CN108893835A - A kind of moisture absorption keeps warm hollow cotton woven and its processing technology - Google Patents
A kind of moisture absorption keeps warm hollow cotton woven and its processing technology Download PDFInfo
- Publication number
- CN108893835A CN108893835A CN201811038426.0A CN201811038426A CN108893835A CN 108893835 A CN108893835 A CN 108893835A CN 201811038426 A CN201811038426 A CN 201811038426A CN 108893835 A CN108893835 A CN 108893835A
- Authority
- CN
- China
- Prior art keywords
- fabric
- moisture absorption
- processing technology
- washing
- cotton woven
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses a kind of processing technology of warming hollow cotton woven of moisture absorption:One, the weaving of fabric:Warp thread includes water-soluble long filament, and weft yarn includes water-soluble long filament;Two, it singes;Three, cold dome:Textile pad caustic soda, desizing enzyme and refining agent, clot are banked up for 24 hours;Wherein, amount of caustic soda control is in 100g/L, and temperature control is at 102 ± 2 DEG C, fabric with liquid rate 100%;Four, drift is boiled:Fabric after cold dome is carried out to boil drift using desizing, scouring and bleaching combined machine, successively by washing, decatize kiering, washing, decatize bleaching, washing, drying;Wherein, the control of kiering base amount is in 80g/L;Five, mercerising:Mercerising concentration of lye is controlled in 200g/L;Six, it dyes;Seven, finished product is formed:Use double fatty acyl amido soft finishing agents;Eight, pre- to shrink;Nine, air is washed.Product of the present invention can obtain the feel of lower grammes per square metre and more fluffy softness while guaranteeing identical appearance style, and have excellent moisture absorption warmth retention property.
Description
Technical field
The present invention relates to textile technology fields, and in particular to a kind of moisture absorption keeps warm hollow cotton woven and its processing technology.
Background technique
Since still air thermal coefficient is small, so contained still air is more in fabric, warming effect is better.It uses
The technology of terylene production doughnut applied it is more, but terylene due to snugness of fit it is poor, research natural fiber
Hollow yarns textile dyeing and finishing technology is very necessary.Tianjin Polytechnic University Ma Huiying in 2005 et al. uses polyvinyl as covering yarn,
Dimension, which is retreated, through weaving produces cotton hollow inclusion triaxial strain gauge.Donghua University Zhao Jing in 2008 so, Zhang Guangxu et al. produce cotton hollow yarns and
Porous yarn, and the porous yarn of cotton hollow yarns, cotton and conventional yarns have been inquired into for the warming effect comparison in knitted fabric, it obtains
Conclusion out:The cotton of hollow structure can obtain optimal moisture absorption warming effect for being knitted.
The course of dissolution of water-soluble poval (PVA) fiber is first to be swollen, and is redissolved.In hydrone enters when swelling
Portion increases fiber volume, but does not disintegrate.For the WATER-SOLUBLE PVA FIBER in fabric, due to the infiltration of hydrone be by
Table and in, so the PVA fiber of outer layer is first swollen, and forms thin film after being swollen and cover surface, hinder hydrone to
Inside is penetrated into.After the PVA Fibrinolysis and entrance aqueous solution of outer layer, the PVA fiber of internal layer could be swollen, dissolve.It is entire molten
It solves, move back dimension process and from outward appearance to inner essence carry out, need the long period.
Due to the limitation of production technology, production application of such yarn on cotton woven is always space state, this
Invention enables final finished to obtain the hand of more excellent moisture absorption warming effect and fluffy softness by improving production technology
Sense.
Summary of the invention
It is an object of the present invention to provide a kind of warming hollow cotton woven of moisture absorption and its processing technologys, to solve the prior art
It is insufficient.
