CN110250918B - Non-stick frying pan - Google Patents
Non-stick frying pan Download PDFInfo
- Publication number
- CN110250918B CN110250918B CN201910654188.4A CN201910654188A CN110250918B CN 110250918 B CN110250918 B CN 110250918B CN 201910654188 A CN201910654188 A CN 201910654188A CN 110250918 B CN110250918 B CN 110250918B
- Authority
- CN
- China
- Prior art keywords
- parts
- stick
- pan
- coating
- percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a cooker, in particular to a non-stick frying pan. The pot comprises a pot body, a grid body and a non-stick coating, wherein the grid body is embedded into or pressed into the inner surface of the pot body, and ribs of the grid body protrude out of the inner surface of the pot body; the non-stick coating is sprayed on the inner surface of the pot body and filled in meshes of the grid body; the coating of the non-stick coating comprises the following components: 3-6 parts of graphene, 5-8 parts of PMMA-coated nano silver and SiO25-8 parts of coated nano aluminum powder, 5-8 parts of calcium carbonate coated nano titanium powder, 5-20 parts of polytetrafluoroethylene resin, 5-20 parts of acrylic latex, 10-20 parts of epoxy promoting resin, 1-2 parts of wetting agent and 20-40 parts of deionized water. The non-stick pan provided by the invention has the advantages that the safety of the non-stick pan is ensured, the high-temperature oxidation resistance of the non-stick pan is improved, and the service life of the non-stick pan is further ensured.
Description
Technical Field
The invention relates to a cooker, in particular to a non-stick frying pan.
Background
At present, people fry and fry food by using a metal product pot. However, the metal pot easily causes the phenomena of sticking, burning and the like of food, and is harmful to human health. From the 60 s of the 20 th century, the non-stick pan began to enter the family life, and the main principle thereof was: a layer of non-stick coating which takes polytetrafluoroethylene as a main raw material is sprayed on the surface of the pan body, the non-stick coating is tightly combined with the base material through high-temperature sintering, and the food is separated from the pan body by utilizing the strong chemical inertia of the non-stick coating, so that the non-stick effect is achieved. However, in the production process of polytetrafluoroethylene, raw materials harmful to human bodies and the environment are used, and thus it is necessary to research and develop green, environmentally friendly and non-stick cookware which is harmless to human bodies and the environment.
Disclosure of Invention
The invention aims to solve the problems in the prior art and provide a non-stick frying pan which is safe and has good high-temperature oxidation resistance.
The purpose of the invention can be realized by the following technical scheme: a non-stick frying pan comprises a pan body, a grid body and a non-stick coating, wherein the grid body is embedded into or pressed into the inner surface of the pan body, and ribs of the grid body protrude out of the inner surface of the pan body; the non-stick coating is sprayed on the inner surface of the pot body and filled in meshes of the grid body; the coating of the non-stick coating comprises the following groupsDividing into: 3-6 parts of graphene, 5-8 parts of PMMA-coated nano silver and SiO25-8 parts of coated nano aluminum powder, 5-8 parts of calcium carbonate coated nano titanium powder, 5-20 parts of polytetrafluoroethylene resin, 5-20 parts of acrylic latex, 10-20 parts of epoxy promoting resin, 1-2 parts of wetting agent and 20-40 parts of deionized water.
In the non-stick frying pan, the pan body is made of an aluminum alloy material, and the aluminum alloy material comprises the following components: 0.2-1.5% of Si, Fe: 0.1-0.3%, Mn0.5-1.5%, Y: 0.005-0.025%, Ce: 0.02-0.10 percent of silver, 0.2-2 percent of nano silver, 0.2-2 percent of aluminum powder, 0.2-2 percent of titanium powder, and the balance of Al and inevitable impurities.
According to the invention, the nano silver, the nano aluminum powder and the nano titanium powder are added into the aluminum alloy material of the pan body and the non-stick coating paint together, so that the non-stick coating is tightly combined with the pan body, the high-temperature oxidation resistance of the non-stick pan is improved while the safety of the non-stick pan is ensured, and the service life of the non-stick pan is further ensured.
Detailed Description
The following are specific examples of the present invention, which are illustrative of the technical solutions of the present invention and are not intended to limit the present invention.
Example 1
A non-stick frying pan comprises a pan body and is made of aluminum alloy materials, wherein the aluminum alloy materials comprise the following components: 0.8% of Si, Fe: 0.2%, Mn 1%, Y: 0.015%, Ce: 0.06 percent, 1.2 percent of nano silver, 1 percent of aluminum powder, 0.8 percent of titanium powder and the balance of Al and inevitable impurities;
the grid body is embedded into or pressed into the inner surface of the pot body, and ribs of the grid body protrude out of the inner surface of the pot body;
the non-stick coating is sprayed on the inner surface of the pot body and filled in the meshes of the grid body; the coating of the non-stick coating comprises the following components: 4 parts of graphene, 6 parts of PMMA-coated nano silver and SiO26 parts of coated nano aluminum powder, 6 parts of calcium carbonate coated nano titanium powder, 15 parts of polytetrafluoroethylene resin, 10 parts of acrylic latex, 15 parts of epoxy promoting resin, 1 part of wetting agent and 30 parts of deionized water.
