CN109106197A - A kind of frying pan - Google Patents

A kind of frying pan Download PDF

Info

Publication number
CN109106197A
CN109106197A CN201811143828.7A CN201811143828A CN109106197A CN 109106197 A CN109106197 A CN 109106197A CN 201811143828 A CN201811143828 A CN 201811143828A CN 109106197 A CN109106197 A CN 109106197A
Authority
CN
China
Prior art keywords
parts
frying pan
thermosphere
layer
panhandle
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201811143828.7A
Other languages
Chinese (zh)
Other versions
CN109106197B (en
Inventor
陈森康
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ningbo Hundred Fei Te Kitchen Tools Co Ltd
Original Assignee
Ningbo Hundred Fei Te Kitchen Tools Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ningbo Hundred Fei Te Kitchen Tools Co Ltd filed Critical Ningbo Hundred Fei Te Kitchen Tools Co Ltd
Priority to CN201811143828.7A priority Critical patent/CN109106197B/en
Publication of CN109106197A publication Critical patent/CN109106197A/en
Application granted granted Critical
Publication of CN109106197B publication Critical patent/CN109106197B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

A kind of frying pan, including pot body and panhandle, the pot body by it is bottom-up successively include first by thermosphere, the second middle layer, third by thermosphere and antistick layer, wherein panhandle, first are made by thermosphere of stainless steel material by thermosphere and third.Frying pan of the invention is heated fast, and is heated evenly.Furthermore the coating safety and environmental protection of antistick layer.

Description

A kind of frying pan
Technical field
The present invention relates to a kind of cooker more particularly to a kind of frying pans.
Background technique
Currently, people are mostly to be decocted to stir-fry and eat product with metal product pot.These metal pans although shape, size are different, It is that preparation method, structure are substantially the same.The second traditional frying pan is included the second pot body and is cast with the second pot body using same material Molding second the bottom of a pan of single layer.
But had and decoct the people for frying food experience and both know about, when with above-mentioned traditional second frying pan pan-fried cooked food, heat meeting It is easily spread around from the middle part in second the bottom of a pan of single layer, and the middle portion temperature in second the bottom of a pan is made to be higher than other positions Temperature so that the food being in the middle part of second the bottom of a pan burns due to excessively heated, is burnt, viscous pot.In recent years, on the market Occurs a kind of frying pan of not viscous food again.It is by coating adherent layer, this method in the second traditional frying pan inner surface Although viscous pot phenomenon can be eliminated, serious defect is produced again at the same time, is on the one hand that intensity and fastness are poor, is easy It falls off；On the other hand it is the adherent layer containing a large amount of chemical components, noxious material can be released in the high temperature process, be unfavorable for people The health of body.
Summary of the invention
The purpose of the present invention is be directed to the above-mentioned problems in the prior art, provide a kind of safety and be heated evenly not The frying pan of viscous pot.
Object of the invention can be realized by the following technical scheme: a kind of frying pan, including pot body and panhandle, the pot Body by it is bottom-up successively include first by thermosphere, the second middle layer, third by thermosphere and antistick layer, wherein panhandle, first It is made by thermosphere of stainless steel material by thermosphere and third.
In above-mentioned frying pan, the component and its content of the stainless steel material are as follows: C0.02-0.2%, Si0.2-1.5%, Cr2.0-7.0%, Mn0.5-1.5%, Ni0.2-0.6%, B0.1-0.5%, Ti0.05-0.3%, Nb0.005-0.02%, Sr0.002-0.008%, surplus are Fe and inevitable impurity.
In above-mentioned frying pan, second middle layer is melted by aluminum plate.
In above-mentioned frying pan, the component and its content of the aluminum plate are as follows: Si0.2-1.5%, Fe:0.1- 0.3%, Mn0.5-1.5%, Y:0.005-0.025%, Ce:0.02-0.10%, surplus are Al and inevitable impurity.
In above-mentioned frying pan, the coating of the antistick layer consist of the following raw materials in parts by weight: polytetrafluoroethylene (PTFE) tree 10-20 parts of rouge, 5-20 parts of acrylic based emulsion, epoxies promote resin 10-20 parts, 0.5-5 parts of carbon nanotube, fumed silica 0.5-5 parts, 0.5-5 parts of nano silver, 1-2 parts of wetting agent, 20-40 parts of deionized water.
Compared with prior art, the present invention has the advantage that
1, the pot body in frying pan by it is bottom-up successively include first by thermosphere, the second middle layer, third by thermosphere and Antistick layer, wherein panhandle, first are made by thermosphere of stainless steel material by thermosphere and third, and the second middle layer is by aluminium alloy layer It is made, by the material in each level of reasonable arrangement, further increases the heated fast and uniform of frying pan.
2, by added in the coating of antistick layer acrylic acid make investment precoat be sintered form a film when volatilization leave away and produced Raw capillary effect can tense the gap of molten resin particle, inhibit the high temperature degradation of a small amount of PTFE, to reduce surface layer The xanthochromia of coating.
Specific embodiment
The following is specific embodiments of the present invention, illustrates that technical scheme of the present invention will be further described, but this hair It is bright to be not limited to these examples.
Embodiment 1
A kind of frying pan, including pot body and panhandle, the pot body is by bottom-up successively including first by thermosphere, second Interbed, third are by thermosphere and antistick layer, and wherein panhandle, first are made by thermosphere of stainless steel material by thermosphere and third； The component and its content of the stainless steel material are as follows: C0.1%, Si0.9%, Cr4.0%, Mn1.0%, Ni0.4%, B0.3%, Ti0.18%, Nb0.012%, Sr0.005%, surplus are Fe and inevitable impurity；Described second Middle layer is melted by aluminum plate, and the component and its content of the aluminum plate are as follows: Si0.8%, Fe:0.2%, Mn1.0%, Y:0.012%, Ce:0.06%, surplus are Al and inevitable impurity；The coating of the antistick layer is by following The raw material of parts by weight forms: 15 parts of polyflon, 12 parts of acrylic based emulsion, epoxies promote 15 parts of resin, carbon to receive 3 parts of mitron, 3 parts of fumed silica, 3 parts of nano silver, 1.5 parts of wetting agent, 30 parts of deionized water.
Embodiment 2
A kind of frying pan, including pot body and panhandle, the pot body is by bottom-up successively including first by thermosphere, second Interbed, third are by thermosphere and antistick layer, and wherein panhandle, first are made by thermosphere of stainless steel material by thermosphere and third； The component and its content of the stainless steel material are as follows: C0.2%, Si0.2%, Cr7.0%, Mn0.5%, Ni0.6%, B0.1%, Ti0.3%, Nb0.005%, Sr0.008%, surplus are Fe and inevitable impurity；Described second Middle layer is melted by aluminum plate, and the component and its content of the aluminum plate are as follows: Si1.5%, Fe0.1%, Mn1.5%, Y0.005%, Ce0.10%, surplus are Al and inevitable impurity；The coating of the antistick layer is by following weight The raw material of number forms: 20 parts of polyflon, 5 parts of acrylic based emulsion, epoxies promote 20 parts of resin, carbon nanotube 0.5 part, 5 parts of fumed silica, 0.5 part of nano silver, 2 parts of wetting agent, 20 parts of deionized water.
Embodiment 3
A kind of frying pan, including pot body and panhandle, the pot body is by bottom-up successively including first by thermosphere, second Interbed, third are by thermosphere and antistick layer, and wherein panhandle, first are made by thermosphere of stainless steel material by thermosphere and third； The component and its content of the stainless steel material are as follows: C0.02%, Si1.5%, Cr2.0%, Mn1.5%, Ni0.2%, B0.5%, Ti0.05%, Nb0.02%, Sr0.002%, surplus are Fe and inevitable impurity；Described second Middle layer is melted by aluminum plate, and the component and its content of the aluminum plate are as follows: Si0.2%, Fe0.3%, Mn0.5%, Y0.025%, Ce:0.02%, surplus are Al and inevitable impurity；The coating of the antistick layer is by following heavy Measure the raw material composition of number: 10 parts of polyflon, 20 parts of acrylic based emulsion, epoxies promote 10 parts of resin, carbon nanometer 5 parts of pipe, 0.5 part of fumed silica, 5 parts of nano silver, 1 part of wetting agent, 40 parts of deionized water.
Frying pan of the invention is heated fast, and is heated evenly.Furthermore the coating safety and environmental protection of antistick layer.
This place embodiment is not exhaustive claimed midpoint of technical range and in embodiment technology In scheme to single or multiple technical characteristics it is same replacement be formed by new technical solution, equally all the present invention claims In the range of protection, and between the parameter that is related to of the present invention program if not otherwise specified, then there is no can not between each other The unique combinations of replacement.
Specific embodiment described herein is only an example for the spirit of the invention.The neck of technology belonging to the present invention The technical staff in domain can do various modifications or supplement or is substituted in a similar manner to described specific embodiment, but simultaneously Spirit or beyond the scope defined by the appended claims of the invention is not deviated by.
It is skilled to this field although present invention has been described in detail and some specific embodiments have been cited For technical staff, as long as it is obvious for can making various changes or correct without departing from the spirit and scope of the present invention.

