CN108827738A - 无损伤去除纺织品涂层的预处理方法 - Google Patents
无损伤去除纺织品涂层的预处理方法 Download PDFInfo
- Publication number
- CN108827738A CN108827738A CN201811018840.5A CN201811018840A CN108827738A CN 108827738 A CN108827738 A CN 108827738A CN 201811018840 A CN201811018840 A CN 201811018840A CN 108827738 A CN108827738 A CN 108827738A
- Authority
- CN
- China
- Prior art keywords
- coating
- sample
- conical flask
- preprocess method
- fabric coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种无损伤去除纺织品涂层的预处理方法,包括如下操作步骤:把样品分别放入三角烧瓶中,每克试样加入能够浸没试样的四氢呋喃试剂,充分地摇动三角烧瓶,在相应温度下进行分解,观察并记录其分解情况,分解时间至少十分钟,将样品洗净烘干,利用目测和显微镜观察其分解效果,若目测基布表面无涂层残留,纱线缝隙间无涂层残留,显微镜下每根纤维的纵截面特征清晰明显,则认为涂层基本去除彻底。本发明采用独特的溶剂和预处理方法,能够在保证纤维组分的前提下,对纺织品涂层中的PA、PU和PVC等组分有较好的去除效果,无须采用常见的几种试剂在不同温度条件下一一试验,节约了检测时间和人力,提高了检测效率。
Description
技术领域
本发明涉及纺织布料处理技术,特别是涉及一种无损伤去除纺织品涂层的预处理方法。
背景技术
目前越来越多的纺织品表面设有涂层,即通过粘合作用在纺织品表面形成的一层或多层薄膜,其不仅能改善织物的外观和风格,而且能增加织物的功能,使织物具有防水、耐水压、通气透湿、阻燃防污以及遮光反射等特殊功能。对于设有涂层的纺织品定量分析,目前国标和外标对去样品预处理方法说明都比较笼统,对于如何萃取掉样品中非纤维物质,均没有给出明确的流程,国标中只写有以适当方法去除,外标中提到了氟氯昂处理、酒精处理、50℃水处理、酶处理和酸处理几种方法。为了获得去除纺织涂层,且不影响纺织品中纤维组分的处理方法,测试人员需要各个试剂去试。
发明内容
针对上述技术问题,本发明提供了一种无损伤去除纺织品涂层的预处理方法,其采用独特的溶剂和预处理方法,能够在保证纤维组分的前提下,对纺织品涂层中的PA、PU和PVC等组分有较好的去除效果,测试效率高,节约了大量时间和人力。
为实现上述技术目的,本发明采用了如下技术方案:
步骤(1)、把设有涂层的纺织试样放入三角烧瓶中,每克试样加入能够浸没试样的四氢呋喃试剂,充分地摇动三角烧瓶,在相应温度下进行分解,观察并记录其分解情况,分解时间至少十分钟;
步骤(2)、将步骤(1)处理后的纺织试样洗净烘干,利用目测和显微镜观察涂层的分解情况,若目测基布表面无涂层残留,纱线缝隙间无涂层残留,显微镜下每根纤维的纵截面特征清晰明显,则涂层基本去除。
作为优选,所述纺织样品的涂层为PA、PU或PVC涂层中的一种或几种组合。
由于采用了上述技术方案,本发明具有如下技术效果:
本发明采用独特的溶剂和预处理方法,能够在保证纤维组分的前提下,对纺织品涂层中的PA、PU和PVC等组分有较好的去除效果,无须采用常见的试剂一一试验,节约了检测时间,提高了检测效率。
具体实施方式
本说明书中公开的所有特征,或公开的所有方法或过程中的步骤,除了互相排斥的特征和/或步骤以外,均可以以任何方式组合。
本说明书中公开的任一特征,除非特别叙述,均可被其他等效或具有类似目的的替代特征加以替换。即,除非特别叙述,每个特征只是一系列等效或类似特征中的一个例子而已。
一种无损伤去除纺织品涂层的预处理方法,包括如下操作步骤:
