CN108795338A - 含有多官能团化合物的丙烯酸酯压敏胶及其制备方法 - Google Patents

含有多官能团化合物的丙烯酸酯压敏胶及其制备方法 Download PDF

Info

Publication number
CN108795338A
CN108795338A CN201710291895.2A CN201710291895A CN108795338A CN 108795338 A CN108795338 A CN 108795338A CN 201710291895 A CN201710291895 A CN 201710291895A CN 108795338 A CN108795338 A CN 108795338A
Authority
CN
China
Prior art keywords
parts
sensitive adhesive
agent
polyfunctional compound
containing polyfunctional
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710291895.2A
Other languages
English (en)
Inventor
贾桂花
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201710291895.2A priority Critical patent/CN108795338A/zh
Publication of CN108795338A publication Critical patent/CN108795338A/zh
Pending legal-status Critical Current

Abstract

本发明公开了含有多官能团化合物的丙烯酸酯压敏胶，属于压敏胶技术领域，包括以下重量份数的原料：丙烯酸丁酯70～90份、甲基丙烯酸缩水甘油酯30～50份、萜烯树脂10～20份、丙烯酸4～7份、硫化剂1～3份、硅橡胶4～8份、软化剂5～10份、补强剂5～10份、防老剂4～7份；补强剂为汽油‑甲苯混合溶剂或者甘油；软化剂为松香脂。本发明还公开了该含有多官能团化合物的丙烯酸酯压敏胶的制备方法。本发明的含有多官能团化合物的丙烯酸酯压敏胶，其独特的配方使其兼具耐高温耐酸碱和耐低温的特性，硬度适中，耐磨性和耐疲劳性都能符合要求；该压敏胶的制备方法，简单环保，制备的压敏胶能符合使用要求，经久耐用，具备很好的经济效益和实用性。