Example 2
A non-stick frying pan comprises a pan body and is made of aluminum alloy materials, wherein the aluminum alloy materials comprise the following components: si 1.5%, Fe: 0.1%, Mn1.5%, Y: 0.005%, Ce: 0.10 percent of nano silver, 0.2 percent of nano silver, 2 percent of aluminum powder, 0.2 percent of titanium powder and the balance of Al and inevitable impurities;
the grid body is embedded into or pressed into the inner surface of the pot body, and ribs of the grid body protrude out of the inner surface of the pot body;
the non-stick coating is sprayed on the inner surface of the pot body and filled in the meshes of the grid body; the coating of the non-stick coating comprises the following components: 6 parts of graphene, 5 parts of PMMA-coated nano silver and SiO28 parts of coated nano aluminum powder, 5 parts of calcium carbonate coated nano titanium powder, 20 parts of polytetrafluoroethylene resin, 5 parts of acrylic latex, 20 parts of epoxy promoting resin, 1 part of wetting agent and 40 parts of deionized water.
Example 3
A non-stick frying pan comprises a pan body and is made of aluminum alloy materials, wherein the aluminum alloy materials comprise the following components: 0.2% of Si, Fe: 0.3%, Mn0.5%, Y: 0.025%, Ce: 0.02 percent of nano silver, 2 percent of nano silver, 0.2 percent of aluminum powder, 2 percent of titanium powder and the balance of Al and inevitable impurities;
the grid body is embedded into or pressed into the inner surface of the pot body, and ribs of the grid body protrude out of the inner surface of the pot body;
the non-stick coating is sprayed on the inner surface of the pot body and filled in the meshes of the grid body; the coating of the non-stick coating comprises the following components: 3 parts of graphene, 8 parts of PMMA-coated nano silver and SiO25 parts of coated nano aluminum powder, 8 parts of calcium carbonate coated nano titanium powder, 5 parts of polytetrafluoroethylene resin, 20 parts of acrylic latex, 10 parts of epoxy promoting resin, 2 parts of wetting agent and 20 parts of deionized water.
Comparative example 1
The paint formulation of the non-stick coating of this comparative example was compared to example 1 except that no nanosilver was added.
Comparative example 2
The paint formulation of the non-stick coating of this comparative example was compared to example 2 except that no nano-aluminum powder was added.
Comparative example 3
The paint formulation of the non-stick coating of this comparative example was compared to example 3, except that no nano-titanium powder was added.
Comparative example 4
Compared with the paint proportioning of the non-stick coating of the comparative example 1, the nano silver in the comparative example is not coated by PMMA, and the nano aluminum powder is not coated by SiO2And (4) coating, wherein the nano titanium powder is not coated with calcium carbonate.
The non-stick coating in the non-stick pan of examples 1-3 and comparative examples 1-4 was subjected to a performance test: the adhesion of the non-stick coating is tested by placing the non-stick coating in a constant temperature oven at 300 ℃ for 5h, and testing whether the tube coating film has shedding, blistering and cracking, and the change performance of the adhesion, and the test is shown in the table.
Table 1: properties of non-stick coating in non-stick Pan in examples 1-3 and comparative examples 1-4
In conclusion, the nano silver, the nano aluminum powder and the nano titanium powder are added into the aluminum alloy material of the pot body and the non-stick coating paint together, so that the non-stick coating is tightly combined with the pot body, the safety of the non-stick pot is ensured, the high-temperature oxidation resistance of the non-stick pot is improved, and the service life of the non-stick pot is further ensured.
The technical scope of the invention claimed by the embodiments herein is not exhaustive and new solutions formed by equivalent replacement of single or multiple technical features in the embodiments are also within the scope of the invention, and all parameters involved in the solutions of the invention do not have mutually exclusive combinations if not specifically stated.
The specific embodiments described herein are merely illustrative of the spirit of the invention. Various modifications or additions may be made to the described embodiments or alternatives may be employed by those skilled in the art without departing from the spirit or ambit of the invention as defined in the appended claims.
While the invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the spirit and scope thereof.
Claims (1)
1. A non-stick pan is characterized by comprising a pan body, a grid body and a non-stick coating, wherein the grid body is embedded into or pressed into the inner surface of the pan body, and ribs of the grid body protrude out of the inner surface of the pan body; the non-stick coating is sprayed on the inner surface of the pot body and filled in meshes of the grid body; the coating of the non-stick coating comprises the following components: 3-6 parts of graphene, 5-8 parts of PMMA-coated nano silver and SiO25-8 parts of coated nano aluminum powder, 5-8 parts of calcium carbonate coated nano titanium powder, 5-20 parts of polytetrafluoroethylene resin, 5-20 parts of acrylic latex, 10-20 parts of epoxy promoting resin, 1-2 parts of wetting agent and 20-40 parts of deionized water; the pot body be made by aluminum alloy material, aluminum alloy material's composition is: 0.2-1.5% of Si, Fe: 0.1-0.3%, Mn0.5-1.5%, Y: 0.005-0.025%, Ce: 0.02-0.10 percent of silver, 0.2-2 percent of nano silver, 0.2-2 percent of aluminum powder, 0.2-2 percent of titanium powder, and the balance of Al and inevitable impurities.