CN109049900A - A kind of processing method of high abrasion three-dimensional pattern folder screen cloth - Google Patents

A kind of processing method of high abrasion three-dimensional pattern folder screen cloth Download PDF

Info

Publication number
CN109049900A
CN109049900A CN201810802257.7A CN201810802257A CN109049900A CN 109049900 A CN109049900 A CN 109049900A CN 201810802257 A CN201810802257 A CN 201810802257A CN 109049900 A CN109049900 A CN 109049900A
Authority
CN
China
Prior art keywords
parts
screen cloth
dimensional pattern
processing method
high abrasion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810802257.7A
Other languages
Chinese (zh)
Inventor
林生雄
蒋石生
黄万能
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FUJIAN SIJIA INDUSTRIAL MATERIAL Co Ltd
Original Assignee
FUJIAN SIJIA INDUSTRIAL MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FUJIAN SIJIA INDUSTRIAL MATERIAL Co Ltd filed Critical FUJIAN SIJIA INDUSTRIAL MATERIAL Co Ltd
Priority to CN201810802257.7A priority Critical patent/CN109049900A/en
Publication of CN109049900A publication Critical patent/CN109049900A/en
Pending legal-status Critical Current

Abstract

The present invention relates to folder screen cloth processing method technical field, in particular to a kind of processing method of high abrasion three-dimensional pattern folder screen cloth.By bonding two layers of transparent face mask layer in the scrim surfaces of folder screen cloth, pass through the medial surface air brushing background patterns in inner layer surface film layer, in the lateral surface air brushing floral designs of inner layer surface film layer, since internal layer face mask layer has certain thickness, so that floral designs is suspended in background patterns, three-dimensional pattern effect is presented；In the selection of material; internal layer face mask layer uses PVC material; and outer layer face mask layer is using TPU material; PVC material is at low cost; welding performance is good, is suitable as the material of internal layer face mask layer, and TPU material compares PVC material; with more preferably wearability and bend resistance ability, the protective effect to internal floral designs can be reinforced.

