CN108903610A - A kind of slaughterhouse - Google Patents
A kind of slaughterhouse Download PDFInfo
- Publication number
- CN108903610A CN108903610A CN201811157189.XA CN201811157189A CN108903610A CN 108903610 A CN108903610 A CN 108903610A CN 201811157189 A CN201811157189 A CN 201811157189A CN 108903610 A CN108903610 A CN 108903610A
- Authority
- CN
- China
- Prior art keywords
- graphite
- parts
- slaughterhouse
- composite material
- graphite composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of slaughterhouses, belong to cookware technical field.Pot body is made by graphite composite material in the slaughterhouse, coats one layer of antistick layer, graphite composite material in pot inner surface:Glass fibre 1-3%, talcum powder 5-10%, aluminium powder 0.3-2%, titanium valve 0.1-0.5%, magnesia 0.5-2%, silicon nitride 0.5-2%, calcium carbonate 0.5-3%, ceramic clay 30-50%, surplus are graphite.Slaughterhouse of the present invention is made using the reasonable graphite composite material of compatibility, is made that slaughterhouse is light-weight, and resistance to heat rating is big, and thermal expansion coefficient is small, and thermal diffusivity and thermal conductivity are high, and heat transfer is fast, and is heated evenly.Furthermore added in the coating of antistick layer of the present invention acrylic acid allow investment precoat volatilization when being sintered film forming leave away caused by capillary effect tense the gap of molten resin particle, inhibit the high temperature degradation of a small amount of PTFE, to reduce the xanthochromia of investment precoat.
Description
Technical field
The present invention relates to a kind of slaughterhouses, belong to cookware technical field.
Background technique
Pot is household implements indispensable in people's daily life, leads to production in the prior art and is made of full cast iron, but
It is but its big with weight, resistance to heat rating is small, thermal expansion coefficient is big, thermal diffusivity and the small disadvantage of thermal conductivity;Also have using pottery
Pot made of porcelain, although the thermal conductivity of porcelain pot is high and thermal expansion coefficient is small, its resistance to heat rating is small, and can only open firing and easily
Rupture;There is also the so-called health pots made of high borosilicate simultaneously, although it is with lower thermal expansion coefficient, it is to heat
It is insensitive.
Summary of the invention
The purpose of the present invention is being directed to the above-mentioned problems in the prior art, the soup of a kind of low-density, high thermal conductivity is provided
Pot.
Object of the invention can be realized by the following technical scheme:A kind of slaughterhouse, the slaughterhouse is by graphite composite material
Pot body is made, coats one layer of antistick layer in pot inner surface, wherein the constituent and its content of the graphite composite material are such as
Under:Glass fibre 1-3%, talcum powder 5-10%, aluminium powder 0.3-2%, titanium valve 0.1-0.5%, magnesia 0.5-2%, silicon nitride
0.5-2%, calcium carbonate 0.5-3%, ceramic clay 30-50%, surplus are graphite and inevitable impurity.
In above-mentioned slaughterhouse, the density of the graphite is 1.72-1.80g/cm3, the ash content of the graphite material≤
0.1%.
In above-mentioned slaughterhouse, the thermal expansion coefficient of the graphite is 4.8 × 10-6/K。
In above-mentioned slaughterhouse, the thermal diffusivity of the graphite is 87.5m^2/s。
In above-mentioned slaughterhouse, the thermal conductivity of the graphite is 130w/mk.
In above-mentioned slaughterhouse, the coating of the antistick layer is made of the raw material of following parts by weight:Polyflon
10-20 parts, 5-20 parts of acrylic based emulsion, epoxies promotion resin 10-20 parts, 0.5-5 parts of carbon nanotube, fumed silica
0.5-5 parts, 0.5-5 parts of nano silver, 1-2 parts of wetting agent, 20-40 parts of deionized water.
Compared with prior art, the invention has the advantages that:
1. slaughterhouse of the present invention is made using the reasonable graphite composite material of compatibility, wherein graphite density is small, light-weight, ash
It is low, quality is high, resistance to compression and fracture resistance are good;It is that graphite soup clay pot made of matrix is light-weight, resistance to heat rating is big, thermal expansion it
Coefficient is small, thermal diffusivity and thermal conductivity are high, heat transfer is fast, and is heated evenly.
2. slaughterhouse of the present invention coats antistick layer on the surface that pot body is made in graphite composite material, pass through the coating in antistick layer
Middle addition acrylic acid allow investment precoat be sintered film forming when volatilization leave away caused by capillary effect tense melting tree
The gap of fat granule, inhibits the high temperature degradation of a small amount of PTFE, to reduce the xanthochromia of investment precoat.
Specific embodiment
The following is specific embodiments of the present invention, illustrates that technical scheme of the present invention will be further described, but this hair
It is bright to be not limited to these examples.
Embodiment 1
Pot body is made by graphite composite material in a kind of slaughterhouse, the slaughterhouse, coats one layer of antistick layer in pot inner surface, wherein
The constituent and its content of the graphite composite material are as follows:Glass fibre 2%, talcum powder 8%, aluminium powder 1.2%, titanium valve
0.4%, magnesia 1.2%, silicon nitride 1.2%, calcium carbonate 2.2%, ceramic clay 40%, surplus is for graphite and inevitably
Impurity.
The density of the graphite is 1.76g/cm3, ash content≤0.1% of the graphite material, the thermal expansion coefficient of graphite
It is 4.8 × 10-6/ K, the thermal diffusivity of graphite are 87.5m^2/ s, the thermal conductivity of graphite are 130w/mk.
