CN108823732A - A kind of production method of thermal fabric - Google Patents
A kind of production method of thermal fabric Download PDFInfo
- Publication number
- CN108823732A CN108823732A CN201810688754.9A CN201810688754A CN108823732A CN 108823732 A CN108823732 A CN 108823732A CN 201810688754 A CN201810688754 A CN 201810688754A CN 108823732 A CN108823732 A CN 108823732A
- Authority
- CN
- China
- Prior art keywords
- fiber
- production method
- thermal fabric
- temperature
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of production method of thermal fabric, includes the following steps:Step 1, modified woolen fiber, cotton fiber, banana fiber, gamma-aminopropyl-triethoxy-silane are mixed, speed of agitator is 85-95r/min, mixing time is 25-35min, then it is re-fed into double screw extruder, polyurethane resin, warming reinforcing agent, barium stearate, deionized water are sequentially added, is squeezed out repeatedly.A kind of production method of thermal fabric of the invention, wool fiber high resilience, the advantages that hygroscopicity is strong, warmth retention property is good, by its surface modification treatment, improve intermolecular force, then it is preferably cohered with other raw materials, cotton fiber has intensity high, and banana fiber anti-microbial property is good, the polyurethane resin of addition further enhances the warmth retention property of fabric, matches between raw material by suitable.
Description
Technical field
The present invention relates to fabric production technical fields, and in particular to a kind of production method of thermal fabric.
Background technique
Fabric is exactly the material for making clothes, and as one of clothes three elements, fabric can not only annotate clothes
Style and characteristic, and the expression effect of the color of clothes, moulding is directly controlled, in clothes big world, the fabric of clothes
It is multifarious, make rapid progress, but generally, high-quality, high-grade fabric, mostly have comfortable wear, sweat-absorbing breathable,
The characteristics of several aspects such as well-pressed, vision is noble, tactile is soft and graceful of dangling, different fabrics have a different gas permeabilities, hygroscopicity,
The performances such as warmth retention property, such as cotton fabric have good gas permeability and hygroscopicity, and it is optimal that comfortable and easy to wear, warmth retention property is good
Children's garment fabric selects the gas permeability that fabric is confirmed when fabric, heat insulating ability, hygroscopicity, the performance characteristics such as static behaviour, and fabric is protected
Warm property has consumer spending very big decisive, therefore the present invention designs a kind of fabric that warmth retention property is good.
Coverstock material is different and preparation process is different, causes the performance of fabric different, and in the prior art, fabric keeps warm
Performance is bad, still needs to further improve.
Summary of the invention
The purpose of the present invention is to provide a kind of production methods of thermal fabric, mentioned above in the background art to solve
Problem.
To achieve the above object, the present invention provides the following technical solutions:
A kind of production method of thermal fabric, includes the following steps:
Step 1 mixes modified woolen fiber, cotton fiber, banana fiber, gamma-aminopropyl-triethoxy-silane, stirring
Revolving speed is 85-95r/min, and mixing time 25-35min is then re-fed into double screw extruder, sequentially adds polyurethane tree
Rouge, warming reinforcing agent, barium stearate, deionized water, squeeze out repeatedly, are then re-fed into multi-functional melt spinning machine, are mixed
Close object A;
Mixture A then, followed by blended, formation rove, is then carried out twisting being formed carefully individually at item by step 3
Yarn is eventually fabricated cylinder yarn then for cheese yarn dyeing, warping, sizing, woven fabric of gaiting, finally carries out arranging process again, this hair is made
Bright thermal fabric.
It is as further scheme of the invention:The modified woolen fiber preparation method is that wool fiber is placed in boiling water
Middle processing 6-10min then takes out drying, then is sent into reflux unit and flows back with epoxy silane coupling KH-560,
Reflux temperature is 95-105 DEG C, and return time 1-2h, subsequent re-dry is to get modified woolen fiber.
It is as further scheme of the invention:The warming reinforcing agent is heulandite, tourmaline according to weight ratio 1:5 groups
At mixture.
It is as further scheme of the invention:The heulandite, tourmaline partial size are 30 mesh.
