CN108821749A - Ceramic storage tank formula and processing technology - Google Patents
Ceramic storage tank formula and processing technology Download PDFInfo
- Publication number
- CN108821749A CN108821749A CN201810977863.2A CN201810977863A CN108821749A CN 108821749 A CN108821749 A CN 108821749A CN 201810977863 A CN201810977863 A CN 201810977863A CN 108821749 A CN108821749 A CN 108821749A
- Authority
- CN
- China
- Prior art keywords
- parts
- storage tank
- raw material
- feldspar
- cash
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of ceramics storage tank formula, is prepared from the following raw materials in parts by weight：60-80 parts of Huguan blueness cash, 15-25 parts of sandstone clinker, 10-20 parts of quartz, 25-40 parts of feldspar, 5-15 parts of kaolin.Ceramic storage tank of the invention solves leakage problems, it can be used in white wine, vinegar and chemical industry, realize the production of large capacity storage tank and jar fermenter, ceramics storage tank outer surface of the invention water absorption rate is less than 1%, it ensure that the non-leakage of ceramic storage tank, and inner surface and middle part water absorption rate are larger, are conducive to beneficial microorganism breeding, so as to be used as jar fermenter.
Description
Technical field
The invention belongs to ceramic storage tank fields, and in particular to a kind of ceramics storage tank formula and processing technology.
Background technique
Firing ceramics large cylinder is with a long history, but due to not can solve leakage problems always technically, the large cylinder of firing is only
Water, grain etc. can be stored, it is impossible to be used in white wine, vinegar and chemical industry, nor storage tank and the fermentation of large capacity can be produced
Cylinder.
Summary of the invention
In order to overcome the above-mentioned deficiencies of the prior art, the present invention provides a kind of ceramic storage tank formula and processing technologies.
A kind of ceramics storage tank formula, is prepared from the following raw materials in parts by weight：60-80 parts of Huguan blueness cash, sandstone clinker 15-
25 parts, 10-20 parts of quartz, 25-40 parts of feldspar, 5-15 parts of kaolin.
Preferably, the ceramics storage tank formula, is prepared from the following raw materials in parts by weight：72 parts of Huguan blueness cash, sandstone are ripe
21 parts of material, quartzy 14 parts, 34 parts of feldspar, 7 parts of kaolin.
The production technology of the ceramic storage tank of the production present invention, includes the following steps：
Step 1：The preliminary treatment of raw material stacks Huguan blueness cash seven to eight months, then in 600-800 DEG C of temperature lower calcination
2-3h, artificial washing feldspar, quartz remove surface impurity；
Step 2：Raw material Huguan blueness cash, quartz, feldspar are carried out coarse crushing processing by the pulverization process of raw material in jaw crusher,
Then in wet process wheel carry out in broken processing, then take 60-80 parts of Huguan blueness cash, 15-25 parts of sandstone clinker, 10-20 parts of quartz,
25-40 parts of feldspar, 5-15 parts of kaolin mixing are fitted into ball mill barrel, and 50-150 parts of water are added and carry out ball milling；
Step 3：By the raw material after ball milling in step 2 carry out except iron handle, using induction 20,000 GS or more high intensity magnetic separation
Machine removes iron；
Step 4：In step 3, except the raw material after iron crosses 50 meshes, then raw material will be put into filter press, slice is made；
Step 5：It is aging, the slice in step 4 is carried out under conditions of improper ventilation, moisture content 14-17% aging；
Step 6：Slice after will be aging in step 5 carries out high pressure vacuum pugging, prepares fine pug；
Step 7：Pug in step 6 is carried out forming processes in such a way that some mechanical cooperation is manual, storage is made by molding
Cylinder green body；
Step 8：Storage tank green body is dried, using indoor seasoning method, temperature control at 23-25 DEG C, humid control 75%,
It is dried using the method for high humidity low temperature；
Step 9：Fine repaired biscuit processing is carried out after storage tank blank forming；
Step 10：High temperature fires storage tank：Storage tank green body is put into 1200-1240 DEG C of Gas kiln and automates firing.
Further, ball milling fineness is that 10000-hole sieve mores than 0.06% in the step 2.
The beneficial effects of the invention are as follows：Ceramic storage tank of the invention solves leakage problems, can be used in white wine, vinegar and
Chemical industry, realizes the production of large capacity storage tank and jar fermenter, and present invention ceramics storage tank outer surface water absorption rate guarantees less than 1%
Ceramic storage tank it is non-leakage, and inner surface and middle part water absorption rate are larger, are conducive to beneficial microorganism breeding, so as to conduct
Jar fermenter uses.
