CN108866724A - Silk Wool and preparation method thereof - Google Patents
Silk Wool and preparation method thereof Download PDFInfo
- Publication number
- CN108866724A CN108866724A CN201811029244.7A CN201811029244A CN108866724A CN 108866724 A CN108866724 A CN 108866724A CN 201811029244 A CN201811029244 A CN 201811029244A CN 108866724 A CN108866724 A CN 108866724A
- Authority
- CN
- China
- Prior art keywords
- silk
- wool
- cocoon
- ripe
- yarns
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
To solve the deficiencies in the prior art, the present invention provides a kind of silk Wools, including:The wool yarns of core.8 or more silk are bonded on the wool yarns lateral wall.The content of the silk is:25-40%.The silk Wool is arrived by prepared by following methods:S1. qualified raw material cocoon is selected;S2. peeling, work of selecting silkworm are carried out;S3. ripe silk head is drawn after carrying out beating, shaking processing to ripe cocoon, and 2 or more ripe silk heads are adhered in wool yarns;S4. the silk being adhered in wool yarns is rotated;Silk thread after bonding carries out twisting sheath operation;S5. the silk thread thickness after twisting sheath is detected;S6. drying operation twice is carried out to the silk thread after detection, it will be on the silk thread network to silk cylinder after drying;Cut off during winder rough defect and.Silk Wool of the present invention has characteristic laniferous and silk characteristic simultaneously, and is not in wide anxious stock, saves the later period and weaves cost.
Description
Technical field
The invention belongs to functional real silk preparation technical fields, and in particular to a kind of silk Wool and its preparation side
Method.
Background technique
Silk refers generally to mutually twist the silk that spins being prepared by silk cocoon silk, refers generally to Bombyx-mori Bave.Silk is referred to as " fiber
Queen ", with its favor of the unique glamour by people through the ages.Silk belongs to protein fibre, contains 18 kinds in fibroin
The amino acid beneficial to human body.Excellent characteristics based on silk, silk are widely used in fields such as clothing, bedding.But
It is that, since silk warmth retention property itself is poor, the silk with part silk characteristic and other fabric properties that has been born is mixed
Textile fabric.Existing silk Wool generally carries out and closes weaving by knitting factory, and structure is general as shown in Figure 1, will be true
Silk 3 forms stock silk after twisting simultaneously with wool yarns 1 two mutually independent silk threads.But this kind of stock silk has the following disadvantages:Silk with
Strength, the elongation of wool yarns have different, i.e.,:The strength of silk is in 4 grams of force per Denier Neils or so, and elongation is on 20% left side
The right side, wool yarns are all lower compared to silk, therefore, wide anxious stock are also easy to produce during making fabric.Meanwhile in same isostension
The case where under, the problem of this kind of stock silk is easy to appear a kind of silk and is straightened, another silk fold or broken end.
Summary of the invention
In view of the problems of the existing technology the present invention, provides a kind of silk Wool, including:Core is linear
Or the wool yarns of near linear setting.8 or more the single natural silks not overlapped are bonded on the wool yarns lateral wall.It is described
The silk thread direction of 8 or more silk is identical and is parallel to each other.The silk content of the composite filament is:25-40%.
Further, it is attached to the silk on the wool yarns surface, the silk gum having by its own and the sheep
Wool yarn bonding.
Further, the silk Wool is prepared by the following method:
S1. qualified raw material cocoon is selected.
S2. peeling, work of selecting silkworm are carried out.After the husks for peeling silk cocoon off, by selecting silkworm, reject light defective cocoon, damaged cocoon and other
The cocoon of unsuitable production.It is stand-by by ripe cocoon is obtained after the progress cocoon cooking operation of gained cocoon.
S3. ripe cocoon is carried out drawing ripe silk head after beating, shaking processing, and by 2 or more ripe silk heads from different
Position is adhered in wool yarns with identical tangential angle.