Description

A kind of processing method of high abrasion three-dimensional pattern folder screen cloth
Technical field
The present invention relates to folder screen cloth processing method technical field, in particular to a kind of high abrasion three-dimensional pattern folder screen cloth Processing method.
Background technique
Folder screen cloth is one kind using grid cloth of weaving as basis material, in one or more layers compound face mask layer of grid cloth two sides.
In order to improve the ornamental value on folder screen cloth surface, often can directly be sprayed in facial mask layer surface screen printing or printing pattern Draw or silk-screen be easy to be worn or scratch in the pattern of facial mask layer surface, influence press from both sides screen cloth surface beauty, and directly air brushing in The pattern of face mask layer outer surface is difficult to reach stereoscopic effect.
Summary of the invention
The technical problems to be solved by the present invention are: providing a kind of processing method of high abrasion three-dimensional pattern folder screen cloth, lead to The face mask layer structure and processing technology for improving folder screen cloth are crossed, makes to press from both sides screen cloth surface with high-wearing feature and persistently beautiful solid Floral designs effect.
In order to solve the above-mentioned technical problem, a kind of the technical solution adopted by the present invention are as follows: high abrasion three-dimensional pattern folder screen cloth Processing method, comprising the following steps:
Step 1: rolling at 160-180 DEG C and transparent PVC film is made；
Step 2: after transparent PVC film cooling, in the lower surface air brushing background patterns of transparent PVC film, transparent The upper surface air brushing floral designs of PVC film；
Step 3: being squeezed out at 140-155 DEG C and be cast obtained transparent TPU film；
Step 4: coating first adhesive in the upper surface of base fabric, the lower surface of transparent PVC film is bonded in base fabric Upper surface；
Step 5: coating second adhesive in PVC film upper surface, transparent TPU film is bonded in the upper table of PVC film Face is made high abrasion three-dimensional pattern and presss from both sides screen cloth；
The first adhesive is prepared by the raw material of following parts by weight:
E-PVC90-110 parts；60-80 parts of dioctyl phthalate；3-5 parts of stabilizer；
The second adhesive is prepared by the raw material of following parts by weight:
90-110 parts of polyester-type PU glue；6-10 parts of bridging agent；5-20 parts of butanone；5-10 parts of toluene；The first adhesive Coated weight with second adhesive is 100-120g/m2；
The PVC film is prepared by the raw material of following parts by weight:
100 parts of polyvinylchloride；40-55 parts of dioctyl phthalate；3-4 parts of barium-zinc liquid stabilizer；Adipic acid 5-15 parts of dioctyl ester；
The TPU film is prepared by the raw material of following parts by weight:
95-110 parts of TPU resin；Smooth master batch 2-7 parts of TPU.
The beneficial effects of the present invention are: in the processing method of high abrasion three-dimensional pattern folder screen cloth provided by the invention, lead to The scrim surfaces crossed in folder screen cloth bond two layers of transparent face mask layer, pass through the medial surface air brushing Background in inner layer surface film layer Case, since internal layer face mask layer has certain thickness, keeps floral designs outstanding in the lateral surface air brushing floral designs of inner layer surface film layer Floating on background patterns, three-dimensional pattern effect is presented makes floral designs be hidden in inside by the protection of the transparent face mask layer of outer layer, It will not be scratched or be worn, make to press from both sides the pattern effect that screen cloth surface has persistently beauty；In the selection of material, internal layer facial mask Layer uses PVC material, and outer layer face mask layer is using TPU material, and PVC material is at low cost, and welding performance is good, is suitable as The material of internal layer face mask layer, and TPU material compares PVC material, has more preferably wearability and bend resistance ability, can reinforce Protective effect to internal floral designs.
Specific embodiment
To explain the technical content, the achieved purpose and the effect of the present invention in detail, it is said below in conjunction with embodiment It is bright.
The most critical design of the present invention is: by the medial surface air brushing background patterns in inner layer surface film layer, in inner layer surface The lateral surface air brushing floral designs of film layer make floral designs be suspended in Background since internal layer face mask layer has certain thickness Three-dimensional pattern effect is presented in case, and internal layer face mask layer uses PVC material, and outer layer face mask layer is using TPU material.
The present invention relates to a kind of processing methods of high abrasion three-dimensional pattern folder screen cloth, comprising the following steps:
Step 1: rolling at 160-180 DEG C and transparent PVC film is made；
Step 2: after transparent PVC film cooling, in the lower surface air brushing background patterns of transparent PVC film, transparent The upper surface air brushing floral designs of PVC film；
Step 3: being squeezed out at 140-155 DEG C and be cast obtained transparent TPU film；
Step 4: coating first adhesive in the upper surface of base fabric, the lower surface of transparent PVC film is bonded in base fabric Upper surface；
Step 5: coating second adhesive in PVC film upper surface, transparent TPU film is bonded in the upper table of PVC film Face is made high abrasion three-dimensional pattern and presss from both sides screen cloth；
The first adhesive is prepared by the raw material of following parts by weight:
E-PVC90-110 parts；60-80 parts of dioctyl phthalate；3-5 parts of stabilizer；
The second adhesive is prepared by the raw material of following parts by weight:
90-110 parts of polyester-type PU glue；6-10 parts of bridging agent；5-20 parts of butanone；5-10 parts of toluene；The first adhesive Coated weight with second adhesive is 100-120g/m2；
The PVC film is prepared by the raw material of following parts by weight:
100 parts of polyvinylchloride；40-55 parts of dioctyl phthalate；3-4 parts of barium-zinc liquid stabilizer；Adipic acid 5-15 parts of dioctyl ester；
The TPU film is prepared by the raw material of following parts by weight:
95-110 parts of TPU resin；Smooth master batch 2-7 parts of TPU.
In the processing method of above-mentioned high abrasion three-dimensional pattern folder screen cloth, by being bonded two layers in the scrim surfaces of folder screen cloth Transparent face mask layer, by the medial surface air brushing background patterns in inner layer surface film layer, in the lateral surface air brushing flower of inner layer surface film layer Line pattern makes floral designs be suspended in background patterns since internal layer face mask layer has certain thickness, and three-dimensional pattern effect is presented, By the protection of the transparent face mask layer of outer layer, floral designs is made to be hidden in inside, will not be scratched or worn, makes to press from both sides screen cloth surface Pattern effect with lasting beauty；In the selection of material, internal layer face mask layer uses PVC material, and outer layer face mask layer uses Be TPU material, PVC material is at low cost, and welding performance is good, is suitable as the material of internal layer face mask layer, and TPU material is compared PVC material has more preferably wearability and bend resistance ability, can reinforce the protective effect to internal floral designs.
