CN108912778A - 一种用于保温墙的保温涂料及其制备方法 - Google Patents
一种用于保温墙的保温涂料及其制备方法 Download PDFInfo
- Publication number
- CN108912778A CN108912778A CN201810790509.9A CN201810790509A CN108912778A CN 108912778 A CN108912778 A CN 108912778A CN 201810790509 A CN201810790509 A CN 201810790509A CN 108912778 A CN108912778 A CN 108912778A
- Authority
- CN
- China
- Prior art keywords
- parts
- thermal insulation
- insulated wall
- insulation coatings
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种用于保温墙的保温涂料，包括以下重量份的原料：水性丙烯酸树脂15～30份、乙烯基酯树脂20～30份、N‑羟甲基丙烯酰胺4～8份、碳化硅6～9份、木质素3～6份、聚丙烯腈4～7份、顺丁烯二酸二异辛酯2～5份、空心玻璃微珠4～6份、氧化铝气凝胶改性珍珠岩5～10份、改性硅藻土6～9份、分散剂2～4份、消泡剂1～3份、增稠剂3～5份及去离子水30～40份。本发明所述用于保温墙的保温涂料导热系数低、隔热保温效果好，抗裂性能好，耐老化性能优，性能稳定，阻燃性好。
Description
技术领域
本发明属于保温涂料技术领域，具体涉及一种用于保温墙的保温涂料及其制备方法。
背景技术
目前我国普遍采用的采暖方式主要为散热器对流采暖模式，如地暖、暖气片等，红外电热膜等辐射采暖系统由于热量分布更加均匀，对人体及其他物体热作用效率更高，正在逐步普及。室内热量传导方式主要为辐射和对流，不论采用对流采暖还是辐射采暖，热辐射在室内热量作用占据重要地位，当热辐射到达墙体表面会被就会被墙体吸收，从而流失至室外。
冬季采暖能耗是中国建筑的主要能耗，中国政府对建筑节能的要求不断提高。为了体现用热公平，摆脱效率低下的集中供热习惯，对于新建建筑和既有建筑的节能改造项目都已实施分户热计量的节能做法。但是，目前的建筑节能保温措施只针对建筑的外围护结构，建筑内的房屋隔墙之间普遍没有采用保温措施，这样不同房屋之间可能是不同的温度，从而产生热压，温度高的房间会出现热流失现象，即热量从温度高的房间向温度低的房间流动。这种用热的不公平现象容易引发各种问题和矛盾，如住户中的热量散失较严重，使得邻居之间用热不均，导致不公平的现象，而且具有较高的建筑能耗，从而影响了我国建筑节能政策的推广。
授权公告号CN103013262B的发明提供了一种内墙保温涂料，包括以下重量份的组分：5份~45份的水；3份~25份的助剂；3份~55份的无机填料；5份~55份的涂料树脂；1份~30份的折射率为2.0以上、粒径不小于1μm的红外反射颜料。但是所述内墙保温涂料效果不佳。