Specific embodiment
The embodiments given below are intended to further illustrate the invention, but is not to be construed as to the scope of the present invention
Limitation, content still falls within this to some nonessential modifications and adaptations of the invention to those skilled in the art according to the present invention
The protection scope of invention.
In ceramics storage tank formula of the invention, Huguan blueness cash is aleuropelitic texture, due to containing more coal, color hair
It is green.Huguan blueness cash rock is mainly made of quartzy flour sand and its cementing clay mineral.Quartz grains are distributed in cementing in isolation
It is cementing at base type in object.Quartz plays adjustment to the plasticity of pug in blank, and can reduce and shrink when dry,
Shorten drying time and prevent blank deformation, moreover it is possible to increase the mechanical strength of green body.Sandstone clinker can reduce green body in drying
Contraction with when firing, can play leanization.Feldspar can reduce the firing temperature of raw material as fluxing agent.It is kaolinic to add
Enter the plasticity of pug can be enhanced.
Embodiment 1：Ceramic storage tank, is made up of following steps：
Step 1：The preliminary treatment of raw material stacks Huguan blueness cash seven to eight months, then in 600-800 DEG C of temperature lower calcination
2-3h, artificial washing feldspar, quartz remove surface impurity；
Step 2：Raw material Huguan blueness cash, quartz, feldspar are carried out coarse crushing processing by the pulverization process of raw material in jaw crusher,
Then in wet process wheel carry out in broken processing, then take 60 parts of Huguan blueness cash, 15 parts of sandstone clinker, quartz 10 parts, 25 parts of feldspar,
5 parts of kaolin mixing are fitted into ball mill barrel, and 50-150 parts of water are added and carry out ball milling；
Step 3：By the raw material after ball milling in step 2 carry out except iron handle, using induction 20,000 GS or more high intensity magnetic separation
Machine removes iron；
Step 4：In step 3, except the raw material after iron crosses 50 meshes, then raw material will be put into filter press, slice is made；
Step 5：It is aging, the slice in step 4 is carried out under conditions of improper ventilation, moisture content 14-17% aging；
Step 6：Slice after will be aging in step 5 carries out high pressure vacuum pugging, prepares fine pug；
Step 7：Pug in step 6 is carried out forming processes in such a way that some mechanical cooperation is manual, storage is made by molding
Cylinder green body；
Step 8：Storage tank green body is dried, using indoor seasoning method, temperature control at 23-25 DEG C, humid control 75%,
It is dried using the method for high humidity low temperature；
Step 9：Fine repaired biscuit processing is carried out after storage tank blank forming；
Step 10：High temperature fires storage tank：Storage tank green body is put into 1200-1240 DEG C of Gas kiln and automates firing.
Embodiment 2：Ceramic storage tank, is made up of following steps：
Step 1：The preliminary treatment of raw material stacks Huguan blueness cash seven to eight months, then in 600-800 DEG C of temperature lower calcination
2-3h, artificial washing feldspar, quartz remove surface impurity；
Step 2：Raw material Huguan blueness cash, quartz, feldspar are carried out coarse crushing processing by the pulverization process of raw material in jaw crusher,
Then in wet process wheel carry out in broken processing, then take 80 parts of Huguan blueness cash, 25 parts of sandstone clinker, quartz 20 parts, 40 parts of feldspar,
15 parts of kaolin mixing are fitted into ball mill barrel, and 50-150 parts of water are added and carry out ball milling；
Step 3：By the raw material after ball milling in step 2 carry out except iron handle, using induction 20,000 GS or more high intensity magnetic separation
Machine removes iron；
Step 4：In step 3, except the raw material after iron crosses 50 meshes, then raw material will be put into filter press, slice is made；
Step 5：It is aging, the slice in step 4 is carried out under conditions of improper ventilation, moisture content 14-17% aging；
Step 6：Slice after will be aging in step 5 carries out high pressure vacuum pugging, prepares fine pug；
Step 7：Pug in step 6 is carried out forming processes in such a way that some mechanical cooperation is manual, storage is made by molding
Cylinder green body；
Step 8：Storage tank green body is dried, using indoor seasoning method, temperature control at 23-25 DEG C, humid control 75%,
It is dried using the method for high humidity low temperature；
Step 9：Fine repaired biscuit processing is carried out after storage tank blank forming；
Step 10：High temperature fires storage tank：Storage tank green body is put into 1200-1240 DEG C of Gas kiln and automates firing.