It is as further scheme of the invention:The cotton fiber, banana fiber partial size are 20-30 mesh.
It is as further scheme of the invention:Extrusion temperature is 185-195 in double screw extruder in the step 1
℃。
It is as further scheme of the invention:Extrusion temperature is 190 DEG C in double screw extruder in the step 1.
It is as further scheme of the invention:Spinning temperature is 225 DEG C in the multi-functional melt spinning machine, winding speed
Degree is 160m/min, and draft temperature is 128 DEG C, and setting temperature is 132 DEG C.
Compared with prior art, the present invention has following beneficial effect:
Its surface modification treatment is improved intermolecular interaction by wool fiber high resilience, the advantages that hygroscopicity is strong, warmth retention property is good
Power is then preferably cohered with other raw materials, and cotton fiber has intensity high, and banana fiber anti-microbial property is good, the polyurethane of addition
Resin further enhances the warmth retention property of fabric, suitable proportion and multiple groups experimental demonstration is passed through between raw material, using spy
Different method processing, not only thermal property is greatly improved the fabric of preparation, furthermore antibiotic property, in terms of also have very
It is big to improve.
Specific embodiment
Combined with specific embodiments below, technical scheme in the embodiment of the invention is clearly and completely described, shows
So, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based on the reality in the present invention
Example is applied, every other embodiment obtained by those of ordinary skill in the art without making creative efforts all belongs to
In the scope of protection of the invention.
Embodiment 1:
A kind of production method of thermal fabric of the present embodiment, includes the following steps:
Step 1 mixes modified woolen fiber, cotton fiber, banana fiber, gamma-aminopropyl-triethoxy-silane, stirring
Revolving speed is 85r/min, and mixing time 25min is then re-fed into double screw extruder, sequentially adds polyurethane resin, protects
Warm reinforcing agent, barium stearate, deionized water, squeeze out repeatedly, are then re-fed into multi-functional melt spinning machine, obtain mixture A;
Mixture A then, followed by blended, formation rove, is then carried out twisting being formed carefully individually at item by step 3
Yarn is eventually fabricated cylinder yarn then for cheese yarn dyeing, warping, sizing, woven fabric of gaiting, finally carries out arranging process again, this hair is made
Bright thermal fabric.
The modified woolen fiber preparation method of the present embodiment is that wool fiber is placed in boiling water to handle 6min, is then taken out
It is dry, then be sent into reflux unit and flow back with epoxy silane coupling KH-560, reflux temperature is 95 DEG C, return time
For 1h, subsequent re-dry is to get modified woolen fiber.
The warming reinforcing agent of the present embodiment is heulandite, tourmaline according to weight ratio 1:The mixture of 5 compositions.
The heulandite, tourmaline partial size of the present embodiment are 30 mesh.
The cotton fiber, banana fiber partial size of the present embodiment are 20 mesh.
Extrusion temperature is 185 DEG C in double screw extruder in the step of the present embodiment one.
Spinning temperature is 225 DEG C, winding speed 160m/min in the multi-functional melt spinning machine of the present embodiment, stretches temperature
Degree is 128 DEG C, and setting temperature is 132 DEG C.
Embodiment 2:
A kind of production method of thermal fabric of the present embodiment, includes the following steps:
Step 1 mixes modified woolen fiber, cotton fiber, banana fiber, gamma-aminopropyl-triethoxy-silane, stirring
Revolving speed is 95r/min, and mixing time 35min is then re-fed into double screw extruder, sequentially adds polyurethane resin, protects
Warm reinforcing agent, barium stearate, deionized water, squeeze out repeatedly, are then re-fed into multi-functional melt spinning machine, obtain mixture A;
Mixture A then, followed by blended, formation rove, is then carried out twisting being formed carefully individually at item by step 3
Yarn is eventually fabricated cylinder yarn then for cheese yarn dyeing, warping, sizing, woven fabric of gaiting, finally carries out arranging process again, this hair is made
Bright thermal fabric.
