CN108864866A - 一种建筑外墙涂料及其制备方法 - Google Patents
一种建筑外墙涂料及其制备方法 Download PDFInfo
- Publication number
- CN108864866A CN108864866A CN201810560439.8A CN201810560439A CN108864866A CN 108864866 A CN108864866 A CN 108864866A CN 201810560439 A CN201810560439 A CN 201810560439A CN 108864866 A CN108864866 A CN 108864866A
- Authority
- CN
- China
- Prior art keywords
- parts
- acrylic emulsion
- building external
- expanded vermiculite
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种建筑外墙涂料,包括以下质量分数的组分:乳液基料100份、填料20‑40份、水15‑35份、乙二醇3‑6份、聚丙烯酸钠1‑3份、六偏磷酸钠2‑3份、羟乙基纤维素1‑4份、十二烷基苯磺酸钠1‑3份、矿物油消泡剂0.5‑1.5份、对氯间二甲基苯酚1‑4份,乳液基料包括纯丙乳液65‑85份、苯丙乳液15‑35份、氯丁胶乳0‑3份,填料包括云母粉15‑35份、改性膨胀蛭石5‑10份;并且提供了涂料的制备方法。本发明的有益效果是:本发明的涂料固着效果好、成膜稳定;由本发明的涂料制成的涂膜质感柔和、耐冲击性强,耐侯性和耐温变性好、不容易开裂,使用寿命长;本发明的制备方法简便、对设备要求不高,易于大规模推广应用。
Description
技术领域
本发明涉及涂料领域,尤其涉及一种建筑外墙涂料及其制备方法。
背景技术
涂料,我们平常所说的油漆只是其中的一种,指涂布于物体表面在一定的条件下能形成薄膜而起保护、装饰或其他特殊功能(绝缘、防锈、防霉、耐热等)的一类液体或固体材料。近年来,水性化、环保化、多功能化和高性能化已经成为建筑外墙涂料发展的趋势。
目前,我国采用的外墙涂料主要以丙烯酸乳液为基料,水性丙烯酸涂料具有成本适中、耐候性好、可调整性大等优点,是近年来发展十分速的一类涂料产品。
涂料在实际应用中往往会曝露在不同季节、不同气候条件下,随着季节、气候条件的变化,经常会出现起泡、粉化、开裂、剥落等现象,直接影响到涂料的使用寿命。有些涂料在北方地区出现此类现象的程度尤甚于南方地区,究其原因发现除了涂料的耐候性和耐低温性外,涂料的耐温变性也是影响使用寿命的一个重要的因素。耐温变性指涂膜经受高温和低温急速变化情况时,抵抗被破坏的能力。耐温变性差的涂膜在骤冷骤热情况下,由于涂膜机械强度变化会引起的开裂、起泡、脱皮等破坏现象。
发明内容
为了解决以上技术问题,本发明提供了一种固着效果好、成膜稳定、不容易开裂并且使用寿命长的建筑外墙涂料。
为了实现上述发明目的,本发明提供了一种建筑外墙涂料,所述涂料包括以下质量分数的组分:乳液基料100份、填料20-40份、水15-35份、乙二醇3-6份、聚丙烯酸钠1-3份、六偏磷酸钠2-3份、羟乙基纤维素1-4份、十二烷基苯磺酸钠1-3份、矿物油消泡剂0.5-1.5份、对氯间二甲基苯酚1-4份。
所述乳液基料包括纯丙乳液65-85份、苯丙乳液15-35份、氯丁胶乳0-3份;所述填料包括云母粉15-35份、改性膨胀蛭石5-10份。
