CN108864458A - A kind of super abrasive anti-fingerprint Buddha's warrior attendant rupture pressure disc - Google Patents
A kind of super abrasive anti-fingerprint Buddha's warrior attendant rupture pressure disc Download PDFInfo
- Publication number
- CN108864458A CN108864458A CN201810580579.1A CN201810580579A CN108864458A CN 108864458 A CN108864458 A CN 108864458A CN 201810580579 A CN201810580579 A CN 201810580579A CN 108864458 A CN108864458 A CN 108864458A
- Authority
- CN
- China
- Prior art keywords
- parts
- buddha
- pressure disc
- rupture pressure
- warrior attendant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of super abrasive anti-fingerprint Buddha's warrior attendant rupture pressure disc, and the Buddha's warrior attendant rupture pressure disc includes PET base and coated on the coating in PET base, the ingredient of the following parts by weight of coating:Polyethylene terephthalate:30 ~ 40 parts, polyvinyl chloride:10 ~ 15 parts, acrylate:15 ~ 20 parts, graphene:5 ~ 10 parts, nano aluminium oxide:10 ~ 15 parts, nano ceramics:5 ~ 10 parts, vinyl acetate:10 ~ 15 parts, magnesium stearate:5 ~ 10 parts, dispersing agent:1 ~ 5 part, crosslinking agent:1 ~ 5 part, curing agent:1 ~ 5 part, plasticizer:1 ~ 5 part, organic solvent:50 ~ 60 parts.The Buddha's warrior attendant rupture pressure disc has good wear-resisting property, and hardness is high, good toughness, and rationally, production cost is low, good in economic efficiency for ingredient collocation.
Description
Technical field
The invention belongs to protect technical field of membrane, and in particular, to a kind of super abrasive anti-fingerprint Buddha's warrior attendant rupture pressure disc.
Background technique
Minnesota Mining and Manufacturing Company develops Buddha's warrior attendant rupture pressure disc earliest, is initially chiefly used in automotive field and building field, mainly viscous
It is attached on glass, prevents glass self-explosion and unexpected broken bring fragment spattering problem, just introduce safeguard film for cellular phone row in recent years
Industry.But it due to the outstanding explosion-proof performance of Buddha's warrior attendant rupture pressure disc, is held in both hands once listing the heat by consumer.Buddha's warrior attendant rupture pressure disc has relatively strong
Scratch resistant, anti-bursting property, can prevent mobile phone screen surprisingly be crushed bring fragment spattering problem, just as being worn to mobile phone screen
One " flak jackets " is gone up.
Since safeguard film for cellular phone lacks market specifications, so the explosion-proof membrane material superiority and inferiority difficulty of Buddha's warrior attendant point on the market.It is reported that beauty
The newest scientific achievement of 3M company of state --- Buddha's warrior attendant explosion-proof lamp is the current most safeguard film for cellular phone material rich in scientific and technological content,
The generally acknowledged Japan of the industry that matches in excellence or beauty, South Korea's material, only a small number of brands, such as insulting height is exactly using this advanced raw material.
For rupture pressure disc, the current country is primarily present following patent document:
The Chinese patent of Publication No. CN106833189A discloses a kind of optics rupture pressure disc and the preparation method and application thereof, the film
Including the coating coated in PET base and PET base, the coating includes according to the raw material of parts by weight:Acrylic resin 10-60
Part, 10-50 parts of polycarbonate, 3-20 parts of cenosphere, 0.1-5 parts of lithium hydroxide, 3-20 parts of ultraviolet absorbing agent, antioxidant
0.02-2 parts, 0.02-2 parts of dispersing agent, 0.1-5 parts of binder, 0.02-2 parts of heat stabilizer, 0.1-5 parts of zinc stearate, transparent agent
0.001-0.2 parts.Each raw material is weighed according to parts by weight, centrifugation, polymerization reaction, melting extrusion obtain coating;By painting obtained
Layer is coated in PET base up to optics rupture pressure disc.The present invention has good mobility, and demolding performace is good, optical clear
Property is good, excellent in cushion effect, has the effect of excellent antiultraviolet, screen color can be made more gorgeous, make display effect
It will not be distorted, be applicable not only to electron membrane, apply also for building film, automobile adhesive film, aircraft rupture pressure disc etc..However, the patent
Provided optics rupture pressure disc, coating stability is poor, high production cost.
