CN108909149A - A kind of space cloth preparation method with solid pattern effect - Google Patents
A kind of space cloth preparation method with solid pattern effect Download PDFInfo
- Publication number
- CN108909149A CN108909149A CN201810802271.7A CN201810802271A CN108909149A CN 108909149 A CN108909149 A CN 108909149A CN 201810802271 A CN201810802271 A CN 201810802271A CN 108909149 A CN108909149 A CN 108909149A
- Authority
- CN
- China
- Prior art keywords
- parts
- pattern
- transparent
- adhesive
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to space cloth preparation method field, in particular to a kind of space cloth preparation method with solid pattern effect.By being bonded two layers of transparent face mask layer on wire drawing screen cloth surface, pass through the first pattern of medial surface air brushing in inner layer surface film layer, medial surface air brushing and staggered second pattern of the first pattern in outer layer surface film layer, since internal layer face mask layer has certain thickness, make staggered first pattern and the second pattern that stereoscopic effect be presented；By the protection of outer layer face mask layer, make the second pattern and the first pattern that floral designs be made to be hidden in inside, will not be scratched or be worn, makes space cloth surface obtained that there is persistently beautiful pattern effect；In the selection of material, the internal layer face mask layer use PVC material that cost is relatively low, welding performance is good, and the TPU material that outer layer face mask layer is strong and environmentally friendly using wear-resisting property, the protective effect to internal pattern can be reinforced.
Description
Technical field
The present invention relates to space cloth preparation method field, in particular to a kind of space cloth preparation with solid pattern effect
Method.
Background technique
The structure of space cloth is usually wire drawing screen cloth layer surface binding face film layer, plays the wear-resisting and bending resistance on space cloth surface
Folding endurance energy uses, surface layer gas leakage in order to prevent since space cloth is chiefly used in air cushion product, requires the face mask layer of space cloth higher
Intensity；It, often can be direct in facial mask layer surface screen printing or air brushing floral designs in order to improve the ornamental value on space cloth surface
The floral designs that air brushing or silk screen are printed on face mask layer surface are easy to be worn or scratch, and influence the beauty on space cloth surface, and straight
Air brushing is connect to be difficult to reach stereoscopic effect in face mask layer outer surface.
Summary of the invention
The technical problem to be solved by the present invention is to：A kind of preparation side of space cloth with solid pattern effect is provided
Method makes space cloth have persistently beautiful three-dimensional patterns effect by the structure and processing technology of room for improvement cloth.
In order to solve the above-mentioned technical problem, the technical solution adopted by the present invention is：
A kind of preparation method of the space cloth with solid pattern effect, includes the following steps：
Step 1：Roll at 165-180 DEG C and transparent PVC film is made；
Step 2：It squeezes out to be cast at 140-155 DEG C and transparent TPU film is made；
Step 3：After transparent PVC film cooling, in the first pattern of lower surface air brushing of transparent PVC film；
Step 4：After transparent TPU film cooling, in the second pattern of lower surface air brushing of transparent TPU film；
Step 5：It is coated with first adhesive in the upper surface of the upper scrim layer of wire drawing screen cloth, by the following table of transparent PVC film
Upper surface of the face paste together in upper scrim layer；
Step 6：It is coated with second adhesive in the upper surface of transparent PVC film, the lower surface of transparent TPU film is fitted in
The space cloth with solid pattern effect is made in the upper surface of PVC film；
The position of second pattern and the first pattern is staggered；
First adhesive in above-mentioned steps is prepared by the raw material of following parts by weight：
E-PVC90-110 parts；60-80 parts of dioctyl phthalate；3-5 parts of stabilizer；
Second adhesive in above-mentioned steps is prepared by the raw material of following parts by weight：
90-110 parts of polyester-type PU glue；6-10 parts of bridging agent；5-20 parts of butanone；5-10 parts of toluene；The first adhesive
Coated weight with second adhesive is 100-120g/m2；
Transparent PVC film in above-mentioned steps is prepared by the raw material of following parts by weight：
100 parts of polyvinylchloride；40-55 parts of dioctyl phthalate；3-4 parts of barium-zinc liquid stabilizer；Adipic acid two
5-15 parts of monooctyl ester；
Transparent TPU film in above-mentioned steps is prepared by the raw material of following parts by weight：
95-110 parts of TPU resin；Smooth master batch 2-7 parts of TPU.
The beneficial effects of the present invention are：The preparation method of space cloth provided by the invention with solid pattern effect
In, by being bonded two layers of transparent face mask layer on wire drawing screen cloth surface, pass through the first figure of medial surface air brushing in inner layer surface film layer
Case, medial surface air brushing and staggered second pattern of the first pattern in outer layer surface film layer, since internal layer face mask layer has one
Determine thickness, makes staggered first pattern and the second pattern that stereoscopic effect be presented；By the protection of outer layer face mask layer, make second
Pattern and the first pattern make floral designs be hidden in inside, will not be scratched or be worn, and have space cloth surface obtained and hold
Beautiful pattern effect long；In the selection of material, internal layer face mask layer uses the PVC material that cost is relatively low, welding performance is good, and
The outer layer face mask layer TPU material strong and environmentally friendly using wear-resisting property, can reinforce the protective effect to internal pattern.