发明内容
本发明提供了一种用于保温墙的保温涂料及其制备方法，解决了背景技术中的问题，本发明所述用于保温墙的保温涂料导热系数低、隔热保温效果好，抗裂性能好，耐老化性能优，性能稳定，阻燃性好。
为了解决现有技术存在的问题，采用如下技术方案：
一种用于保温墙的保温涂料，包括以下重量份的原料：水性丙烯酸树脂15～30份、乙烯基酯树脂20～30份、N-羟甲基丙烯酰胺4～8份、碳化硅6～9份、木质素3～6份、聚丙烯腈4～7份、顺丁烯二酸二异辛酯2～5份、空心玻璃微珠4～6份、氧化铝气凝胶改性珍珠岩5～10份、改性硅藻土6～9份、分散剂2～4份、消泡剂1～3份、增稠剂3～5份及去离子水30～40份。
优选的，所述用于保温墙的保温涂料，包括以下重量份的原料：水性丙烯酸树脂20～25份、乙烯基酯树脂23～28份、N-羟甲基丙烯酰胺5～7份、碳化硅7～8份、木质素4～5份、聚丙烯腈5～6份、顺丁烯二酸二异辛酯3～4份、空心玻璃微珠4.3～5.2份、氧化铝气凝胶改性珍珠岩6～8份、改性硅藻土7～8份、分散剂2.5～3.3份、消泡剂1.5～2.5份、增稠剂3.6～4.4份及去离子水31～39份。
优选的，所述用于保温墙的保温涂料，包括以下重量份的原料：水性丙烯酸树脂23份、乙烯基酯树脂25份、N-羟甲基丙烯酰胺6份、碳化硅7.8份、木质素4.2份、聚丙烯腈5.4份、顺丁烯二酸二异辛酯3.3份、空心玻璃微珠4.9份、氧化铝气凝胶改性珍珠岩7份、改性硅藻土7.2份、分散剂3.1份、消泡剂2份、增稠剂3.9份及去离子水35份。
优选的，所述氧化铝气凝胶改性珍珠岩的制备方法如下：
将膨胀珍珠岩浸泡于事先制备好的氧化铝气凝胶中，采用真空浸渍吸附工艺，使氧化铝气凝胶吸入膨胀珍珠岩空腔内，待老化后，通过常压分级干燥、憎水处理形成氧化铝气凝胶改性珍珠岩。
优选的，所述改性硅藻土的制备方法如下：
先将硅藻土在温度为480～520℃下煅烧1～2h，冷却后，球磨过100～200目筛，然后于8～10%的乙酸溶液中浸泡2～4h后，取出，去离子水洗涤至中性，加入相当于硅藻粉重量2～4%的山梨坦单油酸酯，混匀后，烘干，研磨成纳米粉末，即得。
优选的，所述消泡剂为缩水山梨糖醇月桂酸三脂或聚丙二醇。
优选的，所述分散剂为六偏磷酸钠类润湿剂。
优选的，所述增稠剂为羟乙基纤维素。
一种制备所述用于保温墙的保温涂料的方法，包括以下步骤：
（1）按上述配方称取水性丙烯酸树脂、乙烯基酯树脂、N-羟甲基丙烯酰胺、碳化硅、木质素、聚丙烯腈、顺丁烯二酸二异辛酯、空心玻璃微珠、氧化铝气凝胶改性珍珠岩、改性硅藻土、分散剂、消泡剂、增稠剂及去离子水，备用；
（2）将分散剂和去离子水置于反应釜中搅拌混合均匀，然后加入改性硅藻土、碳化硅、木质素、聚丙烯腈，高速分散均匀，得混合物A；
（3）向步骤（2）所得的混合物A中加入水性丙烯酸树脂、乙烯基酯树脂、N-羟甲基丙烯酰胺及顺丁烯二酸二异辛酯，升温至70℃，先微波处理，再高速分散均匀，得混合物B；
（4）将空心玻璃微珠、氧化铝气凝胶改性珍珠加入至步骤（3）所得的混合物B中，搅拌均匀，然后加入消泡剂和增稠剂，搅拌均匀，即得所述用于保温墙的保温涂料。
