CN108859464A - A kind of efficient transfer membrane and preparation method thereof - Google Patents
A kind of efficient transfer membrane and preparation method thereof Download PDFInfo
- Publication number
- CN108859464A CN108859464A CN201810840763.5A CN201810840763A CN108859464A CN 108859464 A CN108859464 A CN 108859464A CN 201810840763 A CN201810840763 A CN 201810840763A CN 108859464 A CN108859464 A CN 108859464A
- Authority
- CN
- China
- Prior art keywords
- temperature
- surface layer
- weight
- grouped
- score
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to PP field of film preparation, and in particular to a kind of efficient transfer membrane and preparation method thereof.The efficient transfer membrane is made of surface layer 1, surface layer 2 and sandwich layer, and surface layer 1 is grouped as by the group of the following meter of score by weight：Acrylic resin T30S 98.0 ~ 98.5%, ABPP905 1.50 ~ 2.0%, the sum of the above components weight fraction are 100%；Surface layer 2 is grouped as by the group of the following meter of score by weight：Acrylic resin T30S 98.0 ~ 98.5%, ABPP905 1.50 ~ 2.0%, the sum of the above components weight fraction are 100%；Sandwich layer is grouped as by the group of the following meter of score by weight：The PP GRANULES L5E89 65 ~ 75% of packet header Shenhua production, the PP GRANULES L5E89 25 ~ 35% of middleization Quanzhou production.Efficient transfer membrane metal sense obtained by the present invention is strong, anti-oxidant, moisture-proof, surface is adapted to various printing technologies, non-toxic and tasteless, since the product for turning later is free of film layer, effectively prevents white pollution, meets environmentally protective requirement.
Description
Technical field
The invention belongs to PP field of film preparation, and in particular to a kind of efficient transfer membrane and preparation method thereof.
Background technique
Transfer membrane is an intermediate vector, is present on transfer paper base or modeling base, carrying is printed or the pattern of printing, for turning
The stratification elastic membrane on the article being printed is printed to, advertisement, decoration etc. are widely used in.The main component of transfer membrane
It is polypropylene（PP）, the production of PP film is made of that the melt of macromolecule polypropylene is passed through extruder, metering pump, die head first
Sheet material or thick film, then in dedicated stretching-machine, at certain temperature and the speed of setting, while or step by step vertical
Both direction（Longitudinally, laterally）The stretching of upper progress, and by cooling appropriate or heat treatment or special processing（As corona,
Coating etc.）Manufactured film.
Commonly PP film includes：Plain edition bidirectional stretching polypropylene film, heat sealing type biaxial-tension polypropylene film, perfume (or spice)
Cigarette packaging film, Biaxially oriented polypropylene pearl film, Biaxially oriented polypropylene metalized film, matt film etc..
Summary of the invention
In view of the above-mentioned deficiencies in the prior art, it is an object of the present invention to provide a kind of efficient transfer membrane and preparation method thereof.This
The obtained efficient transfer membrane ink-receptive of invention is strong, and metal sense is strong, anti-oxidant, moisture-proof, surface is adapted to various printing technologies,
It is non-toxic and tasteless.
To achieve the purpose of the present invention, it adopts the following technical scheme that：
A kind of efficient transfer membrane is made of surface layer 1, surface layer 2 and sandwich layer,
Surface layer 1 is grouped as by the group of the following meter of score by weight：Acrylic resin T30S 98.0 ~ 98.5%, ABPP905（It is anti-sticking
Masterbatch is tied, Shantou bass spy Science and Technology Ltd. is purchased from）1.50 ~ 2.0%, the sum of the above components weight fraction is 100%；
Surface layer 2 is grouped as by the group of the following meter of score by weight：Acrylic resin T30S（The production of middleization Quanzhou） 98.0~
98.5%, ABPP905 1.50 ~ 2.0%, the sum of the above components weight fraction are 100%；
Sandwich layer is grouped as by the group of the following meter of score by weight：The PP GRANULES L5E89 65 ~ 75% of packet header Shenhua production, in
Change the PP GRANULES L5E89 25 ~ 35% of Quanzhou production.