所述改性膨胀蛭石的制备方法为:将膨胀蛭石加入相对于膨胀蛭石质量20-25倍的浓度为0.2-0.4mol/L的氢氧化钠溶液中,50-60℃搅拌1-2小时,冷却至室温后加入相对于膨胀蛭石质量2-4%的乙二醇继续搅拌20-40分钟,然后进行过滤、洗涤至中性,然后加入到相对于膨胀蛭石质量5-10倍浓度为3-6%的磷酸氢二铵溶液中,浸渍搅拌2-4小时形成均匀浆液,然后经过滤、100-120℃干燥1-2h、500℃焙烧2-4h得到改性膨胀蛭石。
优选地,所述涂料包括以下质量分数的组分:纯丙乳液65份、苯丙乳液35份、氯丁胶乳0份、云母粉20份、改性膨胀蛭石10份、水20份、乙二醇3份、聚丙烯酸钠3份、六偏磷酸钠2份、羟乙基纤维素2份、十二烷基苯磺酸钠2份、矿物油消泡剂1.5份、对氯间二甲基苯酚3份。
优选地,所述涂料包括以下质量分数的组分:纯丙乳液80份、苯丙乳液17份、氯丁胶乳3份、云母粉25份、改性膨胀蛭石5份、水15份、乙二醇5份、聚丙烯酸钠2份、六偏磷酸钠3份、羟乙基纤维素1份、十二烷基苯磺酸钠3份、矿物油消泡剂0.5份、对氯间二甲基苯酚2份。
优选地,所述涂料包括以下质量分数的组分:纯丙乳液78份、苯丙乳液20份、氯丁胶乳2份、云母粉30份、改性膨胀蛭石8份、水30份、乙二醇4份、聚丙烯酸钠1份、六偏磷酸钠2.5份、羟乙基纤维素3份、十二烷基苯磺酸钠1份、矿物油消泡剂1份、对氯间二甲基苯酚1份。
优选地,所述涂料包括以下质量分数的组分:纯丙乳液70份、苯丙乳液29份、氯丁胶乳1份、云母粉15份、改性膨胀蛭石10份、水25份、乙二醇6份、聚丙烯酸钠1份、六偏磷酸钠2.5份、羟乙基纤维素2份、十二烷基苯磺酸钠1份、矿物油消泡剂1份、对氯间二甲基苯酚4份。
优选地,所述涂料包括以下质量分数的组分:纯丙乳液85份、苯丙乳液15份、氯丁胶乳0份、云母粉35份、改性膨胀蛭石6份、水35份、乙二醇4份、聚丙烯酸钠2份、六偏磷酸钠2份、羟乙基纤维素4份、十二烷基苯磺酸钠3份、矿物油消泡剂1.5份、对氯间二甲基苯酚2.5份。
为了更好的实现上述发明目的,本发明还提供了一种以上所述的建筑外墙涂料的制备方法,包括以下步骤:
(1)按照质量配比将水和所述羟乙基纤维素增稠剂添加到容器中,在300-400rpm转速下搅拌3-5min;
(2)按照质量配比加入聚丙烯酸钠、六偏磷酸钠、以及1/2量的矿物油消泡剂,在300-400rpm转速下搅拌3-5min;
(3)在800-1000rpm转速搅拌下按照质量配比加入填料,搅拌30-40min;
(4)在600-800rpm转速搅拌下按照质量配比加入乳液基料,搅拌5-10min
(5)继续加入乙二醇、十二烷基苯磺酸钠、对氯间二甲基苯酚以及剩余矿物油消泡剂,在600-800rpm转速下搅拌5-10min,制得所述建筑外墙涂料。
本发明的有益效果是:本发明的涂料固着效果好、成膜稳定;由本发明的涂料制成的涂膜质感柔和、耐冲击性强,耐侯性和耐温变性好、不容易开裂,使用寿命长;本发明的制备方法简便、对设备要求不高,易于大规模推广应用。
具体实施方式
为能清楚说明本方案的技术特点,下面通过对比例和实施例,对本方案进行阐述。
对比例1
本发明对比例说明了一种建筑外墙涂料,包括以下质量分数的组分:纯丙乳液80份、苯丙乳液20份、云母粉30份、水25份、乙二醇3份、聚丙烯酸钠3份、六偏磷酸钠2份、羟乙基纤维素3份、十二烷基苯磺酸钠2份、矿物油消泡剂1.5份。
将以上质量配比的组分按照传统方法制备涂料。
对比例2
