CN108892537A - A kind of production method for having light glaze forming rice-shaped effect - Google Patents
A kind of production method for having light glaze forming rice-shaped effect Download PDFInfo
- Publication number
- CN108892537A CN108892537A CN201810840377.6A CN201810840377A CN108892537A CN 108892537 A CN108892537 A CN 108892537A CN 201810840377 A CN201810840377 A CN 201810840377A CN 108892537 A CN108892537 A CN 108892537A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- effect
- rice
- shaped
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to it is a kind of form rice-shaped effect have light glaze and preparation method thereof, including 35-45 a parts of potassium feldspar, 12-15 parts of calcite, Chenzhou washes 5-10 parts of mud, 3-7 parts of talcum, 3-7 parts of zirconium silicate, 2-5 parts of zinc oxide, silica 20-30 parts thin.Wet ball grinding, sieving, is tuned into the glaze slip of 45~60 Baume degrees, take appearance it is bright and clean green body leaching glaze after, glazed thickness 0.2-0.4mm, enter roller kiln burning at, it is burnt into 1210~1230 DEG C of oxidizing atmosphere, soak 0.4-1 hours, firing period is 4-4.5 hours.Ultrafine quartz powder that the present invention is, talcum, zirconium silicate are formed in the effect that contracting glaze occurs in the cooling stage of high temperature firing process.Present it is a kind of contract uniformly, orderly, size have cause, the glaze shaped like rice-shaped, then can be used as a kind of new decorative effect, be then a kind of completely new glazing effect.
Description
Technical field
The present invention relates to a kind of production methods for having light glaze for forming rice-shaped effect.
Background technique
Currently, ceramic product in the market does not have the glaze paint of rice-shaped.In domestic ceramics industry, contracting glaze is a kind of lacks
It falls into.If using the feature of its contracting glaze, develop it is a kind of contract uniformly, orderly, size have cause, the glaze shaped like rice-shaped, then may be used
As a kind of new decorative effect, then it is a kind of completely new glazing effect, can be used for decorative daily-use ceramics, the art pottery, building
Ceramic product increases its added value.
Summary of the invention
It is an object of the invention to utilize glaze shrinkage freckle formation mechenism, the small ultra-fine stone of thermal expansion coefficient is introduced in glaze
Ying Fen, talcum, zirconium silicate, then high temperature firing process cooling stage occur contracting glaze effect, contract uniformly, orderly, size
There are cause, the glaze shaped like rice-shaped, then can be used as a kind of new decorative effect, is a kind of completely new glazing effect, can be used for decorating
Domestic ceramics, the art pottery, architectural pottery product increase its added value.
The technical scheme is that：A kind of production method for having light glaze forming rice-shaped effect, it is characterised in that：
（1）By formula as below ingredient（Parts by weight）：
35-45 parts of potassium feldspar, 12-15 parts of calcite, Chenzhou washes 5-10 parts of mud, and 3-7 parts of talcum, 3-7 parts of zirconium silicate, oxygen
Change zinc 2-5 parts, 20-30 parts of micro silica.
（2）Wet ball grinding 12-20 hours, select material：Ball：Water=1:1.5:0.5-0.6；
（3）Glaze after ball milling crosses 80 meshes, then is tuned into the glaze slip of 45~60 Baume degrees of concentration；
（4）After the green body leaching glaze for taking appearance bright and clean, glazed thickness 0.2-0.4mm reenters roller kiln burning at 1210~1230
DEG C oxidizing atmosphere in be burnt into, soak 0.5-1 hours, firing period be 4-4.5 hour, gained glaze surface formation the grain of rice
Shape effect has light glaze.
A kind of grain of rice glaze that the present invention is produced by above-mentioned preparation method；Small ultra-fine of thermal expansion coefficient is introduced in glaze
Silica flour, talcum, zirconium silicate then occur the effect of contracting glaze in the cooling stage of high temperature firing process, contract uniformly, orderly, greatly
It is small to have cause, the glaze shaped like rice-shaped, then it can be used as a kind of new decorative effect, be then a kind of completely new glazing effect.
Specific embodiment
（1）By formula as below ingredient（Parts by weight）：
43 parts of potassium feldspar, 10 parts of calcite, Chenzhou washes 7 parts of mud, and 5 parts of talcum, 5 parts of zirconium silicate, 3 parts of zinc oxide, micro silica
27 parts.
（2）Wet ball grinding 12-20 hours, select material：Ball：Water=1:1.5:0.5；
（3）Glaze after ball milling crosses 80 meshes, then is tuned into the glaze slip of 45 Baume degrees of concentration；
（4）After the green body leaching glaze for taking appearance bright and clean, glazed thickness 0.2mm reenters roller kiln burning in 1210 DEG C of oxic gas
It being burnt into atmosphere, soak 0.5 hour, firing period is 4 hours, and formation rice-shaped effect in gained glaze surface has light glaze,
Uniform, orderly, size, which is presented, in glaze paint cause, the glaze shaped like rice-shaped, then can be used as a kind of new decorative effect, then is a kind of complete
New glazing effect.
Claims (2)
1. a kind of production method for having light glaze for forming rice-shaped effect, it is characterised in that：
（1）By formula as below ingredient（Parts by weight）：
35-45 parts of potassium feldspar, 12-15 parts of calcite, Chenzhou washes 5-10 parts of mud, and 3-7 parts of talcum, 3-7 parts of zirconium silicate, oxygen
Change zinc 2-5 parts, 20-30 parts of micro silica；
The sum of each component percentage composition is 100%；
（2）Wet ball grinding 12-20 hours, select material：Ball：Water=1:1.5:0.5-0.6；
（3）Glaze after ball milling crosses 80 meshes, then is tuned into the glaze slip of 45~60 Baume degrees of concentration；
（4）After the green body leaching glaze for taking appearance bright and clean, glazed thickness 0.2-0.4mm reenters roller kiln burning at 1210~1230
DEG C oxidizing atmosphere in be burnt into, soak 0.5-1 hours, firing period be 4-4.5 hour, gained glaze surface formation the grain of rice
Shape effect has light glaze.
2. a kind of rice-shaped effect of the method as described in claim 1 production has light glaze.