优选的，所述步骤（3）中微波处理的时间为10～15分钟。
本发明与现有技术相比，其具有以下有益效果：
本发明所述用于保温墙的保温涂料导热系数低、隔热保温效果好，抗裂性能好，耐老化性能优，性能稳定，阻燃性好，具体如下：
（1）本发明采用水性丙烯酸树脂、乙烯基酯树脂、N-羟甲基丙烯酰胺、碳化硅、木质素、聚丙烯腈、顺丁烯二酸二异辛酯、空心玻璃微珠、氧化铝气凝胶改性珍珠岩、改性硅藻土、分散剂、消泡剂、增稠剂及去离子水作为原料，水性丙烯酸树脂具有良好的物理、化学性能，它对金属和非金属材料的表面具有优异的粘接强度，介电性能良好，变定收缩率小，制品尺寸稳定性好，硬度高，柔韧性较好，对碱及大部分溶剂稳定且起防腐作用；水性丙烯酸树脂与其他原料协同作用，可以实现在被涂覆基材表面有效提高涂层漆膜的连整性、耐水性和耐沾污性，效果明显优于普通的涂料；
（2）本发明在原料中添加了氧化铝气凝胶改性珍珠岩，经氧化铝气凝胶改性的珍珠岩性能更优，保温性能更好，更有利于提高产品的综合性能。
具体实施方式
下面结合具体实施例，进一步阐述本发明。这些实施例仅用于说明本发明而不用于限制本发明的范围。
实施例1
本实施例涉及一种用于保温墙的保温涂料，包括以下重量份的原料：水性丙烯酸树脂15份、乙烯基酯树脂20份、N-羟甲基丙烯酰胺4份、碳化硅6份、木质素3份、聚丙烯腈4份、顺丁烯二酸二异辛酯2份、空心玻璃微珠4份、氧化铝气凝胶改性珍珠岩5份、改性硅藻土6份、分散剂2份、消泡剂1份、增稠剂3份及去离子水30份。
其中，所述氧化铝气凝胶改性珍珠岩的制备方法如下：
将膨胀珍珠岩浸泡于事先制备好的氧化铝气凝胶中，采用真空浸渍吸附工艺，使氧化铝气凝胶吸入膨胀珍珠岩空腔内，待老化后，通过常压分级干燥、憎水处理形成氧化铝气凝胶改性珍珠岩。
其中，所述改性硅藻土的制备方法如下：
先将硅藻土在温度为480℃下煅烧1h，冷却后，球磨过100～200目筛，然后于8%的乙酸溶液中浸泡2h后，取出，去离子水洗涤至中性，加入相当于硅藻粉重量2%的山梨坦单油酸酯，混匀后，烘干，研磨成纳米粉末，即得。
其中，所述消泡剂为缩水山梨糖醇月桂酸三脂。
其中，所述分散剂为六偏磷酸钠类润湿剂。
其中，所述增稠剂为羟乙基纤维素。
一种制备所述用于保温墙的保温涂料的方法，包括以下步骤：
（1）按上述配方称取水性丙烯酸树脂、乙烯基酯树脂、N-羟甲基丙烯酰胺、碳化硅、木质素、聚丙烯腈、顺丁烯二酸二异辛酯、空心玻璃微珠、氧化铝气凝胶改性珍珠岩、改性硅藻土、分散剂、消泡剂、增稠剂及去离子水，备用；
（2）将分散剂和去离子水置于反应釜中搅拌混合均匀，然后加入改性硅藻土、碳化硅、木质素、聚丙烯腈，高速分散均匀，得混合物A；
（3）向步骤（2）所得的混合物A中加入水性丙烯酸树脂、乙烯基酯树脂、N-羟甲基丙烯酰胺及顺丁烯二酸二异辛酯，升温至70℃，先微波处理，再高速分散均匀，得混合物B；
（4）将空心玻璃微珠、氧化铝气凝胶改性珍珠加入至步骤（3）所得的混合物B中，搅拌均匀，然后加入消泡剂和增稠剂，搅拌均匀，即得所述用于保温墙的保温涂料。
其中，所述步骤（3）中微波处理的时间为10分钟。
实施例2
