CN108797121A - 一种提高棉线韧性的方法 - Google Patents

一种提高棉线韧性的方法 Download PDF

Info

Publication number
CN108797121A
CN108797121A CN201810401594.5A CN201810401594A CN108797121A CN 108797121 A CN108797121 A CN 108797121A CN 201810401594 A CN201810401594 A CN 201810401594A CN 108797121 A CN108797121 A CN 108797121A
Authority
CN
China
Prior art keywords
parts
cotton thread
immersion
soak
toughness
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810401594.5A
Other languages
English (en)
Inventor
李贺
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Hengyi Textile Technology Co Ltd
Original Assignee
Anhui Hengyi Textile Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Hengyi Textile Technology Co Ltd filed Critical Anhui Hengyi Textile Technology Co Ltd
Priority to CN201810401594.5A priority Critical patent/CN108797121A/zh
Publication of CN108797121A publication Critical patent/CN108797121A/zh
Pending legal-status Critical Current

Abstract

一种提高棉线韧性的方法，涉及纺织加工技术领域，其特征在于：包括以下操作步骤，选取材料、初次浸泡、混合材料、进行除杂、再次浸泡、进行除液。本发明方法合理、实施方便、产品韧性高、拉伸性能良好。

Description

一种提高棉线韧性的方法
技术领域
本发明涉及纺织加工技术领域，具体涉及一种提高棉线韧性的方法。
背景技术
棉线是用棉花纤维搓纺而成的线。
现在的棉线我发现有好多，有各种各样的名字，但是不外乎全棉的，晴棉的(也就是混纺的)全晴的和人造棉的。棉线是用棉花纤维搓纺而成的线。装订用棉线有上光与不上光两种，包装形式有直轴型、塔轴型两种。塔轴型多用于锁线加工，其规格根据专业标准有以下几种:42支纱4股和6股，60支纱4股和6股的白色蜡光塔线，其型号分别为S424，S426、S604、S606，也可记作42S/4、42S/6、60S/4、60S/6，其中S表示支纱，斜线下的数字表示股数装订用棉线有上光与不上光两种，包装形式有直轴型、塔轴型两种。塔轴型多用于锁线加工，其规格根据专业标准有以下几种:42支纱4股和6股，60支纱4股和6股的白色蜡光塔线，其型号分别为S424，S426、S604、S606，也可记作42S/4、42S/6、60S/4、60S/6，其中S表示支纱，斜线下的数字表示股数。
常温下，在一杯清水中不断加入食盐，并用筷子不停地搅拌，直到食盐不再溶解为止。将一根棉线放入配制好的浓盐水里浸泡一下，拿出来放在桌上晾干。将晾干后的用手提起，点燃一根火柴去烧棉线。这时，你会发现，棉线从下端一直燃烧到上端，但烧过后的线灰仍象一根线一样没有被烧断。为了方便比较，我们再来烧一根没有浸过盐水的普通棉线，结果，烧完的棉线没有留存下线灰。
但是现在的许多的棉线的韧性不是特别的好，一拉就断，而且棉线断了之后会有多余的线头，这样在后续的使用上要重新清理，也非常的不方便，会浪费使用者的大量的时间。
发明内容
本发明所要解决的技术问题在于克服现有的技术缺陷提供一种方法合理、实施方便、产品韧性高、拉伸性能良好的一种提高棉线韧性的方法。
本发明所要解决的技术问题采用以下的技术方案来实现：
一种提高棉线韧性的方法，其特征在于：包括以下操作步骤，
步骤一、选取材料：选取已经制备好的棉线，然后放在清水中浸泡25-35分钟，然后放在干燥、温度为50-60℃的房间中静置，直至水分消失；
步骤二、初次浸泡：将静置后的棉线取出然后放入一份浸泡液中浸泡2-3个小时；
步骤三、混合材料：将浸泡后的棉线放入设备中，且加入混合料然后震荡混合30-45分钟；由于材料上有液体，从而具有一定的吸附效果；
步骤四、进行除杂：将混合后的材料放置在振动筛网上进行震荡筛选，将多余的料震荡除去；
步骤五、再次浸泡：将震荡后的材料放入另一份浸泡液中浸泡2-3个小时；
步骤六、进行除液：将浸泡后的材料放入干燥、温度为65-75℃的房间中静置，直至水分消失；
所述浸泡液包括以下重量份的材料制成，