Claims (5)

1. a kind of frying pan, which is characterized in that including pot body and panhandle, the pot body is successively heated including first by bottom-up Layer, the second middle layer, third by thermosphere and antistick layer, wherein panhandle, first by thermosphere and third by thermosphere by stainless steel Material is made.
2. frying pan according to claim 1, which is characterized in that the component and its content of the stainless steel material are such as Under: C0.02-0.2%, Si0.2-1.5%, Cr2.0-7.0%, Mn0.5-1.5%, Ni0.2-0.6%, B0.1-0.5%, Ti0.05-0.3%, Nb0.005-0.02%, Sr0.002-0.008%, surplus are Fe and inevitable impurity.
3. frying pan according to claim 1, which is characterized in that second middle layer is melted by aluminum plate.
4. frying pan according to claim 3, which is characterized in that the component and its content of the aluminum plate are as follows: Si0.2-1.5%, Fe:0.1-0.3%, Mn0.5-1.5%, Y:0.005-0.025%, Ce:0.02-0.10%, surplus Al And inevitable impurity.
5. frying pan according to claim 1, which is characterized in that the coating of the antistick layer by following parts by weight raw material Composition: 10-20 parts of polyflon, 5-20 parts of acrylic based emulsion, epoxies promote resin 10-20 parts, carbon nanotube 0.5-5 parts, 0.5-5 parts of fumed silica, 0.5-5 parts of nano silver, 1-2 parts of wetting agent, 20-40 parts of deionized water.
CN201811143828.7A 2018-09-29 2018-09-29 Frying pan Active CN109106197B (en)