Description

含有多官能团化合物的丙烯酸酯压敏胶及其制备方法
技术领域
本发明属于压敏胶技术领域，具体涉及含有多官能团化合物的丙烯酸酯压敏胶及其制备方法。
背景技术
压敏胶粘剂的简称。是一类具有对压力有敏感性的胶粘剂。主要用于制备压敏胶带。
压敏胶的粘附力(胶粘带与被粘表面加压粘贴后所表现的剥离力)必须大于粘着力(即所谓用手指轻轻接触胶粘带时显示出来的手感粘力)。按其主要成分可分为橡胶型和树脂型两类。除主要成分外，还要加入其他辅助成分，如增粘树脂、增塑剂、填料、粘度调整剂、硫化剂、防老剂、溶剂等配合而成。
发明内容
发明目的：本发明的目的在于提供含有多官能团化合物的丙烯酸酯压敏胶，使其性能优越，同时兼具耐高温耐酸碱和耐低温，硬度适中，耐磨性和耐疲劳性都能符合要求；本发明的另一目的是提供该含有多官能团化合物的丙烯酸酯压敏胶的制备方法。
技术方案：为实现上述发明目的，本发明采用如下技术方案：
含有多官能团化合物的丙烯酸酯压敏胶，包括以下重量份数的原料：丙烯酸丁酯70～90份、甲基丙烯酸缩水甘油酯30～50份、萜烯树脂10～20份、丙烯酸4～7份、硫化剂1～3份、硅橡胶4～8份、软化剂5～10份、补强剂5～10份、防老剂4～7份；所述的补强剂为汽油-甲苯混合溶剂或者甘油；所述的软化剂为松香脂。
所述的原料还包括重量份数为5～10份的陶土或者碳酸钙。
所述的防老剂为甘油。
所述的硫化剂为硫磺。
所述的含有多官能团化合物的丙烯酸酯压敏胶的制备方法，包括以下步骤：
1)按照比例将丙烯酸丁酯在55～60℃进行塑炼；将甲基丙烯酸缩水甘油酯和萜烯树脂在75～80℃进行一段混炼；将塑炼后的丙烯酸丁酯加入一段混炼的混合物中在80～90℃进行二段混炼，得到混炼完毕的混合物；
2)向混炼完毕的混合物中加入丙烯酸、硫化剂、硅橡胶、软化剂和防老剂，于200℃-220℃，压力11～13Mpa下反应20min中再加入补强剂后热压成型23～28min。
所述的塑炼时间为30～50分钟，所述的一段混炼时间为40～60分钟，所述的二段混炼的时间为30～40分钟。
发明原理：在制备之前，丙烯酸丁酯必须进行塑炼；不添加大量软化剂、增塑剂的原因是因为配方中加入了合成橡胶。丙烯酸丁酯和甲基丙烯酸缩水甘油酯的共混物加入萜烯树脂，使其具有半有效的硫化体系，可以使得胶料的阻尼性能好，配合其他配方，使得其兼具耐低温性能。
有益效果：与现有技术相比，本发明的含有多官能团化合物的丙烯酸酯压敏胶，其独特的配方使得其兼具耐高温耐酸碱和耐低温的特性，硬度适中，耐磨性和耐疲劳性都能符合要求；该压敏胶的制备方法，简单环保，制备的压敏胶能符合使用要求，经久耐用，具备很好的经济效益和实用性。
具体实施方式
下面结合具体实施方式对本发明做进一步的说明。
实施例1含有多官能团化合物的丙烯酸酯压敏胶a
含有多官能团化合物的丙烯酸酯压敏胶，包括以下重量份数的原料：丙烯酸丁酯70份、甲基丙烯酸缩水甘油酯30份、萜烯树脂10份、丙烯酸2份、硫化剂1份、硅橡胶4份、软化剂5份、补强剂5份、防老剂2份；补强剂为汽油-甲苯混合溶剂；软化剂为松香脂。原料还包括重量份数为5份的碳酸钙。防老剂为甘油。硫化剂为硫磺。
含有多官能团化合物的丙烯酸酯压敏胶的制备方法：包括以下步骤：
1)按照比例将丙烯酸丁酯在55℃进行塑炼；将甲基丙烯酸缩水甘油酯和萜烯树脂在75℃进行一段混炼；将塑炼后的丙烯酸丁酯加入一段混炼的混合物中在80℃进行二段混炼，得到混炼完毕的混合物；2)向混炼完毕的混合物中加入丙烯酸、硫化剂、硅橡胶、软化剂和防老剂，于180℃，压力11Mpa下反应20min中再加入补强剂后热压成型23min，制得含有多官能团化合物的丙烯酸酯压敏胶a。含有多官能团化合物的丙烯酸酯压敏胶的制备方法，塑炼时间为30分钟，所述的一段混炼时间为40分钟，所述的二段混炼的时间为30分钟。
实施例2含有多官能团化合物的丙烯酸酯压敏胶b
含有多官能团化合物的丙烯酸酯压敏胶，包括以下重量份数的原料：丙烯酸丁酯90份、甲基丙烯酸缩水甘油酯50份、萜烯树脂20份、丙烯酸3份、硫化剂3份、硅橡胶8份、软化剂10份、补强剂10份、防老剂3份；补强剂为甘油；软化剂为松香脂。原料还包括重量份数为10份的陶土。防老剂为甘油。硫化剂为硫磺。
含有多官能团化合物的丙烯酸酯压敏胶的制备方法：包括以下步骤：
1)按照比例将丙烯酸丁酯在60℃进行塑炼；将甲基丙烯酸缩水甘油酯和萜烯树脂在80℃进行一段混炼；将塑炼后的丙烯酸丁酯加入一段混炼的混合物中在90℃进行二段混炼，得到混炼完毕的混合物；2)向混炼完毕的混合物中加入丙烯酸、硫化剂、硅橡胶、软化剂和防老剂，于200℃，压力13Mpa下反应20min中再加入补强剂后热压成型28min，制得含有多官能团化合物的丙烯酸酯压敏胶b。含有多官能团化合物的丙烯酸酯压敏胶的制备方法，所述的塑炼时间为50分钟，所述的一段混炼时间为60分钟，所述的二段混炼的时间为40分钟。
实施例3含有多官能团化合物的丙烯酸酯压敏胶c
含有多官能团化合物的丙烯酸酯压敏胶，包括以下重量份数的原料：丙烯酸丁酯80份、甲基丙烯酸缩水甘油酯40份、萜烯树脂15份、丙烯酸2.5份、硫化剂2份、硅橡胶6份、软化剂8份、补强剂8份、防老剂2.5份；补强剂为甘油；软化剂为松香脂。原料还包括重量份数为8份的碳酸钙。防老剂为甘油。硫化剂为硫磺。
含有多官能团化合物的丙烯酸酯压敏胶的制备方法：包括以下步骤：
1)按照比例将丙烯酸丁酯在58℃进行塑炼；将甲基丙烯酸缩水甘油酯和萜烯树脂在78℃进行一段混炼；将塑炼后的丙烯酸丁酯加入一段混炼的混合物中85℃进行二段混炼，得到混炼完毕的混合物；2)向混炼完毕的混合物中加入丙烯酸、硫化剂、硅橡胶、软化剂和防老剂，于190℃，压力12Mpa下反应20min中再加入补强剂后热压成型25min，制得含有多官能团化合物的丙烯酸酯压敏胶c。含有多官能团化合物的丙烯酸酯压敏胶的制备方法，所述的塑炼时间为40分钟，所述的一段混炼时间为50分钟，所述的二段混炼的时间为35分钟。
实施例4性能测试
将实施例1～3中制备的含有多官能团化合物的丙烯酸酯压敏胶a、含有多官能团化合物的丙烯酸酯压敏胶b和含有多官能团化合物的丙烯酸酯压敏胶c在常温下进行耐高温和耐酸碱测试，发现这些含有多官能团化合物的丙烯酸酯压敏胶的寿命延长了四倍。

