CN104960296B - A kind of PP delustrings are without glue composite membrane and preparation method thereof - Google Patents
A kind of PP delustrings are without glue composite membrane and preparation method thereof Download PDFInfo
- Publication number
- CN104960296B CN104960296B CN201510448621.0A CN201510448621A CN104960296B CN 104960296 B CN104960296 B CN 104960296B CN 201510448621 A CN201510448621 A CN 201510448621A CN 104960296 B CN104960296 B CN 104960296B
- Authority
- CN
- China
- Prior art keywords
- temperature
- top layer
- composite membrane
- raw material
- percetage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of PP delustrings without glue composite membrane and preparation method thereof, belong to polymeric material field.Composite membrane is made up of top layer 1, top layer 2 and sandwich layer；The raw material components and percetage by weight on top layer 1 are：Delustring material 100%；The raw material components and percetage by weight on top layer 2 are：Heat-sealing material 96.50 97.50%, antiblocking agent 2.50 3.50%；The raw material components and percetage by weight of sandwich layer are：PP 98.00 98.20%, antistatic additive 1.10 1.30%, slipping agent 0.70%.The thickness of obtained composite membrane is 10 15 microns, and extinction performance is excellent, and strong without the compound fastness of glue, preparation method is simple, is conducive to popularization and application.
Description
Technical field
The invention belongs to polymeric material field, and in particular to a kind of PP delustrings are without glue composite membrane and preparation method thereof.
Background technology
As the change of people's aesthetic standards, the requirement to package packing supplies are constantly updated, it is in package material surface feature
Existing diversity requirements, from many-sided reaction article such as aesthetics, restocking effect, advertising and show manufacturer and stimulate consumer sense
The special-effect of official's vision.Matt film is a kind of film for packaging of low gloss haze into diffusing reflection extinction effect, film surface
Similar paper, the gloss with height, its surface reflection is weak and soft, and surface gloss is less than 15%, mist degree 70% with
On, with comfortable feel, the quiet elegance of outward appearance, during printing color can reproduction true to nature many advantages, such as, ordinary packing film is nothing
What method reached.The top layer that present invention control easily occurs during heated compounded is shunk and causes the situation of film fold, is realized
With other solvent-free direct combinations of plastics soft material, by force, compound fastness fully meets use requirement to the compound fastness of storeroom, and
There is no organic solvent to volatilize in production process and pollute environment.
The content of the invention
It is an object of the invention to provide a kind of PP delustrings without glue composite membrane and preparation method thereof, the thickness of obtained composite membrane
It is 10-15 microns to spend, and extinction performance is excellent, and strong without the compound fastness of glue, preparation method is simple, is conducive to popularization and application.
To achieve the above object, the present invention is adopted the following technical scheme that：
A kind of PP delustrings are made up of without glue composite membrane top layer 1, top layer 2 and sandwich layer；The raw material components and weight hundred on top layer 1
Fraction is：Delustring material 100%；The raw material components and percetage by weight on top layer 2 are：Heat-sealing material 96.50-97.50%, antiblocking agent
2.50-3.50%；The raw material components and percetage by weight of sandwich layer are：It is PP 98.00-98.20%, antistatic additive 1.10-1.30%, refreshing
Lubrication prescription 0.70%.The thickness of obtained composite membrane is 10-15 microns.
It is molded using biaxial tension after three-decker co-extrusion.Process parameter control is as follows：Main extruder temperature 240-250
DEG C, 240-260 DEG C of skin temperature, 28-30 DEG C of tank temperature, 30-37 DEG C of chilling roller temperature, 240-250 DEG C of die head temperature, vertical draw temperature
115-129 DEG C of degree, longitudinal stretching than 4.78, it is horizontal draw 165-179 DEG C of temperature, cross directional stretch ratio 9-9.4, horizontal drawing wind speed 85-95%,
Corona 27-31.
Remarkable advantage of the invention is：The thickness of obtained composite membrane is 10-15 microns, and extinction performance is excellent, without glue
Compound fastness is strong, and preparation method is simple, is conducive to popularization and application.