Specific embodiment
To explain the technical content, the achieved purpose and the effect of the present invention in detail, it is explained below in conjunction with embodiment.
The design of most critical of the present invention is：By wire drawing screen cloth surface be bonded two layers of transparent face mask layer, by
The first pattern of medial surface air brushing of internal layer face mask layer, in the medial surface air brushing of outer layer surface film layer and the first pattern staggered the
Two patterns make staggered first pattern and the second pattern that stereoscopic effect be presented since internal layer face mask layer has certain thickness.
The preparation method of the present invention relates to a kind of space cloth with solid pattern effect, includes the following steps：
Step 1：Roll at 165-180 DEG C and transparent PVC film is made；
Step 2：It squeezes out to be cast at 140-155 DEG C and transparent TPU film is made；
Step 3：After transparent PVC film cooling, in the first pattern of lower surface air brushing of transparent PVC film；
Step 4：After transparent TPU film cooling, in the second pattern of lower surface air brushing of transparent TPU film；
Step 5：It is coated with first adhesive in the upper surface of the upper scrim layer of wire drawing screen cloth, by the following table of transparent PVC film
Upper surface of the face paste together in upper scrim layer；
Step 6：It is coated with second adhesive in the upper surface of transparent PVC film, the lower surface of transparent TPU film is fitted in
The space cloth with solid pattern effect is made in the upper surface of PVC film；
The position of second pattern and the first pattern is staggered；
First adhesive in above-mentioned steps is prepared by the raw material of following parts by weight：
E-PVC90-110 parts；60-80 parts of dioctyl phthalate；3-5 parts of stabilizer；
Second adhesive in above-mentioned steps is prepared by the raw material of following parts by weight：
90-110 parts of polyester-type PU glue；6-10 parts of bridging agent；5-20 parts of butanone；5-10 parts of toluene；The first adhesive
Coated weight with second adhesive is 100-120g/m2；
Transparent PVC film in above-mentioned steps is prepared by the raw material of following parts by weight：
100 parts of polyvinylchloride；40-55 parts of dioctyl phthalate；3-4 parts of barium-zinc liquid stabilizer；Adipic acid two
5-15 parts of monooctyl ester；
Transparent TPU film in above-mentioned steps is prepared by the raw material of following parts by weight：
95-110 parts of TPU resin；Smooth master batch 2-7 parts of TPU.
In the preparation method of the above-mentioned space cloth with solid pattern effect, by being bonded two layers thoroughly on wire drawing screen cloth surface
Bright face mask layer, by the first pattern of medial surface air brushing in inner layer surface film layer, in the medial surface air brushing and the of outer layer surface film layer
Staggered second pattern of one pattern makes staggered first pattern and the since internal layer face mask layer has certain thickness
Stereoscopic effect is presented in two patterns；By the protection of outer layer face mask layer, the second pattern and the first pattern is made to be hidden in floral designs
Inside will not be scratched or be worn, and space cloth surface obtained is made to have persistently beautiful pattern effect；In the selection of material
On, internal layer face mask layer is using the PVC material that cost is relatively low, welding performance is good, and outer layer face mask layer uses wear-resisting property strong and ring
The TPU material of guarantor, can reinforce the protective effect to internal pattern.
Further, in the preparation method of the above-mentioned space cloth with solid pattern effect, the online of the wire drawing screen cloth
The material of layer of cloth is polyester PET fiber.
Further, in the preparation method of the above-mentioned space cloth with solid pattern effect, the first adhesive by with
The raw material of lower parts by weight is prepared：
E-PVC100 parts；70 parts of dioctyl phthalate；4 parts of stabilizer.
Further, in the preparation method of the above-mentioned space cloth with solid pattern effect, the second adhesive by with
The raw material of lower parts by weight is prepared：
100 parts of polyester-type PU glue；8 parts of bridging agent；12 parts of butanone；7 parts of toluene.
Further, in the preparation method of the above-mentioned space cloth with solid pattern effect, the first adhesive and
The coated weight of two adhesives is 110g/m2。
Further, in the preparation method of the above-mentioned space cloth with solid pattern effect, the transparent PVC film by with
The raw material of lower parts by weight is prepared：
100 parts of polyvinylchloride；47 parts of dioctyl phthalate；3.5 parts of barium-zinc liquid stabilizer；Adipic acid two is pungent
8 parts of ester.