Further, in the processing method of above-mentioned high abrasion three-dimensional pattern folder screen cloth, the material of the base fabric is polyester PET fiber.
Further, in the processing method of above-mentioned high abrasion three-dimensional pattern folder screen cloth, the material of the base fabric is that poly-vinegar is fine Dimension.
Further, in the processing method of above-mentioned high abrasion three-dimensional pattern folder screen cloth, the first adhesive is by following heavy The raw material of amount part is prepared:
E-PVC100 parts；70 parts of dioctyl phthalate；4 parts of stabilizer.
Further, in the processing method of above-mentioned high abrasion three-dimensional pattern folder screen cloth, the second adhesive is by following heavy The raw material of amount part is prepared:
100 parts of polyester-type PU glue；8 parts of bridging agent；10 parts of butanone；7 parts of toluene.
Further, in the processing method of above-mentioned high abrasion three-dimensional pattern folder screen cloth, the first adhesive and second is glued The coated weight of mixture is 110g/m2。
Further, in the processing method of above-mentioned high abrasion three-dimensional pattern folder screen cloth, the PVC film is by following weight The raw material of part is prepared:
100 parts of polyvinylchloride；45 parts of dioctyl phthalate；4 parts of barium-zinc liquid stabilizer；Dioctyl adipate 8 parts.
Further, in the processing method of above-mentioned high abrasion three-dimensional pattern folder screen cloth, the TPU film is by following weight The raw material of part is prepared:
105 parts of TPU resin；5 parts of the smooth master batch of TPU.
Embodiment 1
A kind of processing method of high abrasion three-dimensional pattern folder screen cloth, comprising the following steps:
Step 1: rolling at 160 DEG C and transparent PVC film is made；
Step 2: after transparent PVC film cooling, in the lower surface air brushing background patterns of transparent PVC film, transparent The upper surface air brushing floral designs of PVC film；
Step 3: being squeezed out at 140 DEG C and be cast obtained transparent TPU film；
Step 4: coating first adhesive in the upper surface of base fabric, the lower surface of transparent PVC film is bonded in base fabric Upper surface；
Step 5: coating second adhesive in PVC film upper surface, transparent TPU film is bonded in the upper table of PVC film Face is made high abrasion three-dimensional pattern and presss from both sides screen cloth；
The first adhesive is prepared by raw material below:
E-PVC90g；Dioctyl phthalate 60g；Stabilizer 3g；
The second adhesive is prepared by raw material below:
Polyester-type PU glue 90g；Bridging agent 6g；Butanone 5g；Toluene 5g；The painting of the first adhesive and second adhesive The amount of covering is 100g/m2；
The PVC film is prepared by raw material below:
Polyvinylchloride 100g；Dioctyl phthalate 40g；Barium-zinc liquid stabilizer 3g；Dioctyl adipate 5g；
The TPU film is prepared by raw material below:
TPU resin 95g；The smooth master batch 2g of TPU.
The material of the base fabric is polyester PET fiber.
Embodiment 2
A kind of processing method of high abrasion three-dimensional pattern folder screen cloth, comprising the following steps:
Step 1: rolling at 180 DEG C and transparent PVC film is made；
Step 2: after transparent PVC film cooling, in the lower surface air brushing background patterns of transparent PVC film, transparent The upper surface air brushing floral designs of PVC film；
Step 3: being squeezed out at 155 DEG C and be cast obtained transparent TPU film；
Step 4: coating first adhesive in the upper surface of base fabric, the lower surface of transparent PVC film is bonded in base fabric Upper surface；
Step 5: coating second adhesive in PVC film upper surface, transparent TPU film is bonded in the upper table of PVC film Face is made high abrasion three-dimensional pattern and presss from both sides screen cloth；
The first adhesive is prepared by raw material below:
E-PVC90-110g；Dioctyl phthalate 80g；Stabilizer 5g；
The second adhesive is prepared by raw material below:
Polyester-type PU glue 110g；Bridging agent 10g；Butanone 20g；Toluene 10g；The first adhesive and second adhesive Coated weight be 120g/m2；
The PVC film is prepared by raw material below:
Polyvinylchloride 100g；The pungent 55g of phthalic acid two；Barium-zinc liquid stabilizer 4g；Dioctyl adipate 15g；
The TPU film is prepared by raw material below:
TPU 110g；The smooth master batch 7g of TPU.
The material of the base fabric is polyester fiber.
Embodiment 3
A kind of processing method of high abrasion three-dimensional pattern folder screen cloth, comprising the following steps:
Step 1: rolling at 170 DEG C and transparent PVC film is made；
Step 2: after transparent PVC film cooling, in the lower surface air brushing background patterns of transparent PVC film, transparent The upper surface air brushing floral designs of PVC film；
Step 3: being squeezed out at 147 DEG C and be cast obtained transparent TPU film；
Step 4: coating first adhesive in the upper surface of base fabric, the lower surface of transparent PVC film is bonded in base fabric Upper surface；
Step 5: coating second adhesive in PVC film upper surface, transparent TPU film is bonded in the upper table of PVC film Face is made high abrasion three-dimensional pattern and presss from both sides screen cloth；
The material of the base fabric is polyester fiber.
The first adhesive is prepared by raw material below:
E-PVC100g；Dioctyl phthalate 70g；Stabilizer 4g.
The second adhesive is prepared by raw material below:
Polyester-type PU glue 100g；Bridging agent 8g；Butanone 10g；Toluene 7g.
The coated weight of the first adhesive and second adhesive is 110g/m2。
The PVC film is prepared by raw material below:
Polyvinylchloride 100g；Dioctyl phthalate 45g；Barium-zinc liquid stabilizer 4g；Dioctyl adipate 8g.
The TPU film is prepared by raw material below:
TPU resin 105g；The smooth master batch 5g of TPU.
In conclusion in the processing method of high abrasion three-dimensional pattern folder screen cloth provided by the invention, by folder screen cloth Scrim surfaces bond two layers of transparent face mask layer, by the medial surface air brushing background patterns in inner layer surface film layer, in inner layer surface film The lateral surface air brushing floral designs of layer make floral designs be suspended in background patterns since internal layer face mask layer has certain thickness, Three-dimensional pattern effect, which is presented, by the protection of the transparent face mask layer of outer layer makes floral designs be hidden in inside, will not be scratched or Abrasion makes to press from both sides the pattern effect that screen cloth surface has persistently beauty；In the selection of material, internal layer face mask layer uses PVC material Matter, and outer layer face mask layer, using TPU material, PVC material is at low cost, and welding performance is good, is suitable as internal layer face mask layer Material, and TPU material compares PVC material, has more preferably wearability and bend resistance ability, can reinforce to internal decorative pattern The protective effect of pattern.
The above description is only an embodiment of the present invention, is not intended to limit the scope of the invention, all to utilize this hair Equivalents made by bright description are applied directly or indirectly in relevant technical field, are similarly included in this hair In bright scope of patent protection.

