CN108892457A - A kind of fire resistant flame retardant material for building - Google Patents
A kind of fire resistant flame retardant material for building Download PDFInfo
- Publication number
- CN108892457A CN108892457A CN201810783555.6A CN201810783555A CN108892457A CN 108892457 A CN108892457 A CN 108892457A CN 201810783555 A CN201810783555 A CN 201810783555A CN 108892457 A CN108892457 A CN 108892457A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- flame retardant
- fire resistant
- resistant flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of fire resistant flame retardant materials for building, it is characterised in that：Raw material including following parts by weight：50-70 parts of aluminous refractory cement, 10-20 parts of flyash, 10-20 parts of Reactive alumina, 5-7 parts of expanded vermiculite powder, 3-6 parts of refractory brick powder, 30-35 parts of calcium stearate, 40-50 parts of diatomite, 2-4 parts of carbide slag, 3-5 parts of calcium carbonate crystal whisker, 20-30 parts of kaolin, 10-16 parts of sericite, 5-8 parts of mullite, 1-3 parts of magnesia, 3-5 parts of schorl powder, 1-3 parts of aluminium oxide, 1-4 parts of tea tree ethereal oil, 10-15 parts of N- dodecyl ethanol amine, 10-15 parts of white glue with vinyl, 70-100 parts of water.Construction material comprehensive performance of the invention is superior, and not only intensity is high, antibacterial is good, moreover, fire retardant property is good, is worthy to be popularized.
Description
Technical field
The present invention relates to a kind of construction materials, and in particular to a kind of fire resistant flame retardant material for building.
Background technique
The material used in construction projects is referred to as construction material.Construction material can be divided into structural material, ornament materials
With certain proprietary materials.Structural material includes timber, bamboo wood, stone material, cement, concrete, metal, brick and tile, ceramics, glass, work
Engineering plastics, composite material etc.；Ornament materials include various coating, paint, coating, veneer, assorted brick and tile, with special-effect
Glass；Proprietary material is referred to for waterproof, moisture-proof, anti-corrosion, fire prevention, fire-retardant, sound insulation, heat preservation, sealing etc..In order to preferably match
The needs for closing architectural engineering, providing a kind of fire resistant flame retardant material for building becomes particularly significant.
Summary of the invention
It is an object of the invention to：A kind of fire resistant flame retardant material for building is provided.
To achieve the goals above, the present invention provides the following technical solutions：
A kind of fire resistant flame retardant material for building, the raw material including following parts by weight：
50-70 parts of aluminous refractory cement, 10-20 parts of flyash, 10-20 parts of Reactive alumina, expanded vermiculite powder
5-7 parts, 3-6 parts of refractory brick powder, 30-35 parts of calcium stearate, 40-50 parts of diatomite, 2-4 parts of carbide slag, calcium carbonate crystal whisker 3-5
Part, 20-30 parts of kaolin, 10-16 parts of sericite, 5-8 parts of mullite, 1-3 parts of magnesia, 3-5 parts of schorl powder, aluminium oxide
1-3 parts, 1-4 parts of tea tree ethereal oil, 10-15 parts of N- dodecyl ethanol amine, 10-15 parts of white glue with vinyl, 70-100 parts of water.
Preferably, a kind of fire resistant flame retardant material for building further includes 3-6 parts of glass microballoon.
Preferably, a kind of fire resistant flame retardant material for building further includes 0.5-1 parts of cinder.
Preferably, a kind of fire resistant flame retardant material for building further includes 1-3 parts of zinc borate.
Preferably, a kind of fire resistant flame retardant material for building further includes 1-3 parts of white carbon black.
Preferably, a kind of fire resistant flame retardant material for building further includes 3-6 parts of medical stone powder.
Preferably, a kind of fire resistant flame retardant material for building, the raw material including following parts by weight：
55 parts of aluminous refractory cement, 12 parts of flyash, 12 parts of Reactive alumina, 6 parts of expanded vermiculite powder, refractory brick
4 parts of powder, 32 parts of calcium stearate, 45 parts of diatomite, 3 parts of carbide slag, 4 parts of calcium carbonate crystal whisker, 25 parts of kaolin, 12 parts of sericite,
6 parts of mullite, 2 parts of magnesia, 4 parts of schorl powder, 2 parts of aluminium oxide, 2 parts of tea tree ethereal oil, 4 parts of glass microballoon, cinder 0.6
Part, 2 parts of zinc borate, 2 parts of white carbon black, 4 parts of medical stone powder, 12 parts of N- dodecyl ethanol amine, 12 parts of white glue with vinyl, 80 parts of water.