本实施例涉及一种用于保温墙的保温涂料，包括以下重量份的原料：水性丙烯酸树脂30份、乙烯基酯树脂30份、N-羟甲基丙烯酰胺8份、碳化硅9份、木质素6份、聚丙烯腈7份、顺丁烯二酸二异辛酯5份、空心玻璃微珠6份、氧化铝气凝胶改性珍珠岩10份、改性硅藻土9份、分散剂4份、消泡剂3份、增稠剂5份及去离子水40份。
其中，所述氧化铝气凝胶改性珍珠岩的制备方法如下：
将膨胀珍珠岩浸泡于事先制备好的氧化铝气凝胶中，采用真空浸渍吸附工艺，使氧化铝气凝胶吸入膨胀珍珠岩空腔内，待老化后，通过常压分级干燥、憎水处理形成氧化铝气凝胶改性珍珠岩。
其中，所述改性硅藻土的制备方法如下：
先将硅藻土在温度为520℃下煅烧2h，冷却后，球磨过100～200目筛，然后于10%的乙酸溶液中浸泡4h后，取出，去离子水洗涤至中性，加入相当于硅藻粉重量4%的山梨坦单油酸酯，混匀后，烘干，研磨成纳米粉末，即得。
其中，所述消泡剂为聚丙二醇。
其中，所述分散剂为六偏磷酸钠类润湿剂。
其中，所述增稠剂为羟乙基纤维素。
一种制备所述用于保温墙的保温涂料的方法，包括以下步骤：
（1）按上述配方称取水性丙烯酸树脂、乙烯基酯树脂、N-羟甲基丙烯酰胺、碳化硅、木质素、聚丙烯腈、顺丁烯二酸二异辛酯、空心玻璃微珠、氧化铝气凝胶改性珍珠岩、改性硅藻土、分散剂、消泡剂、增稠剂及去离子水，备用；
（2）将分散剂和去离子水置于反应釜中搅拌混合均匀，然后加入改性硅藻土、碳化硅、木质素、聚丙烯腈，高速分散均匀，得混合物A；
（3）向步骤（2）所得的混合物A中加入水性丙烯酸树脂、乙烯基酯树脂、N-羟甲基丙烯酰胺及顺丁烯二酸二异辛酯，升温至70℃，先微波处理，再高速分散均匀，得混合物B；
（4）将空心玻璃微珠、氧化铝气凝胶改性珍珠加入至步骤（3）所得的混合物B中，搅拌均匀，然后加入消泡剂和增稠剂，搅拌均匀，即得所述用于保温墙的保温涂料。
其中，所述步骤（3）中微波处理的时间为15分钟。
实施例3
本实施例涉及一种用于保温墙的保温涂料，包括以下重量份的原料：水性丙烯酸树脂20份、乙烯基酯树脂23份、N-羟甲基丙烯酰胺5份、碳化硅7份、木质素4份、聚丙烯腈5份、顺丁烯二酸二异辛酯3份、空心玻璃微珠4.3份、氧化铝气凝胶改性珍珠岩6份、改性硅藻土7份、分散剂2.5份、消泡剂1.5份、增稠剂3.6份及去离子水31份。
其中，所述氧化铝气凝胶改性珍珠岩的制备方法如下：
将膨胀珍珠岩浸泡于事先制备好的氧化铝气凝胶中，采用真空浸渍吸附工艺，使氧化铝气凝胶吸入膨胀珍珠岩空腔内，待老化后，通过常压分级干燥、憎水处理形成氧化铝气凝胶改性珍珠岩。
其中，所述改性硅藻土的制备方法如下：
先将硅藻土在温度为490℃下煅烧1.5h，冷却后，球磨过100～200目筛，然后于9%的乙酸溶液中浸泡3h后，取出，去离子水洗涤至中性，加入相当于硅藻粉重量3%的山梨坦单油酸酯，混匀后，烘干，研磨成纳米粉末，即得。
其中，所述消泡剂为聚丙二醇。
其中，所述分散剂为六偏磷酸钠类润湿剂。
其中，所述增稠剂为羟乙基纤维素。
一种制备所述用于保温墙的保温涂料的方法，包括以下步骤：