Further, in the preparation method of the above-mentioned space cloth with solid pattern effect, the transparent TPU film by with
The raw material of lower parts by weight is prepared：
105 parts of TPU resin；4 parts of the smooth master batch of TPU.
Embodiment 1
A kind of preparation method of the space cloth with solid pattern effect, includes the following steps：
Step 1：Roll at 165 DEG C and transparent PVC film is made；
Step 2：It squeezes out to be cast at 140 DEG C and transparent TPU film is made；
Step 3：After transparent PVC film cooling, in the first pattern of lower surface air brushing of transparent PVC film；
Step 4：After transparent TPU film cooling, in the second pattern of lower surface air brushing of transparent TPU film；
Step 5：It is coated with first adhesive in the upper surface of the upper scrim layer of wire drawing screen cloth, by the following table of transparent PVC film
Upper surface of the face paste together in upper scrim layer；
Step 6：It is coated with second adhesive in the upper surface of transparent PVC film, the lower surface of transparent TPU film is fitted in
The space cloth with solid pattern effect is made in the upper surface of PVC film；
The position of second pattern and the first pattern is staggered；
First adhesive in above-mentioned steps is prepared by raw material below：
E-PVC90-110g；Dioctyl phthalate 60g；Stabilizer 3g；
Second adhesive in above-mentioned steps is prepared by raw material below：
Polyester-type PU glue 90-110g；Bridging agent 6-10g；Butanone 5-20g；Toluene 5-10g；The first adhesive and
The coated weight of two adhesives is 100g/m2；
Transparent PVC film in above-mentioned steps is prepared by raw material below：
Polyvinylchloride 100g；Dioctyl phthalate 40g；Barium-zinc liquid stabilizer 3g；Dioctyl adipate 5g；
Transparent TPU film in above-mentioned steps is prepared by raw material below：
TPU resin 95g；The smooth master batch 2g of TPU.
The material of the upper scrim layer of the wire drawing screen cloth is polyester PET fiber.
Embodiment 2
A kind of preparation method of the space cloth with solid pattern effect, includes the following steps：
Step 1：Roll at 180 DEG C and transparent PVC film is made；
Step 2：It squeezes out to be cast at 155 DEG C and transparent TPU film is made；
Step 3：After transparent PVC film cooling, in the first pattern of lower surface air brushing of transparent PVC film；
Step 4：After transparent TPU film cooling, in the second pattern of lower surface air brushing of transparent TPU film；
Step 5：It is coated with first adhesive in the upper surface of the upper scrim layer of wire drawing screen cloth, by the following table of transparent PVC film
Upper surface of the face paste together in upper scrim layer；
Step 6：It is coated with second adhesive in the upper surface of transparent PVC film, the lower surface of transparent TPU film is fitted in
The space cloth with solid pattern effect is made in the upper surface of PVC film；
The position of second pattern and the first pattern is staggered；
First adhesive in above-mentioned steps is prepared by raw material below：
E-PVC90-110g；Dioctyl phthalate 80g；Stabilizer 5g；
Second adhesive in above-mentioned steps is prepared by raw material below：
Polyester-type PU glue 110g；Bridging agent 10g；Butanone 20g；Toluene 10g；The first adhesive and second adhesive
Coated weight is 120g/m2；
Transparent PVC film in above-mentioned steps is prepared by raw material below：
Polyvinylchloride 100g；Dioctyl phthalate 55g；Barium-zinc liquid stabilizer 4g；Dioctyl adipate 15g；
Transparent TPU film in above-mentioned steps is prepared by raw material below：
TPU resin 110g；The smooth master batch 7g of TPU.
The material of the upper scrim layer of the wire drawing screen cloth is polyester PET fiber.
Embodiment 3
A kind of preparation method of the space cloth with solid pattern effect, includes the following steps：
Step 1：Roll at 170 DEG C and transparent PVC film is made；
Step 2：It squeezes out to be cast at 147 DEG C and transparent TPU film is made；
Step 3：After transparent PVC film cooling, in the first pattern of lower surface air brushing of transparent PVC film；
Step 4：After transparent TPU film cooling, in the second pattern of lower surface air brushing of transparent TPU film；
Step 5：It is coated with first adhesive in the upper surface of the upper scrim layer of wire drawing screen cloth, by the following table of transparent PVC film
Upper surface of the face paste together in upper scrim layer；
Step 6：It is coated with second adhesive in the upper surface of transparent PVC film, the lower surface of transparent TPU film is fitted in
The space cloth with solid pattern effect is made in the upper surface of PVC film；
The position of second pattern and the first pattern is staggered；
The material of the upper scrim layer of the wire drawing screen cloth is polyester PET fiber.
The first adhesive is prepared by raw material below：
E-PVC100g；Dioctyl phthalate 70g；Stabilizer 4g.