聚乙烯树脂13-17份、水性丙烯酸乳液7-11份、、聚氧乙烯聚氧丙醇胺醚1-6份、纳米氧化镧1-4份、十二烷基三甲基氯化铵1-5份、硅烷偶联剂KH5705-9份、邻苯二甲酸二辛酯2-7份、生物助剂6-10份；
制备方式：将上述的材料依次置于反应釜中混合均匀，升温至220-260℃，保温搅拌1～2h，得到混合料静置备用；然后加入重量份30份的去离子水且降温到100-120℃，混合搅拌至形成流动性好的浆体；
所述生物助剂包括以下重量份的材料制成，
连翘1份、拳参2份、贯众3份、牛黄4份、射干5份、白蔹6份、白花蛇舌草7份、紫花地丁1份、羚羊角2份、黄药子3份、鸡矢藤4份；
制备方式为：制备方式为：将上述的材料放在85-95℃的烘干设备中平铺，然后烘干4-5个小时，然后放入研磨设备中研磨成粉末状即可；
所述混合料包括以下重量份的材料制成，
氨基树脂19-24份、改性海泡石粉5-11份、纳米二氧化钛2-7份、甲乙酮5-9份、邻苯二甲酸二辛酯1-4份、海藻酸钠1-5份、甲基丙二醇1-6份、2-甲基咪唑1-5份、木质素磺酸1-3份、去离子水25-30份；
制备方式：将上述的材料放入反应釜中，然后升温至170-200℃，保温搅拌1～2h，得到混合浆料；然后将浆料压入三辊机中，研磨至粒径小于20μm，装罐即可；
所述改性海泡石粉的制备方式为：将海泡石研磨且过300-400目筛，然后加入脂肪醇聚氧乙烯醚在常温下搅拌混合10min，然后升温至80-85℃保温研磨30min，再加水搅拌制成固含量达到25-35％的溶液，所得混合液送入喷雾干燥机中干燥，制得20-40目的球形颗粒，并于100-110℃下烘干；
所述脂肪醇聚氧乙烯醚与海泡石的质量比为1：4.1；
所述棉线为人造棉或者混纺棉中的一种。
本发明的有益效果为：本发明的产品适用于工业生产，不适用于服装、家装产品的生产，而使用的混合料、浸泡液不是常规的产品，且也可以与其他的原料混合使用，而且产品的耐磨、拉伸的性能都非常的好，而且非常的紧致，保证在持续拉拽的过程中不会出现断裂，而且产品的粘合性能、韧性都性能非常的好，并且使用的生物助剂不仅能够起到中和毒素的效果，还能够增加产品的韧性以及耐压、耐磨的性能，产品能够用于多种基体材质上，产品功能广，而且物耗少、成本低、无毒无副反应，可加工性能好、成型容易。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面进一步阐述本发明。
实施例1
一种提高棉线韧性的方法，其特征在于：包括以下操作步骤，
步骤一、选取材料：选取已经制备好的棉线，然后放在清水中浸泡25分钟，然后放在干燥、温度为50℃的房间中静置，直至水分消失；
步骤二、初次浸泡：将静置后的棉线取出然后放入一份浸泡液中浸泡2个小时；
步骤三、混合材料：将浸泡后的棉线放入设备中，且加入混合料然后震荡混合30分钟；由于材料上有液体，从而具有一定的吸附效果；
步骤四、进行除杂：将混合后的材料放置在振动筛网上进行震荡筛选，将多余的料震荡除去；
步骤五、再次浸泡：将震荡后的材料放入另一份浸泡液中浸泡2个小时；
步骤六、进行除液：将浸泡后的材料放入干燥、温度为65℃的房间中静置，直至水分消失；
所述浸泡液包括以下重量份的材料制成，
聚乙烯树脂13-17份、水性丙烯酸乳液7-11份、、聚氧乙烯聚氧丙醇胺醚1-6份、纳米氧化镧1-4份、十二烷基三甲基氯化铵1-5份、硅烷偶联剂KH5705-9份、邻苯二甲酸二辛酯2-7份、生物助剂6-10份；
制备方式：将上述的材料依次置于反应釜中混合均匀，升温至220-260℃，保温搅拌1～2h，得到混合料静置备用；然后加入重量份30份的去离子水且降温到100-120℃，混合搅拌至形成流动性好的浆体；
所述生物助剂包括以下重量份的材料制成，
连翘1份、拳参2份、贯众3份、牛黄4份、射干5份、白蔹6份、白花蛇舌草7份、紫花地丁1份、羚羊角2份、黄药子3份、鸡矢藤4份；
制备方式为：制备方式为：将上述的材料放在85-95℃的烘干设备中平铺，然后烘干4-5个小时，然后放入研磨设备中研磨成粉末状即可；
所述混合料包括以下重量份的材料制成，
氨基树脂19-24份、改性海泡石粉5-11份、纳米二氧化钛2-7份、甲乙酮5-9份、邻苯二甲酸二辛酯1-4份、海藻酸钠1-5份、甲基丙二醇1-6份、2-甲基咪唑1-5份、木质素磺酸1-3份、去离子水25-30份；
制备方式：将上述的材料放入反应釜中，然后升温至170-200℃，保温搅拌1～2h，得到混合浆料；然后将浆料压入三辊机中，研磨至粒径小于20μm，装罐即可；
所述改性海泡石粉的制备方式为：将海泡石研磨且过300-400目筛，然后加入脂肪醇聚氧乙烯醚在常温下搅拌混合10min，然后升温至80-85℃保温研磨30min，再加水搅拌制成固含量达到25-35％的溶液，所得混合液送入喷雾干燥机中干燥，制得20-40目的球形颗粒，并于100-110℃下烘干；
所述脂肪醇聚氧乙烯醚与海泡石的质量比为1：4.1；
所述棉线为人造棉或者混纺棉中的一种。
实施例2
一种提高棉线韧性的方法，其特征在于：包括以下操作步骤，