Preferably, a kind of fire resistant flame retardant material for building, the raw material including following parts by weight：
60 parts of aluminous refractory cement, 18 parts of flyash, 18 parts of Reactive alumina, 5.5 parts of expanded vermiculite powder, fire resisting
5 parts of brick powder, 34 parts of calcium stearate, 47 parts of diatomite, 2.5 parts of carbide slag, 3.5 parts of calcium carbonate crystal whisker, 27 parts of kaolin, sericite
15 parts, 7 parts of mullite, 1.5 parts of magnesia, 3.5 parts of schorl powder, 1.5 parts of aluminium oxide, 3 parts of tea tree ethereal oil, glass microballoon 5
Part, 0.8 part of cinder, 1.5 parts of zinc borate, 1.5 parts of white carbon black, 5 parts of medical stone powder, 14 parts of N- dodecyl ethanol amine, white glue with vinyl
14 parts, 90 parts of water.
The beneficial effects of the present invention are：
Construction material comprehensive performance of the invention is superior, and not only intensity is high, antibacterial is good, moreover, fire retardant property is good, value
It must promote.
Specific embodiment
Embodiment 1
A kind of fire resistant flame retardant material for building, the raw material including following parts by weight：
50 parts of aluminous refractory cement, 10 parts of flyash, 10 parts of Reactive alumina, 5 parts of expanded vermiculite powder, refractory brick
3 parts of powder, 30 parts of calcium stearate, 40 parts of diatomite, 2 parts of carbide slag, 3 parts of calcium carbonate crystal whisker, 20 parts of kaolin, 10 parts of sericite,
5 parts of mullite, 1 part of magnesia, 3 parts of schorl powder, 1 part of aluminium oxide, 1 part of tea tree ethereal oil, 3 parts of glass microballoon, cinder 0.5
Part, 1 part of zinc borate, 1 part of white carbon black, 3 parts of medical stone powder, 10 parts of N- dodecyl ethanol amine, 10 parts of white glue with vinyl, 70 parts of water.
Embodiment 2
A kind of fire resistant flame retardant material for building, the raw material including following parts by weight：
55 parts of aluminous refractory cement, 12 parts of flyash, 12 parts of Reactive alumina, 6 parts of expanded vermiculite powder, refractory brick
4 parts of powder, 32 parts of calcium stearate, 45 parts of diatomite, 3 parts of carbide slag, 4 parts of calcium carbonate crystal whisker, 25 parts of kaolin, 12 parts of sericite,
6 parts of mullite, 2 parts of magnesia, 4 parts of schorl powder, 2 parts of aluminium oxide, 2 parts of tea tree ethereal oil, 4 parts of glass microballoon, cinder 0.6
Part, 2 parts of zinc borate, 2 parts of white carbon black, 4 parts of medical stone powder, 12 parts of N- dodecyl ethanol amine, 12 parts of white glue with vinyl, 80 parts of water.
Embodiment 3
A kind of fire resistant flame retardant material for building, the raw material including following parts by weight：
60 parts of aluminous refractory cement, 18 parts of flyash, 18 parts of Reactive alumina, 5.5 parts of expanded vermiculite powder, fire resisting
5 parts of brick powder, 34 parts of calcium stearate, 47 parts of diatomite, 2.5 parts of carbide slag, 3.5 parts of calcium carbonate crystal whisker, 27 parts of kaolin, sericite
15 parts, 7 parts of mullite, 1.5 parts of magnesia, 3.5 parts of schorl powder, 1.5 parts of aluminium oxide, 3 parts of tea tree ethereal oil, glass microballoon 5
Part, 0.8 part of cinder, 1.5 parts of zinc borate, 1.5 parts of white carbon black, 5 parts of medical stone powder, 14 parts of N- dodecyl ethanol amine, white glue with vinyl
14 parts, 90 parts of water.
Embodiment 4
A kind of fire resistant flame retardant material for building, the raw material including following parts by weight：
70 parts of aluminous refractory cement, 20 parts of flyash, 20 parts of Reactive alumina, 7 parts of expanded vermiculite powder, refractory brick
6 parts of powder, 35 parts of calcium stearate, 50 parts of diatomite, 4 parts of carbide slag, 5 parts of calcium carbonate crystal whisker, 30 parts of kaolin, 16 parts of sericite,
8 parts of mullite, 3 parts of magnesia, 5 parts of schorl powder, 3 parts of aluminium oxide, 4 parts of tea tree ethereal oil, 6 parts of glass microballoon, 1 part of cinder,
3 parts of zinc borate, 3 parts of white carbon black, 6 parts of medical stone powder, 15 parts of N- dodecyl ethanol amine, 15 parts of white glue with vinyl, 100 parts of water.
