CN108149362A - A kind of high performance garment material of flame-proof antibiotic and preparation method thereof - Google Patents
A kind of high performance garment material of flame-proof antibiotic and preparation method thereof Download PDFInfo
- Publication number
- CN108149362A CN108149362A CN201810158692.0A CN201810158692A CN108149362A CN 108149362 A CN108149362 A CN 108149362A CN 201810158692 A CN201810158692 A CN 201810158692A CN 108149362 A CN108149362 A CN 108149362A
- Authority
- CN
- China
- Prior art keywords
- parts
- flame
- high performance
- proof antibiotic
- garment material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of high performance garment materials of flame-proof antibiotic, include the raw material of following parts by weight：80 90 parts of cotton fiber, 60 70 parts of bamboo charcoal fiber, 28 32 parts of silver fiber, 20 24 parts of antibacterial complexing agent, 16 18 parts of flame-retardant additive, 8 10 parts of ammonium persulfate, 58 parts of diatomite in powder, 46 parts of viscose rayon, 13 parts of boron nitride, 12 parts of melamine.A kind of high performance garment material of flame-proof antibiotic of the present invention, garment material comfort height while antibacterial, excellent fireproof performance, in addition, the safe and non-toxic environmental protection of material component, has higher practical value and good application prospect.
Description
Technical field
The present invention relates to garment material technical fields, and in particular to a kind of high performance garment material of flame-proof antibiotic and its system
Preparation Method.
Background technology
Clothes are made with fabric, and fabric is exactly the material for making clothes, as one of clothes three elements, fabric
The style and characteristic of clothes can not only be annotated, and directly control the color of clothes, moulding expression effect, presentation comes from
The noble quality of body is perfect, soft, commonly uses garment material, cotton fabric：Refer to cotton or cotton and cotton chemical mixed yarn
The fabric that line is made into, good permeability, good hygroscopicity is comfortable and easy to wear, is highly practical popular fabric, can be divided into pure cotton system
Product, blended two major class of cotton；Linen look fabric：The pure linen be formed by weaving by flaxen fiber and fiber crops and other fiber blends or intertexture
Fabric be referred to as linen look fabric, the common feature of linen look fabric is quality hard tough, rough stiffening, cool and comfortable, hygroscopicity
It is good, it is ideal summer clothes fabric, linen look fabric can be divided into pure spinning and blended two class；
Wire type fabric：The high-grade variety in textile, refer mainly to be by mulberry silk, tussah silk, artificial silk, filament of synthetic fibre
The fabric of primary raw material, it has the advantages that thin light, soft, smooth, graceful, magnificent, comfortable；Wool fabrics：It is with wool, rabbit
Hair, camel hair, wool type chemical fiber are fabric made of primary raw material, and generally based on wool, it is high-grade clothing throughout the year
Fabric has many advantages, such as that elasticity is good, crease-resistant, well-pressed, strong to stand up to hard wear, warmth retention property is strong, Comfortable attractive, pure color, deep to be consumed
The welcome of person；Pure chemical fiber fabric：Chemical fiber plus material with its fastness is big, good, well-pressed, wear-resisting washable, the easy keeping collection of elasticity and by
People's likes, pure chemical fiber fabric is the fabric formed by pure chemistry fibrous woven, spy of the characteristic by its chemical fibre in itself
Property determine, chemical fibre can be according to different needs, be processed into certain length, and is made into imitative silk, imitative by different technique
Cotton, imitative fiber crops, elastic force imitates hair, middle length imitates the fabrics such as hair.
In the prior art, garment material feel is stiff, and wearing comfort is not very high, while antibacterial, flame retardant property are poor,
Limit the technology development of garment material.
Invention content
In view of the drawbacks of the prior art, the object of the present invention is to provide a kind of high performance garment materials of flame-proof antibiotic, should
Garment material comfort height while antibacterial, excellent fireproof performance, in addition, the safe and non-toxic environmental protection of material component, has higher reality
With value and good application prospect.
The present invention solves technical problem and adopts the following technical scheme that：
The present invention provides a kind of high performance garment materials of flame-proof antibiotic, include the raw material of following parts by weight：
80-90 parts of cotton fiber, 60-70 parts of bamboo charcoal fiber, 28-32 parts of silver fiber, 20-24 parts of antibacterial complexing agent, flame-retardant additive
16-18 parts, 8-10 parts of ammonium persulfate, 5-8 parts of diatomite in powder, 4-6 parts of viscose rayon, 1-3 parts of boron nitride, 1-2 parts of melamine.