步骤一、选取材料：选取已经制备好的棉线，然后放在清水中浸泡35分钟，然后放在干燥、温度为60℃的房间中静置，直至水分消失；
步骤二、初次浸泡：将静置后的棉线取出然后放入一份浸泡液中浸泡3个小时；
步骤三、混合材料：将浸泡后的棉线放入设备中，且加入混合料然后震荡混合45分钟；由于材料上有液体，从而具有一定的吸附效果；
步骤四、进行除杂：将混合后的材料放置在振动筛网上进行震荡筛选，将多余的料震荡除去；
步骤五、再次浸泡：将震荡后的材料放入另一份浸泡液中浸泡3个小时；
步骤六、进行除液：将浸泡后的材料放入干燥、温度为75℃的房间中静置，直至水分消失；
所述浸泡液包括以下重量份的材料制成，
聚乙烯树脂13-17份、水性丙烯酸乳液7-11份、、聚氧乙烯聚氧丙醇胺醚1-6份、纳米氧化镧1-4份、十二烷基三甲基氯化铵1-5份、硅烷偶联剂KH5705-9份、邻苯二甲酸二辛酯2-7份、生物助剂6-10份；
制备方式：将上述的材料依次置于反应釜中混合均匀，升温至220-260℃，保温搅拌1～2h，得到混合料静置备用；然后加入重量份30份的去离子水且降温到100-120℃，混合搅拌至形成流动性好的浆体；
所述生物助剂包括以下重量份的材料制成，
连翘1份、拳参2份、贯众3份、牛黄4份、射干5份、白蔹6份、白花蛇舌草7份、紫花地丁1份、羚羊角2份、黄药子3份、鸡矢藤4份；
制备方式为：制备方式为：将上述的材料放在85-95℃的烘干设备中平铺，然后烘干4-5个小时，然后放入研磨设备中研磨成粉末状即可；
所述混合料包括以下重量份的材料制成，
氨基树脂19-24份、改性海泡石粉5-11份、纳米二氧化钛2-7份、甲乙酮5-9份、邻苯二甲酸二辛酯1-4份、海藻酸钠1-5份、甲基丙二醇1-6份、2-甲基咪唑1-5份、木质素磺酸1-3份、去离子水25-30份；
制备方式：将上述的材料放入反应釜中，然后升温至170-200℃，保温搅拌1～2h，得到混合浆料；然后将浆料压入三辊机中，研磨至粒径小于20μm，装罐即可；
所述改性海泡石粉的制备方式为：将海泡石研磨且过300-400目筛，然后加入脂肪醇聚氧乙烯醚在常温下搅拌混合10min，然后升温至80-85℃保温研磨30min，再加水搅拌制成固含量达到25-35％的溶液，所得混合液送入喷雾干燥机中干燥，制得20-40目的球形颗粒，并于100-110℃下烘干；
所述脂肪醇聚氧乙烯醚与海泡石的质量比为1：4.1；
所述棉线为人造棉或者混纺棉中的一种。
实施例3
一种提高棉线韧性的方法，其特征在于：包括以下操作步骤，
步骤一、选取材料：选取已经制备好的棉线，然后放在清水中浸泡30分钟，然后放在干燥、温度为55℃的房间中静置，直至水分消失；
步骤二、初次浸泡：将静置后的棉线取出然后放入一份浸泡液中浸泡2.5个小时；
步骤三、混合材料：将浸泡后的棉线放入设备中，且加入混合料然后震荡混合40分钟；由于材料上有液体，从而具有一定的吸附效果；
步骤四、进行除杂：将混合后的材料放置在振动筛网上进行震荡筛选，将多余的料震荡除去；
步骤五、再次浸泡：将震荡后的材料放入另一份浸泡液中浸泡2.5个小时；
步骤六、进行除液：将浸泡后的材料放入干燥、温度为70℃的房间中静置，直至水分消失；
所述浸泡液包括以下重量份的材料制成，
聚乙烯树脂13-17份、水性丙烯酸乳液7-11份、、聚氧乙烯聚氧丙醇胺醚1-6份、纳米氧化镧1-4份、十二烷基三甲基氯化铵1-5份、硅烷偶联剂KH5705-9份、邻苯二甲酸二辛酯2-7份、生物助剂6-10份；
制备方式：将上述的材料依次置于反应釜中混合均匀，升温至220-260℃，保温搅拌1～2h，得到混合料静置备用；然后加入重量份30份的去离子水且降温到100-120℃，混合搅拌至形成流动性好的浆体；
所述生物助剂包括以下重量份的材料制成，
连翘1份、拳参2份、贯众3份、牛黄4份、射干5份、白蔹6份、白花蛇舌草7份、紫花地丁1份、羚羊角2份、黄药子3份、鸡矢藤4份；
制备方式为：制备方式为：将上述的材料放在85-95℃的烘干设备中平铺，然后烘干4-5个小时，然后放入研磨设备中研磨成粉末状即可；
所述混合料包括以下重量份的材料制成，
氨基树脂19-24份、改性海泡石粉5-11份、纳米二氧化钛2-7份、甲乙酮5-9份、邻苯二甲酸二辛酯1-4份、海藻酸钠1-5份、甲基丙二醇1-6份、2-甲基咪唑1-5份、木质素磺酸1-3份、去离子水25-30份；
制备方式：将上述的材料放入反应釜中，然后升温至170-200℃，保温搅拌1～2h，得到混合浆料；然后将浆料压入三辊机中，研磨至粒径小于20μm，装罐即可；
所述改性海泡石粉的制备方式为：将海泡石研磨且过300-400目筛，然后加入脂肪醇聚氧乙烯醚在常温下搅拌混合10min，然后升温至80-85℃保温研磨30min，再加水搅拌制成固含量达到25-35％的溶液，所得混合液送入喷雾干燥机中干燥，制得20-40目的球形颗粒，并于100-110℃下烘干；
所述脂肪醇聚氧乙烯醚与海泡石的质量比为1：4.1；
所述棉线为人造棉或者混纺棉中的一种。
通过实验，测定本发明实施例1-3与普通混纺棉的性能与效果，如下表：
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (3)