Specific embodiment
Embodiment 1
A kind of PP delustrings are made up of without glue composite membrane top layer 1, top layer 2 and sandwich layer；The raw material components and weight hundred on top layer 1
Fraction is：Delustring material 100%；The raw material components and percetage by weight on top layer 2 are：Heat-sealing material 96.50%, antiblocking agent 3.50%；Core
Layer raw material components and percetage by weight be：PP 98.00%, antistatic additive 1.30%, slipping agent 0.70%.Obtained composite membrane
Thickness is 10 microns.
It is molded using biaxial tension after three-decker co-extrusion.Process parameter control is as follows：240 DEG C of main extruder temperature,
240 DEG C of skin temperature, 28 DEG C of tank temperature, 30 DEG C of chilling roller temperature, 240 DEG C of die head temperature, vertical 115 DEG C of temperature of drawing, longitudinal stretching
Than 4.78, horizontal 165 DEG C of temperature of drawing, cross directional stretch ratio 9, horizontal drawing wind speed 85%, corona 27.
Embodiment 2
A kind of PP delustrings are made up of without glue composite membrane top layer 1, top layer 2 and sandwich layer；The raw material components and weight hundred on top layer 1
Fraction is：Delustring material 100%；The raw material components and percetage by weight on top layer 2 are：Heat-sealing material 97.50%, antiblocking agent 2.50%；Core
Layer raw material components and percetage by weight be：PP 98.20%, antistatic additive 1.10%, slipping agent 0.70%.Obtained composite membrane
Thickness is 15 microns.
It is molded using biaxial tension after three-decker co-extrusion.Process parameter control is as follows：250 DEG C of main extruder temperature,
260 DEG C of skin temperature, 30 DEG C of tank temperature, 37 DEG C of chilling roller temperature, 250 DEG C of die head temperature, vertical 129 DEG C of temperature of drawing, longitudinal stretching
Than 4.78, horizontal 179 DEG C of temperature of drawing, cross directional stretch ratio 9.4, horizontal drawing wind speed 95%, corona 31.
Embodiment 3
A kind of PP delustrings are made up of without glue composite membrane top layer 1, top layer 2 and sandwich layer；The raw material components and weight hundred on top layer 1
Fraction is：Delustring material 100%；The raw material components and percetage by weight on top layer 2 are：Heat-sealing material 97.00%, antiblocking agent 3.00%；Core
Layer raw material components and percetage by weight be：PP 98.10%, antistatic additive 1.20%, slipping agent 0.70%.Obtained composite membrane
Thickness is 12 microns.
It is molded using biaxial tension after three-decker co-extrusion.Process parameter control is as follows：245 DEG C of main extruder temperature,
250 DEG C of skin temperature, 29 DEG C of tank temperature, 33 DEG C of chilling roller temperature, 245 DEG C of die head temperature, vertical 120 DEG C of temperature of drawing, longitudinal stretching
Than 4.78, horizontal 170 DEG C of temperature of drawing, cross directional stretch ratio 9.2, horizontal drawing wind speed 90%, corona 29.
The foregoing is only presently preferred embodiments of the present invention, all impartial changes done according to scope of the present invention patent with
Modification, should all belong to covering scope of the invention.
Claims (1)
1. a kind of PP delustrings are without glue composite membrane, it is characterised in that：It is made up of top layer 1, top layer 2 and sandwich layer；The raw material group on top layer 1
Divide and percetage by weight is：Delustring material 100%；The raw material components and percetage by weight on top layer 2 are：Heat-sealing material 97.00%, resist blocking and that
Agent 3.00%；The raw material components and percetage by weight of sandwich layer are：PP 98.10%, antistatic additive 1.20%, slipping agent 0.70%；It is obtained
Composite membrane thickness be 12 microns；It is molded using biaxial tension after three-decker co-extrusion, process parameter control is as follows：It is main to squeeze
245 DEG C of out-of-machine temperature, 250 DEG C of skin temperature, 29 DEG C of tank temperature, 33 DEG C of chilling roller temperature, 245 DEG C of die head temperature, vertical drawing temperature
120 DEG C, longitudinal stretching than 4.78, horizontal 170 DEG C of temperature of drawing, cross directional stretch ratio 9.2, horizontal drawing wind speed 90%, corona 29.