（1）按上述配方称取水性丙烯酸树脂、乙烯基酯树脂、N-羟甲基丙烯酰胺、碳化硅、木质素、聚丙烯腈、顺丁烯二酸二异辛酯、空心玻璃微珠、氧化铝气凝胶改性珍珠岩、改性硅藻土、分散剂、消泡剂、增稠剂及去离子水，备用；
（2）将分散剂和去离子水置于反应釜中搅拌混合均匀，然后加入改性硅藻土、碳化硅、木质素、聚丙烯腈，高速分散均匀，得混合物A；
（3）向步骤（2）所得的混合物A中加入水性丙烯酸树脂、乙烯基酯树脂、N-羟甲基丙烯酰胺及顺丁烯二酸二异辛酯，升温至70℃，先微波处理，再高速分散均匀，得混合物B；
（4）将空心玻璃微珠、氧化铝气凝胶改性珍珠加入至步骤（3）所得的混合物B中，搅拌均匀，然后加入消泡剂和增稠剂，搅拌均匀，即得所述用于保温墙的保温涂料。
其中，所述步骤（3）中微波处理的时间为13分钟。
实施例4
本实施例涉及一种用于保温墙的保温涂料，包括以下重量份的原料：水性丙烯酸树脂25份、乙烯基酯树脂28份、N-羟甲基丙烯酰胺7份、碳化硅8份、木质素5份、聚丙烯腈6份、顺丁烯二酸二异辛酯4份、空心玻璃微珠5.2份、氧化铝气凝胶改性珍珠岩8份、改性硅藻土8份、分散剂3.3份、消泡剂2.5份、增稠剂4.4份及去离子水39份。
其中，所述氧化铝气凝胶改性珍珠岩的制备方法如下：
将膨胀珍珠岩浸泡于事先制备好的氧化铝气凝胶中，采用真空浸渍吸附工艺，使氧化铝气凝胶吸入膨胀珍珠岩空腔内，待老化后，通过常压分级干燥、憎水处理形成氧化铝气凝胶改性珍珠岩。
其中，所述改性硅藻土的制备方法如下：
先将硅藻土在温度为500℃下煅烧1.5h，冷却后，球磨过100～200目筛，然后于9%的乙酸溶液中浸泡3h后，取出，去离子水洗涤至中性，加入相当于硅藻粉重量3%的山梨坦单油酸酯，混匀后，烘干，研磨成纳米粉末，即得。
其中，所述消泡剂为缩水山梨糖醇月桂酸三脂。
其中，所述分散剂为六偏磷酸钠类润湿剂。
其中，所述增稠剂为羟乙基纤维素。
一种制备所述用于保温墙的保温涂料的方法，包括以下步骤：
（1）按上述配方称取水性丙烯酸树脂、乙烯基酯树脂、N-羟甲基丙烯酰胺、碳化硅、木质素、聚丙烯腈、顺丁烯二酸二异辛酯、空心玻璃微珠、氧化铝气凝胶改性珍珠岩、改性硅藻土、分散剂、消泡剂、增稠剂及去离子水，备用；
（2）将分散剂和去离子水置于反应釜中搅拌混合均匀，然后加入改性硅藻土、碳化硅、木质素、聚丙烯腈，高速分散均匀，得混合物A；
（3）向步骤（2）所得的混合物A中加入水性丙烯酸树脂、乙烯基酯树脂、N-羟甲基丙烯酰胺及顺丁烯二酸二异辛酯，升温至70℃，先微波处理，再高速分散均匀，得混合物B；
（4）将空心玻璃微珠、氧化铝气凝胶改性珍珠加入至步骤（3）所得的混合物B中，搅拌均匀，然后加入消泡剂和增稠剂，搅拌均匀，即得所述用于保温墙的保温涂料。
其中，所述步骤（3）中微波处理的时间为13分钟。
实施例5
本实施例涉及一种用于保温墙的保温涂料，包括以下重量份的原料：水性丙烯酸树脂23份、乙烯基酯树脂25份、N-羟甲基丙烯酰胺6份、碳化硅7.8份、木质素4.2份、聚丙烯腈5.4份、顺丁烯二酸二异辛酯3.3份、空心玻璃微珠4.9份、氧化铝气凝胶改性珍珠岩7份、改性硅藻土7.2份、分散剂3.1份、消泡剂2份、增稠剂3.9份及去离子水35份。
其中，所述氧化铝气凝胶改性珍珠岩的制备方法如下：