Preferably, a kind of efficient transfer membrane, is made of surface layer 1, surface layer 2 and sandwich layer,
Surface layer 1 is grouped as by the group of the following meter of score by weight：Acrylic resin T30S 98.3%, ABPP905 1.70%, it is above
The sum of each component weight fraction is 100%；
Surface layer 2 is grouped as by the group of the following meter of score by weight：Acrylic resin T30S 98.3%, ABPP905 1.70%, it is above
The sum of each component weight fraction is 100%；
Sandwich layer is grouped as by the group of the following meter of score by weight：The PP GRANULES L5E89 70%, Zhong Huaquan of packet header Shenhua production
The PP GRANULES L5E89 30% of state production.
A method of preparing efficiently transfer membrane as described above：It is formed using biaxial tension after three-decker co-extrusion.
The method for preparing efficient transfer membrane, design parameter are：The temperature of main extruder is：It is 250 DEG C ~ 260 DEG C, auxiliary
The temperature of extruder I is：230 DEG C ~ 250 DEG C, the temperature of auxiliary extruder II is：230 DEG C ~ 250 DEG C, the temperature of trilamellar membrane head is：
246 DEG C, the temperature of sharp cooling roll is：37 DEG C, the temperature of sink is：39 DEG C, the parameter of vertical machine drawing is：Preheating temperature 126 DEG C ~ 143
DEG C, 125 DEG C ~ 131 DEG C of draft temperature, 143 DEG C of setting temperature, the parameter of transverse stretching machine is：It 163 DEG C ~ 174.5 DEG C of preheating temperature, draws
153.5 DEG C of temperature are stretched, 164 DEG C ~ 166 DEG C of setting temperature, indulges machine drawing draw ratio：4.854.
The present invention has the following advantages that compared with the prior art：
Efficient transfer membrane ink-receptive produced by the present invention is strong, and metal sense is strong, wear-resisting, can multiple Reusability, reduce production and
Use cost；Anti-oxidant, moisture-proof, surface is adapted to various printing technologies, non-toxic and tasteless, since the product for turning later is free of film
Layer, effectively prevents white pollution, meets environmentally protective requirement.
Specific embodiment
Further to disclose rather than the present invention is limited, the present invention is described in further detail below in conjunction with example.
Embodiment 1
A kind of efficient transfer membrane is made of surface layer 1, surface layer 2 and sandwich layer,
Surface layer 1 is grouped as by the group of the following meter of score by weight：Acrylic resin T30S 98.0%, ABPP905（Anti-stick is female
Material）2.0%, the sum of the above components weight fraction is 100%；
Surface layer 2 is grouped as by the group of the following meter of score by weight：Acrylic resin T30S 98.0%, ABPP905 2.0%, it is above
The sum of each component weight fraction is 100%；
Sandwich layer is grouped as by the group of the following meter of score by weight：The PP GRANULES L5E89 65%, Zhong Huaquan of packet header Shenhua production
The PP GRANULES L5E89 35% of state production.
A method of preparing efficiently transfer membrane as described above：It is formed using biaxial tension after three-decker co-extrusion,
The temperature of main extruder is：250 DEG C, the temperature of auxiliary extruder I is：230 DEG C, the temperature of auxiliary extruder II is：230 DEG C, three layers
The temperature of film head is：246 DEG C, the temperature of sharp cooling roll is：37 DEG C, the temperature of sink is：39 DEG C, the parameter of vertical machine drawing is：Preheating
126 DEG C of temperature, 131 DEG C of draft temperature, 143 DEG C of setting temperature, the parameter of transverse stretching machine is：163 DEG C of preheating temperature, draft temperature
153.5 DEG C, 164 DEG C of setting temperature, indulge machine drawing draw ratio：4.854.
Embodiment 2
A kind of efficient transfer membrane is made of surface layer 1, surface layer 2 and sandwich layer,
Surface layer 1 is grouped as by the group of the following meter of score by weight：Acrylic resin T30S 98.3%, ABPP905 1.70%, it is above
The sum of each component weight fraction is 100%；
Surface layer 2 is grouped as by the group of the following meter of score by weight：Acrylic resin T30S 98.3%, ABPP905 1.70%, it is above
The sum of each component weight fraction is 100%；
Sandwich layer is grouped as by the group of the following meter of score by weight：The PP GRANULES L5E89 70%, Zhong Huaquan of packet header Shenhua production
The PP GRANULES L5E89 30% of state production.
A method of preparing efficiently transfer membrane as described above：It is formed using biaxial tension after three-decker co-extrusion,
Design parameter is shown in Table 1.