把样品分别放入三角烧瓶中,每克试样加适量如100m1的四氢呋喃试剂,能够浸没试样即可,充分地摇动三角烧瓶,在相应温度下进行分解,观察并记录其分解情况,分解时间至少十分钟,将样品洗净烘干,利用目测和显微镜观察其分解效果,若目测基布表面无涂层残留,纱线缝隙间无涂层残留,显微镜下每根纤维的纵截面特征清晰明显,则认为涂层基本去除彻底。
本发明采用四氢呋喃作为去除基布表面涂层的试剂,四氢呋喃是一类杂环有机化合物,它是最强的极性醚类之一,在化学反应和萃取时用做一种中等极性的溶剂。能够不损伤织物中的天然纤维,特别适用于纺织样品的涂层为PA、PU或PVC涂层中的一种或几种组合的情况,四氢呋喃对三者均有较好的去除效果,旨在去除、剥离涂层,不一定溶解,只要和基布面料分离就可以了,能够保证基布的纤维组分不受损伤,不影响布料在预处理之后的定量分析,提高检测精度。因此本发明能够节约人力资源,测试人员如果优先选择四氢呋喃试剂去除涂层,不用拿常见的试剂分别在3种温度下去一一做实验,每份样品测试周期节约大概4小时,长期以往节约了大量的时间。测试人员根据FZ/T 01057.4附录B详细列出的各种纤维在不同试剂中溶解状态,若纺织试样的基布本身纤维不溶解于四氢呋喃试剂,可优选采用本发明方法进行涂层预处理,节约测试时间和人力,适应不断增长的测试业务需求。
下面就常见的试剂的溶解结果进行比对。实验分为试剂无法使涂层溶解,其作用仅是使涂层溶胀,对基布的吸附力下降,进一步采用机械法借助外力使涂层从基布上去除;部分试剂使涂层从基布脱落并溶解在溶剂中,溶液呈浑浊状态。经过进行比较后,优选出溶解(剥离)涂层最佳溶剂。
表1聚丙烯酸酯涂层化学溶解性能表
备注:机械法去除涂层主要是采用外力揉搓样品表面以使涂层从基布上脱落。
由表1可知,对于PA涂层,四氢呋喃,N-N二甲基甲酰胺,环己酮,环己酮/丙酮混合溶液虽不能溶解涂层,但可机械法去除涂层,其中以环己酮,环己酮/丙酮混合溶液,四氢呋喃处理涂层速度最快,效果最好,N-N二甲基甲酰胺处理涂层时,速度比较慢,有时效果还不是特别好。所以综合而言,对于PA类涂层织物,其最佳溶解方式是四氢呋喃,常温溶解即可,环己酮随着温度升高,去除越来越容易,但样品会褪色损伤,一般不建议选用环己酮。
表2聚酯型聚氨酯涂层化学溶解性能表
根据表2可知,对于聚酯型聚氨酯涂层选择二甲基甲酰胺,四氢呋喃,环己酮,环己酮/丙酮混合溶液均可使涂层溶解,同时试验中观察到室温下以二甲基甲酰胺,四氢呋喃处理涂层的速度最快,效果最好,根据标准FZ/T 01095二甲基甲酰胺可溶解氨纶纤维,故对于含有氨纶纤维的样品的情况宜优先选择四氢呋喃。
表3聚氯乙烯涂层化学溶解性能表
由表3可知,采用丙酮,环己酮,二甲基甲酰胺,四氢呋喃均可溶解或涂层从基布上脱落,在室温下,丙酮在某些情况处理涂层出现涂层未自行脱落的现象,四氢呋喃处理涂层速度最快,效果最好。因此,对于PVC涂层织物可使用环己酮,二甲基甲酰胺,四氢呋喃溶剂进行涂层的去除。
本次实验主要针对PA,PU和PVC涂层进行了大量研究工作,结合表1,表2和表3可知,四氢呋喃对PA,PU和PVC涂层三者都具有较好的去除效果,在试样组分的情况下,可优先选择四氢呋喃作为去除涂层的溶剂。
本发明并不局限于前述的具体实施方式。本发明扩展到任何在本说明书中披露的新特征或任何新的组合,以及披露的任一新的方法或过程的步骤或任何新的组合。
Claims (2)
1.一种无损伤去除纺织品涂层的预处理方法,其特征在于,包括如下操作步骤:
步骤(1)、把设有涂层的纺织试样放入三角烧瓶中,每克试样加入能够浸没试样的四氢呋喃试剂,充分地摇动三角烧瓶,在相应温度下进行分解,观察并记录其分解情况,分解时间至少十分钟;
步骤(2)、将步骤(1)处理后的纺织试样洗净烘干,利用目测和显微镜观察涂层的分解情况,若目测基布表面无涂层残留,纱线缝隙间无涂层残留,显微镜下每根纤维的纵截面特征清晰明显,则涂层基本去除。
2.根据权利要求1所述的一种无损伤去除纺织品涂层的预处理方法,其特征在于:所述纺织样品的涂层为PA、PU或PVC涂层中的一种或几种组合。