Embodiment 3：Ceramic storage tank, is made up of following steps：
Step 1：The preliminary treatment of raw material stacks Huguan blueness cash seven to eight months, then in 600-800 DEG C of temperature lower calcination
2-3h, artificial washing feldspar, quartz remove surface impurity；
Step 2：Raw material Huguan blueness cash, quartz, feldspar are carried out coarse crushing processing by the pulverization process of raw material in jaw crusher,
Then in wet process wheel carry out in broken processing, then take 68 parts of Huguan blueness cash, 19 parts of sandstone clinker, quartz 16 parts, 27 parts of feldspar,
12 parts of kaolin mixing are fitted into ball mill barrel, and 50-150 parts of water are added and carry out ball milling；
Step 3：By the raw material after ball milling in step 2 carry out except iron handle, using induction 20,000 GS or more high intensity magnetic separation
Machine removes iron；
Step 4：In step 3, except the raw material after iron crosses 50 meshes, then raw material will be put into filter press, slice is made；
Step 5：It is aging, the slice in step 4 is carried out under conditions of improper ventilation, moisture content 14-17% aging；
Step 6：Slice after will be aging in step 5 carries out high pressure vacuum pugging, prepares fine pug；
Step 7：Pug in step 6 is carried out forming processes in such a way that some mechanical cooperation is manual, storage is made by molding
Cylinder green body；
Step 8：Storage tank green body is dried, using indoor seasoning method, temperature control at 23-25 DEG C, humid control 75%,
It is dried using the method for high humidity low temperature；
Step 9：Fine repaired biscuit processing is carried out after storage tank blank forming；
Step 10：High temperature fires storage tank：Storage tank green body is put into 1200-1240 DEG C of Gas kiln and automates firing.
Embodiment 4：Ceramic storage tank, is made up of following steps：
Step 1：The preliminary treatment of raw material stacks Huguan blueness cash seven to eight months, then in 600-800 DEG C of temperature lower calcination
2-3h, artificial washing feldspar, quartz remove surface impurity；
Step 2：Raw material Huguan blueness cash, quartz, feldspar are carried out coarse crushing processing by the pulverization process of raw material in jaw crusher,
Then in wet process wheel carry out in broken processing, then take 72 parts of Huguan blueness cash, 21 parts of sandstone clinker, quartz 14 parts, 34 parts of feldspar,
7 parts of kaolin mixing are fitted into ball mill barrel, and 50-150 parts of water are added and carry out ball milling；
Step 3：By the raw material after ball milling in step 2 carry out except iron handle, using induction 20,000 GS or more high intensity magnetic separation
Machine removes iron；
Step 4：In step 3, except the raw material after iron crosses 50 meshes, then raw material will be put into filter press, slice is made；
Step 5：It is aging, the slice in step 4 is carried out under conditions of improper ventilation, moisture content 14-17% aging；
Step 6：Slice after will be aging in step 5 carries out high pressure vacuum pugging, prepares fine pug；
Step 7：Pug in step 6 is carried out forming processes in such a way that some mechanical cooperation is manual, storage is made by molding
Cylinder green body；
Step 8：Storage tank green body is dried, using indoor seasoning method, temperature control at 23-25 DEG C, humid control 75%,
It is dried using the method for high humidity low temperature；
Step 9：Fine repaired biscuit processing is carried out after storage tank blank forming；
Step 10：High temperature fires storage tank：Storage tank green body is put into 1200-1240 DEG C of Gas kiln and automates firing.
Comparative example 1：Ceramic storage tank, is made up of following steps：
Step 1：The preliminary treatment of raw material stacks black sand earthenware seven to eight months, then in 600-800 DEG C of temperature lower calcination 2-
3h, artificial washing feldspar, quartz remove surface impurity；
Step 2：Raw material black sand earthenware, quartz, feldspar are carried out in jaw crusher coarse crushing processing, connect by the pulverization process of raw material
Carried out in wet process wheel in broken processing, then take 60 parts of black sand earthenware, 15 parts of sandstone clinker, quartzy 10 parts, 25 parts of feldspar, kaolinite
Native 5 parts of mixing are fitted into ball mill barrel, and 50-150 parts of water are added and carry out ball milling；
Step 3：By the raw material after ball milling in step 2 carry out except iron handle, using induction 20,000 GS or more high intensity magnetic separation
Machine removes iron；
Step 4：In step 3, except the raw material after iron crosses 50 meshes, then raw material will be put into filter press, slice is made；
Step 5：It is aging, the slice in step 4 is carried out under conditions of improper ventilation, moisture content 14-17% aging；
Step 6：Slice after will be aging in step 5 carries out high pressure vacuum pugging, prepares fine pug；
Step 7：Pug in step 6 is carried out forming processes in such a way that some mechanical cooperation is manual, storage is made by molding
Cylinder green body；
Step 8：Storage tank green body is dried, using indoor seasoning method, temperature control at 23-25 DEG C, humid control 75%,
It is dried using the method for high humidity low temperature；
Step 9：Fine repaired biscuit processing is carried out after storage tank blank forming；
Step 10：High temperature fires storage tank：Storage tank green body is put into 1200-1240 DEG C of Gas kiln and automates firing.