Summary of the invention
It is above-mentioned to solve the problems, such as, the purpose of the present invention is to provide a kind of super abrasive anti-fingerprint Buddha's warrior attendant rupture pressure disc,
The Buddha's warrior attendant rupture pressure disc has good wear-resisting property, and hardness is high, good toughness, and rationally, production cost is low for ingredient collocation, economy effect
Benefit is good.
In order to achieve the above objectives, the technical scheme is that:
A kind of super abrasive anti-fingerprint Buddha's warrior attendant rupture pressure disc, the Buddha's warrior attendant rupture pressure disc include PET base and coated on the painting in PET base
Layer, the ingredient of the following parts by weight of coating:Polyethylene terephthalate:30 ~ 40 parts, polyvinyl chloride:10 ~ 15 parts, third
Olefin(e) acid ester:15 ~ 20 parts, graphene:5 ~ 10 parts, nano aluminium oxide:10 ~ 15 parts, nano ceramics:5 ~ 10 parts, vinyl acetate:10~
15 parts, magnesium stearate:5 ~ 10 parts, dispersing agent:1 ~ 5 part, crosslinking agent:1 ~ 5 part, curing agent:1 ~ 5 part, plasticizer:It is 1 ~ 5 part, organic
Solvent:50 ~ 60 parts.
Further, the Buddha's warrior attendant rupture pressure disc includes the ingredient of following parts by weight:Polyethylene terephthalate:35~
40 parts, polyvinyl chloride:10 ~ 13 parts, acrylate:16 ~ 20 parts, graphene:5 ~ 8 parts, nano aluminium oxide:12 ~ 15 parts, nanometer pottery
Porcelain:7 ~ 10 parts, vinyl acetate:13 ~ 15 parts, magnesium stearate:5 ~ 8 parts, dispersing agent:3 ~ 5 parts, crosslinking agent:2 ~ 5 parts, curing agent:1~
3 parts, plasticizer:1 ~ 4 part, organic solvent:55 ~ 60 parts.
Further, the Buddha's warrior attendant rupture pressure disc includes the ingredient of following parts by weight:Polyethylene terephthalate:35
Part, polyvinyl chloride:13 parts, acrylate:17 parts, graphene:6 parts, nano aluminium oxide:12 parts, nano ceramics:8 parts, acetic acid second
Alkene:14 parts, magnesium stearate:7 parts, dispersing agent:3 parts, crosslinking agent:2 parts, curing agent:3 parts, plasticizer:4 parts, organic solvent:55
Part.
Further, plasticizer is di-sec-octyl phthalate, diethyl phthalate or tributyl citrate.
Further, the dispersing agent is potassium citrate or linoleic acid sodium.
Further, the crosslinking agent is titanate esters crosslinking agent, aluminate coupling agent or silane coupling agent.
Further, the curing agent is aminoethyl piperazine, trimethylhexamethylenediamine or m-xylene diamine.
Further, the organic solvent is ethyl alcohol or propylene glycol solution.
Further, the preparation method of the coating includes the following steps:Claim poly terephthalic acid second respectively according to the proportion
Diol ester, polyvinyl chloride, acrylate, the graphene melting mixing at 500 ~ 600 DEG C, are stirred to react 20 ~ 40min, add
Nano aluminium oxide, nano ceramics, vinyl acetate, magnesium stearate and 20 ~ 30 weight parts organic solvents, in 600 ~ 800 revs/min turn
Speed is lower to stir 10 ~ 15min, is uniformly mixed, then mixture is transferred in kneading machine, dispersing agent, crosslinking agent, solidification is added
Agent, plasticizer and remaining organic solvent, are kneaded 10 ~ 20min, and double screw extruder is added in obtained material, squeeze in twin-screw
Then machine melting extrusion out cools down to get the coating.