将膨胀珍珠岩浸泡于事先制备好的氧化铝气凝胶中，采用真空浸渍吸附工艺，使氧化铝气凝胶吸入膨胀珍珠岩空腔内，待老化后，通过常压分级干燥、憎水处理形成氧化铝气凝胶改性珍珠岩。
其中，所述改性硅藻土的制备方法如下：
先将硅藻土在温度为500℃下煅烧1.5h，冷却后，球磨过100～200目筛，然后于9%的乙酸溶液中浸泡3h后，取出，去离子水洗涤至中性，加入相当于硅藻粉重量3%的山梨坦单油酸酯，混匀后，烘干，研磨成纳米粉末，即得。
其中，所述消泡剂为缩水山梨糖醇月桂酸三脂。
其中，所述分散剂为六偏磷酸钠类润湿剂。
其中，所述增稠剂为羟乙基纤维素。
一种制备所述用于保温墙的保温涂料的方法，包括以下步骤：
（1）按上述配方称取水性丙烯酸树脂、乙烯基酯树脂、N-羟甲基丙烯酰胺、碳化硅、木质素、聚丙烯腈、顺丁烯二酸二异辛酯、空心玻璃微珠、氧化铝气凝胶改性珍珠岩、改性硅藻土、分散剂、消泡剂、增稠剂及去离子水，备用；
（2）将分散剂和去离子水置于反应釜中搅拌混合均匀，然后加入改性硅藻土、碳化硅、木质素、聚丙烯腈，高速分散均匀，得混合物A；
（3）向步骤（2）所得的混合物A中加入水性丙烯酸树脂、乙烯基酯树脂、N-羟甲基丙烯酰胺及顺丁烯二酸二异辛酯，升温至70℃，先微波处理，再高速分散均匀，得混合物B；
（4）将空心玻璃微珠、氧化铝气凝胶改性珍珠加入至步骤（3）所得的混合物B中，搅拌均匀，然后加入消泡剂和增稠剂，搅拌均匀，即得所述用于保温墙的保温涂料。
其中，所述步骤（3）中微波处理的时间为13分钟。
对比例
授权公告号CN103013262B的发明提供的一种内墙保温涂料。
按照同样的国家标准分别对实施例1～5、对比例中的保温涂料进行性能测试，测试结果如下表：
从上表可以看出，本发明所述的保温涂料性能优于对比例。
本发明所述用于保温墙的保温涂料导热系数低、隔热保温效果好，抗裂性能好，耐老化性能优，性能稳定，阻燃性好，具体如下：
（1）本发明采用水性丙烯酸树脂、乙烯基酯树脂、N-羟甲基丙烯酰胺、碳化硅、木质素、聚丙烯腈、顺丁烯二酸二异辛酯、空心玻璃微珠、氧化铝气凝胶改性珍珠岩、改性硅藻土、分散剂、消泡剂、增稠剂及去离子水作为原料，水性丙烯酸树脂具有良好的物理、化学性能，它对金属和非金属材料的表面具有优异的粘接强度，介电性能良好，变定收缩率小，制品尺寸稳定性好，硬度高，柔韧性较好，对碱及大部分溶剂稳定且起防腐作用；水性丙烯酸树脂与其他原料协同作用，可以实现在被涂覆基材表面有效提高涂层漆膜的连整性、耐水性和耐沾污性，效果明显优于普通的涂料；
（2）本发明在原料中添加了氧化铝气凝胶改性珍珠岩，经氧化铝气凝胶改性的珍珠岩性能更优，保温性能更好，更有利于提高产品的综合性能。
以上对本发明的具体实施例进行了描述。需要理解的是，本发明并不局限于上述特定实施方式，本领域技术人员可以在权利要求的范围内做出各种变形或修改，这并不影响本发明的实质内容。
Claims (10)
1.一种用于保温墙的保温涂料，其特征在于，包括以下重量份的原料：水性丙烯酸树脂15～30份、乙烯基酯树脂20～30份、N-羟甲基丙烯酰胺4～8份、碳化硅6～9份、木质素3～6份、聚丙烯腈4～7份、顺丁烯二酸二异辛酯2～5份、空心玻璃微珠4～6份、氧化铝气凝胶改性珍珠岩5～10份、改性硅藻土6～9份、分散剂2～4份、消泡剂1～3份、增稠剂3～5份及去离子水30～40份。