S4. the silk being adhered in wool yarns is rotated, so that the silk thread of each ripe cocoon is parallel to each other and is bonded in wool yarns.Bonding
Silk thread afterwards carries out twisting sheath operation, twists sheath length 15-18cm.
S5. the silk thread thickness after twisting sheath is detected, when twist the silk thread after sheath it is meticulous when, the new ripe silk of supplement adherency
Head, and continue to carry out rotation bonding described in step S4 and twist sheath operation.
S6. to the Filament winding after detection smallUpper progress first time drying.It carries out drying for second later.Second
It, will be wound on small after dryingOn composite filament using on bobbin-winding machine network to silk cylinder.Rough defect is cut off during winder.
Further, raw material cocoon qualified described in step S1 is:Reelability percentage is greater than 70%, and myriametre is hung time lower than 2.5 times,
The neat rate of cocoon width is greater than 75% raw material cocoon.
Further, when carrying out beating operation described in step S3, control operation temperature is:86-94℃.Carry out step S3 institute
When stating shaking operation, control operation temperature is:38-42℃.
Further, tangential angle described in step S3 is 30-50 °.The tangential angle is silk axis and wool axis
Between included angle.
Further, it is attached the wool yarns of ripe cocoon silk described in step S3, is controlled by tension controller, makes wool yarns
It is being adhered to wound on smallOn process in, keep 0.03-0.06 grams of force per Denier Neil tension.
Further, it is parallel to each other and is bonded between the ripe cocoon silk of wool yarns described in step S4, there is 0.01-
The spacing of 0.05mm.
Further, when rotating the silk being adhered in wool yarns described in step S4, keep ripe cocoon positioned at 40-45 DEG C
In hot water environment.
Further, drying includes for the first time described in step S6:Under the conditions of 105-120 DEG C of steam hot wind, 5- is dried
30 seconds.Drying includes for the second time described in step S6:The small of silk thread will have been woundIt is placed in 105-120 DEG C of drying room and dries
It is 5-8 hours dry.
One of the present invention has at least the following advantages:
1. composite filament of the present invention has silk and wool characteristic, when the later period knits factory's weaving, under same isostension, energy
Guarantee that silk is flat very, compound (1) silk thread will not break or generate wide anxious stock.Also, it is straight with wool yarns to be significantly reduced weaving mill
When engaging stock, due to generating the fabric flaw point of wide anxious stock initiation.
2. silk Wool of the present invention, solve that knit wool yarns or silk when factory's silk is weaved together with wool yarns easy
The difficult point of broken end.
3. silk Wool of the present invention, and can reduce knit factory impregnated, the processing charges of reeling, doubling process
With feedstock processing expense, at least 30,000 yuan/ton of silks can be saved.
4. the silk Wool that silk Wool preparation method of the present invention is prepared, silk and wool yarns it
Between bond securely, finished product is generally not in the problem of silk falls off, and finished product yields can reach 95% or more, greatly subtract
Cost of spinning is lacked.
Detailed description of the invention
Fig. 1 show the structural schematic diagram of existing silk Wool.
Fig. 2 show the structural schematic diagram of silk Wool of the present invention.
Fig. 3 show the silk glued construction schematic diagram of silk Wool of the present invention.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, below in conjunction with attached drawing, to the present invention into
One step is described in detail.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not used to limit this
Invention.
Embodiment 1
A kind of silk Wool, as shown in Fig. 2, including:Core linearly or near linear setting wool yarns 1.
Bonding is enclosed with the silk 2 of 8 or 16 or 18 or 32 or other quantity on 1 lateral wall of wool yarns.The silk 2
Dosage depend on meet on 1 lateral wall of wool yarns wrap up silk 2 necessary dosage.The silk thread side of each silk 2
To identical and be parallel to each other, 2 content of silk of the composite filament is:30%.Applicant has found after study, using this kind of structure
The silk Wool of preparation needs the content of strict control silk 2 therein between 25%-40%, otherwise is easy
The problem of existing composite filament comprehensive performance decline.In addition, comparing existing structure, silk is in wool using the composite filament of this kind of structure
The distribution on yarn surface is even closer, and tension distribution is uniform.