Comparative example 2：Ceramic storage tank, is made up of following steps：
Step 1：The preliminary treatment of raw material stacks black sand earthenware seven to eight months, then in 600-800 DEG C of temperature lower calcination 2-
3h, artificial washing feldspar, quartz remove surface impurity；
Step 2：Raw material black sand earthenware, quartz, feldspar are carried out in jaw crusher coarse crushing processing, connect by the pulverization process of raw material
Carried out in wet process wheel in broken processing, then take 80 parts of black sand earthenware, 25 parts of sandstone clinker, quartzy 20 parts, 40 parts of feldspar, kaolinite
Native 15 parts of mixing are fitted into ball mill barrel, and 50-150 parts of water are added and carry out ball milling；
Step 3：By the raw material after ball milling in step 2 carry out except iron handle, using induction 20,000 GS or more high intensity magnetic separation
Machine removes iron；
Step 4：In step 3, except the raw material after iron crosses 50 meshes, then raw material will be put into filter press, slice is made；
Step 5：It is aging, the slice in step 4 is carried out under conditions of improper ventilation, moisture content 14-17% aging；
Step 6：Slice after will be aging in step 5 carries out high pressure vacuum pugging, prepares fine pug；
Step 7：Pug in step 6 is carried out forming processes in such a way that some mechanical cooperation is manual, storage is made by molding
Cylinder green body；
Step 8：Storage tank green body is dried, using indoor seasoning method, temperature control at 23-25 DEG C, humid control 75%,
It is dried using the method for high humidity low temperature；
Step 9：Fine repaired biscuit processing is carried out after storage tank blank forming；
Step 10：High temperature fires storage tank：Storage tank green body is put into 1200-1240 DEG C of Gas kiln and automates firing.
Comparative example 3：Ceramic storage tank, is made up of following steps：
Step 1：The preliminary treatment of raw material stacks Huguan blueness cash seven to eight months, artificial washing feldspar, quartz, removes surface
Impurity；
Step 2：Raw material Huguan blueness cash, quartz, feldspar are carried out coarse crushing processing by the pulverization process of raw material in jaw crusher,
Then in wet process wheel carry out in broken processing, then take 68 parts of Huguan blueness cash, 19 parts of sandstone clinker, quartz 16 parts, 27 parts of feldspar,
12 parts of kaolin mixing are fitted into ball mill barrel, and 50-150 parts of water are added and carry out ball milling；
Step 3：By the raw material after ball milling in step 2 carry out except iron handle, using induction 20,000 GS or more high intensity magnetic separation
Machine removes iron；
Step 4：In step 3, except the raw material after iron crosses 50 meshes, then raw material will be put into filter press, slice is made；
Step 5：It is aging, the slice in step 4 is carried out under conditions of improper ventilation, moisture content 14-17% aging；
Step 6：Slice after will be aging in step 5 carries out high pressure vacuum pugging, prepares fine pug；
Step 7：Pug in step 6 is carried out forming processes in such a way that some mechanical cooperation is manual, storage is made by molding
Cylinder green body；
Step 8：Storage tank green body is dried, using indoor seasoning method, temperature control at 23-25 DEG C, humid control 75%,
It is dried using the method for high humidity low temperature；
Step 9：Fine repaired biscuit processing is carried out after storage tank blank forming；
Step 10：High temperature fires storage tank：Storage tank green body is put into 1200-1240 DEG C of Gas kiln and automates firing.