Preferably, the high performance garment material of the flame-proof antibiotic includes the raw material of following parts by weight：
85 parts of cotton fiber, 65 parts of bamboo charcoal fiber, 30 parts of silver fiber, 22 parts of antibacterial complexing agent, 17 parts of flame-retardant additive, ammonium persulfate
9 parts, 6.5 parts of diatomite in powder, 5 parts of viscose rayon, 2 parts of boron nitride, 1.5 parts of melamine.
Preferably, the antibacterial complexing agent is isothiazoline -3- ketone, bamboo vinegar, polyurethanes, according to weight ratio
（5-9）:（3-5）:The mixture of 2 compositions.
Preferably, the antibacterial complexing agent is isothiazoline -3- ketone, bamboo vinegar, polyurethanes, according to weight ratio 7:
4:The mixture of 2 compositions.
Preferably, the flame-retardant additive is ferroso-ferric oxide, barium metaborate, tricresyl phosphate (2,3- dibromopropyl) ester, is pressed
According to weight ratio 5:2：The mixture of 3 compositions.
Preferably, the diatomite in powder grain size is 5-9mm.
The present invention also provides a kind of preparation methods of the high performance garment material of flame-proof antibiotic, include the following steps：
Step 1 weighs each component raw material as required；
Step 2, by cotton fiber, bamboo charcoal fiber, silver fiber, antibacterial complexing agent, flame-retardant additive, ammonium persulfate, diatomite in powder,
Viscose rayon, boron nitride, melamine are added in homogenizer, speed of agitator 600-700r/min, mixing time 1-
2h, then individually, followed by blended, formation rove, then carry out twisting forming spun yarn into item, be eventually fabricated cylinder yarn；
Step 3 then by cheese yarn dyeing, warping, sizing, woven fabric of gaiting, finally carries out arranging process again, is made the present invention's
The high performance garment material of flame-proof antibiotic.
Preferably, the preparation process of the high performance garment material of the flame-proof antibiotic is：
Step 1 weighs each component raw material as required；
Step 2, by cotton fiber, bamboo charcoal fiber, silver fiber, antibacterial complexing agent, flame-retardant additive, ammonium persulfate, diatomite in powder,
Viscose rayon, boron nitride, melamine are added in homogenizer, speed of agitator 650r/min, mixing time 1.5, then
Individually into item, followed by blended, formation rove, then carry out twisting forming spun yarn, be eventually fabricated cylinder yarn；
Step 3 then by cheese yarn dyeing, warping, sizing, woven fabric of gaiting, finally carries out arranging process again, is made the present invention's
The high performance garment material of flame-proof antibiotic.
Compared with prior art, the present invention has following advantageous effect：
（1）A kind of high performance garment material cotton fiber of flame-proof antibiotic of the present invention, bamboo charcoal fiber, silver fiber as main base-material,
Cotton fiber, the bamboo charcoal fiber of addition can improve the comfort level of fabric, and the silver fiber of addition has antibacterial action, three's raw material warp
Multigroup experimental demonstration and the compatibility of science are crossed, middle antibiotic property and comfort level are very much improved compared with prior art, are added
The flame-retardant additive, the antibacterial complexing agent that enter improve anti-flammability, the antibiotic property of material, and boron nitride, the melamine of addition are further
Improve the flame retardant property of fabric.
（2）A kind of high performance garment material of flame-proof antibiotic of the present invention, antibacterial complexing agent is isothiazoline -3- ketone, bamboo
The mixture of vinegar liquid, polyurethanes, by the quality for changing isothiazoline -3- ketone, bamboo vinegar, polyurethanes substance
Than probing into the anti-microbial property for reaching best, by multigroup experimental demonstration, obtaining isothiazoline -3- ketone, bamboo vinegar, poly- amino first
Acid esters, the mass ratio of substance exist（5-9）:（3-5）:During 2 range, flame retardant property is best.
（3）A kind of high performance garment material of flame-proof antibiotic of the present invention, garment material comfort height while antibacterial,
Excellent fireproof performance, in addition, the safe and non-toxic environmental protection of material component, has higher practical value and good application prospect.