The silk Wool is arrived by prepared by following methods:
S1. qualified raw material cocoon is selected.
S2. peeling, work of selecting silkworm are carried out.After the husks for peeling silk cocoon off, by selecting silkworm, reject light defective cocoon, damaged cocoon and other
The cocoon of unsuitable production.It is stand-by by ripe cocoon is obtained after the progress cocoon cooking operation of gained cocoon.
S3. the silk thread head that ripe silk 2 is drawn after beating, shaking processing is carried out to ripe cocoon, and by 2 or 3 or 4 or 6
The silk thread head of root or the ripe silk 2 of other quantity is adhered in wool yarns 1 from different positions with identical tangential angle.Institute
Stating beating is the process that thread silk is drawn from the cocoon layer surface of ripe cocoon.The shaking is will to pass through beating groped end cocoon cocoon layer surface
Mixed and disorderly thread silk removes, and is processed into the process of the positive end cocoon of a cocoon one.
S4. the silk being adhered in wool yarns 1 is rotated, so that the silk thread of each ripe cocoon is parallel to each other and is bonded in wool yarns 1.
Silk thread after bonding carries out twisting sheath operation, twists sheath length 17cm.The twirl sheath is exactly to pass through machine part, utilizes section before and after strand
Mutually twist the process twisted.The sheath length of twisting is the length mutually twisted and twisted.
S5. the silk thread thickness after twisting sheath is detected, when twist the silk thread after sheath it is meticulous when, the new ripe silk of supplement adherency
2 silk thread head, and continue to carry out rotation bonding described in step S4 and twist sheath operation.It has been found that silk thread mistake after twisting sheath
When thin, that is, it is insufficient to represent the silk 2 bonded in wool yarns 1.By detection-increasing silk operation of the step, sheep can be effectively prevented
The problem of there is silk 2 and bonds deficiency in 1 surface of wool yarn, bonds even without silk 2.
S6. to the Filament winding after detection smallOn in driving operation process carry out first time drying.It carries out later
Second of drying.It, will be wound on small after second driesOn composite filament using on bobbin-winding machine network to silk cylinder.In winder
Rough defect is cut off in the process.Applicant has found after study, should if carrying out excision operation to the silk thread for having rough defect in step S5
Although operation can cut off rough defect at the first time, it can also cause wool yarns 1, which silk 2 occur in this section, bonds unstable show
As causing product quality wild effect occur.And rough defect excision operation is carried out during last winder, at this point, silk sheep
Hair composite filament has been formed, and the package stability of silk thread will not be influenced carrying out excision operation, to improve the matter of product
Measure stability.
Embodiment 2
Based on silk Wool described in embodiment 1, qualified raw material cocoon described in step S1 is:Reelability percentage is greater than
70%, myriametre hangs secondary lower than 2.5 times, raw material cocoon of the neat rate of cocoon width greater than 75%.It is available using the raw material cocoon of the standard
The higher silk Wool of quality, reduce preparation process in 2 breaks of silk the problem of, stablize silk Wool it is thick
Carefully.
Embodiment 3
Based on silk Wool described in embodiment 1, when carrying out beating operation described in step S3, operation temperature is controlled
For:94℃.When carrying out the operation of shaking described in step S3, control operation temperature is:42℃.
Embodiment 4
Based on silk Wool described in embodiment 1, when carrying out beating operation described in step S3, operation temperature is controlled
For:86℃.When carrying out the operation of shaking described in step S3, control operation temperature is:38℃.
Embodiment 5
Based on silk Wool described in embodiment 1, when carrying out beating operation described in step S3, operation temperature is controlled
For:90℃.When carrying out the operation of shaking described in step S3, control operation temperature is:40℃.