The coating of the antistick layer is made of the raw material of following parts by weight:15 parts of polyflon, propylene yogurt
12 parts of glue, epoxies promote 15 parts of resin, 3 parts of carbon nanotube, 3 parts of fumed silica, 3 parts of nano silver, 1.5 parts of wetting agent,
30 parts of deionized water.
Embodiment 2
Pot body is made by graphite composite material in a kind of slaughterhouse, the slaughterhouse, coats one layer of antistick layer in pot inner surface, wherein
The constituent and its content of the graphite composite material are as follows:Glass fibre 1%, talcum powder 10%, aluminium powder 0.3%, titanium
Powder 0.5%, magnesia 0.5%, silicon nitride 2%, calcium carbonate 0.5%, ceramic clay 30%, surplus is for graphite and inevitably
Impurity.
The density of the graphite is 1.72g/cm3, ash content≤0.1% of the graphite material, the thermal expansion coefficient of graphite
It is 4.8 × 10-6/ K, the thermal diffusivity of graphite are 87.5m^2/ s, the thermal conductivity of graphite are 130w/mk.
The coating of the antistick layer is made of the raw material of following parts by weight:20 parts of polyflon, propylene yogurt
5 parts of glue, epoxies promote 20 parts of resin, 0.5 part of carbon nanotube, 5 parts of fumed silica, 0.5 part of nano silver, 2 parts of wetting agent,
20 parts of deionized water.
Embodiment 3
Pot body is made by graphite composite material in a kind of slaughterhouse, the slaughterhouse, coats one layer of antistick layer in pot inner surface, wherein
The constituent and its content of the graphite composite material are as follows:Glass fibre 3%, talcum powder 5%, aluminium powder 2%, titanium valve
0.1%, magnesia 2%, silicon nitride 0.5%, calcium carbonate 3%, ceramic clay 35%, surplus be graphite and inevitably it is miscellaneous
Matter.
The density of the graphite is 1.80g/cm3, ash content≤0.1% of the graphite material, the thermal expansion coefficient of graphite
It is 4.8 × 10-6/ K, the thermal diffusivity of graphite are 87.5m^2/ s, the thermal conductivity of graphite are 130w/mk.
The coating of the antistick layer is made of the raw material of following parts by weight:10 parts of polyflon, propylene yogurt
20 parts of glue, epoxies promote 10 parts of resin, 5 parts of carbon nanotube, 0.5 part of fumed silica, 5 parts of nano silver, 1 part of wetting agent,
40 parts of deionized water.
Slaughterhouse of the present invention is made using the reasonable graphite composite material of compatibility, and wherein graphite density is small, light-weight, ash
It is low, quality is high, resistance to compression and fracture resistance are good;Light-weight for graphite soup clay pot made of matrix it, resistance to heat rating is big, thermal expansion
Coefficient is small, and thermal diffusivity and thermal conductivity are high, and heat transfer is fast, and is heated evenly.Furthermore slaughterhouse of the present invention is made in graphite composite material
The surface of pot body coats antistick layer, by adding acrylic acid in the coating of antistick layer investment precoat is waved when being sintered and forming a film
The gap of molten resin particle can be tensed by sending out capillary effect caused by leaving away, and inhibit the high temperature degradation of a small amount of PTFE, from
And reduce the xanthochromia of investment precoat.In the above-described embodiments, the slaughterhouse performance of embodiment 1 is best.
This place embodiment is not exhaustive claimed midpoint of technical range and in embodiment technology
In scheme to single or multiple technical characteristics it is same replacement be formed by new technical solution, equally all the present invention claims
In the range of protection, and between the parameter that is related to of the present invention program if not otherwise specified, then there is no can not between each other
The unique combinations of replacement.
Specific embodiment described herein is only an example for the spirit of the invention.The neck of technology belonging to the present invention
The technical staff in domain can do various modifications or supplement or is substituted in a similar manner to described specific embodiment, but simultaneously
Spirit or beyond the scope defined by the appended claims of the invention is not deviated by.
It is skilled to this field although present invention has been described in detail and some specific embodiments have been cited
For technical staff, as long as it is obvious for can making various changes or correct without departing from the spirit and scope of the present invention.
Claims (6)
1. a kind of slaughterhouse, it is characterised in that:Pot body is made by graphite composite material in the slaughterhouse, coats one layer not in pot inner surface
Adhesion coating, wherein the constituent and its content of the graphite composite material are as follows:Glass fibre 1-3%, talcum powder 5-10%,
Aluminium powder 0.3-2%, titanium valve 0.1-0.5%, magnesia 0.5-2%, silicon nitride 0.5-2%, calcium carbonate 0.5-3%, ceramic clay
30-50%, surplus are graphite and inevitable impurity.
2. slaughterhouse according to claim 1, it is characterised in that:The density of the graphite is 1.72-1.80g/cm3, the stone
Ash content≤0.1% of ink material.
3. slaughterhouse according to claim 1, it is characterised in that:The thermal expansion coefficient of the graphite is 4.8 × 10-6/K。
4. slaughterhouse according to claim 1, it is characterised in that:The thermal diffusivity of the graphite is 87.5m^2/s。
5. slaughterhouse according to claim 1, it is characterised in that:The thermal conductivity of the graphite is 130w/mk.
6. slaughterhouse according to claim 1, it is characterised in that:The coating of the antistick layer by following parts by weight raw material
Composition:10-20 parts of polyflon, 5-20 parts of acrylic based emulsion, epoxies promote resin 10-20 parts, carbon nanotube
0.5-5 parts, 0.5-5 parts of fumed silica, 0.5-5 parts of nano silver, 1-2 parts of wetting agent, 20-40 parts of deionized water.