The present invention uses following technical scheme:
A kind of processing technology of the warming hollow cotton woven of moisture absorption, includes the following steps:
Step 1: the weaving of fabric:Warp thread includes water-soluble long filament, and weft yarn includes water-soluble long filament;
Step 2: singing:Using gas gassing frame makes fabric pass sequentially through a positive and a negative twice singeing fire hole, singes
4 grades of grade or more;
Step 3: cold dome:Textile pad caustic soda, desizing enzyme and refining agent, clot are banked up for 24 hours;Wherein, amount of caustic soda control
System is in 100g/L, and temperature control is at 102 ± 2 DEG C, fabric with liquid rate 100%;
Step 4: boiling drift:Fabric after cold dome is carried out to boil drift using desizing, scouring and bleaching combined machine, successively by washing, steam cooker
Practice, washing, decatize bleaching, washing, drying;Wherein, the control of kiering base amount is in 80g/L;
Step 5: mercerising:Mercerising concentration of lye is controlled in 200g/L;
Step 6: dyeing;
Step 7: finished product is formed:Soft finish and stentering forming are carried out to fabric using forming machine;Wherein, soft finish
Use double fatty acyl amido soft finishing agents;
Step 8: pre- shrink:Combine preshrinking machine using rubber blanket-blanket, make fabric through to washing shrinkage control 3% with
It is interior;
Step 9: air is washed:Dry air is carried out to fabric using air washing machine to wash, and yarn is made to restore fluffy hollow state;
Wherein speed control is in 8-10m/min.
Further, Step 1: the weaving of fabric:16, warp thread, include a 50D water solubility long filament, remaining is fine for cotton
Dimension, weft yarn 12, include a 75D water solubility long filament, remaining is cotton fiber, and spinning system is compact spinning;Weaving process is the same as general
Logical cotton woven, density 108*56.
Further, the control of step 2 concentration of refining agent is in 5g/L.
Further, step 6 is dyed using pad dyeing.
The warming hollow cotton woven of moisture absorption that above-mentioned processing technology processing obtains.
Beneficial effects of the present invention:
1, the present invention increases pre-treatment cold dome, boils the alkali charge of drift to guarantee that water-soluble long filament can dissolve removal;It reduces
Mercerising alkali concentration keeps fabric feeling really up to the mark while guaranteeing mercerization effect;Use double fatty acyl amido soft finishing agents
Instead of traditional cation soft finishing agent, keep fabric feeling more plentiful, and there is preferable hydrophily;It is washed, is made by air
Yarn is restored to hollow structure, the more fluffy softness of feel.
2, the method for the present invention can guarantee water-soluble long filament by thorough dissolution removal, and required time is short, and yarn is made to restore fluffy
The hollow state of pine, the fabric of production is compared with the common fabric of identical yarn count specification, and grammes per square metre can reduce 22%, and thermal resistance is kept
Constant, dampness reduces by 7%.That is product can obtain lower grammes per square metre and more fluffy while guaranteeing identical appearance style
Soft feel, and there is excellent moisture absorption warmth retention property.
Specific embodiment
The present invention is done below with reference to embodiment and is further explained.The following example is merely to illustrate the present invention, but
It is not used to limit practical range of the invention.
Embodiment 1
The processing technology of the warming hollow cotton woven of moisture absorption
Step 1: the weaving of fabric:16, warp thread, include a 50D water solubility long filament, remaining is cotton fiber, weft yarn 12
Branch includes a 75D water solubility long filament, remaining is cotton fiber, and spinning system is compact spinning;Weaving process is the same as common cotton tatting
Object, density 108*56;Wherein, water-soluble long filament is vinal;
Step 2: singing:Using gas gassing frame makes fabric pass sequentially through a positive and a negative twice singeing fire hole, singes
4 grades of grade or more;
Step 3: cold dome:Textile pad caustic soda, desizing enzyme and refining agent, clot are banked up for 24 hours;Wherein, amount of caustic soda control
System is in 100g/L, and concentration of refining agent control is in 5g/L, and temperature control is at 102 ± 2 DEG C, fabric with liquid rate 100%;
Step 4: boiling drift:Fabric after cold dome is carried out to boil drift using desizing, scouring and bleaching combined machine, successively by washing, steam cooker
Practice, washing, decatize bleaching, washing, drying;Wherein, the control of kiering base amount is in 80g/L;
Step 5: mercerising:Mercerising concentration of lye is controlled in 200g/L;
Step 6: dyeing:It is dyed using pad dyeing;
Step 7: finished product is formed:Soft finish and stentering forming are carried out to fabric using forming machine;Wherein, soft finish
Use double fatty acyl amido soft finishing agents;
Step 8: pre- shrink:Combine preshrinking machine using rubber blanket-blanket, make fabric through to washing shrinkage control 3% with
It is interior, and further promote feel;
Step 9: air is washed:Dry air is carried out to fabric using air washing machine to wash, and yarn is made to restore fluffy hollow state;
Wherein speed control is in 8-10m/min.