本发明对比例说明了一种建筑外墙涂料,包括以下质量分数的组分:纯丙乳液70份、苯丙乳液30份、云母粉20份、水20份、乙二醇2份、聚丙烯酸钠2份、六偏磷酸钠2份、羟乙基纤维素2份、十二烷基苯磺酸钠1份、矿物油消泡剂1份。
将以上质量配比的组分按照传统方法制备涂料。
实施例1
本发明实施例提供了一种改性膨胀蛭石的制备方法,包括以下步骤:将膨胀蛭石加入相对于膨胀蛭石质量20-25倍的浓度为0.2-0.4mol/L的氢氧化钠溶液中,50-60℃搅拌1-2小时,冷却至室温后加入相对于膨胀蛭石质量2-4%的乙二醇继续搅拌20-40分钟,然后进行过滤、洗涤至中性,然后加入到相对于膨胀蛭石质量5-10倍浓度为3-6%的磷酸氢二铵溶液中,浸渍搅拌2-4小时形成均匀浆液,然后经过滤、100-120℃干燥1-2h、500℃焙烧2-4h得到改性膨胀蛭石。
实施例2
本发明实施例提供了一种建筑外墙涂料,包括以下质量分数的组分:纯丙乳液65份、苯丙乳液35份、氯丁胶乳0份、云母粉20份、按照实施例1提供的方法制备的改性膨胀蛭石10份、水20份、乙二醇3份、聚丙烯酸钠3份、六偏磷酸钠2份、羟乙基纤维素2份、十二烷基苯磺酸钠2份、矿物油消泡剂1.5份、对氯间二甲基苯酚3份。
将以上质量配比的组分按照以下步骤制备涂料:
(1)按照质量配比将水和所述羟乙基纤维素增稠剂添加到容器中,在300rpm转速下搅拌5min;
(2)按照质量配比加入聚丙烯酸钠、六偏磷酸钠、以及1/2量的矿物油消泡剂,在300rpm转速下搅拌3min;
(3)在800rpm转速搅拌下按照质量配比加入填料,搅拌30min;
(4)在600rpm转速搅拌下按照质量配比加入乳液基料,搅拌5min
(5)继续加入乙二醇、十二烷基苯磺酸钠、对氯间二甲基苯酚以及剩余矿物油消泡剂,在600rpm转速下搅拌10min,制得所述建筑外墙涂料。
实施例3
本发明实施例提供了一种建筑外墙涂料,包括以下质量分数的组分:纯丙乳液80份、苯丙乳液17份、氯丁胶乳3份、云母粉25份、按照实施例1提供的方法制备的改性膨胀蛭石5份、水15份、乙二醇5份、聚丙烯酸钠2份、六偏磷酸钠3份、羟乙基纤维素1份、十二烷基苯磺酸钠3份、矿物油消泡剂0.5份、对氯间二甲基苯酚2份。
将以上质量配比的组分按照以下步骤制备涂料:
(1)按照质量配比将水和所述羟乙基纤维素增稠剂添加到容器中,在350rpm转速下搅拌4min;
(2)按照质量配比加入聚丙烯酸钠、六偏磷酸钠、以及1/2量的矿物油消泡剂,在350rpm转速下搅拌4min;
(3)在1000rpm转速搅拌下按照质量配比加入填料,搅拌35min;
(4)在700rpm转速搅拌下按照质量配比加入乳液基料,搅拌8min
(5)继续加入乙二醇、十二烷基苯磺酸钠、对氯间二甲基苯酚以及剩余矿物油消泡剂,在700rpm转速下搅拌8min,制得所述建筑外墙涂料。
实施例4
本发明实施例提供了一种建筑外墙涂料,包括以下质量分数的组分:纯丙乳液78份、苯丙乳液20份、氯丁胶乳2份、云母粉30份、按照实施例1提供的方法制备的改性膨胀蛭石8份、水30份、乙二醇4份、聚丙烯酸钠1份、六偏磷酸钠2.5份、羟乙基纤维素3份、十二烷基苯磺酸钠1份、矿物油消泡剂1份、对氯间二甲基苯酚1份。
将以上质量配比的组分按照以下步骤制备涂料:
(1)按照质量配比将水和所述羟乙基纤维素增稠剂添加到容器中,在400rpm转速下搅拌3min;
(2)按照质量配比加入聚丙烯酸钠、六偏磷酸钠、以及1/2量的矿物油消泡剂,在400rpm转速下搅拌5min;
