CN1088554A - Composite artificial marble making technology - Google Patents
Composite artificial marble making technology Download PDFInfo
- Publication number
- CN1088554A CN1088554A CN 92114750 CN92114750A CN1088554A CN 1088554 A CN1088554 A CN 1088554A CN 92114750 CN92114750 CN 92114750 CN 92114750 A CN92114750 A CN 92114750A CN 1088554 A CN1088554 A CN 1088554A
- Authority
- CN
- China
- Prior art keywords
- trace
- artificial marble
- mould
- alumina cement
- decorative pattern
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of structure material, especially build the top layer veneer.
The purpose of this invention is to provide a kind of follow-on manufacture method, it can increase surface hardness and slickness effectively effectively in artificial marble making.
Method of the present invention is achieved in that 1 part of unsaturated polyester resin, 1 part in 100 order silicon carbide, 1 part of high-alumina cement, 2 parts of pigment, cobalt naphthenate styrene solution trace, cyclohexanone peroxide paste trace furnishing pasty state is brushed in mould with brush then, makes decorative pattern with pigment again.
With 1 part of high-alumina cement, sand, 2 parts in stone, 0.5 part in 60 purpose silicon carbide add micro amount of sodium fluosilicate and grey silicon ash and add terra alba, and the titanium dioxide trace is blunged and is put into the mould that makes decorative pattern.
Description
The present invention relates to a kind of structure material, especially build the top layer veneer.
The marble that uses in the building; the natural collection of a kind of process is through processing; another kind is by single blank chemosynthesis; this blank is first in the regulation zone before manufacturing; be coated with one deck releasing agent; raw material is put into mould after mixing; vibrate floating but this technology has such problem, use Jin Gangsha, high-alumina cement; sand; the surface smoothing that terra alba, titanium dioxide etc. are made, the uniform marble of hard; the surface does not but have can prevent damaged protective layer, and regular meeting influences the quality of artificial marble like this.For addressing this problem, just increase Jin Gangsha usually.Though be to increase hardness, be difficult for reaching requirement on stone surface smooth finish and the smoothness.
The purpose of this invention is to provide a kind of follow-on method, it can increase top layer stiffness and slickness effectively in artificial marble making.
Method of the present invention is achieved in that closes 1 part in vibrin with insatiable hunger, adds husky part of the above golden steel of 100 orders, add 1 part of high alumina cement, add 2 parts of pigment, add naphthenic acid and bore benzene second dilute solution trace, add cycloethanone peroxide slurry trace back furnishing pasty state, brush in mould with brush then.
Again with 1 part of high-alumina cement, sand, 2 parts in stone, husky 0.5 part of 60 purposes gold steel adds micro amount of sodium fluosilicate and grey silicon ash, adds terra alba, the titanium dioxide trace, that blunges puts into the mould that makes decorative pattern.
The present invention is because only need add a certain amount of Sodium Silicofluoride on former making method basis, grey silicon ash and put and be coated with ND water reducer and silicone oil 1 on the mould: so 1 mixing solutions is realized hardness and the synchronous requirement of slickness easily.
Claims (3)
1, artificial marble material for building, particularly marble surface hardness and slick treatment process, this method have the micro amount of sodium fluosilicate of adding and grey silicon ash, and 60 orders gold steel sand.
2,, it is characterized in that adding Trace Fluoride water glass and grey silicon ash according to the described method of claim 1.
3,, it is characterized in that adding micro amount of sodium fluosilicate, grey silicon ash according to claim 1,2 described methods.