Claims (8)

1. a kind of processing method of high abrasion three-dimensional pattern folder screen cloth, which comprises the following steps:
Step 1: rolling at 160-180 DEG C and transparent PVC film is made；
Step 2: after transparent PVC film cooling, in the lower surface air brushing background patterns of transparent PVC film, in transparent PVC film Upper surface air brushing floral designs；
Step 3: being squeezed out at 140-155 DEG C and be cast obtained transparent TPU film；
Step 4: coating first adhesive in the upper surface of base fabric, the lower surface of transparent PVC film is bonded in the upper table of base fabric Face；
Step 5: coating second adhesive in PVC film upper surface, transparent TPU film is bonded in the upper surface of PVC film, is made It obtains high abrasion three-dimensional pattern and presss from both sides screen cloth；
The first adhesive is prepared by the raw material of following parts by weight:
E-PVC90-110 parts；60-80 parts of dioctyl phthalate；3-5 parts of stabilizer；
The second adhesive is prepared by the raw material of following parts by weight:
90-110 parts of polyester-type PU glue；6-10 parts of bridging agent；5-20 parts of butanone；5-10 parts of toluene；The first adhesive and The coated weight of two adhesives is 100-120g/m2；
The PVC film is prepared by the raw material of following parts by weight:
100 parts of polyvinylchloride；40-55 parts of dioctyl phthalate；3-4 parts of barium-zinc liquid stabilizer；Dioctyl adipate 5-15 parts；
The TPU film is prepared by the raw material of following parts by weight:
95-110 parts of TPU resin；Smooth master batch 2-7 parts of TPU.
2. the processing method of high abrasion three-dimensional pattern folder screen cloth according to claim 1, which is characterized in that the base fabric Material is polyester PET fiber.
3. the processing method of high abrasion three-dimensional pattern folder screen cloth according to claim 1, which is characterized in that the base fabric Material is polyester fiber.
4. the processing method of high abrasion three-dimensional pattern folder screen cloth according to claim 1, which is characterized in that described first is viscous Mixture is prepared by the raw material of following parts by weight:
E-PVC100 parts；70 parts of dioctyl phthalate；4 parts of stabilizer.
5. the processing method of high abrasion three-dimensional pattern folder screen cloth according to claim 1, which is characterized in that described second is viscous Mixture is prepared by the raw material of following parts by weight:
100 parts of polyester-type PU glue；8 parts of bridging agent；10 parts of butanone；7 parts of toluene.
6. the processing method of high abrasion three-dimensional pattern folder screen cloth according to claim 1, which is characterized in that described first is viscous Mixture and the coated weight of second adhesive are 110g/m2。
7. the processing method of high abrasion three-dimensional pattern folder screen cloth according to claim 1, which is characterized in that the PVC is thin Film is prepared by the raw material of following parts by weight:
100 parts of polyvinylchloride；45 parts of dioctyl phthalate；4 parts of barium-zinc liquid stabilizer；8 parts of dioctyl adipate.
8. the processing method of high abrasion three-dimensional pattern folder screen cloth according to claim 1, which is characterized in that the TPU is thin Film is prepared by the raw material of following parts by weight:
105 parts of TPU resin；5 parts of the smooth master batch of TPU.
CN201810802257.7A 2018-07-20 2018-07-20 A kind of processing method of high abrasion three-dimensional pattern folder screen cloth Pending CN109049900A (en)