Specific embodiment
With reference to specific embodiment, the technical solution in the embodiment of the present invention is clearly and completely described, is shown
So, described embodiment is only part of the embodiment of the present invention, instead of all the embodiments.Based on the reality in the present invention
Apply example, those of ordinary skill in the art's all other embodiments obtained without making creative work all belong to
In the scope of protection of the invention.
Embodiment 1.
A kind of high performance garment material of flame-proof antibiotic of the present embodiment includes the raw material of following parts by weight：
80 parts of cotton fiber, 60 parts of bamboo charcoal fiber, 28 parts of silver fiber, 20 parts of antibacterial complexing agent, 16 parts of flame-retardant additive, ammonium persulfate
8 parts, 5 parts of diatomite in powder, 4 parts of viscose rayon, 1 part of boron nitride, 1 part of melamine.
The antibacterial complexing agent of the present embodiment is isothiazoline -3- ketone, bamboo vinegar, polyurethanes, according to weight ratio 7:
4:The mixture of 2 compositions.
The flame-retardant additive of the present embodiment is ferroso-ferric oxide, barium metaborate, tricresyl phosphate (2,3- dibromopropyl) ester, is pressed
According to weight ratio 5:2：The mixture of 3 compositions.
The diatomite in powder grain size of the present embodiment is 5mm.
A kind of preparation method of the high performance garment material of flame-proof antibiotic of the present embodiment, includes the following steps：
Step 1 weighs each component raw material as required；
Step 2, by cotton fiber, bamboo charcoal fiber, silver fiber, antibacterial complexing agent, flame-retardant additive, ammonium persulfate, diatomite in powder,
Viscose rayon, boron nitride, melamine are added in homogenizer, speed of agitator 600r/min, mixing time 1h, then single
Item is alone become, followed by blended, formation rove, then carries out twisting forming spun yarn, is eventually fabricated cylinder yarn；
Step 3 then by cheese yarn dyeing, warping, sizing, woven fabric of gaiting, finally carries out arranging process again, is made the present invention's
The high performance garment material of flame-proof antibiotic.
Embodiment 2.
A kind of high performance garment material of flame-proof antibiotic of the present embodiment includes the raw material of following parts by weight：
90 parts of cotton fiber, 70 parts of bamboo charcoal fiber, 32 parts of silver fiber, 24 parts of antibacterial complexing agent, 18 parts of flame-retardant additive, ammonium persulfate
10 parts, 8 parts of diatomite in powder, 6 parts of viscose rayon, 3 parts of boron nitride, 2 parts of melamine.
The antibacterial complexing agent of the present embodiment is isothiazoline -3- ketone, bamboo vinegar, polyurethanes, according to weight ratio 7:
4:The mixture of 2 compositions.
The flame-retardant additive of the present embodiment is ferroso-ferric oxide, barium metaborate, tricresyl phosphate (2,3- dibromopropyl) ester, is pressed
According to weight ratio 5:2:The mixture of 3 compositions.
The diatomite in powder grain size of the present embodiment is 9mm.
A kind of preparation method of the high performance garment material of flame-proof antibiotic of the present embodiment, includes the following steps：
Step 1 weighs each component raw material as required；
Step 2, by cotton fiber, bamboo charcoal fiber, silver fiber, antibacterial complexing agent, flame-retardant additive, ammonium persulfate, diatomite in powder,
Viscose rayon, boron nitride, melamine are added in homogenizer, speed of agitator 700r/min, mixing time 2h, then single
Item is alone become, followed by blended, formation rove, then carries out twisting forming spun yarn, is eventually fabricated cylinder yarn；
Step 3 then by cheese yarn dyeing, warping, sizing, woven fabric of gaiting, finally carries out arranging process again, is made the present invention's
The high performance garment material of flame-proof antibiotic.
Embodiment 3.
A kind of high performance garment material of flame-proof antibiotic of the present embodiment includes the raw material of following parts by weight：
85 parts of cotton fiber, 65 parts of bamboo charcoal fiber, 30 parts of silver fiber, 22 parts of antibacterial complexing agent, 17 parts of flame-retardant additive, ammonium persulfate
9 parts, 6.5 parts of diatomite in powder, 5 parts of viscose rayon, 2 parts of boron nitride, 1.5 parts of melamine.
The antibacterial complexing agent of the present embodiment is isothiazoline -3- ketone, bamboo vinegar, polyurethanes, according to weight ratio 7:
4:The mixture of 2 compositions.