The modified woolen fiber preparation method of the present embodiment is that wool fiber is placed in boiling water to handle 10min, is then taken
Drying out, then be sent into reflux unit and flow back with epoxy silane coupling KH-560, reflux temperature is 105 DEG C, reflux
Time is 2h, and subsequent re-dry is to get modified woolen fiber.
The warming reinforcing agent of the present embodiment is heulandite, tourmaline according to weight ratio 1:The mixture of 5 compositions.
The heulandite, tourmaline partial size of the present embodiment are 30 mesh.
The cotton fiber, banana fiber partial size of the present embodiment are 30 mesh.
Extrusion temperature is 195 DEG C in double screw extruder in the step of the present embodiment one.
Spinning temperature is 225 DEG C, winding speed 160m/min in the multi-functional melt spinning machine of the present embodiment, stretches temperature
Degree is 128 DEG C, and setting temperature is 132 DEG C.
Embodiment 3:
A kind of production method of thermal fabric of the present embodiment, includes the following steps:
Step 1 mixes modified woolen fiber, cotton fiber, banana fiber, gamma-aminopropyl-triethoxy-silane, stirring
Revolving speed is 90r/min, and mixing time 30min is then re-fed into double screw extruder, sequentially adds polyurethane resin, protects
Warm reinforcing agent, barium stearate, deionized water, squeeze out repeatedly, are then re-fed into multi-functional melt spinning machine, obtain mixture A;
Mixture A then, followed by blended, formation rove, is then carried out twisting being formed carefully individually at item by step 3
Yarn is eventually fabricated cylinder yarn then for cheese yarn dyeing, warping, sizing, woven fabric of gaiting, finally carries out arranging process again, this hair is made
Bright thermal fabric.
The modified woolen fiber preparation method of the present embodiment is that wool fiber is placed in boiling water to handle 8min, is then taken out
Dry, then be sent into reflux unit and flow back with epoxy silane coupling KH-560, reflux temperature is 100 DEG C, when reflux
Between be 1.5h, subsequent re-dry is to get modified woolen fiber.
The warming reinforcing agent of the present embodiment is heulandite, tourmaline according to weight ratio 1:The mixture of 5 compositions.
The heulandite, tourmaline partial size of the present embodiment are 30 mesh.
The cotton fiber, banana fiber partial size of the present embodiment are 25 mesh.
Extrusion temperature is 190 DEG C in double screw extruder in the step of the present embodiment one.
Spinning temperature is 225 DEG C, winding speed 160m/min in the multi-functional melt spinning machine of the present embodiment, stretches temperature
Degree is 128 DEG C, and setting temperature is 132 DEG C.
Embodiment 4:
A kind of production method of thermal fabric of the present embodiment, includes the following steps:
Step 1 mixes modified woolen fiber, cotton fiber, banana fiber, gamma-aminopropyl-triethoxy-silane, stirring
Revolving speed is 80r/min, and mixing time 20min is then re-fed into double screw extruder, sequentially adds polyurethane resin, protects
Warm reinforcing agent, barium stearate, deionized water, squeeze out repeatedly, are then re-fed into multi-functional melt spinning machine, obtain mixture A;
Mixture A then, followed by blended, formation rove, is then carried out twisting being formed carefully individually at item by step 3
Yarn is eventually fabricated cylinder yarn then for cheese yarn dyeing, warping, sizing, woven fabric of gaiting, finally carries out arranging process again, this hair is made
Bright thermal fabric.
The modified woolen fiber preparation method of the present embodiment is that wool fiber is placed in boiling water to handle 4min, is then taken out
It is dry, then be sent into reflux unit and flow back with epoxy silane coupling KH-560, reflux temperature is 90 DEG C, return time
For 0.6h, subsequent re-dry is to get modified woolen fiber.
The warming reinforcing agent of the present embodiment is heulandite, tourmaline according to weight ratio 1:The mixture of 5 compositions.
The heulandite, tourmaline partial size of the present embodiment are 30 mesh.
The cotton fiber, banana fiber partial size of the present embodiment are 15 mesh.
Extrusion temperature is 180 DEG C in double screw extruder in the step of the present embodiment one.
Spinning temperature is 225 DEG C, winding speed 160m/min in the multi-functional melt spinning machine of the present embodiment, stretches temperature
Degree is 128 DEG C, and setting temperature is 132 DEG C.