The beneficial effects of the present invention are:
The Buddha's warrior attendant rupture pressure disc has good wear-resisting property, and hardness is high, good toughness, and rationally, production cost is low for ingredient collocation, warp
It helps profitable.
Specific embodiment
A kind of super abrasive anti-fingerprint Buddha's warrior attendant rupture pressure disc provided by the present invention, the Buddha's warrior attendant rupture pressure disc include PET base and
Coated on the coating in PET base, the ingredient of the following parts by weight of coating:Polyethylene terephthalate:30 ~ 40 parts,
Polyvinyl chloride:10 ~ 15 parts, acrylate:15 ~ 20 parts, graphene:5 ~ 10 parts, nano aluminium oxide:10 ~ 15 parts, nano ceramics:5
~ 10 parts, vinyl acetate:10 ~ 15 parts, magnesium stearate:5 ~ 10 parts, dispersing agent:1 ~ 5 part, crosslinking agent:1 ~ 5 part, curing agent:1~5
Part, plasticizer:1 ~ 5 part, organic solvent:50 ~ 60 parts.
Further, the Buddha's warrior attendant rupture pressure disc includes the ingredient of following parts by weight:Polyethylene terephthalate:35~
40 parts, polyvinyl chloride:10 ~ 13 parts, acrylate:16 ~ 20 parts, graphene:5 ~ 8 parts, nano aluminium oxide:12 ~ 15 parts, nanometer pottery
Porcelain:7 ~ 10 parts, vinyl acetate:13 ~ 15 parts, magnesium stearate:5 ~ 8 parts, dispersing agent:3 ~ 5 parts, crosslinking agent:2 ~ 5 parts, curing agent:1~
3 parts, plasticizer:1 ~ 4 part, organic solvent:55 ~ 60 parts.
Further, the Buddha's warrior attendant rupture pressure disc includes the ingredient of following parts by weight:Polyethylene terephthalate:35
Part, polyvinyl chloride:13 parts, acrylate:17 parts, graphene:6 parts, nano aluminium oxide:12 parts, nano ceramics:8 parts, acetic acid second
Alkene:14 parts, magnesium stearate:7 parts, dispersing agent:3 parts, crosslinking agent:2 parts, curing agent:3 parts, plasticizer:4 parts, organic solvent:55
Part.
Further, plasticizer is di-sec-octyl phthalate, diethyl phthalate or tributyl citrate.
Further, the dispersing agent is potassium citrate or linoleic acid sodium.
Further, the crosslinking agent is titanate esters crosslinking agent, aluminate coupling agent or silane coupling agent.
Further, the curing agent is aminoethyl piperazine, trimethylhexamethylenediamine or m-xylene diamine.
Further, the organic solvent is ethyl alcohol or propylene glycol solution.
Further, the preparation method of the coating includes the following steps:Claim poly terephthalic acid second respectively according to the proportion
Diol ester, polyvinyl chloride, acrylate, the graphene melting mixing at 500 ~ 600 DEG C, are stirred to react 20 ~ 40min, add
Nano aluminium oxide, nano ceramics, vinyl acetate, magnesium stearate and 20 ~ 30 weight parts organic solvents, in 600 ~ 800 revs/min turn
Speed is lower to stir 10 ~ 15min, is uniformly mixed, then mixture is transferred in kneading machine, dispersing agent, crosslinking agent, solidification is added
Agent, plasticizer and remaining organic solvent, are kneaded 10 ~ 20min, and double screw extruder is added in obtained material, squeeze in twin-screw
Then machine melting extrusion out cools down to get the coating.
It should be noted that the above examples are only used to illustrate the technical scheme of the present invention and are not limiting.Although referring to compared with
Good embodiment describes the invention in detail, those skilled in the art should understand that, it can be to the technology of invention
Scheme is modified or replaced equivalently, and without departing from the range of technical solution of the present invention, should all be covered in power of the invention
In sharp claimed range.