(3)在900rpm转速搅拌下按照质量配比加入填料,搅拌30min;
(4)在800rpm转速搅拌下按照质量配比加入乳液基料,搅拌5min
(5)继续加入乙二醇、十二烷基苯磺酸钠、对氯间二甲基苯酚以及剩余矿物油消泡剂,在800rpm转速下搅拌5min,制得所述建筑外墙涂料。
实施例5
本发明实施例提供了一种建筑外墙涂料,包括以下质量分数的组分:纯丙乳液70份、苯丙乳液29份、氯丁胶乳1份、云母粉15份、按照实施例1提供的方法制备的改性膨胀蛭石10份、水25份、乙二醇6份、聚丙烯酸钠1份、六偏磷酸钠2.5份、羟乙基纤维素2份、十二烷基苯磺酸钠1份、矿物油消泡剂1份、对氯间二甲基苯酚4份。
将以上质量配比的组分按照以下步骤制备涂料:
(1)按照质量配比将水和所述羟乙基纤维素增稠剂添加到容器中,在400rpm转速下搅拌5min;
(2)按照质量配比加入聚丙烯酸钠、六偏磷酸钠、以及1/2量的矿物油消泡剂,在400rpm转速下搅拌3min;
(3)在800rpm转速搅拌下按照质量配比加入填料,搅拌40min;
(4)在700rpm转速搅拌下按照质量配比加入乳液基料,搅拌10min
(5)继续加入乙二醇、十二烷基苯磺酸钠、对氯间二甲基苯酚以及剩余矿物油消泡剂,在700rpm转速下搅拌10min,制得所述建筑外墙涂料。
实施例6
本发明实施例提供了一种建筑外墙涂料,包括以下质量分数的组分:纯丙乳液85份、苯丙乳液15份、氯丁胶乳0份、云母粉35份、按照实施例1提供的方法制备的改性膨胀蛭石6份、水35份、乙二醇4份、聚丙烯酸钠2份、六偏磷酸钠2份、羟乙基纤维素4份、十二烷基苯磺酸钠3份、矿物油消泡剂1.5份、对氯间二甲基苯酚2.5份。
将以上质量配比的组分按照以下步骤制备涂料:
(1)按照质量配比将水和所述羟乙基纤维素增稠剂添加到容器中,在300rpm转速下搅拌4min;
(2)按照质量配比加入聚丙烯酸钠、六偏磷酸钠、以及1/2量的矿物油消泡剂,在300rpm转速下搅拌4min;
(3)在1000rpm转速搅拌下按照质量配比加入填料,搅拌35min;
(4)在800rpm转速搅拌下按照质量配比加入乳液基料,搅拌5min
(5)继续加入乙二醇、十二烷基苯磺酸钠、对氯间二甲基苯酚以及剩余矿物油消泡剂,在800rpm转速下搅拌5min,制得所述建筑外墙涂料。
实验例
将对比例1-2和实施例2-6制得的涂料按照GB/T 9755-2014提供的方法分别制板涂膜进行性能检测,观察涂膜外观,并且检测耐水性、耐碱性、耐洗刷性、耐人工气候老化性、耐温变性。以上7种样品的涂膜外观均为正常,192h耐水性和96h耐碱性均无异常,4000次耐洗刷性测试均为漆膜未损坏。
耐人工气候老化性检测结果如表1所示,以上7种样品400h后的老化均未出现粉化和开裂;600h的老化后,对比例1-2、实施例1和5未添加氯丁胶乳的样品出现了1级粉化;1200h的老化后,对比例1-2、实施例1和5这些未添加氯丁胶乳的样品出现了2级粉化,其中对比例1-2的样品还出现了1级开裂。
耐温变性检测结果如表2所示,以上7种样品在3次耐温变循环后均无异常;6次耐温变循环后,对比例1-2这两个未添加改性膨胀蛭石和氯丁胶乳的样品出现了1级开裂;24次耐温变循环后,对比例1-2、实施例1和5未添加氯丁胶乳的样品均出现了开裂。
总结以上实验结果,本发明的建筑外墙涂料,在其他条件均能满足施工要求指标的情况下,耐人工气候老化性和耐温变性有了很大的提高,特别是在温差变化大的地区使用,能够有效延长涂膜的使用寿命。
表1耐人工气候老化性