Using beating operation is carried out in beating operating temperature range described in embodiment 3-5, not only separated by beating silk cocoon
Effect is preferable, is easy to carry out beating operation, and is not in the phenomenon that silk cocoon is by well-done or gelatinization.Using embodiment 3-5 institute
It states and carries out shaking operation in shaking operating temperature range, can effectively control the silk thread separation property of silk cocoon, convenient for finding single line
Captacula.
Embodiment 6
Based on silk Wool described in embodiment 1, tangential angle described in step S3 is 50 °;The tangential angle is
Included angle between the axis of silk 2 and the axis of wool yarns 1.It is attached the wool yarns 1 of ripe silk 2 described in step S3, leads to
The control of overtension controller, is being adhered to wool yarns 1 wound on smallOn process in, keep 0.06 grams of force per Denier Neil
Tension.It is parallel to each other and is bonded between 2 line of ripe silk of wool yarns 1 described in step S4, the spacing with 0.05mm.
Embodiment 7
Based on silk Wool described in embodiment 1, tangential angle described in step S3 is 30 °;The tangential angle is
Included angle between 1 axis of 2 axis of silk and wool yarns.The wool yarns 1 of ripe silk 2 are attached described in step S3, by opening
Force controller control, is being adhered to wool yarns 1 wound on smallOn process in, keep 0.03 grams of force per Denier Neil
Power.It is parallel to each other and is bonded between 2 line of ripe silk of wool yarns 1 described in step S4, the spacing with 0.01mm.
Embodiment 8
Based on silk Wool described in embodiment 1, tangential angle described in step S3 is 40 °;The tangential angle is
Included angle between 2 axis of silk and wool axis.It is attached the wool yarns 1 of ripe silk 2 described in step S3, passes through tension
Controller control, is being adhered to wool yarns 1 wound on smallOn process in, keep 0.04 grams of force per Denier Neil tension.
It is parallel to each other and is bonded between 2 line of ripe silk of wool yarns 1 described in step S4, the spacing with 0.03mm.
Using tangential angle described in embodiment 6-8, silk 2 can be effectively controlled in the adhesive capacity on 1 surface of wool yarns, and is protected
Keep steady fixed production efficiency.
Using the tension of wool yarns 1 described in embodiment 6-8, wool can be made to keep as straight as possible, so that silk 2 be made to exist
Adherency makes to can produce necessary stress, is adhered to the silk gum on 2 surface of silk firmly in wool yarns 1.Meanwhile in the stress
Under, 1 surface of wool yarns on the basis of not influencing intensity itself, can be such that the surface silk thread unit of wool yarns 1 itself mutually produces
Further strengthen the adherency firmness of silk 2 so as to be conducive to the infiltration of 2 silk gum of silk in raw small interval.
Using the spacing between 2 line of ripe silk described in embodiment 6-8, effective 2 amount of silk control and sheep may be implemented
2 distributed degrees of silk on hair surface improve the uniformity of dyeing effect while keeping silk characteristic.
Embodiment 9
Based on silk Wool described in embodiment 1, when rotation described in step S4 is adhered to the ripe cocoon in wool yarns 1,
Keep ripe cocoon in 45 DEG C of hot water environment.
Embodiment 10
Based on silk Wool described in embodiment 1, when rotation described in step S4 is adhered to the ripe cocoon in wool yarns 1,
Keep ripe cocoon in 40 DEG C of hot water environment.
Embodiment 11
Based on silk Wool described in embodiment 1, when rotation described in step S4 is adhered to the ripe cocoon in wool yarns 1,
Keep ripe cocoon in 40 DEG C of hot water environment.
Applicant has found after study, although silk 2 can also be wrapped in wool surfaces at room temperature, at this point,
The surface of silk 2 and wool yarns 1 only passes through physical friction power and mutually attaches, and may still can occur in water-washing process certain
Mutually sliding, deforms so as to cause composite filament.And silk cocoon is placed in hot water environment described in embodiment 7-9, it can make
The natural silk gum on 2 surface of silk has certain viscosity, to make silk 2 as shown in figure 3, can adhere to by natural silk glue-line
It is mutually adhesively fixed on 1 surface of wool yarns, and with the villus 101 on 1 surface of wool yarns, reduces silk 2 with wool yarns 1 and phase occurs
Mutually while sliding, a possibility that silk 2 falls off is reduced.