1 technical parameter of table
Obtained laminated film with a thickness of 24.7 μm, density 0.905, line speed：480m/min exports yield：,
5627g/h。
The performance data of 2 24.7 μm of table of efficient transfer membrane
Embodiment 3
A kind of efficient transfer membrane is made of surface layer 1, surface layer 2 and sandwich layer,
Surface layer 1 is grouped as by the group of the following meter of score by weight：Acrylic resin T30S 98.5%, ABPP905（Anti-stick is female
Material）1.50%, the sum of the above components weight fraction is 100%；
Surface layer 2 is grouped as by the group of the following meter of score by weight：Acrylic resin T30S 98.5%, ABPP905 1.50%, it is above
The sum of each component weight fraction is 100%；
Sandwich layer is grouped as by the group of the following meter of score by weight：The PP GRANULES L5E89 75%, Zhong Huaquan of packet header Shenhua production
The PP GRANULES L5E89 25% of state production.
A method of preparing efficiently transfer membrane as described above：It is formed using biaxial tension after three-decker co-extrusion.
The method for preparing efficient transfer membrane, design parameter are：The temperature of main extruder is：260 DEG C, auxiliary extruder
I temperature is：250 DEG C, the temperature of auxiliary extruder II is：250 DEG C, the temperature of trilamellar membrane head is：246 DEG C, the temperature of sharp cooling roll
For：37 DEG C, the temperature of sink is：39 DEG C, the parameter of vertical machine drawing is：143 DEG C of preheating temperature, 125 DEG C of draft temperature, setting temperature
143 DEG C, the parameter of transverse stretching machine is：It 174.5 DEG C of preheating temperature, 153.5 DEG C of draft temperature, 166 DEG C of setting temperature, indulges machine drawing and stretches
Than：4.854.
The foregoing is merely presently preferred embodiments of the present invention, all equivalent changes done according to scope of the present invention patent with
Modification, is all covered by the present invention.
Claims (4)
1. a kind of efficient transfer membrane is made of surface layer 1, surface layer 2 and sandwich layer, it is characterised in that：
Surface layer 1 is grouped as by the group of the following meter of score by weight：Acrylic resin T30S 98.0 ~ 98.5%, ABPP905 1.50 ~
2.0%, the sum of the above components weight fraction is 100%；
Surface layer 2 is grouped as by the group of the following meter of score by weight：Acrylic resin T30S 98.0 ~ 98.5%, ABPP905 1.50 ~
2.0%, the sum of the above components weight fraction is 100%；
Sandwich layer is grouped as by the group of the following meter of score by weight：The PP GRANULES L5E89 65 ~ 75% of packet header Shenhua production, in
Change the PP GRANULES L5E89 25 ~ 35% of Quanzhou production.
2. a kind of efficient transfer membrane according to claim 1, is made of surface layer 1, surface layer 2 and sandwich layer, it is characterised in that：
Surface layer 1 is grouped as by the group of the following meter of score by weight：Acrylic resin T30S 98.3%, ABPP905 1.70%, it is above
The sum of each component weight fraction is 100%；
Surface layer 2 is grouped as by the group of the following meter of score by weight：Acrylic resin T30S 98.3%, ABPP905 1.70%, it is above
The sum of each component weight fraction is 100%；
Sandwich layer is grouped as by the group of the following meter of score by weight：The PP GRANULES L5E89 70%, Zhong Huaquan of packet header Shenhua production
The PP GRANULES L5E89 30% of state production.
3. a kind of method for preparing efficiently transfer membrane as claimed in claim 1 or 2, it is characterised in that：It is total using three-decker
Biaxial tension forms after extrusion molding.
4. the method according to claim 3 for preparing efficient transfer membrane, it is characterised in that：The temperature of main extruder is：250
DEG C ~ 260 DEG C, the temperature of auxiliary extruder I is：230 DEG C ~ 250 DEG C, the temperature of auxiliary extruder II is：230 DEG C ~ 250 DEG C, trilamellar membrane
Head temperature be：246 DEG C, the temperature of sharp cooling roll is：37 DEG C, the temperature of sink is：39 DEG C, the parameter of vertical machine drawing is：Preheating temperature
126 DEG C ~ 143 DEG C of degree, 125 DEG C ~ 131 DEG C of draft temperature, 143 DEG C of setting temperature, the parameter of transverse stretching machine is：163 DEG C of preheating temperature ~
174.5 DEG C, 153.5 DEG C of draft temperature, 164 DEG C ~ 166 DEG C of setting temperature, indulge machine drawing draw ratio：4.854.