The second adhesive is prepared by raw material below：
Polyester-type PU glue 100g；Bridging agent 8g；Butanone 12g；Toluene 7g.
The coated weight of the first adhesive and second adhesive is 110g/m2。
The transparent PVC film is prepared by raw material below：
Polyvinylchloride 100g；Dioctyl phthalate 47g；Barium-zinc liquid stabilizer 3.5g；Dioctyl adipate
8g。
The transparent TPU film is prepared by raw material below：
TPU resin 105g；The smooth master batch 4g of TPU.
In conclusion in the preparation method of the space cloth provided by the invention with solid pattern effect, by wire drawing
Screen cloth surface is bonded two layers of transparent face mask layer, by the first pattern of medial surface air brushing in inner layer surface film layer, in outer layer surface film
The medial surface air brushing of layer and staggered second pattern of the first pattern make to interlock since internal layer face mask layer has certain thickness
Stereoscopic effect is presented in the first pattern and the second pattern of arrangement；By the protection of outer layer face mask layer, make the second pattern and the first figure
Case makes floral designs be hidden in inside, will not be scratched or be worn, and space cloth surface obtained is made to have persistently beautiful pattern
Effect；In the selection of material, internal layer face mask layer is using the PVC material that cost is relatively low, welding performance is good, and outer layer face mask layer is adopted
The TPU material strong and environmentally friendly with wear-resisting property, can reinforce the protective effect to internal pattern.
The above description is only an embodiment of the present invention, is not intended to limit the scope of the invention, all to utilize this hair
Equivalents made by bright description are applied directly or indirectly in relevant technical field, are similarly included in this hair
In bright scope of patent protection.
Claims (7)
1. a kind of space cloth preparation method with solid pattern effect, which is characterized in that include the following steps：
Step 1：Roll at 165-180 DEG C and transparent PVC film is made；
Step 2：It squeezes out to be cast at 140-155 DEG C and transparent TPU film is made；
Step 3：After transparent PVC film cooling, in the first pattern of lower surface air brushing of transparent PVC film；
Step 4：After transparent TPU film cooling, in the second pattern of lower surface air brushing of transparent TPU film；
Step 5：It is coated with first adhesive in the upper surface of the upper scrim layer of wire drawing screen cloth, by the following table face paste of transparent PVC film
Together in the upper surface of upper scrim layer；
Step 6：It is coated with second adhesive in the upper surface of transparent PVC film, the lower surface of transparent TPU film is fitted in into PVC
The space cloth with solid pattern effect is made in the upper surface of film；
The position of second pattern and the first pattern is staggered；
First adhesive in above-mentioned steps is prepared by the raw material of following parts by weight：
E-PVC90-110 parts；60-80 parts of dioctyl phthalate；3-5 parts of stabilizer；
Second adhesive in above-mentioned steps is prepared by the raw material of following parts by weight：
90-110 parts of polyester-type PU glue；6-10 parts of bridging agent；5-20 parts of butanone；5-10 parts of toluene；The first adhesive and
The coated weight of two adhesives is 100-120g/m2；
Transparent PVC film in above-mentioned steps is prepared by the raw material of following parts by weight：
100 parts of polyvinylchloride；40-55 parts of dioctyl phthalate；3-4 parts of barium-zinc liquid stabilizer；Dioctyl adipate
5-15 parts；
Transparent TPU film in above-mentioned steps is prepared by the raw material of following parts by weight：
95-110 parts of TPU resin；Smooth master batch 2-7 parts of TPU.
2. the space cloth preparation method according to claim 1 with solid pattern effect, which is characterized in that the wire drawing
The material of the upper scrim layer of screen cloth is polyester PET fiber.
3. the space cloth preparation method according to claim 1 with solid pattern effect, which is characterized in that described first
Adhesive is prepared by the raw material of following parts by weight：
E-PVC100 parts；70 parts of dioctyl phthalate；4 parts of stabilizer.
4. the space cloth preparation method according to claim 1 with solid pattern effect, which is characterized in that described second
Adhesive is prepared by the raw material of following parts by weight：
100 parts of polyester-type PU glue；8 parts of bridging agent；12 parts of butanone；7 parts of toluene.
5. the space cloth preparation method according to claim 1 with solid pattern effect, which is characterized in that described first
Adhesive and the coated weight of second adhesive are 110g/m2。
6. the space cloth preparation method according to claim 1 with solid pattern effect, which is characterized in that described transparent
PVC film is prepared by the raw material of following parts by weight：
100 parts of polyvinylchloride；47 parts of dioctyl phthalate；3.5 parts of barium-zinc liquid stabilizer；Dioctyl adipate 8
Part.
7. the space cloth preparation method according to claim 1 with solid pattern effect, which is characterized in that described transparent
TPU film is prepared by the raw material of following parts by weight：
105 parts of TPU resin；4 parts of the smooth master batch of TPU.