Embodiment 12
Based on silk Wool described in embodiment 1, twirl sheath described in step S4 is operated, and twists sheath length 18cm.
Embodiment 13
Based on silk Wool described in embodiment 1, twirl sheath described in step S4 is operated, and twists sheath length 16cm.
Embodiment 14
Based on silk Wool described in embodiment 1, twirl sheath described in step S4 is operated, and twists sheath length 15cm.
Applicant has found after study, for the silk Wool of structure of the invention, twists sheath length according to silk sheep
Hair composite filament fineness, control twirl sheath length can play in 15-18cm effectively to be distributed moisture content, enhancing obvolvent, removes
The effect of Bu Fen little Lei.It is too short to will lead to the phenomenon that silk 2 is separated from each other with wool yarns 1 appearance.
Embodiment 15
Based on silk Wool described in embodiment 1, drying includes for the first time described in step S6:In 120 DEG C of steam
Under the conditions of hot wind, dry 5 seconds.Drying includes for the second time described in step S6:The small of silk thread will have been woundIt is placed on 120 DEG C of baking
Drying 5 hours in dry chamber.
Embodiment 16
Based on silk Wool described in embodiment 1, drying includes for the first time described in step S6:In 105 DEG C of steam
Under the conditions of hot wind, dry 30 seconds.Drying includes for the second time described in step S6:The small of silk thread will have been woundIt is placed on 105 DEG C
Drying 8 hours in drying room.
Embodiment 17
Based on silk Wool described in embodiment 1, drying includes for the first time described in step S6:In 110 DEG C of steam
Under the conditions of hot wind, dry 15 seconds.Drying includes for the second time described in step S6:The small of silk thread will have been woundIt is placed on 11 DEG C of baking
Drying 6 hours in dry chamber.
Applicant has found after study, using traditional first drying technology, it is easy to occur smallExternal silk thread is de-
Water is serious, thus there is the problems such as hardening, embrittlement, and internal silk thread dries deficiency, and silk thread occur is mutually bonded, to remove
It is difficult, silk 2 adheres to insecure, silk 2 and shrinks under hygrothermal environment leads to 1 fold of wool yarns.Using the technology,
Primary quickly damp and hot drying, can make silk Wool that extra moisture be discharged, while keeping certain flexibility, with
Just by silk Wool wound on smallOn, while silk 2 and wool silk have carried out a degree of contraction, but rolling up
It is flat around it is carried out by force.Second drying carries out in arid and hot environment, due to silk thread itself eliminated it is extra
Moisture, the effect that second drying primarily serves and reduces regain, reduces deadlocked power can be with when silk thread being made to carry out winder operation
It is smoothly sequentially unwound, is not in fluffing and cutting phenomenon.Wool yarns 1 and silk 2 can be made to be formed simultaneously, eliminate phase
Mutual internal stress reduces composite filament and occurs the asynchronous shrinking percentage of silk 2 and wool yarns 1 during the drying process, utmostly keeps away
Exempt from the possibility that composite filament generates fold.
One of the present invention has at least the following advantages:
1. composite filament of the present invention has silk and wool characteristic, when the later period knits factory's weaving, under same isostension, energy
Guarantee that silk is flat very, compound (1) silk thread will not break or generate wide anxious stock.Also, it is straight with wool yarns to be significantly reduced weaving mill
When engaging stock, due to generating the fabric flaw point of wide anxious stock initiation.
2. silk Wool of the present invention, solve that knit wool yarns or silk when factory's silk is weaved together with wool yarns easy
The difficult point of broken end.
3. silk Wool of the present invention, and can reduce knit factory impregnated, the processing charges of reeling, doubling process
With feedstock processing expense, at least 30,000 yuan/ton of silks can be saved.