Embodiment 5
A kind of fire resistant flame retardant material for building, the raw material including following parts by weight：
60 parts of aluminous refractory cement, 18 parts of flyash, 18 parts of Reactive alumina, 5.5 parts of expanded vermiculite powder, fire resisting
5 parts of brick powder, 34 parts of calcium stearate, 47 parts of diatomite, 2.5 parts of carbide slag, 3.5 parts of calcium carbonate crystal whisker, 27 parts of kaolin, sericite
15 parts, 7 parts of mullite, 1.5 parts of magnesia, 3.5 parts of schorl powder, 1.5 parts of aluminium oxide, 3 parts of tea tree ethereal oil, N- dodecyl
14 parts of ethanol amine, 14 parts of white glue with vinyl, 90 parts of water.
Claims (8)
1. a kind of fire resistant flame retardant material for building, it is characterised in that：Raw material including following parts by weight：
50-70 parts of aluminous refractory cement, 10-20 parts of flyash, 10-20 parts of Reactive alumina, expanded vermiculite powder 5-7
Part, 3-6 parts of refractory brick powder, 30-35 parts of calcium stearate, 40-50 parts of diatomite, 2-4 parts of carbide slag, 3-5 parts of calcium carbonate crystal whisker, height
Soil 20-30 parts of ridge, 10-16 parts of sericite, 5-8 parts of mullite, 1-3 parts of magnesia, 3-5 parts of schorl powder, aluminium oxide 1-3
Part, 1-4 parts of tea tree ethereal oil, 10-15 parts of N- dodecyl ethanol amine, 10-15 parts of white glue with vinyl, 70-100 parts of water.
2. a kind of fire resistant flame retardant material for building according to claim 1, it is characterised in that：It further include glass microballoon 3-6
Part.
3. a kind of fire resistant flame retardant material for building according to claim 2, it is characterised in that：It further include 0.5-1 parts of cinder.
4. a kind of fire resistant flame retardant material for building according to claim 3, it is characterised in that：It further include 1-3 parts of zinc borate.
5. a kind of fire resistant flame retardant material for building according to claim 4, it is characterised in that：It further include 1-3 parts of white carbon black.
6. a kind of fire resistant flame retardant material for building according to claim 5, it is characterised in that：It further include medical stone powder 3-6
Part.
7. a kind of fire resistant flame retardant material for building according to claim 6, it is characterised in that：Original including following parts by weight
Material：
55 parts of aluminous refractory cement, 12 parts of flyash, 12 parts of Reactive alumina, 6 parts of expanded vermiculite powder, refractory brick powder 4
Part, 32 parts of calcium stearate, 45 parts of diatomite, 3 parts of carbide slag, 4 parts of calcium carbonate crystal whisker, 25 parts of kaolin, 12 parts of sericite, Mo Lai
6 parts of stone, 2 parts of magnesia, 4 parts of schorl powder, 2 parts of aluminium oxide, 2 parts of tea tree ethereal oil, 4 parts of glass microballoon, 0.6 part of cinder, boron
2 parts of sour zinc, 2 parts of white carbon black, 4 parts of medical stone powder, 12 parts of N- dodecyl ethanol amine, 12 parts of white glue with vinyl, 80 parts of water.
8. a kind of fire resistant flame retardant material for building according to claim 6, it is characterised in that：Original including following parts by weight
Material：
60 parts of aluminous refractory cement, 18 parts of flyash, 18 parts of Reactive alumina, 5.5 parts of expanded vermiculite powder, refractory brick powder
5 parts, 34 parts of calcium stearate, 47 parts of diatomite, 2.5 parts of carbide slag, 3.5 parts of calcium carbonate crystal whisker, 27 parts of kaolin, sericite 15
Part, 7 parts of mullite, 1.5 parts of magnesia, 3.5 parts of schorl powder, 1.5 parts of aluminium oxide, 3 parts of tea tree ethereal oil, 5 parts of glass microballoon,
0.8 part of cinder, 1.5 parts of zinc borate, 1.5 parts of white carbon black, 5 parts of medical stone powder, 14 parts of N- dodecyl ethanol amine, white glue with vinyl 14
Part, 90 parts of water.