The flame-retardant additive of the present embodiment is ferroso-ferric oxide, barium metaborate, tricresyl phosphate (2,3- dibromopropyl) ester, is pressed
According to weight ratio 5:2：The mixture of 3 compositions.
The diatomite in powder grain size of the present embodiment is 7mm.
A kind of preparation method of the high performance garment material of flame-proof antibiotic of the present embodiment, includes the following steps：
Step 1 weighs each component raw material as required；
Step 2, by cotton fiber, bamboo charcoal fiber, silver fiber, antibacterial complexing agent, flame-retardant additive, ammonium persulfate, diatomite in powder,
Viscose rayon, boron nitride, melamine are added in homogenizer, speed of agitator 650r/min, mixing time 1.5h, then
Individually into item, followed by blended, formation rove, then carry out twisting forming spun yarn, be eventually fabricated cylinder yarn；
Step 3 then by cheese yarn dyeing, warping, sizing, woven fabric of gaiting, finally carries out arranging process again, is made the present invention's
The high performance garment material of flame-proof antibiotic.
Embodiment 4.
A kind of high performance garment material of flame-proof antibiotic of the present embodiment includes the raw material of following parts by weight：
78 parts of cotton fiber, 58 parts of bamboo charcoal fiber, 26 parts of silver fiber, 18 parts of antibacterial complexing agent, 14 parts of flame-retardant additive, ammonium persulfate
6 parts, 4 parts of diatomite in powder, 3 parts of viscose rayon, 0.8 part of boron nitride, 0.8 part of melamine.
The antibacterial complexing agent of the present embodiment is isothiazoline -3- ketone, bamboo vinegar, polyurethanes, according to weight ratio 7:
4:The mixture of 2 compositions.
The flame-retardant additive of the present embodiment is ferroso-ferric oxide, barium metaborate, tricresyl phosphate (2,3- dibromopropyl) ester, is pressed
According to weight ratio 5:2：The mixture of 3 compositions.
The diatomite in powder grain size of the present embodiment is 4mm.
A kind of preparation method of the high performance garment material of flame-proof antibiotic of the present embodiment, includes the following steps：
Step 1 weighs each component raw material as required；
Step 2, by cotton fiber, bamboo charcoal fiber, silver fiber, antibacterial complexing agent, flame-retardant additive, ammonium persulfate, diatomite in powder,
Viscose rayon, boron nitride, melamine are added in homogenizer, speed of agitator 550r/min, mixing time 50min,
It individually, followed by blended, formation rove, then carries out twisting forming spun yarn into item again, is eventually fabricated cylinder yarn；
Step 3 then by cheese yarn dyeing, warping, sizing, woven fabric of gaiting, finally carries out arranging process again, is made the present invention's
The high performance garment material of flame-proof antibiotic.
Embodiment 5.
A kind of high performance garment material of flame-proof antibiotic of the present embodiment includes the raw material of following parts by weight：
92 parts of cotton fiber, 72 parts of bamboo charcoal fiber, 34 parts of silver fiber, 26 parts of antibacterial complexing agent, 20 parts of flame-retardant additive, ammonium persulfate
12 parts, 9 parts of diatomite in powder, 8 parts of viscose rayon, 4 parts of boron nitride, 3 parts of melamine.
The antibacterial complexing agent of the present embodiment is isothiazoline -3- ketone, bamboo vinegar, polyurethanes, according to weight ratio 7:
4:The mixture of 2 compositions.
The flame-retardant additive of the present embodiment is ferroso-ferric oxide, barium metaborate, tricresyl phosphate (2,3- dibromopropyl) ester, is pressed
According to weight ratio 5:2：The mixture of 3 compositions.
The diatomite in powder grain size of the present embodiment is 10mm.
A kind of preparation method of the high performance garment material of flame-proof antibiotic of the present embodiment, includes the following steps：
Step 1 weighs each component raw material as required；
Step 2, by cotton fiber, bamboo charcoal fiber, silver fiber, antibacterial complexing agent, flame-retardant additive, ammonium persulfate, diatomite in powder,
Viscose rayon, boron nitride, melamine are added in homogenizer, speed of agitator 750r/min, mixing time 2.5h, then
Individually into item, followed by blended, formation rove, then carry out twisting forming spun yarn, be eventually fabricated cylinder yarn；
Step 3 then by cheese yarn dyeing, warping, sizing, woven fabric of gaiting, finally carries out arranging process again, is made the present invention's
The high performance garment material of flame-proof antibiotic.