Comparative example 4：Ceramic storage tank, is made up of following steps：
Step 1：The preliminary treatment of raw material stacks Huguan blueness cash seven to eight months, artificial washing feldspar, quartz, removes surface
Impurity；
Step 2：Raw material Huguan blueness cash, quartz, feldspar are carried out coarse crushing processing by the pulverization process of raw material in jaw crusher,
Then in wet process wheel carry out in broken processing, then take 72 parts of Huguan blueness cash, 21 parts of sandstone clinker, quartz 14 parts, 34 parts of feldspar,
7 parts of kaolin mixing are fitted into ball mill barrel, and 50-150 parts of water are added and carry out ball milling；
Step 3：By the raw material after ball milling in step 2 carry out except iron handle, using induction 20,000 GS or more high intensity magnetic separation
Machine removes iron；
Step 4：In step 3, except the raw material after iron crosses 50 meshes, then raw material will be put into filter press, slice is made；
Step 5：It is aging, the slice in step 4 is carried out under conditions of improper ventilation, moisture content 14-17% aging；
Step 6：Slice after will be aging in step 5 carries out high pressure vacuum pugging, prepares fine pug；
Step 7：Pug in step 6 is carried out forming processes in such a way that some mechanical cooperation is manual, storage is made by molding
Cylinder green body；
Step 8：Storage tank green body is dried, using indoor seasoning method, temperature control at 23-25 DEG C, humid control 75%,
It is dried using the method for high humidity low temperature；
Step 9：Fine repaired biscuit processing is carried out after storage tank blank forming；
Step 10：High temperature fires storage tank：Storage tank green body is put into 1200-1240 DEG C of Gas kiln and automates firing.
Water absorption rate test：Cylinder piece crust, cylinder piece endothelium, cylinder piece middle part, each position are taken to the ceramic storage tank of every group of firing
3 samples are taken to carry out water absorption rate measurement according to QB/T3299-1996.Test result is as shown in table 1.
As can be seen from Table 1,1-4 of the embodiment of the present invention is substantially better than comparative example 1-4.By comparative test it is found that utilizing
Huguan blueness cash, less than 1%, ensure that ceramic storage tank is non-leakage as ceramics storage tank outer surface water absorption rate made from raw material, and internal
Breeding with middle part water absorption rate compared with microorganism of going a long way；By the way that Huguan blueness cash is carried out high-temperature calcination processing so that ceramics in advance
The water absorption rate of the outer surface of storage tank reduces, so that the outer surface of ceramic storage tank is more fine and close, so that the performance of ceramic storage tank
More preferably.
Claims (4)
1. a kind of ceramics storage tank formula, it is characterised in that be to be prepared from the following raw materials in parts by weight：60-80 parts of Huguan blueness cash,
15-25 parts of sandstone clinker, 10-20 parts of quartz, 25-40 parts of feldspar, 5-15 parts of kaolin.
2. ceramics storage tank formula according to claim 1, it is characterised in that be to be prepared from the following raw materials in parts by weight：Pot
Close green 72 parts of cash, 21 parts of sandstone clinker, quartzy 14 parts, 34 parts of feldspar, 7 parts of kaolin.
3. a kind of production technology for producing ceramics storage tank described in claim 1, it is characterised in that include the following steps：
Step 1：The preliminary treatment of raw material stacks Huguan blueness cash seven to eight months, then in 600-800 DEG C of temperature lower calcination
2-3h, artificial washing feldspar, quartz remove surface impurity；
Step 2：Raw material Huguan blueness cash, quartz, feldspar are carried out coarse crushing processing by the pulverization process of raw material in jaw crusher,
Then in wet process wheel carry out in broken processing, then take 60-80 parts of Huguan blueness cash, 15-25 parts of sandstone clinker, 10-20 parts of quartz,
25-40 parts of feldspar, 5-15 parts of kaolin mixing are fitted into ball mill barrel, and 50-150 parts of water are added and carry out ball milling；
Step 3：By the raw material after ball milling in step 2 carry out except iron handle, using induction 20,000 GS or more high intensity magnetic separation
Machine removes iron；
Step 4：In step 3, except the raw material after iron crosses 50 meshes, then raw material will be put into filter press, slice is made；
Step 5：It is aging, the slice in step 4 is carried out under conditions of improper ventilation, moisture content 14-17% aging；
Step 6：Slice after will be aging in step 5 carries out high pressure vacuum pugging, prepares fine pug；
Step 7：Pug in step 6 is carried out forming processes in such a way that some mechanical cooperation is manual, storage is made by molding
Cylinder green body；
Step 8：Storage tank green body is dried, using indoor seasoning method, temperature control at 23-25 DEG C, humid control 75%,
It is dried using the method for high humidity low temperature；
Step 9：Fine repaired biscuit processing is carried out after storage tank blank forming；
Step 10：High temperature fires storage tank：Storage tank green body is put into 1200-1240 DEG C of Gas kiln and automates firing.
4. the production technology of ceramic storage tank according to claim 3, it is characterised in that：Ball milling fineness is ten thousand in the step 2
Hole tails over 0.06%.