4. the silk Wool that silk Wool preparation method of the present invention is prepared, silk and wool yarns it
Between bond securely, finished product is generally not in the problem of silk falls off, and finished product yields can reach 95% or more, greatly reduce
Cost of spinning.
It should be noted that and understand, in the case where not departing from spirit and scope required by the claims in the present invention, energy
It is enough that various modifications and improvements are made to the present invention of foregoing detailed description.It is therefore desirable to protection technical solution range not by
The limitation of given any specific exemplary teachings.
Claims (10)
1. silk Wool, which is characterized in that including:Core linearly or near linear setting wool yarns;The sheep
8 or more single natural silks parallel each other are bonded on wool yarn lateral wall;The silk content of the composite filament is:25-40%.
2. silk Wool according to claim 1, which is characterized in that it is attached to the silk on the wool yarns surface,
The silk gum having by silk itself and the wool yarns bond.
3. silk Wool according to claim 1, which is characterized in that the silk Wool passes through following sides
Method is prepared:
S1. qualified raw material cocoon is selected;
S2. peeling, work of selecting silkworm are carried out;After the husks for peeling silk cocoon off, by selecting silkworm, light defective cocoon, damaged cocoon and other discomforts are rejected
The cocoon of symphysis production;It is stand-by by ripe cocoon is obtained after the progress cocoon cooking operation of gained cocoon;
S3. ripe cocoon is carried out drawing ripe silk head after beating, shaking processing, and by 2 or more ripe silk heads from different positions,
It is adhered in wool yarns with identical tangential angle;
S4. the silk being adhered in wool yarns is rotated, so that the silk thread of each ripe cocoon is parallel to each other and is bonded in wool yarns;After bonding
Silk thread carries out twisting sheath operation, twists sheath length 15-18cm;
S5. the silk thread thickness after twisting sheath is detected, when twist the silk thread after sheath it is meticulous when, the new ripe silk head of supplement adherency,
And continues to carry out rotation bonding described in step S4 and twist sheath operation;
S6. to the Filament winding after detection smallUpper progress first time drying;It carries out drying for second later;Second of drying
After, it will be wound on smallOn composite filament using on bobbin-winding machine network to silk cylinder;Rough defect is cut off during winder.
4. silk Wool according to claim 3, which is characterized in that qualified raw material cocoon described in step S1 is:Solution
The rate of relaxing is greater than 70%, and myriametre hangs secondary lower than 2.5 times, raw material cocoon of the neat rate of cocoon width greater than 75%.
5. silk Wool according to claim 3, which is characterized in that when carrying out beating operation described in step S3, control
Operation temperature processed is:86-94℃;When carrying out the operation of shaking described in step S3, control operation temperature is:38-42℃.
6. silk Wool according to claim 3, which is characterized in that tangential angle described in step S3 is 30-50 °;
Included angle of the tangential angle between silk axis and wool axis.
7. silk Wool according to claim 3, which is characterized in that be attached the sheep of ripe cocoon silk described in step S3
Wool yarn is controlled by tension controller, is being adhered to wool yarns wound on smallOn process in, keep 0.03-0.06
The tension of grams of force per Denier Neil.
8. silk Wool according to claim 3, which is characterized in that be parallel to each other described in step S4 and be bonded in wool
Between the ripe cocoon silk of yarn, the spacing with 0.01-0.05mm.
9. silk Wool according to claim 3, which is characterized in that rotation described in step S4 is adhered in wool yarns
Silk when, keep ripe cocoon in 40-45 DEG C of hot water environment.
10. silk Wool according to claim 3, which is characterized in that drying includes for the first time described in step S6:?
Under the conditions of 105-120 DEG C of steam hot wind, dry 5-30 seconds;Drying includes for the second time described in step S6:Silk thread will have been wound
It is smallIt is placed on drying 5-8 hours in 105-120 DEG C of drying room.