Claims (9)
1. a kind of super abrasive anti-fingerprint Buddha's warrior attendant rupture pressure disc, which is characterized in that the Buddha's warrior attendant rupture pressure disc includes PET base and is coated on
Coating in PET base, the ingredient of the following parts by weight of coating:Polyethylene terephthalate:30 ~ 40 parts, polychlorostyrene second
Alkene:10 ~ 15 parts, acrylate:15 ~ 20 parts, graphene:5 ~ 10 parts, nano aluminium oxide:10 ~ 15 parts, nano ceramics:5 ~ 10 parts,
Vinyl acetate:10 ~ 15 parts, magnesium stearate:5 ~ 10 parts, dispersing agent:1 ~ 5 part, crosslinking agent:1 ~ 5 part, curing agent:1 ~ 5 part, plasticising
Agent:1 ~ 5 part, organic solvent:50 ~ 60 parts.
2. super abrasive anti-fingerprint Buddha's warrior attendant rupture pressure disc according to claim 1, which is characterized in that the Buddha's warrior attendant rupture pressure disc includes
The ingredient of following parts by weight:Polyethylene terephthalate:35 ~ 40 parts, polyvinyl chloride:10 ~ 13 parts, acrylate:16~20
Part, graphene:5 ~ 8 parts, nano aluminium oxide:12 ~ 15 parts, nano ceramics:7 ~ 10 parts, vinyl acetate:13 ~ 15 parts, magnesium stearate:
5 ~ 8 parts, dispersing agent:3 ~ 5 parts, crosslinking agent:2 ~ 5 parts, curing agent:1 ~ 3 part, plasticizer:1 ~ 4 part, organic solvent:55 ~ 60 parts.
3. super abrasive anti-fingerprint Buddha's warrior attendant rupture pressure disc according to claim 1, which is characterized in that the Buddha's warrior attendant rupture pressure disc includes
The ingredient of following parts by weight:Polyethylene terephthalate:35 parts, polyvinyl chloride:13 parts, acrylate:17 parts, graphite
Alkene:6 parts, nano aluminium oxide:12 parts, nano ceramics:8 parts, vinyl acetate:14 parts, magnesium stearate:7 parts, dispersing agent:It 3 parts, hands over
Join agent:2 parts, curing agent:3 parts, plasticizer:4 parts, organic solvent:55 parts.
4. super abrasive anti-fingerprint Buddha's warrior attendant rupture pressure disc according to claim 1, which is characterized in that plasticizer is phthalic acid
Di-sec-octyl, diethyl phthalate or tributyl citrate.
5. super abrasive anti-fingerprint Buddha's warrior attendant rupture pressure disc according to claim 1, which is characterized in that the dispersing agent is citric acid
Potassium or linoleic acid sodium.
6. super abrasive anti-fingerprint Buddha's warrior attendant rupture pressure disc according to claim 1, which is characterized in that the crosslinking agent is titanate esters
Crosslinking agent, aluminate coupling agent or silane coupling agent.
7. super abrasive anti-fingerprint Buddha's warrior attendant rupture pressure disc according to claim 1, which is characterized in that the curing agent is aminoethyl
Piperazine, trimethylhexamethylenediamine or m-xylene diamine.
8. super abrasive anti-fingerprint Buddha's warrior attendant rupture pressure disc according to claim 1, which is characterized in that the organic solvent is ethyl alcohol
Or propylene glycol solution.
9. super abrasive anti-fingerprint Buddha's warrior attendant rupture pressure disc described according to claim 1 ~ any one of 8, which is characterized in that the coating
Preparation method include the following steps:According to the proportion respectively claim polyethylene terephthalate, polyvinyl chloride, acrylate,
Graphene melting mixing at 500 ~ 600 DEG C, is stirred to react 20 ~ 40min, adds nano aluminium oxide, nano ceramics, acetic acid second
Alkene, magnesium stearate and 20 ~ 30 weight parts organic solvents stir 10 ~ 15min under 600 ~ 800 revs/min of revolving speed, are uniformly mixed,
Then mixture is transferred in kneading machine, dispersing agent, crosslinking agent, curing agent, plasticizer and remaining organic solvent is added, is kneaded
Double screw extruder is added in obtained material by 10 ~ 20min, in double screw extruder melting extrusion, is then cooled down to get institute
State coating.