Claims (6)

1.含有多官能团化合物的丙烯酸酯压敏胶，其特征在于：包括以下重量份数的原料：丙烯酸丁酯70～90份、甲基丙烯酸缩水甘油酯30～50份、萜烯树脂10～20份、丙烯酸4～7份、硫化剂1～3份、硅橡胶4～8份、软化剂5～10份、补强剂5～10份、防老剂4～7份；所述的补强剂为汽油-甲苯混合溶剂或者甘油；所述的软化剂为松香脂。
2.根据权利要求1所述的含有多官能团化合物的丙烯酸酯压敏胶，其特征在于：所述的原料还包括重量份数为5～10份的陶土或者碳酸钙。
3.根据权利要求1所述的含有多官能团化合物的丙烯酸酯压敏胶，其特征在于：所述的防老剂为甘油。
4.根据权利要求1所述的含有多官能团化合物的丙烯酸酯压敏胶，其特征在于：所述的硫化剂为硫磺。
5.权利要求1～4中任意一项所述的含有多官能团化合物的丙烯酸酯压敏胶的制备方法，其特征在于：包括以下步骤：
1)按照比例将丙烯酸丁酯在55～60℃进行塑炼；将甲基丙烯酸缩水甘油酯和萜烯树脂在75～80℃进行一段混炼；将塑炼后的丙烯酸丁酯加入一段混炼的混合物中在80～90℃进行二段混炼，得到混炼完毕的混合物；
2)向混炼完毕的混合物中加入丙烯酸、硫化剂、硅橡胶、软化剂和防老剂，于200℃-220℃，压力11～13Mpa下反应20min中再加入补强剂后热压成型23～28min。
6.根据权利要求5所述的含有多官能团化合物的丙烯酸酯压敏胶的制备方法，其特征在于：所述的塑炼时间为30～50分钟，所述的一段混炼时间为40～60分钟，所述的二段混炼的时间为30～40分钟。
CN201710291895.2A 2017-04-28 2017-04-28 含有多官能团化合物的丙烯酸酯压敏胶及其制备方法 Pending CN108795338A (zh)