A kind of high performance garment material of flame-proof antibiotic of the present invention, the garment material comfort is high while antibacterial, fire-retardant
It has excellent performance, in addition, the safe and non-toxic environmental protection of material component, has higher practical value and good application prospect.
It is obvious to a person skilled in the art that the present invention is not limited to the details of above-mentioned exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Profit requirement rather than above description limit, it is intended that all by what is fallen within the meaning and scope of the equivalent requirements of the claims
Variation is included within the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in each embodiment can also be properly combined, forms those skilled in the art
The other embodiment being appreciated that.
Claims (8)
1. a kind of high performance garment material of flame-proof antibiotic, which is characterized in that include the raw material of following parts by weight：
80-90 parts of cotton fiber, 60-70 parts of bamboo charcoal fiber, 28-32 parts of silver fiber, 20-24 parts of antibacterial complexing agent, flame-retardant additive
16-18 parts, 8-10 parts of ammonium persulfate, 5-8 parts of diatomite in powder, 4-6 parts of viscose rayon, 1-3 parts of boron nitride, 1-2 parts of melamine.
A kind of 2. high performance garment material of flame-proof antibiotic according to claim 1, which is characterized in that the flame-proof antibiotic
High performance garment material includes the raw material of following parts by weight：
85 parts of cotton fiber, 65 parts of bamboo charcoal fiber, 30 parts of silver fiber, 22 parts of antibacterial complexing agent, 17 parts of flame-retardant additive, ammonium persulfate
9 parts, 6.5 parts of diatomite in powder, 5 parts of viscose rayon, 2 parts of boron nitride, 1.5 parts of melamine.
A kind of 3. high performance garment material of flame-proof antibiotic according to claim 1 or 2, which is characterized in that the antibacterial
Complexing agent is isothiazoline -3- ketone, bamboo vinegar, polyurethanes, according to weight ratio（5-9）:（3-5）:The mixing of 2 compositions
Object.
4. the high performance garment material of a kind of flame-proof antibiotic according to claim 3, which is characterized in that the antibacterial is compound
Agent is isothiazoline -3- ketone, bamboo vinegar, polyurethanes, according to weight ratio 7:4:The mixture of 2 compositions.
5. the high performance garment material of a kind of flame-proof antibiotic according to claim 1 or 2, which is characterized in that described fire-retardant
Additive is ferroso-ferric oxide, barium metaborate, tricresyl phosphate (2,3- dibromopropyl) ester, according to weight ratio 5:2：The mixing of 3 compositions
Object.
A kind of 6. high performance garment material of flame-proof antibiotic according to claim 1 or 2, which is characterized in that the diatom
Native powder diameter is 5-9mm.
A kind of 7. method for preparing the high performance garment material of flame-proof antibiotic as claimed in claim 1 or 2, which is characterized in that
Include the following steps：
Step 1 weighs each component raw material as required；
Step 2, by cotton fiber, bamboo charcoal fiber, silver fiber, antibacterial complexing agent, flame-retardant additive, ammonium persulfate, diatomite in powder,
Viscose rayon, boron nitride, melamine are added in homogenizer, speed of agitator 600-700r/min, mixing time 1-
2h, then individually, followed by blended, formation rove, then carry out twisting forming spun yarn into item, be eventually fabricated cylinder yarn；
Step 3 then by cheese yarn dyeing, warping, sizing, woven fabric of gaiting, finally carries out arranging process again, is made the present invention's
The high performance garment material of flame-proof antibiotic.
A kind of 8. preparation method of the high performance garment material of flame-proof antibiotic according to claim 7, which is characterized in that institute
Stating step is：
Step 1 weighs each component raw material as required；
Step 2, by cotton fiber, bamboo charcoal fiber, silver fiber, antibacterial complexing agent, flame-retardant additive, ammonium persulfate, diatomite in powder,
Viscose rayon, boron nitride, melamine are added in homogenizer, speed of agitator 650r/min, mixing time 1.5h, then
Individually into item, followed by blended, formation rove, then carry out twisting forming spun yarn, be eventually fabricated cylinder yarn；
Step 3 then by cheese yarn dyeing, warping, sizing, woven fabric of gaiting, finally carries out arranging process to get the present invention's again
The high performance garment material of flame-proof antibiotic.