1.一种提高棉线韧性的方法，其特征在于：包括以下操作步骤，
步骤一、选取材料：选取已经制备好的棉线，然后放在清水中浸泡25-35分钟，然后放在干燥、温度为50-60℃的房间中静置，直至水分消失；
步骤二、初次浸泡：将静置后的棉线取出然后放入一份浸泡液中浸泡2-3个小时；
步骤三、混合材料：将浸泡后的棉线放入设备中，且加入混合料然后震荡混合30-45分钟；
步骤四、进行除杂：将混合后的材料放置在振动筛网上进行震荡筛选，将多余的料震荡除去；
步骤五、再次浸泡：将震荡后的材料放入另一份浸泡液中浸泡2-3个小时；
步骤六、进行除液：将浸泡后的材料放入干燥、温度为65-75℃的房间中静置，直至水分消失。
2.根据权利要求1所述的一种提高棉线韧性的方法，其特征在于：所述浸泡液包括以下重量份的材料制成，
聚乙烯树脂13-17份、水性丙烯酸乳液7-11份、、聚氧乙烯聚氧丙醇胺醚1-6份、纳米氧化镧1-4份、十二烷基三甲基氯化铵1-5份、硅烷偶联剂KH5705-9份、邻苯二甲酸二辛酯2-7份、生物助剂6-10份；
制备方式：将上述的材料依次置于反应釜中混合均匀，升温至220-260℃，保温搅拌1～2h，得到混合料静置备用；然后加入重量份30份的去离子水且降温到100-120℃，混合搅拌至形成流动性好的浆体。
3.根据权利要求1所述的一种提高棉线韧性的方法，其特征在于：所述混合料包括以下重量份的材料制成，
氨基树脂19-24份、改性海泡石粉5-11份、纳米二氧化钛2-7份、甲乙酮5-9份、邻苯二甲酸二辛酯1-4份、海藻酸钠1-5份、甲基丙二醇1-6份、2-甲基咪唑1-5份、木质素磺酸1-3份、去离子水25-30份；
制备方式：将上述的材料放入反应釜中，然后升温至170-200℃，保温搅拌1～2h，得到混合浆料；然后将浆料压入三辊机中，研磨至粒径小于20μm，装罐即可。
CN201810401594.5A 2018-04-28 2018-04-28 一种提高棉线韧性的方法 Pending CN108797121A (zh)