Embodiment 5:
A kind of production method of thermal fabric of the present embodiment, includes the following steps:
Step 1 mixes modified woolen fiber, cotton fiber, banana fiber, gamma-aminopropyl-triethoxy-silane, stirring
Revolving speed is 100r/min, and mixing time 30min is then re-fed into double screw extruder, sequentially adds polyurethane resin, protects
Warm reinforcing agent, barium stearate, deionized water, squeeze out repeatedly, are then re-fed into multi-functional melt spinning machine, obtain mixture A;
Mixture A then, followed by blended, formation rove, is then carried out twisting being formed carefully individually at item by step 3
Yarn is eventually fabricated cylinder yarn then for cheese yarn dyeing, warping, sizing, woven fabric of gaiting, finally carries out arranging process again, this hair is made
Bright thermal fabric.
The modified woolen fiber preparation method of the present embodiment is that wool fiber is placed in boiling water to handle 12min, is then taken
Drying out, then be sent into reflux unit and flow back with epoxy silane coupling KH-560, reflux temperature is 110 DEG C, reflux
Time is 2.3h, and subsequent re-dry is to get modified woolen fiber.
The warming reinforcing agent of the present embodiment is heulandite, tourmaline according to weight ratio 1:The mixture of 5 compositions.
The heulandite, tourmaline partial size of the present embodiment are 30 mesh.
The cotton fiber, banana fiber partial size of the present embodiment are 35 mesh.
Extrusion temperature is 200 DEG C in double screw extruder in the step of the present embodiment one.
Spinning temperature is 225 DEG C, winding speed 160m/min in the multi-functional melt spinning machine of the present embodiment, stretches temperature
Degree is 128 DEG C, and setting temperature is 132 DEG C.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (8)
1. a kind of production method of thermal fabric, which is characterized in that include the following steps:
Step 1 mixes modified woolen fiber, cotton fiber, banana fiber, gamma-aminopropyl-triethoxy-silane, stirring
Revolving speed is 85-95r/min, and mixing time 25-35min is then re-fed into double screw extruder, sequentially adds polyurethane tree
Rouge, warming reinforcing agent, barium stearate, deionized water, squeeze out repeatedly, are then re-fed into multi-functional melt spinning machine, are mixed
Close object A;
Mixture A then, followed by blended, formation rove, is then carried out twisting being formed carefully individually at item by step 3
Yarn is eventually fabricated cylinder yarn then for cheese yarn dyeing, warping, sizing, woven fabric of gaiting, finally carries out arranging process again, this hair is made
Bright thermal fabric.
2. a kind of production method of thermal fabric according to claim 1, which is characterized in that the modified woolen fiber system
Preparation Method is wool fiber is placed in boiling water to handle 6-10min, then takes out drying, then with epoxy silane coupling KH-
It flows back in 560 feeding reflux units, reflux temperature is 95-105 DEG C, return time 1-2h, and subsequent re-dry is to get changing
Property wool fiber.
3. a kind of production method of thermal fabric according to claim 1, which is characterized in that the warming reinforcing agent is piece
Zeolite, tourmaline are according to weight ratio 1:The mixture of 5 compositions.
4. a kind of production method of thermal fabric according to claim 3, which is characterized in that the heulandite, tourmaline
Partial size is 30 mesh.
5. a kind of production method of thermal fabric according to claim 1, which is characterized in that the cotton fiber, banana are fine
Dimension partial size is 20-30 mesh.
6. a kind of production method of thermal fabric according to claim 1, which is characterized in that twin-screw in the step 1
Extrusion temperature is 185-195 DEG C in extruder.
7. a kind of production method of thermal fabric according to claim 6, which is characterized in that twin-screw in the step 1
Extrusion temperature is 190 DEG C in extruder.
8. a kind of production method of thermal fabric according to claim 1, which is characterized in that the multi-functional melt spinning
Spinning temperature is 225 DEG C, winding speed 160m/min in machine, and draft temperature is 128 DEG C, and setting temperature is 132 DEG C.