2.根据权利要求1所述的用于保温墙的保温涂料，其特征在于，包括以下重量份的原料：水性丙烯酸树脂20～25份、乙烯基酯树脂23～28份、N-羟甲基丙烯酰胺5～7份、碳化硅7～8份、木质素4～5份、聚丙烯腈5～6份、顺丁烯二酸二异辛酯3～4份、空心玻璃微珠4.3～5.2份、氧化铝气凝胶改性珍珠岩6～8份、改性硅藻土7～8份、分散剂2.5～3.3份、消泡剂1.5～2.5份、增稠剂3.6～4.4份及去离子水31～39份。
3.根据权利要求1所述的用于保温墙的保温涂料，其特征在于，包括以下重量份的原料：水性丙烯酸树脂23份、乙烯基酯树脂25份、N-羟甲基丙烯酰胺6份、碳化硅7.8份、木质素4.2份、聚丙烯腈5.4份、顺丁烯二酸二异辛酯3.3份、空心玻璃微珠4.9份、氧化铝气凝胶改性珍珠岩7份、改性硅藻土7.2份、分散剂3.1份、消泡剂2份、增稠剂3.9份及去离子水35份。
4.根据权利要求1所述的用于保温墙的保温涂料，其特征在于，所述氧化铝气凝胶改性珍珠岩的制备方法如下：
将膨胀珍珠岩浸泡于事先制备好的氧化铝气凝胶中，采用真空浸渍吸附工艺，使氧化铝气凝胶吸入膨胀珍珠岩空腔内，待老化后，通过常压分级干燥、憎水处理形成氧化铝气凝胶改性珍珠岩。
5.根据权利要求1所述的用于保温墙的保温涂料，其特征在于，所述改性硅藻土的制备方法如下：
先将硅藻土在温度为480～520℃下煅烧1～2h，冷却后，球磨过100～200目筛，然后于8～10%的乙酸溶液中浸泡2～4h后，取出，去离子水洗涤至中性，加入相当于硅藻粉重量2～4%的山梨坦单油酸酯，混匀后，烘干，研磨成纳米粉末，即得。
6.根据权利要求1所述的用于保温墙的保温涂料，其特征在于，所述消泡剂为缩水山梨糖醇月桂酸三脂或聚丙二醇。
7.根据权利要求1所述的用于保温墙的保温涂料，其特征在于，所述分散剂为六偏磷酸钠类润湿剂。
8.根据权利要求1所述的用于保温墙的保温涂料，其特征在于，所述增稠剂为羟乙基纤维素。
9.一种制备权利要求1～8任一项所述用于保温墙的保温涂料的方法，其特征在于，包括以下步骤：
（1）按上述配方称取水性丙烯酸树脂、乙烯基酯树脂、N-羟甲基丙烯酰胺、碳化硅、木质素、聚丙烯腈、顺丁烯二酸二异辛酯、空心玻璃微珠、氧化铝气凝胶改性珍珠岩、改性硅藻土、分散剂、消泡剂、增稠剂及去离子水，备用；
（2）将分散剂和去离子水置于反应釜中搅拌混合均匀，然后加入改性硅藻土、碳化硅、木质素、聚丙烯腈，高速分散均匀，得混合物A；
（3）向步骤（2）所得的混合物A中加入水性丙烯酸树脂、乙烯基酯树脂、N-羟甲基丙烯酰胺及顺丁烯二酸二异辛酯，升温至70℃，先微波处理，再高速分散均匀，得混合物B；
（4）将空心玻璃微珠、氧化铝气凝胶改性珍珠加入至步骤（3）所得的混合物B中，搅拌均匀，然后加入消泡剂和增稠剂，搅拌均匀，即得所述用于保温墙的保温涂料。
10.根据权利要求9所述的制备方法，其特征在于，所述步骤（3）中微波处理的时间为10～15分钟。