CN108840615A - 一种高性能保温建筑材料 - Google Patents

一种高性能保温建筑材料 Download PDF

Info

Publication number
CN108840615A
CN108840615A CN201810907061.4A CN201810907061A CN108840615A CN 108840615 A CN108840615 A CN 108840615A CN 201810907061 A CN201810907061 A CN 201810907061A CN 108840615 A CN108840615 A CN 108840615A
Authority
CN
China
Prior art keywords
parts
construction material
performance heat
insulating construction
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810907061.4A
Other languages
English (en)
Inventor
孙金梅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xuzhou Hehe New Building Materials Co Ltd
Original Assignee
Xuzhou Hehe New Building Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xuzhou Hehe New Building Materials Co Ltd filed Critical Xuzhou Hehe New Building Materials Co Ltd
Priority to CN201810907061.4A priority Critical patent/CN108840615A/zh
Publication of CN108840615A publication Critical patent/CN108840615A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高性能保温建筑材料，按重量份计，含有以下重量份的组分：膨胀珍珠岩20‑30份，灰钙粉25‑45份、石英砂15‑25份，粉煤灰40‑60份，氯化钙6‑14份，填料10‑14份，水泥30‑50份，催化剂3‑8份，聚乙二醇1‑6份，建筑石膏20‑30份，秸秆纤维20‑30份。本发明提供一种高性能保温建筑材料，能够实现建筑材料良好的保温、抗压、抗拉等性能，保证建筑材料的稳定性，并且添加的石英砂增加了耐磨效果。

Description

一种高性能保温建筑材料
技术领域
本发明涉及建筑材料领域，具体涉及一种高性能保温建筑材料。
背景技术
随着建筑节能的推行和发展，保温隔热材料及制品越来越受到人们的重视。而目前使用的材料在各种性能上均不够理想，尤其是在保温、耐酸碱、耐候性等方面不能满足人们的需要。传统保温材料只具有单一热阻性能，另外有些建筑材料中使用了甲醛或者芳香族碳氢化合物等不利于人们身体的化合物，已经逐渐被淘汰出市场，生态建筑材料将是未来的一种趋势。
发明内容
本发明提供一种高性能保温建筑材料，能够实现建筑材料良好的保温、抗压、抗拉等性能，保证建筑材料的稳定性，并且添加的石英砂增加了耐磨效果。
为实现上述目的，本高性能保温建筑材料，按重量份计，含有以下重量份的组分：膨胀珍珠岩20-30份，灰钙粉25-45份、石英砂15-25份，粉煤灰40-60份，氯化钙6-14份，填料10-14份，水泥30-50份，催化剂3-8份，聚乙二醇1-6份，建筑石膏20-30份，秸秆纤维20-30份。
进一步的，所述填料为硅丙乳液。
进一步的，还包括阻燃剂、稳定剂和固化剂，
进一步的，按重量份数计，所述阻燃剂为2-4份，稳定剂0.5-1.6份，固化剂0.2-1.2份。
进一步的，所述阻燃剂为三氧化二锑。
进一步的，所述秸秆纤维为玉米和小麦混合纤维。
与现有技术相比，本高性能保温建筑材料由于通过胀珍珠岩、灰钙粉25-45份、石英砂、粉煤灰和秸秆纤维混合，能够实现建筑材料良好的保温、抗压、抗拉等性能，保证建筑材料的稳定性，并且添加的石英砂增加了耐磨效果。
具体实施方式
为了加深对本发明的理解，下面将结合实施例对本发明作进一步详述，该实施例仅用于解释本发明，并不构成对本发明的保护范围的限定。
实施例1
一种高性能建筑保温材料，按重量份计含有以下重量份的组分：膨胀珍珠岩20份，灰钙粉45份、石英砂25份，粉煤灰60份，氯化钙6份，填料硅丙乳液14份，水泥50份，催化剂8份，聚乙二醇1份，建筑石膏30份，玉米和小麦混合纤维秸秆20份。
实施例2
一种高性能建筑保温材料，按重量份计含有以下重量份的组分：膨胀珍珠岩30份，灰钙粉25份、石英砂15份，粉煤灰40份，氯化钙14份，填料硅丙乳液12份，水泥30份，催化剂5份，聚乙二醇5份，建筑石膏25份，玉米和小麦混合纤维秸秆24份，另外还包括阻燃剂三氧化二锑2份，稳定剂0.5份，固化剂1.2份。
实施例3
一种高性能建筑保温材料，按重量份计含有以下重量份的组分：膨胀珍珠岩25份，灰钙粉30份、石英砂16份，粉煤灰50份，氯化钙10份，填料硅丙乳液10份，水泥40份，催化剂3份，聚乙二醇6份，建筑石膏20份，玉米和小麦混合纤维秸秆30份，另外还包括阻燃剂三氧化二锑4份，稳定剂1.6份，固化剂0.2份。
实施例4
一种高性能建筑保温材料，按重量份计含有以下重量份的组分：膨胀珍珠岩28份，灰钙粉35份、石英砂18份，粉煤灰43份，氯化钙12份，填料硅丙乳液13份，水泥32份，催化剂4份，聚乙二醇3份，建筑石膏24份，玉米和小麦混合纤维秸秆26份，另外还包括阻燃剂三氧化二锑2.5份，稳定剂1.2份，固化剂0.8份。

Claims (6)

1.高性能建筑保温材料，其特征在于，按重量份计，含有以下重量份的组分：膨胀珍珠岩20-30份，灰钙粉25-45份、石英砂15-25份，粉煤灰40-60份，氯化钙6-14份，填料10-14份，水泥30-50份，催化剂3-8份，聚乙二醇1-6份，建筑石膏20-30份，秸秆纤维20-30份。
2.根据权利要求1所述的高性能保温建筑材料，其特征在于，所述填料为硅丙乳液。
3.根据权利要求1或2所述的高性能保温建筑材料，其特征在于，还包括阻燃剂、稳定剂和固化剂。
4.根据权利要求3所述的高性能保温建筑材料，其特征在于，按重量份数计，所述阻燃剂为2-4份，稳定剂0.5-1.6份，固化剂0.2-1.2份。
5.根据权利要求4所述的高性能保温建筑材料，其特征在于，所述阻燃剂为三氧化二锑。
6.根据权利要求1所述的高性能保温建筑材料，其特征在于，所述秸秆纤维为玉米和小麦混合纤维。
CN201810907061.4A 2018-08-10 2018-08-10 一种高性能保温建筑材料 Pending CN108840615A (zh)