wood powder 44.5 (partial size 74~250 microns >=60%), oneself
Diacid powder 50 (particle diameter distribution is 74~100 microns), (particle diameter distribution is 100~150 micron 100~150 to acrylic resin 5
Micron), superfine silica gel powder 0.5 (particle diameter distribution is 13~18 microns).
Preparation method：
1, adipic acid powder is dried 2 hours in 75 DEG C of environment；
2, it is uniformly mixed after superfine silica gel powder is added in the powder obtained by the first step；
3, acrylic resin is added in the powder obtained by second step, is uniformly mixed；
4, wood powder is added in the powder obtained by third step, is uniformly mixed, cross 80 mesh screens；
5, plate glass special mildewproof isolation powder is obtained.
In embodiment gained fungus-proof insulating powder performance test and use parameter, the results are shown in Table 1.
The performance test results of 1 fungus-proof insulating powder of table and use parameter
The above is only the preferred embodiments of the present invention, and is not intended to limit the present invention in any form,
Any simple modification made to the above embodiment according to the technical essence of the invention, equivalent variations and modification, belong to
The range of technical solution of the present invention.
Claims (4)
1. a kind of glass fungus-proof insulating powder, which is characterized in that the component containing following parts by weight：
2. a kind of glass fungus-proof insulating powder according to claim 1, it is characterised in that：The acrylic resin is poly- methyl
Methyl acrylate bead particles, have some strength and transparency, rounded, uniform particle sizes, and particle diameter distribution is 100~150 micro-
Rice, polymethyl methacrylate bead particles surface static electrification being capable of adsorbed water molecule.
3. a kind of glass fungus-proof insulating powder according to claim 1, it is characterised in that：The superfine silica gel powder is silica
Powder, partial size are 13~18 microns.
4. a kind of glass fungus-proof insulating powder according to claim 1, it is characterised in that：The particle diameter distribution of the wood powder is 74
~250 microns, the particle diameter distribution of the adipic acid powder is 74~100 microns.