It is above-mentioned not refer to that technique is well-known technique in industry.
Comparative example 1
The processing technology of normal conon woven
Step 1: 16, warp thread are cotton fiber, weft yarn 12 are cotton fiber;Step 3 cold dome:Textile pad is moved back
Enzyme is starched, 8h is banked up in clot;Step 4 kiering base amount is in 60g/L;Step 5 mercerising concentration of lye is in 220g/L;Step 7 uses
Cationic soft finishing agent;Without step 9;The other the same as in Example 1.
The normal conon tatting of the moisture absorption that embodiment 1 is obtained warming hollow cotton woven and the identical weave specification of comparative example 1
Object compares as follows in terms of grammes per square metre, feel, thermal resistance and dampness:
Grammes per square metre | Feel | Thermal resistance | Dampness | |
Hollow cotton woven | 230gsm | Fluffy softness | 0.02℃m2/W | 4.1(m2·Pa)/W |
Normal conon woven | 295gsm | It is stiffening | 0.02℃m2/W | 4.4(m2·Pa)/W |
Claims (5)
- The processing technology of hollow cotton woven 1. a kind of moisture absorption keeps warm, which is characterized in that include the following steps:Step 1: the weaving of fabric:Warp thread includes water-soluble long filament, and weft yarn includes water-soluble long filament;Step 2: singing:Using gas gassing frame makes fabric pass sequentially through a positive and a negative twice singeing fire hole, class 4 grade of singing More than;Step 3: cold dome:Textile pad caustic soda, desizing enzyme and refining agent, clot are banked up for 24 hours;Wherein, amount of caustic soda control exists 100g/L, temperature control is at 102 ± 2 DEG C, fabric with liquid rate 100%;Step 4: boiling drift:Fabric after cold dome is carried out to boil drift using desizing, scouring and bleaching combined machine, successively by washing, decatize kiering, water It washes, decatize bleaching, washing, drying;Wherein, the control of kiering base amount is in 80g/L;Step 5: mercerising:Mercerising concentration of lye is controlled in 200g/L;Step 6: dyeing;Step 7: finished product is formed:Soft finish and stentering forming are carried out to fabric using forming machine;Wherein, soft finish uses Double fatty acyl amido soft finishing agents;Step 8: pre- shrink:Combine preshrinking machine using rubber blanket-blanket, makes fabric through controlling within 3% to washing shrinkage;Step 9: air is washed:Dry air is carried out to fabric using air washing machine to wash, and yarn is made to restore fluffy hollow state;Wherein Speed is controlled in 8-10m/min.
- The processing technology of hollow cotton woven 2. moisture absorption according to claim 1 keeps warm, which is characterized in that Step 1: knitting The weaving of object:16, warp thread, include a 50D water solubility long filament, remaining is cotton fiber, weft yarn 12, water-soluble comprising a 75D Property long filament, remaining is cotton fiber, and spinning system is compact spinning;Weaving process is the same as common cotton woven, density 108*56.
- The processing technology of hollow cotton woven 3. moisture absorption according to claim 1 keeps warm, which is characterized in that step 2 refining Agent concentration is controlled in 5g/L.
- The processing technology of hollow cotton woven 4. moisture absorption according to claim 1 keeps warm, which is characterized in that step 6 uses Pad dyeing dyeing.
- The hollow cotton woven 5. the moisture absorption that the processing of processing technology described in claim 1-4 any claim obtains keeps warm.