表2耐温变性
本发明未经描述的技术特征可以通过或采用现有技术实现,在此不再赘述,当然,上述说明并非是对本发明的限制,本发明也并不仅限于上述举例,本技术领域的普通技术人员在本发明的实质范围内所做出的变化、改型、添加或替换,也应属于本发明的保护范围。
Claims (8)
1.一种建筑外墙涂料,其特征在于,所述涂料包括以下质量分数的组分:乳液基料100份、填料20-40份、水15-35份、乙二醇3-6份、聚丙烯酸钠1-3份、六偏磷酸钠2-3份、羟乙基纤维素1-4份、十二烷基苯磺酸钠1-3份、矿物油消泡剂0.5-1.5份、对氯间二甲基苯酚1-4份。
2.根据权利要求1所述的建筑外墙涂料,其特征在于,所述乳液基料包括纯丙乳液65-85份、苯丙乳液15-35份、氯丁胶乳0-3份;所述填料包括云母粉15-35份、改性膨胀蛭石5-10份。
3.根据权利要求1-2任一项所述的建筑外墙涂料,其特征在于,所述改性膨胀蛭石的制备方法为:
将膨胀蛭石加入相对于膨胀蛭石质量20-25倍的浓度为0.2-0.4mol/L的氢氧化钠溶液中,50-60℃搅拌1-2小时,冷却至室温后加入相对于膨胀蛭石质量2-4%的乙二醇继续搅拌20-40分钟,然后进行过滤、洗涤至中性,然后加入到相对于膨胀蛭石质量5-10倍浓度为3-6%的磷酸氢二铵溶液中,浸渍搅拌2-4小时形成均匀浆液,然后经过滤、100-120℃干燥1-2h、500℃焙烧2-4h得到改性膨胀蛭石。
4.根据权利要求1-3任一项所述的建筑外墙涂料,其特征在于,所述涂料包括以下质量分数的组分:纯丙乳液65份、苯丙乳液35份、氯丁胶乳0份、云母粉20份、改性膨胀蛭石10份、水20份、乙二醇3份、聚丙烯酸钠3份、六偏磷酸钠2份、羟乙基纤维素2份、十二烷基苯磺酸钠2份、矿物油消泡剂1.5份、对氯间二甲基苯酚3份。
5.根据权利要求1-4任一项所述的建筑外墙涂料,其特征在于,所述涂料包括以下质量分数的组分:纯丙乳液80份、苯丙乳液17份、氯丁胶乳3份、云母粉25份、改性膨胀蛭石5份、水15份、乙二醇5份、聚丙烯酸钠2份、六偏磷酸钠3份、羟乙基纤维素1份、十二烷基苯磺酸钠3份、矿物油消泡剂0.5份、对氯间二甲基苯酚2份。
6.根据权利要求1-5任一项所述的建筑外墙涂料,其特征在于,所述涂料包括以下质量分数的组分:纯丙乳液78份、苯丙乳液20份、氯丁胶乳2份、云母粉30份、改性膨胀蛭石8份、水30份、乙二醇4份、聚丙烯酸钠1份、六偏磷酸钠2.5份、羟乙基纤维素3份、十二烷基苯磺酸钠1份、矿物油消泡剂1份、对氯间二甲基苯酚1份。
7.一种如权利要求1-6任一项所述的建筑外墙涂料的制备方法,其特征在于,包括以下步骤:
(1)按照质量配比将水和所述羟乙基纤维素增稠剂添加到容器中,在300-400rpm转速下搅拌3-5min;
(2)按照质量配比加入聚丙烯酸钠、六偏磷酸钠、以及1/2量的矿物油消泡剂,在300-400rpm转速下搅拌3-5min;
(3)在800-1000rpm转速搅拌下按照质量配比加入填料,搅拌30-40min;
(4)在600-800rpm转速搅拌下按照质量配比加入乳液基料,搅拌5-10min
(5)继续加入乙二醇、十二烷基苯磺酸钠、对氯间二甲基苯酚以及剩余矿物油消泡剂,在600-800rpm转速下搅拌5-10min,制得所述建筑外墙涂料。
8.根据权利要求7所述的建筑外墙涂料的制备方法,其特征在于,所述乳液基料包括纯丙乳液65-85份、苯丙乳液15-35份、氯丁胶乳0-3份;所述填料包括云母粉15-35份、改性膨胀蛭石5-10份。